CN102145997A - 一种含有钒铁渣的耐火浇注料 - Google Patents

一种含有钒铁渣的耐火浇注料 Download PDF

Info

Publication number
CN102145997A
CN102145997A CN2011101150958A CN201110115095A CN102145997A CN 102145997 A CN102145997 A CN 102145997A CN 2011101150958 A CN2011101150958 A CN 2011101150958A CN 201110115095 A CN201110115095 A CN 201110115095A CN 102145997 A CN102145997 A CN 102145997A
Authority
CN
China
Prior art keywords
vanadium iron
iron slag
refractory castable
aggregate
phase
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101150958A
Other languages
English (en)
Inventor
郝建璋
高坤
洪俊辉
黎建明
张金阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pangang Group Research Institute Co Ltd
Pangang Group Co Ltd
Original Assignee
Pangang Group Research Institute Co Ltd
Pangang Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pangang Group Research Institute Co Ltd, Pangang Group Co Ltd filed Critical Pangang Group Research Institute Co Ltd
Priority to CN2011101150958A priority Critical patent/CN102145997A/zh
Publication of CN102145997A publication Critical patent/CN102145997A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种含有钒铁渣的耐火浇注料。该含有钒铁渣的耐火浇注料包含粗骨料、细骨料和由钒铁渣细粉形成的结合剂。本发明的耐火浇注料的耐火性能优异，并且可以使大量的钒铁渣得到回收利用。

Description

一种含有钒铁渣的耐火浇注料
技术领域
本发明涉及一种耐火浇注料，具体地讲，涉及一种含有钒铁渣的耐火浇注料。
背景技术
目前，我国冶金工业快速地发展，耐火材料的消耗量越来越大，但可用于耐火材料的资源比较少。因此，科技人员一直致力于开发可用作耐火材料的资源。
此外，在利用钒钛磁铁矿冶炼钒铁时，会产生大量的钒铁渣。大量的钒铁渣堆积而无法得到回收利用，这不仅造成了环境的污染，而且造成资源的浪费。
发明内容
本发明的目的在于克服上述和/或其他方面的不足，而提供一种含有钒铁渣的新型耐火浇注料。
根据本发明的含有钒铁渣的耐火浇注料可以包含粗骨料、细骨料和由钒铁渣细粉形成的结合剂。
根据本发明的含有钒铁渣的耐火浇注料，粗骨料可以是粒度为2mm～10mm的钒铁渣骨料、高铝质骨料和铝镁质骨料中的至少一种。细骨料可以是粒度小于2mm的钒铁渣骨料、高铝质骨料和铝镁质骨料中的至少一种。结合剂的粒度可以为-325目。
根据本发明的含有钒铁渣的耐火浇注料，钒铁渣可以含有按重量百分比计的78％～83％的Al2O3、10％～17％的CaO、1.0％～2.5％的MgO、0.2％～0.8％的FeO、0.6％～0.8％的SiO2和1.3％～4.0％的钒氧化物。钒铁渣可以含有按体积百分比计的35％～40％的铝酸钙相、45％～55％的二铝酸一钙相、4％～7％的α-Al2O3相、7％～8％的玻璃质相、1％～3％的金属相和3％～5％的尖晶石相。
根据本发明的含有钒铁渣的耐火浇注料，含有钒铁渣的耐火浇注料可以包含按重量百分比计的30％～50％的粗骨料、20％～40％的细骨料和10％～30％的由钒铁渣细粉形成的结合剂。含有钒铁渣的耐火浇注料还可以含有按重量百分比计的5％～15％的碳化硅粉和5％～10％的石墨粉。
根据本发明的耐火浇注料的结合剂由耐火性能优异的钒铁渣细粉形成，因此，根据发明的耐火浇注料的耐火性能优异。此外，根据本发明的耐火浇注料的骨料可以由钒铁渣形成，因此，使大量的钒铁渣得到回收利用。
具体实施方式
下面将详细地描述根据本发明的示例性实施例。
根据本发明的耐火浇注料主要由粗骨料、细骨料和由钒铁渣细粉形成的结合剂形成。
本发明使用的钒铁渣包含按重量百分比计的78％～83％的Al2O3、10％～17％的CaO、1.0％～2.5％的MgO、0.2％～0.8％的FeO、0.6％～0.8％的SiO2和1.3％～4.0％的钒氧化物。此外，钒铁渣主要由按体积百分比计的35％～40％的铝酸钙相、45％～55％的二铝酸一钙相、4％～7％的α-Al2O3相、7％～8％的玻璃质相、1％～3％的金属相和3％～5％的尖晶石相组成。
下面将分别对粗骨料、细骨料和结合剂进行详细的描述。
根据本发明的耐火浇注料包含按重量百分比计的30％～50％的粗骨料、20％～40％的细骨料和10％～30％的由钒铁渣细粉形成的结合剂。
耐火浇注料的粗骨料可以是粒度为2mm～10mm的钒铁渣骨料、高铝质骨料和铝镁质骨料中的至少一种。耐火浇注料的细骨料可以是粒度小于2mm的钒铁渣骨料、高铝质骨料和铝镁质骨料中的至少一种。本发明使用的高铝质骨料含有按重量百分比计的45％～90％的氧化铝和10％-55％的二氧化硅。本发明使用的铝镁质骨料含有按重量百分比计的50％～80％的氧化铝和5％～30％的氧化镁。本领域的技术人员将认识到的是，所使用的高铝质骨料和铝镁质骨料的组分和含量不限于上述的组分和含量。此外，当钒铁渣用作粗骨料和/或细骨料时，可以将钒铁渣破碎粉磨至相应的粒度以得到钒铁渣细骨料和/或钒铁渣粗骨料。
按上述含量将上述粒度的粗骨料和细骨料进行混合时，粗骨料和细骨料因在耐火浇注料中堆积密实而可以很好地起到耐火浇注料骨架的作用。
本发明的耐火浇注料的结合剂是钒铁渣细粉，具体地讲，是将钒铁渣破碎粉磨至-325目而得到的细粉。即，钒铁渣细粉的粒度小于325目。由于钒铁渣中含有大量的Al2O3，所以具有很好的水化特性。因此，钒铁渣细粉可以用作耐火浇注料的结合剂。此外，当将钒铁渣破碎粉磨至-325目时，钒铁渣细粉的水化特性优异。
本发明的耐火浇注料可以用于钢包、钢包盖、中间包、中间包盖等。
本发明的耐火浇注料还可以含有按重量百分比计的5％～15％的碳化硅粉和5％～10％的石墨粉，此时，碳化硅粉和石墨粉的总质量在耐火浇注料中的含量不应低于10％。当根据本发明的耐火浇注料中含有碳化硅粉和石墨粉时，耐火浇注料可以用于高炉铁渣沟。
然而，本发明的耐火浇注料不限于上述的组分。为了改善耐火浇注料的性能，本发明的耐火浇注料还可以包含减水剂、缓凝剂、防爆纤维等，此外，还可以包含诸如硅微粉、氧化铝细粉等的各种微粉。
在使用过程中，可以将配制好的耐火浇注料加入适量的水并搅拌均匀，然后进行浇注成型。
表1示出了根据本发明的多个示例性实施例。其中，粗骨料、细骨料中未标出的部分均表示由钒铁渣形成。
表1
Figure BSA00000489027500031
在上述实施例中，使用的粗骨料的粒度在大约2mm～大约10mm的范围内，使用的细骨料的粒度小于大约2mm，使用的结合剂的粒度为-325目。
通过表1中的各个实施例的性能可以看出，本发明的含有钒铁渣的耐火浇注料的性能优异且强度很高，因此可以代替传统的耐火浇注料而作为高强度的耐火浇注料使用。

Claims (8)

1.一种含有钒铁渣的耐火浇注料，其特征在于，所述含有钒铁渣的耐火浇注料包含粗骨料、细骨料和由钒铁渣细粉形成的结合剂。
2.如权利要求1所述的含有钒铁渣的耐火浇注料，其特征在于，所述粗骨料是粒度为2mm～10mm的钒铁渣骨料、高铝质骨料和铝镁质骨料中的至少一种。
3.如权利要求1所述的含有钒铁渣的耐火浇注料，其特征在于，所述细骨料是粒度小于2mm的钒铁渣骨料、高铝质骨料和铝镁质骨料中的至少一种。
4.如权利要求1所述的含有钒铁渣的耐火浇注料，其特征在于，所述结合剂的粒度为-325目。
5.如权利要求1、2和3中任一项所述的含有钒铁渣的耐火浇注料，其特征在于，所述钒铁渣含有按重量百分比计的78％～83％的Al2O3、10％～17％的CaO、1.0％～2.5％的MgO、0.2％～0.8％的FeO、0.6％～0.8％的SiO2和1.3％～4.0％的钒氧化物。
6.如权利要求1、2和3中任一项所述的含有钒铁渣的耐火浇注料，其特征在于，所述钒铁渣含有按体积百分比计的35％～40％的铝酸钙相、45％～55％的二铝酸一钙相、4％～7％的α-Al2O3相、7％～8％的玻璃质相、1％～3％的金属相和3％～5％的尖晶石相。
7.如权利要求1所述的含有钒铁渣的耐火浇注料，其特征在于，所述含有钒铁渣的耐火浇注料包含按重量百分比计的30％～50％的粗骨料、20％～40％的细骨料和10％～30％的由钒铁渣细粉形成的结合剂。
8.如权利要求7所述的含有钒铁渣的耐火浇注料，其特征在于，所述含有钒铁渣的耐火浇注料还含有按重量百分比计的5％～15％的碳化硅粉和5％～10％的石墨粉。
CN2011101150958A 2011-05-05 2011-05-05 一种含有钒铁渣的耐火浇注料 Pending CN102145997A (zh)