CN102151929A - Vacuum brazing process of copper-aluminum (Cu-Al) pipe panel radiator - Google Patents
Vacuum brazing process of copper-aluminum (Cu-Al) pipe panel radiator Download PDFInfo
- Publication number
- CN102151929A CN102151929A CN 201110125716 CN201110125716A CN102151929A CN 102151929 A CN102151929 A CN 102151929A CN 201110125716 CN201110125716 CN 201110125716 CN 201110125716 A CN201110125716 A CN 201110125716A CN 102151929 A CN102151929 A CN 102151929A
- Authority
- CN
- China
- Prior art keywords
- vacuum
- copper
- fluid
- copper pipe
- vacuum brazing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a vacuum brazing process of a copper-aluminum (Cu-Al) pipe panel radiator. The vacuum brazing process is characterized by comprising the following steps: (1) milling a liquid infusion pipe groove on an aluminum plate, wherein, the shape of the liquid infusion pipe groove is matched with that of a copper pipe; (2) placing a brazing foil in the liquid infusion pipe groove, and then placing the copper pipe in the liquid infusion pipe groove; and (3) fixing and tightly pressing the aluminum plate by tooling, and then placing the aluminum plate in a vacuum furnace for welding under the conditions as follows: a. heating to 260-280 DEG C, and performing heat preservation for 1-1.5 hours under the vacuum degree of not less than 9.0*10<-3>Pa; b. heating to 365-375 DEG C, and performing heat preservation for 1-1.5 hours under the vacuum degree of not less than 5.6*10<-3>Pa; c. heating to 395-410 DEG C, performing heat preservation for 10-15 minutes, and powering off for cooling under the vacuum degree of not less than 5.6*10<-3>Pa; and d. cooling to 290-300 DEG C within 30-45 minutes after powering off, and finally taking out the aluminum plate from the furnace. In the process, the copper pipe is in a snake shape, and the liquid infusion pipe groove is also in a snake shape matched with the copper pipe. By utilizing the vacuum brazing process, problems such as poor working environments as well as post-welding deformation and troublesome treatment of the product are solved, and meanwhile the purposes of quantity production and product quality improvement are realized.
Description
Technical field
The present invention relates to a kind of vacuum brazing technique, especially a kind of vacuum brazing technique of copper aluminium tube plate type radiator belongs to copper aluminum pipe plate radiator and makes the field.
Background technology
For copper aluminum pipe plate radiator, realize that it is key problem in technology that dissimilar metal connects.Existing method of attachment is argon arc welding and gas brazing.Argon arc welding connects not only that labour intensity is big, poor working environment, and product postwelding easy deformation; Gas brazing connects not only inefficiency, and postwelding needs to clear up the residual brazing flux of product surface, avoids residual brazing flux that product is caused corrosion, more than two kinds of processes all be difficult for realizing producing in batches and forming the weld seams of densification.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, a kind of vacuum brazing technique of copper aluminium tube plate type radiator is provided, both solved the problem of poor working environment, solve the product post welding distortion again and handled the problem that bothers, realized batch process, the purpose of improving the quality of products simultaneously.
According to technical scheme provided by the invention, the vacuum brazing technique of described copper aluminium tube plate type radiator, feature is to comprise following processing step:
(1) mill out the fluid-through tube groove on aluminium sheet, the shape and the copper pipe of described fluid-through tube groove are complementary;
(2) in the fluid-through tube groove, place the solder paper tinsel, copper pipe is positioned in the fluid-through tube groove again;
(3) adopt frock to be fixed and clamped aluminium sheet, be placed in the vacuum drying oven and weld; The condition of described welding is:
A, be heated to 260 ~ 280 ℃ the insulation 1 ~ 1.5 hour, vacuum 〉=9.0 * 10
-3Pa;
B, be heated to 365 ~ 375 ℃ the insulation 1 ~ 1.5 hour, vacuum 〉=5.6 * 10
-3Pa;
C, be heated to 395 ~ 410 ℃ of insulations after 10 ~ 15 minutes, begin outage cooling, vacuum 〉=5.6 * 10
-3Pa;
D, outage are cooled to 290 ~ 300 ℃, and temperature fall time is 30 ~ 45min, comes out of the stove.
Described copper pipe is snakelike, described fluid-through tube groove for copper pipe be complementary snakelike.
Described solder paper tinsel is that the trade mark is the solder paper tinsel of Zn89AlCu.
Described frock comprises jig plate and lower press plate, and last jig plate and lower press plate are by bolting, and bolt is provided with spring, and spring is fixed on the bolt by nut.
The present invention had both solved the problem of poor working environment, had solved the product post welding distortion again and had handled the problem that bothers, and had realized batch process, the purpose of improving the quality of products simultaneously; Production efficiency height, low, the minimizing environmental pollution of labour intensity, and reduced weld defect, guaranteed product quality.
Description of drawings
Fig. 1 is the schematic diagram of aluminium sheet of the present invention.
Fig. 2 is the schematic diagram of frock of the present invention.
The specific embodiment
The invention will be further described below in conjunction with concrete drawings and Examples.
As shown in Figure 2: frock used in the present invention comprises jig plate 1 and lower press plate 2, and last jig plate 1 and lower press plate 2 are fixing by bolt 3, and bolt 3 is provided with spring 4, and spring 4 is fixed on the bolt 3 by nut 5.
Embodiment one: a kind of vacuum brazing technique of copper aluminium tube plate type radiator comprises following processing step:
(1) mill out snakelike fluid-through tube groove on aluminium sheet 6, the shape of described fluid-through tube groove and copper pipe 7 are complementary;
(2) placing the trade mark in the fluid-through tube groove is the solder paper tinsel 8 of Zn89AlCu, copper pipe 7 is positioned in the fluid-through tube groove, as shown in Figure 1 again;
(3) adopt frock to be fixed and clamped aluminium sheet 6, be placed in the vacuum drying oven and weld; The condition of described welding is:
A, be heated to 260 ℃ the insulation 1.5 hours, vacuum 〉=9.0 * 10
-3Pa;
B, be heated to 365 ℃ the insulation 1.5 hours, vacuum 〉=5.6 * 10
-3Pa;
C, be heated to 395 ℃ of insulations after 15 minutes, begin outage cooling, vacuum 〉=5.6 * 10
-3Pa;
D, outage are cooled to 290 ℃, and temperature fall time is 45min, comes out of the stove.
Embodiment two: a kind of vacuum brazing technique of copper aluminium tube plate type radiator comprises following processing step:
(1) mill out snakelike fluid-through tube groove on aluminium sheet 6, the shape of described fluid-through tube groove and copper pipe 7 are complementary;
(2) placing the trade mark in the fluid-through tube groove is the solder paper tinsel 8 of Zn89AlCu, copper pipe 7 is positioned in the fluid-through tube groove, as shown in Figure 1 again;
(3) adopt frock to be fixed and clamped aluminium sheet 6, be placed in the vacuum drying oven and weld; The condition of described welding is:
A, be heated to 280 ℃ the insulation 1 hour, vacuum 〉=9.0 * 10
-3Pa;
B, be heated to 375 ℃ the insulation 1 hour, vacuum 〉=5.6 * 10
-3Pa;
C, be heated to 410 ℃ of insulations after 10 minutes, begin outage cooling, vacuum 〉=5.6 * 10
-3Pa;
D, outage are cooled to 300 ℃, and temperature fall time is 30min, comes out of the stove.
Embodiment three: a kind of vacuum brazing technique of copper aluminium tube plate type radiator comprises following processing step:
(1) mill out snakelike fluid-through tube groove on aluminium sheet 6, the shape of described fluid-through tube groove and copper pipe 7 are complementary;
(2) placing the trade mark in the fluid-through tube groove is the solder paper tinsel 8 of Zn89AlCu, copper pipe 7 is positioned in the fluid-through tube groove, as shown in Figure 1 again;
(3) adopt frock to be fixed and clamped aluminium sheet 6, be placed in the vacuum drying oven and weld; The condition of described welding is:
A, be heated to 270 ℃ the insulation 1.2 hours, vacuum 〉=9.0 * 10
-3Pa;
B, be heated to 370 ℃ the insulation 1.2 hours, vacuum 〉=5.6 * 10
-3Pa;
C, be heated to 400 ℃ of insulations after 12 minutes, begin outage cooling, vacuum 〉=5.6 * 10
-3Pa;
D, outage are cooled to 295 ℃, and temperature fall time is 35min, comes out of the stove.
Claims (4)
1. the vacuum brazing technique of a copper aluminium tube plate type radiator is characterized in that, comprises following processing step:
(1) mill out the fluid-through tube groove on aluminium sheet, the shape and the copper pipe of described fluid-through tube groove are complementary;
(2) in the fluid-through tube groove, place the solder paper tinsel, copper pipe is positioned in the fluid-through tube groove again;
(3) adopt frock to be fixed and clamped aluminium sheet, be placed in the vacuum drying oven and weld; The condition of described welding is:
A, be heated to 260 ~ 280 ℃ the insulation 1 ~ 1.5 hour, vacuum 〉=9.0 * 10
-3Pa;
B, be heated to 365 ~ 375 ℃ the insulation 1 ~ 1.5 hour, vacuum 〉=5.6 * 10
-3Pa;
C, be heated to 395 ~ 410 ℃ of insulations after 10 ~ 15 minutes, begin outage cooling, vacuum 〉=5.6 * 10
-3Pa;
D, outage are cooled to 290 ~ 300 ℃, and temperature fall time is 30 ~ 45min, comes out of the stove.
2. the vacuum brazing technique of copper aluminium tube plate type radiator as claimed in claim 1 is characterized in that: described copper pipe is snakelike, described fluid-through tube groove for copper pipe be complementary snakelike.
3. the vacuum brazing technique of copper aluminium tube plate type radiator as claimed in claim 1 is characterized in that: described solder paper tinsel is that the trade mark is the solder paper tinsel of Zn89AlCu.
4. the vacuum brazing technique of copper aluminium tube plate type radiator as claimed in claim 1, it is characterized in that: described frock comprises jig plate (1) and lower press plate (2), last jig plate (1) and lower press plate (2) are fixing by bolt (3), bolt (3) is provided with spring (4), and spring (4) is fixed on the bolt (3) by nut (5).