CN102199777A - Formula of magnesium alloy surface washing liquid - Google Patents
Formula of magnesium alloy surface washing liquid Download PDFInfo
- Publication number
- CN102199777A CN102199777A CN 201010131861 CN201010131861A CN102199777A CN 102199777 A CN102199777 A CN 102199777A CN 201010131861 CN201010131861 CN 201010131861 CN 201010131861 A CN201010131861 A CN 201010131861A CN 102199777 A CN102199777 A CN 102199777A
- Authority
- CN
- China
- Prior art keywords
- magnesium alloy
- formula
- whiten
- alloy
- alloy surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a formula of a magnesium alloy surface washing liquid, which mainly comprises the following components of: 40-99% of phosphoric acid, 0.01-0.1% of complexing agent and 0.9-59.99% of solvent. Using the formula to clean the surface of a magnesium alloy product can increase washing speed, shorten washing time, save labor hour and lower production cost; the raw materials for the formula have low harm to operators; and the formula can quickly wash away acid mud and oxides on the surface of a magnesium alloy to obtain the magnesium alloy product with brilliant white and uniform color, and simultaneously provide the surface with a uniform structure for the post-treatment of the magnesium alloy.
Description
[technical field]
The present invention relates to a kind of Mg alloy surface and whiten liquid formula, specially refer to the prescription that whitens liquid after a kind of Mg alloy surface etching.
[background technology]
Magnesium alloy application at present is very extensive, and its use range comprises motorcycle, portable type hand-operated tools, camera component and notebook computer shell.Domestic had the company and the turnout of a lot of production magnesium alloy notebook computer shells bigger, and this is that along with development of times, the portable magnesium-alloy material is with widespread use more because magnesium alloy has light and advantage such as to reclaim caused.
Because magnesium alloy is more active, be easy to generate the surface that one deck smut remains in workpiece after the etching, this will bring difficulty to aftertreatment, it will influence the outward appearance of product surface simultaneously, and etching part is owing to become with strong acid response organization that microcosmic is uneven to be there are differences with etching part not, so by carrying out whitening technique, can reduce the difference between them, for aftertreatment provides the relatively surface of homogeneous of condition of surface, etching demoulding institute residuals can be removed clean simultaneously, and the existing method that whitens mostly adopts and manually carries out wiping with rag or hairbrush, so that the smut of removing after the etching is residual, this method has been wasted great amount of manpower, material resources, the length that expends time in, and removing is clean inadequately.
[summary of the invention]
In view of this, the purpose of this invention is to provide a kind of Mg alloy surface and whiten liquid formula, utilize this prescription the magnesium-alloy material surface to be cleaned to have the speed of whitening fast, the time weak point can be saved man-hour, reduced production cost simultaneously, the raw materials used harm to operator of should filling a prescription simultaneously is little, and the sour mud and the oxide compound of flush away Mg alloy surface fast, the acquisition outward appearance is a brilliant white, the magnesium-alloy material of color even, the while also can provide the surface of weave construction homogeneous for the aftertreatment of magnesium alloy.
For achieving the above object, propose a kind of Mg alloy surface and whiten liquid formula, it mainly comprises:
Phosphatase 24 0-99%;
Complexing agent 0.01-0.1%;
Solvent 0.9-59.99%.
Preferably, described complexing agent is 6-hexylidene triamine pentamethylene phosphonic acids, Amino Trimethylene Phosphonic Acid, 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid or other organic phospho acids.
Compared to prior art, Mg alloy surface of the present invention whitens liquid formula, and it is fast that it whitens speed, and the time pipe nipple is man-hour approximately, has reduced production cost simultaneously, fast the sour mud and the oxide compound of flush away Mg alloy surface.
[embodiment]
Further specify the present invention below by embodiment.
Embodiment 1
Be configured according to following prescription and whiten liquid:
Phosphoric acid (85%) 90%;
6-hexylidene triamine pentamethylene phosphonic acids 0.02%;
Water 9.98%.
In present embodiment, utilize this to whiten liquid and be 15-25 ℃ whitening temperature, whiten the mode of soaking that adopts, whiten in time of 30 seconds can quick flush away Mg alloy surface sour mud and oxide compound, the acquisition outward appearance is a brilliant white, the magnesium-alloy material of color even, the while also can provide the surface of weave construction homogeneous for the aftertreatment of magnesium alloy.
Embodiment 2
Be configured according to following prescription and whiten liquid:
Phosphoric acid (85%) 40%;
Amino Trimethylene Phosphonic Acid 0.02%;
Water 59.98%.
In present embodiment, utilize this to whiten liquid and be 15-25 ℃ whitening temperature, whiten the mode of soaking that adopts, whiten in time of 20 seconds can quick flush away Mg alloy surface sour mud and oxide compound, the acquisition outward appearance is a brilliant white, the magnesium-alloy material of color even, the while also can provide the surface of weave construction homogeneous for the aftertreatment of magnesium alloy.
Embodiment 3
Be configured according to following prescription and whiten liquid:
Phosphoric acid (85%) 99%;
1-Hydroxy Ethylidene-1,1-Diphosphonic Acid 0.02%;
Water 0.98%.
In present embodiment, this phosphoric acid (85%) is industry phosphoric acid (section selects the phosphoric acid of other concentration for use among other embodiment), utilize this to whiten liquid and be 15-25 ℃ whitening temperature, whiten the mode of soaking that adopts, whiten in time of 20 seconds can quick flush away Mg alloy surface sour mud and oxide compound, the acquisition outward appearance is a brilliant white, the magnesium-alloy material of color even, and the while also can provide the surface of weave construction homogeneous for the aftertreatment of magnesium alloy.
In addition, complexing agent of the present invention also can be phosphonic acids butane-1,2 in other embodiment, 4-tricarboxylic acid, 2-HPAA, 2-phosphonic acids butane-1,2,4-tricarboxylic acid.
The above is preferred embodiment of the present invention only, is not to be used for limiting practical range of the present invention, and is every according to equivalence variation and modification that the present invention did, is all covered by the scope of claims of the present invention.
Claims (6)
1. a Mg alloy surface whitens liquid formula, it is characterized in that, mainly comprises:
Phosphatase 24 0-99%;
Complexing agent 0.01-0.1%;
Solvent 0.9-59.99%.
2. Mg alloy surface as claimed in claim 1 whitens liquid formula, it is characterized in that, mainly comprises: described complexing agent is 6-hexylidene triamine pentamethylene phosphonic acids, Amino Trimethylene Phosphonic Acid, 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid or other organic phospho acids.
3. Mg alloy surface as claimed in claim 1 whitens liquid formula, it is characterized in that, mainly comprises: described solvent is a water.
4. whiten liquid formula as claim 1,2 or 3 described Mg alloy surfaces, it is characterized in that, mainly comprise:
Phosphoric acid (85%) 90%;
6-hexylidene triamine pentamethylene phosphonic acids 0.02%;
Water 9.98%.
5. whiten liquid formula as claim 1,2 or 3 described Mg alloy surfaces, it is characterized in that, mainly comprise:
Phosphoric acid (85%) 40%;
Amino Trimethylene Phosphonic Acid 0.02%;
Water 59.98%.
6. whiten liquid formula as claim 1,2 or 3 described Mg alloy surfaces, it is characterized in that, mainly comprise:
Phosphoric acid (85%) 99%;
1-Hydroxy Ethylidene-1,1-Diphosphonic Acid 0.02%;
Water 0.98%.