CN102190460A - 钢化仿瓷涂料 - Google Patents

钢化仿瓷涂料 Download PDF

Info

Publication number
CN102190460A
CN102190460A CN 201010123606 CN201010123606A CN102190460A CN 102190460 A CN102190460 A CN 102190460A CN 201010123606 CN201010123606 CN 201010123606 CN 201010123606 A CN201010123606 A CN 201010123606A CN 102190460 A CN102190460 A CN 102190460A
Authority
CN
China
Prior art keywords
coating
water
parts
powder
polyvinyl acetate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010123606
Other languages
English (en)
Other versions
CN102190460B (zh
Inventor
梁振华
梁轩齐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201010123606 priority Critical patent/CN102190460B/zh
Publication of CN102190460A publication Critical patent/CN102190460A/zh
Application granted granted Critical
Publication of CN102190460B publication Critical patent/CN102190460B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种钢化仿瓷涂料，该涂料主要重量组分：甲基纤维素6～10，聚醋酸乙烯乳液50～80，氢氧化钙粉250～320，方解石粉250～320，颜料1～3，消泡剂0.05～0.5，余量为水。先加入聚醋酸乙烯乳液倍量的水稀释；并将甲基纤维素加入剩余量的水中溶解24～48小时，经分散、静置备用；将上述两种溶液加入分散机中混合，再加入颜料、消泡剂分散，最后加入氢氧化钙和方解石粉剂，待分散均匀后，经研磨制成仿瓷涂料。本发明涂料耐水擦洗，涂层不裂纹，耐水擦洗性能达到国家外墙涂料标准；具有表面光滑坚固耐用且环保，可防水、防火；成本低，易于远距离运输，存储期长等优点。

Description

钢化仿瓷涂料
技术领域
本发明涉及一种建筑装饰涂料，特别是一种钢化仿瓷涂料。
技术背景
传统涂料都是以各种树脂、聚合乳液等胶粘剂作为膜物，加上颜料、填料，辅以各种助剂而成。产品质量必须靠膜物来实现。相类似涂料中，普遍采用聚乙烯醇缩甲醛组为粘结成膜物，如97106666.3号“钢化仿瓷涂料”专利申请，是由聚乙烯醇、碳酸钙、三氧化镁·四氧化硅结晶水合物、甲酸胺、硅酸铝、4’4一二氨基苯乙烯二磺酸异氰酸苯酯、壬酸、甲醛、氨水和水组合成。这种厚质涂料没有光泽度，防水性很差，附着力不强，不能耐水擦洗；含有刺激气味微毒物质，危害人的健康。而用其它乳液作为膜物的厚质涂料，造价高，包装费用高，不能远距离运输、销售半径小，且储存期短，一般为15～30天，用户难以接受。
发明内容
本发明的目的在于能够克服上述技术存在的缺点。提供一种钢化仿瓷涂料。该仿瓷涂料具有耐水擦洗，涂层不裂纹，表面光滑坚固耐用且环保；成本低，易于远距离运输，存储期长等优点。
本发明以Ca(OH)2粉和方解石粉做填料，利用Ca(OH)2在空气中与CO2反应，生成CaCO3(方解石的成分)这一原理，来实现产品的质量达到防水性、硬度、附着力等指标。化学反应式为：
Ca(OH)2+CO2＝＝＝CaCO3↓+H2O
CaCO3是方解石的主要成分，与填料中的方解石粉在胶粘剂的作用下，能有机的结合成一体，施工时在压力(刮压)的作用下能缩小方解石微粒间的间距，增加致密度，待涂料中Ca(OH)2与空气中的CO2反应充分完全后，随着水分的蒸发，便形成了坚硬的CaCO3涂层。本发明用Ca(OH)2填料进行自然化学反应可大大提高产品质量。
本发明还应用了一种涂料中极不常用的有机化工原料：甲基纤维素作为主要粘结剂。这种原料有极高的粘结、保湿、润滑性能，使产品具有柔和、丰满的光度，并且性质稳定，遇强碱Ca(OH)2不絮凝，具有其它纤维素衍生物无法取代的优点，再配以少量的聚醋酸乙烯乳液以增强产品的附着力，并且聚醋酸乙烯乳液成膜后具有柔韧的弹性，能防止涂层裂纹的产生。
为实现上述目的，本发明钢化仿瓷涂料的主要组分及其重量份数为(以1000重量份配制)：
甲基纤维素粘度：勃氏4000-5000mp        6～10
聚醋酸乙烯乳液                         50～80
氢氧化钙粉                             250～320
方解石粉                               250～320
无机或群青颜料                         1～3
磷酸三丁酯消泡剂                       0.05～0.5
水                                     余量
按上述配量加入聚醋酸乙烯乳液一倍量的水稀释；并将甲基纤维素加入剩余量的水中溶解24～48小时，经分散、静置备用；将上述两种溶液加入分散机中混合，再加入颜料、消泡剂分散，最后加入氢氧化钙和方解石粉剂，待分散均匀后，经研磨制成钢化仿瓷涂料。
本发明采用粉剂填料中氢氧化钙粉、方解石粉的细度为500～800目。
本发明具有的优点和积极效果：1、与106涂料或ST涂料相比较，本发明产品具有极好的装饰性能，平滑如镜、光彩照人、光滑细腻、坚固如瓷；2、制造施工简单，运输费用低，销售半径大，成本低，每吨造价仅600～700元；3、产品耐水擦洗，耐水擦洗性能达到国家外墙涂料标准，坚固耐用且环保，可防水、防火、质量稳定。
具体实施方式
实施例1
配制1000kg涂料的原料用量：甲基纤维素(粘度：勃氏4000-5000mp)7kg，聚醋酸乙烯乳液70kg，氢氧化钙粉(800目)300kg，方解石粉(800目)300kg，群青2kg，磷酸三丁脂0.08kg，余量为水。
配制方法：
按上述配量加入聚醋酸乙烯乳液一倍量的水(140kg)稀释备用；并将甲基纤维素加入剩余量的水(约181kg)中溶解24～48小时，经分散机分散，静置备用；将上述两种溶液加入分散机中混合，再加入颜料、消泡剂分散，最后加入氢氧化钙和方解石粉剂，待分散均匀后，经三辊磨研磨制成钢化仿瓷涂料。
施工方法：
待墙体基层坚固、干燥后，用本品采用刮涂的方法，刮涂二至三遍，待涂层六～七成干时，再用薄钢片刮板批压一遍。
实施例2
配制1000kg涂料的原料用量：甲基纤维素(粘度：勃氏4000-5000mp)10kg，聚醋酸乙烯乳液80kg，氢氧化钙粉(500目)320kg，方解石粉(500目)320kg，群青3kg，磷酸三丁脂0.1kg，
余量为水。
配制和施工方法同实施例1。
实施例3
配制1000kg涂料的原料用量：甲基纤维素(粘度：勃氏4000-5000mp)8kg，聚醋酸乙烯乳液60kg，氢氧化钙粉(500目)280kg，方解石粉(500目)280kg，群青2kg，磷酸三丁脂0.2kg，
余量为水。
配制和施工方法同实施例1。

Claims (2)

1.一种钢化仿瓷涂料，其特征在于：以1000重量份配制，该涂料的主要组分及其重量份数为：
甲基纤维素粘度：勃氏4000-5000mp        6～10
聚醋酸乙烯乳液                         50～80
氢氧化钙粉                             250～320
方解石粉                               250～320
无机或群青颜料                         1～3
磷酸三丁酯消泡剂                       0.05～0.5
水                                     余量
按上述配量加入聚醋酸乙烯乳液一倍量的水稀释；并将甲基纤维素加入剩余量的水中溶解24～48小时，经分散、静置备用；将上述两种溶液加入分散机中混合，再加入颜料、消泡剂分散，最后加入氢氧化钙和方解石粉剂，待分散均匀后，经研磨制成钢化仿瓷涂料。
2.根据权利要求1所述的钢化仿瓷涂料，其特征在于：所述氢氧化钙粉、方解石粉的细度为500～800目。
CN 201010123606 2010-03-11 2010-03-11 钢化仿瓷涂料 Expired - Fee Related CN102190460B (zh)