CN102199801A - 高强无捻聚酯单丝多级牵伸工艺 - Google Patents
高强无捻聚酯单丝多级牵伸工艺 Download PDFInfo
- Publication number
- CN102199801A CN102199801A CN 201110159464 CN201110159464A CN102199801A CN 102199801 A CN102199801 A CN 102199801A CN 201110159464 CN201110159464 CN 201110159464 CN 201110159464 A CN201110159464 A CN 201110159464A CN 102199801 A CN102199801 A CN 102199801A
- Authority
- CN
- China
- Prior art keywords
- strength
- pair
- entering
- polyester filament
- drafting process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及高强无捻聚酯单丝多级牵伸工艺，属于高分子纤维功能材料技术领域。高强无捻聚酯单丝生产工艺技术流程如下：湿料斗—>切片增粘—>在密封条件下的干切片料斗—>螺杆挤出机熔融纺丝—>上油—>第一对热辊—>第二对热辊—>第三对热定型辊—>导丝盘—>卷绕成型—>包装。本发明优点：本项目创新研究采用一步法制造工艺技术，具有技术先进，生产效率高，产品质量如纤度均匀、强度高、条干好，节能降耗效果显著等特点。产品的高附加值，可大大提升企业的盈利水平，提高行业经济效率和市场竞争能力，对企业的可持续发展起到积极的推动作用。
Description
技术领域
本发明涉及高强无捻聚酯单丝多级牵伸工艺，属于高分子纤维功能材料技术领域。
背景技术
近年来，日本集成研究、开发IT产业用高强无捻聚酯单丝的工艺发展极快。它已经不仅仅作为印刷筛网用，而是作为高档印花筛网和IT产业线路板在诸多性能方面独特性，作为新材料而大大超越以往的应用领域。据估算，今后几年内世界需求量年增长率约在20-25%左右。随着市场向亚洲转移，国内也有非常大的潜在市场，目前国内IT产业用高强无捻聚酯单丝市场需求量大约在1000吨/年以上，即1000吨以上的市场需求，预计今后几年内需求量将会以20％的年增长率迅速扩大。为满足生产总量继续增长和产品质量不断提高的双重需要，尽快提高我国IT产业用高强无捻聚酯单丝的技术水平创新能力，有效替代进口是当务之急，这也正是我国IT产业用高强无捻聚酯单丝业面临的重大任务。
我国现存的IT产业用高强无捻聚酯单丝是采用两步法生产，设备陈旧、产量低、强度低而且纤维的条干不好，不能满足日益发展IT产业用。
发明内容
为了克服上述的不足，本发明采取的技术方案如下：
采用单孔喷丝板、三对热辊加导丝盘牵伸技术，纤度均匀、强力高、沸水收缩率低、适应多品种的特点。
高强无捻聚酯单丝生产工艺技术流程如下：
湿料斗—>切片增粘—>在密封条件下的干切片料斗—>螺杆挤出机熔融纺丝—>上油—> 第一对热辊—>第二对热辊—>第三对热定型辊—>导丝盘—>卷绕成型—>包装。
工艺路线说明：切片必须进行结晶、干燥、增粘后，切片经密封的干切片料斗进入螺杆挤出机熔融挤出，由熔体管道进入纺丝箱体，纺丝箱体中进行分配、计量，各自形成若干股流量完全相等的熔体支流，进入纺丝组件，经喷丝板喷出，形成熔体细流，经侧吹风对吹冷却凝固，再经纺丝甬道进入上油装置，通过导丝器进入第一对热辊，在第一对热辊缠绕一定的圈数后进入第二对热辊，丝在一棍和二辊之间有一定的牵伸，在二辊绕一定的圈数后进入第三对热定型辊，在三辊经过热定型的丝进入导丝盘，通过导丝盘进入卷绕机卷绕成型。
本发明的关键技术与创新点：
本发明的核心是①切片增粘纺丝的工艺，湿切片经过结晶，干燥后在一定的温度和时间内进行增粘，粘度要求均一，因为这是保证纺丝顺利进行的关键所在，也对成品的物理指标起关键的作用。它的原理是：切片结晶温度和时间的控制、切片干燥时间的控制、最主要的是切片增粘温度、时间和真空度的控制。 ②牵伸速度和温度及牵伸倍数等工艺条件，一辊的速度和温度及一辊和二辊的速度差决定牵伸倍数，决定丝的强力和伸长，二辊的温度和三辊的温度的控制决定丝的各项物理指标能不能达到到用户的要求。目前这两项技术在国内尚属空白，预期项目主要技术经济指标 达到或超过国际先进水平。单丝的牵伸速度和温度的控制技术填补国内空白。
本发明优点：本项目创新研究采用一步法制造工艺技术，具有技术先进，生产效率高，产品质量如纤度均匀、强度高、条干好，节能降耗效果显著等特点。产品的高附加值，可大大提升企业的盈利水平，提高行业经济效率和市场竞争能力，对企业的可持续发展起到积极的推动作用。
具体实施方式
本发明采取的技术方案如下：
采用单孔喷丝板、三对热辊加导丝盘牵伸技术，纤度均匀、强力高、沸水收缩率低、适应多品种的特点。
高强无捻聚酯单丝生产工艺技术流程如下：
湿料斗—>切片增粘—>在密封条件下的干切片料斗—>螺杆挤出机熔融纺丝—>上油—> 第一对热辊—>第二对热辊—>第三对热定型辊—>导丝盘—>卷绕成型—>包装。
工艺路线说明：切片必须进行结晶、干燥、增粘后，切片经密封的干切片料斗进入螺杆挤出机熔融挤出，由熔体管道进入纺丝箱体，纺丝箱体中进行分配、计量，各自形成若干股流量完全相等的熔体支流，进入纺丝组件，经喷丝板喷出，形成熔体细流，经侧吹风对吹冷却凝固，再经纺丝甬道进入上油装置，通过导丝器进入第一对热辊，在第一对热辊缠绕一定的圈数后进入第二对热辊，丝在一棍和二辊之间有一定的牵伸，在二辊绕一定的圈数后进入第三对热定型辊，在三辊经过热定型的丝进入导丝盘，通过导丝盘进入卷绕机卷绕成型。
Claims (1)
1.高强无捻聚酯单丝多级牵伸工艺，其特征在于：生产工艺技术流程如下：湿料斗—>切片增粘—>在密封条件下的干切片料斗—>螺杆挤出机熔融纺丝—>上油—>第一对热辊—>第二对热辊—>第三对热定型辊—>导丝盘—>卷绕成型—>包装。