CN102174745A - Mould-proof antibacterial braid processing method - Google Patents
Mould-proof antibacterial braid processing method Download PDFInfo
- Publication number
- CN102174745A CN102174745A CN 201110029084 CN201110029084A CN102174745A CN 102174745 A CN102174745 A CN 102174745A CN 201110029084 CN201110029084 CN 201110029084 CN 201110029084 A CN201110029084 A CN 201110029084A CN 102174745 A CN102174745 A CN 102174745A
- Authority
- CN
- China
- Prior art keywords
- processing method
- water
- antibacterial
- antimildew
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a mould-proof antibacterial braid processing method, which relates to the field of weaving. The production processing method comprises the following steps of: aerating 4.9 to 19.5 parts of water, 0.1 to 0.5 part of heterocycle derivate complex and 80 to 95 parts of spinning oil solution by using a pneumatic pump and stirring until the three materials are uniformly mixed; adsorbing the prepared water/heterocycle derivate complex/oil solution mixture on the surface of a fiber in an oil cooling process of a polypropylene fiber molding process, wherein most of water is volatilized because the surface temperature is about 100 to 180 DEG C which is relatively high when a polypropylene fiber is just molded; and performing warp dressing, buckle inserting and cloth weaving on the molded polypropylene fiber. By the method, the problem of mildewing of a braid product in the processes such as storage, marine transport and the like in the plum rain season can be solved on the basis of ensuring that production cost is nearly unchanged.
Description
Technical field:
The present invention relates to field of textiles, be specifically related to a kind of antimildew and antibacterial ribbon processing method.
Background technology:
Along with growth in the living standard, people are more and more higher to the requirement of textiles.Except to the price of textiles, comfortableness etc., various requirement is proposed also.It is exactly one of them that mildew-resistant requires.Wherein black-koji mould and spherical black wool bacterium are to cause the mouldy smelly main bacteria seed of textiles, and textiles has as follows at the method for antimildew and antibacterial at present:
In the antimildew and antibacterial method aspect the synthetic fiber: have in the fibre forming process, in the former master batch of fiber, add antibacterials, carry out spinning moulding, thereby obtain anti-bacterial fibre.As Chinese patent 00107688.4 is the core-skin composite spinning fiber that contains nano-scale silver powder; The antimildew and antibacterial fiber that Chinese patent 00100636.3 gets for chitosan derivatives and viscose co-blended spinning.
Antimildew and antibacterial function for finished fiber and fabric has the method for carrying out chemical surface treatment and coating.Coating process is after antiseptic and the binding agent mixing, carries out the coating covering at fiber or fabric face, and this method can directly influence the feel of fabric.As Chinese patent 96200511.8 is the antimicrobial of carrier for binding agent.
With respect to these articles for daily use of ribbon, above the whole bag of tricks all exists a common issue with, and that is exactly complex process, cost height.
Summary of the invention:
The purpose of this invention is to provide a kind of antimildew and antibacterial ribbon processing method, it can guarantee that the processing cost almost on the basis of invariable, has solved ribbon product mouldy problem in processes such as plum rain season storage, marine transportation.
In order to solve the existing problem of background technology, the present invention is by the following technical solutions: its production and processing method is: stir 4.9～19.5 parts of water, 0.1～0.5 part of Hete rocyclic derivatives compound, 80～95 parts of spinning by pulsometer with finish earlier (1) to its inflation, evenly mixes to the three; (2) oil cooling but in the operation on the polypropylene fibre moulding process, water/Hete rocyclic derivatives compound/finish the mixture for preparing is adsorbed on fiber surface, since during polypropylene fibre moulding just, higher about 100～180 ℃ of surface temperature, and the wherein most of water of general portion is volatilized; (3) with the polypropylene fibre after the moulding by warping, wear the button and weave cotton cloth and machine-shaping.
Described finish is to be prepared from by aliphatic acid polyethenoxy ether, castor oil polyoxyethylene ether, aliphatic alcohol polyoxyvinethene phosphate sylvite, polyethers.
Described Hete rocyclic derivatives compound is to be generated by oxine, the reaction of 2-sulfurio benzo thiazole compound.
The present invention has following beneficial effect: can guarantee that the processing cost almost on the basis of invariable, has solved ribbon product mouldy problem in processes such as plum rain season storage, marine transportation.
The specific embodiment:
This specific embodiment is by the following technical solutions: its production and processing method is: stir 4.9～19.5 parts of water, 0.1～0.5 part of Hete rocyclic derivatives compound, 80～95 parts of spinning by pulsometer with finish earlier (1) to its inflation, evenly mixes to the three; (2) oil cooling but in the operation on the polypropylene fibre moulding process, water/Hete rocyclic derivatives compound/finish the mixture for preparing is adsorbed on fiber surface, because during polypropylene fibre moulding just, higher about 100～180 ℃ of surface temperature is with wherein most of water is all volatilized; (3) with the polypropylene fibre after the moulding by warping, wear the button and weave cotton cloth and machine-shaping.
Described finish is to be prepared from by aliphatic acid polyethenoxy ether, castor oil polyoxyethylene ether, aliphatic alcohol polyoxyvinethene phosphate sylvite, polyethers.
Described Hete rocyclic derivatives compound is to be generated by oxine, the reaction of 2-sulfurio benzo thiazole compound.
This specific embodiment is by in the thermoplastic fibre process of manufacture, the Hete rocyclic derivatives compound is added in the finish, can guarantee that the processing cost almost on the basis of invariable, has solved ribbon product mouldy problem in processes such as plum rain season storage, marine transportation.
Claims (3)
1. antimildew and antibacterial ribbon processing method, the production and processing method that it is characterized in that it is: stir 4.9～19.5 parts of water, 0.1～0.5 part of Hete rocyclic derivatives compound, 80～95 parts of spinning by pulsometer with finish earlier (1) to its inflation, evenly mixes to the three; (2) oil cooling but in the operation on the polypropylene fibre moulding process, water/Hete rocyclic derivatives compound/finish the mixture for preparing is adsorbed on fiber surface, because during polypropylene fibre moulding just, higher about 100～180 ℃ of surface temperature is with wherein most of water is all volatilized; (3) with the polypropylene fibre after the moulding by warping, wear the button and weave cotton cloth and machine-shaping.
2. a kind of antimildew and antibacterial ribbon processing method according to claim 1 is characterized in that described finish is to be prepared from by aliphatic acid polyethenoxy ether, castor oil polyoxyethylene ether, aliphatic alcohol polyoxyvinethene phosphate sylvite, polyethers.
3. a kind of antimildew and antibacterial ribbon processing method according to claim 1 is characterized in that described Hete rocyclic derivatives compound is to be generated by oxine, the reaction of 2-sulfurio benzo thiazole compound.