CN102189442A - Grinding and polishing method for low-plasticity metal plate straps - Google Patents
Grinding and polishing method for low-plasticity metal plate straps Download PDFInfo
- Publication number
- CN102189442A CN102189442A CN2010101239045A CN201010123904A CN102189442A CN 102189442 A CN102189442 A CN 102189442A CN 2010101239045 A CN2010101239045 A CN 2010101239045A CN 201010123904 A CN201010123904 A CN 201010123904A CN 102189442 A CN102189442 A CN 102189442A
- Authority
- CN
- China
- Prior art keywords
- metal plate
- polishing
- belt
- inductile
- inductile metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a grinding and polishing method for low-plasticity metal plate straps. Different grinding media and polishing media are adopted for the low-plasticity metal plate straps made of different materials; and technologies such as grinding, polishing and the like are carried out on the low-plasticity metal so as to remove defects such as rolled stripping grains and the like on the upper surfaces and the lower surfaces of the plate straps, lead the upper surfaces and the lower surfaces of the plate straps to be bright and attractive, and further increase the corrosion resistance of the metal plate straps.
Description
Technical field
The present invention relates to a kind of sanding and polishing method of inductile metal plate and belt.
Background technology
Because inductile metal room temperature plastic deformation abilities such as magnesium are poor, its strip nearly all is hot rolling or warm-rolling finished product, rolling temperature all is higher than 200 ℃ usually, can't normally use the rolling mill practice lubricant medium, nearly all strip all is the dried material that rolls into, so its surface ratio is more coarse, must carry out the processing such as sanding and polishing on surface, just the such surfaces bright attractive in appearance of cold rolled sheet such as similar iron and steel, aluminium alloy can be arranged, can be for directly using.
Summary of the invention
To achieve these goals, the invention provides a kind of sanding and polishing method of inductile metal plate and belt, the inductile metal is implemented the stages such as grinding and buffing, the purpose of sanding and polishing is the rolling stroke of defective such as line of removing the strip upper and lower surface, make strip upper and lower surface light attractive in appearance, and then improve the corrosion resistance of inductile metal plate and belt.
The present invention includes following step:
A. the warm-rolling rolling with the inductile metal enters sander afterwards by the uncoiling supplied materials;
B. sander is with the certain linear velocity of polishing medium adapted of low mesh number, to the processing of polishing of inductile metal plate and belt upper and lower surface, is intended to remove visible rolling stroke of line of strip upper and lower surface;
C. purge inductile metal plate and belt surface with high-velocity fluid, promptly the method for fluid removal of contamination is removed polishing processing back at the remaining abrasive material of metal plate and belt upper and lower surface;
D. polishing machine uses the polishing medium greater than some order numbers among the step b to be equipped with certain linear velocity, and inductile metal plate and belt upper and lower surface is polished processing, makes inductile metal plate and belt upper and lower surface reach the effect of light attractive in appearance;
E. the inductile metal plate and belt of polishing is removed the polishing material that the surface finish of inductile metal plate and belt stays with the method for fluid removal of contamination, enter subsequent processing at last.
According to the material difference of inductile metal plate and belt, the material of described polishing medium is also different with the order number, and the material of polishing medium is also different with the order number, and the processing step of grinding and buffing increases and decreases to some extent.
The invention has the beneficial effects as follows: this method can be to inductile metal processing, and making has the strip surface of drawing the line defective to become light strip surface attractive in appearance after originally rolling, and then improve its corrosion resistance.
Description of drawings
Fig. 1 is a processing process schematic diagram of the present invention.
The specific embodiment
Be illustrated in figure 1 as the schematic diagram of processing process of the present invention, it comprises following step:
A. the warm-rolling rolling with the inductile metal enters sander afterwards by uncoiling supplied materials 1;
B. sander is with the certain linear velocity of polishing medium adapted of low mesh number, to 2 processing of polishing of inductile metal plate and belt upper and lower surface, is intended to remove visible rolling stroke of line of strip upper and lower surface;
C. purge inductile metal plate and belt surface with high-velocity fluid, promptly the method for fluid removal of contamination 3 is removed polishing 2 processing backs at the remaining abrasive material of metal plate and belt upper and lower surface;
D. polishing machine uses the polishing medium greater than some order numbers among the step b to be equipped with certain linear velocity, and inductile metal plate and belt upper and lower surface is polished 4 processing, makes inductile metal plate and belt upper and lower surface reach the effect of light attractive in appearance;
E. remove the polishing material that inductile metal plate and belt surface finish 4 stays to polishing the 4 inductile metal plate and belts of handling with the method for fluid removal of contamination 5, enter subsequent processing 6 at last.
Material difference according to strip, the material of polishing medium is also different with the order number, the material of polishing medium is also different with the order number, wherein pass through the processing of the inventive method, the inductile metal plate and belt can be removed the rolling stroke of defective such as line on surface, make product surface light attractive in appearance and then improve its erosion-resisting performance, wherein polishing can be divided into corase grind and two stages of fine grinding, and polishing fluid can be divided into thick throwing and thin two stages of throwing.Become winding as AZ31 magnesium alloy warm-rolling, under the condition that uncoiling supplied materials tension force is carried, roughly grind with certain linear velocity with 60-90 purpose sander earlier, blow away the remaining abrasive material of product surface with high velocity air again, carry out fine grinding with 100-150 purpose sander with certain linear velocity again, blow away the remaining abrasive material of product surface with high velocity air again.Visible rolling stroke of line of goods upper and lower surface mainly removed in polishing, forms the strip surface of no rolling stroke of line.Apply with polishing machine then and slightly throw with certain linear velocity with the polishing medium of compositions such as 150-230 order aluminium oxide or carborundum powder and burnishing oil wax, behind high pressure water washing, make product surface reach basic light effect attractive in appearance, carefully throw with certain linear velocity with the polishing medium of compositions such as 240-320 order aluminium oxide or carborundum powder and burnishing oil wax at last, make product surface reach complete light effect attractive in appearance.
Basic principle of the present invention, principal character and advantage of the present invention have more than been described.As usual; the present invention is not restricted to the described embodiments; that describes in the foregoing description and the specification just illustrates principle of the present invention; under the prerequisite that does not break away from core technology of the present invention and processing range; attached technological parameter of the present invention also needs respective change because of the variation of the inductile metal material trade mark, and these variations all belong to protection scope of the present invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (2)
1. an inductile metal plate and belt sanding and polishing method is characterized in that, comprises following step:
A. the warm-rolling rolling with the inductile metal enters sander afterwards by the uncoiling supplied materials;
B. sander is with the certain linear velocity of polishing medium adapted of low mesh number, to the processing of polishing of inductile metal plate and belt upper and lower surface, is intended to remove visible rolling stroke of line of strip upper and lower surface;
C. purge inductile metal plate and belt surface with high-velocity fluid, promptly the method for fluid removal of contamination is removed polishing processing back at the remaining abrasive material of metal plate and belt upper and lower surface;
D. polishing machine uses the polishing medium greater than some order numbers among the step b to be equipped with certain linear velocity, and inductile metal plate and belt upper and lower surface is polished processing, makes inductile metal plate and belt upper and lower surface reach the effect of light attractive in appearance;
E. the inductile metal plate and belt of polishing is removed the polishing material that the surface finish of inductile metal plate and belt stays with the method for fluid removal of contamination, enter subsequent processing at last.
2. inductile metal plate and belt sanding and polishing method as claimed in claim 1, it is characterized in that according to the material difference of inductile metal plate and belt, the material of described polishing medium is also different with the order number, the material of polishing medium is also different with the order number, and the processing step of grinding and buffing increases and decreases to some extent.