CN102180664A - Doped and modified ceramic capacitor material for voltage equalization of zinc oxide doped arrester - Google Patents
Doped and modified ceramic capacitor material for voltage equalization of zinc oxide doped arrester Download PDFInfo
- Publication number
- CN102180664A CN102180664A CN2010106030708A CN201010603070A CN102180664A CN 102180664 A CN102180664 A CN 102180664A CN 2010106030708 A CN2010106030708 A CN 2010106030708A CN 201010603070 A CN201010603070 A CN 201010603070A CN 102180664 A CN102180664 A CN 102180664A
- Authority
- CN
- China
- Prior art keywords
- percent
- capacitor material
- ceramic capacitor
- oxide
- arrester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a doped and modified ceramic capacitor material for voltage equalization of a zinc oxide doped arrester. The high-voltage ceramic capacitor material consists of 80 to 84 percent of strontium titanate (SrTiO3), 8 to 10 percent of bismuth oxide (BiO), 0.5 to 2 percent of titanium dioxid (TiO2), 0.1 to 1 percent of manganese dioxide (MnO2), 4 to 8 percent of yttrium oxide (Y2O3) and 3 to 5 percent of magnesium titanate (MgTiO3). Due to the formula, the solid capacitance limit of a SrTiO3 lattice is increased, intense peak shifting and widening effects are generated, the capacitance temperature characteristic is improved, the electric constant is increased to 2,500, the medium consumption is less than 0.0001, the change ratio of high-temperature stability capacitance is less than 10 percent along with the temperature change, and excellent lightning protecting and voltage equalizing effects are achieved.
Description
Technical field
The present invention relates to a kind of capacitance material, especially the higfh-tension ceramics capacitance material.
Background technology
Because thunderbolt the time is easy to generate High Temperature High Pressure, present high-voltage capacitance majority is lower in the hot operation temperature range, and rate of temperature change is too high when high temperature, can not satisfy in the equipment such as lightning rod and use, and it is little to hold limit limit admittedly.
Summary of the invention
Purpose of the present invention provides a kind of and is subjected to the solid appearance limit big, the higfh-tension ceramics capacitance material that stability is strong.
A kind of Zinc-Oxide Arrester of doping vario-property is all pressed and is used ceramic capacitor material, it is characterized in that by strontium titanate SrTiO
380~84%, bismuth oxide BiO8-10%, titanium dioxide TiO
20.5-2%, Manganse Dioxide MnO
20.1-1%, yttrium oxide Y
2O
34-8%, magnesium titanate MgTiO
3The high-pressure porcelain capacitor material that 3-5% forms.
Adopt this prescription, just can make and hold limit increase in the strontium titanate lattice admittedly, produce intensive and move peak and broadening effect, improve temperature characteristics of capacitance, improving electric constant simultaneously is 2500, dielectric loss is less than 0.0001, and the high-temperature stability capacity varies with temperature rate and diminishes in 10%, and good lightning-arrest all pressure effects are arranged.
Embodiment
During concrete enforcement, we are with strontium titanate SrTiO
3, bismuth oxide BiO, yttrium oxide Y
2O
3Press formula rate and mix the compression moulding of back adding polyvinyl alcohol, sintering obtains ceramic condenser in 1250 to 1400 degrees centigrade of scopes then.
When proportioning, we are at first with Strontium carbonate powder SrCO
3With titanium dioxide TiO
2, magnesium oxide MgO and titanium dioxide TiO
2According to certain proportioning, mix through ball milling, carry out drying, then at 1000 to 1200 degrees centigrade of synthetic strontium titanate SrTiO that obtain
3, magnesium titanate MgTiO
3Obtaining strontium titanate SrTiO
3, magnesium titanate MgTiO
3After, above-mentioned all the other materials etc. mix according to the proportioning stirring ball-milling, dilute with small amount of acetone, high-speed stirring (7000r/min) 20min, inorganic materials is fully disperseed, the polyvinyl alcohol of adding 8% carries out mist projection granulating, place 130 ℃ of baking oven 1h then, just can obtain the electrical condenser of this prescription, its specific inductivity is 2500, and dielectric loss is less than 0.0001, compressive strength is greater than 16KV/mm, temperature profile is when 200 spend, and electric capacitance change is not more than 10%, and is the high-performance negative temperature coefficient ceramics material of linear change.
Claims (3)
1. the Zinc-Oxide Arrester of a doping vario-property is all pressed and is used ceramic capacitor material, it is characterized in that by strontium titanate SrTiO
380~84%, bismuth oxide BiO8-10%, titanium dioxide TiO
20.5-2%, Manganse Dioxide MnO
20.1-1%, yttrium oxide Y
2O
34-8%, magnesium titanate MgTiO
3The high-pressure porcelain capacitor material that 3-5% forms.
2. the Zinc-Oxide Arrester of doping vario-property as claimed in claim 1 is all pressed and is used ceramic capacitor material, it is characterized in that strontium titanate SrTiO
3, bismuth oxide BiO, yttrium oxide Y
2O
3Press formula rate and mix the compression moulding of back adding polyvinyl alcohol, sintering obtains ceramic condenser in 1250 to 1400 degrees centigrade of scopes then.
3. the change zinc thunder arrester of doping vario-property as claimed in claim 1 is all pressed and is used ceramic capacitor material, it is characterized in that just Strontium carbonate powder SrCO
3With titanium dioxide TiO
2, magnesium oxide MgO and titanium dioxide TiO
2According to certain proportioning, mix through ball milling, carry out drying, then at 1000 to 1200 degrees centigrade of synthetic strontium titanate SrTiO that obtain
3, magnesium titanate MgTiO
3