CN102140302A - Shock-resistant plant essential oil woodware paint - Google Patents
Shock-resistant plant essential oil woodware paint Download PDFInfo
- Publication number
- CN102140302A CN102140302A CN2011101074742A CN201110107474A CN102140302A CN 102140302 A CN102140302 A CN 102140302A CN 2011101074742 A CN2011101074742 A CN 2011101074742A CN 201110107474 A CN201110107474 A CN 201110107474A CN 102140302 A CN102140302 A CN 102140302A
- Authority
- CN
- China
- Prior art keywords
- percent
- essential oil
- shock resistance
- wood lacquer
- plants essential
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses shock-resistant plant essential oil woodware paint, which is characterized by consisting of the following components in percentage by weight: 25-35 percent of alkyd resin, 30-45 percent of castor oil modified alkyd resin, 2-4 percent of vinyl chloride-vinyl acetate resin, 8-17 percent of organic solvent, 0.5-1.0 percent of dispersant, 4-8 percent of matting powder, 0.8-1.5 percent of wax powder, 0.6-1.2 percent of anti-settling agent, 0.2-0.4 percent of defoaming agent, 0.3-0.5 percent of organosilicone surfactant and 0.5-1.5 percent of ultraviolet absorber. The invention aims to overcome the defects existing in the prior art and provides the woodware paint which has the advantages of shock resistance, short paint smell residence time, high fullness, chemical resistance, bending resistance, super-smooth hand feeling, flat paint film and perfect and uniform decoration property.
Description
Technical field
The present invention relates to a kind of wood lacquer, particularly a kind of shock resistance plants essential oil wood lacquer.
Background technology
In the use after the furniture application is finished, film aging, the residual taste of paint film is of long duration, the paint film suppleness is poor, the easy failure surface paint film of furniture collision impact, the residual taste of imitation wood's formaldehyde, and these problems perplex people's life staying idle at home for a long time.And these problems all can solve with lacquer by the brushing woodenware.Present many wood lacquers all can not solve or can not address these problems fully, particularly paint film paints problems such as the of long duration and paint film shock resistance difference of residual taste, tracing it to its cause, mainly is that the resin oleic acid of present employed wood lacquer is poor, the paint film suppleness is poor, and film aging is fast.
Summary of the invention
The objective of the invention is in order to overcome weak point of the prior art, provide shock resistance, paint taste residence time short, high fullness ratio, chemical resistant properties, anti-bending, superslide feel, paint film is smooth and the wood lacquer of ornamental perfect unity.
In order to achieve the above object, the present invention adopts following scheme:
A kind of wood lacquer of shock resistance plants essential oil is characterized in that being made up of the component of following weight percent:
Synolac 25-35%, castor oil modified Synolac 30-45%,
Vinyl chloride-vinyl acetate resin 2-4%, organic solvent 8-17%,
Dispersion agent 0.5-1.0%, flatting silica 4-8%,
Wax powder 0.8-1.5%, anti-settling agent 0.6-1.2%,
Defoamer 0.2-0.4%, organic silicon surfactant 0.3-0.5%,
Ultraviolet absorbers 0.5-1.5%.
The wood lacquer of aforesaid a kind of shock resistance plants essential oil, wherein said Synolac are the modification oil-free alkyd resin, and model is Setal 29SS-80;
Aforesaid a kind of shock resistance, not xanthochromic wood lacquer, wherein said organic solvent is the mixture of n-butyl acetate and 1-Methoxy-2-propyl acetate;
The wood lacquer of aforesaid a kind of shock resistance plants essential oil, wherein said dispersion agent are the modified polyurethane dispersion agent;
The wood lacquer of aforesaid a kind of shock resistance plants essential oil, wherein said flatting silica are the aerosil flatting silica;
The wood lacquer of aforesaid a kind of shock resistance plants essential oil, wherein said wax powder are tetrafluoroethylene wax powder;
The wood lacquer of aforesaid a kind of shock resistance plants essential oil, wherein said anti-settling agent are polyamine wax;
The defoamer of the wood lacquer of aforesaid a kind of shock resistance plants essential oil is broken bubble polysiloxane solution;
The wood lacquer of aforesaid a kind of shock resistance plants essential oil, wherein said organic silicon surfactant are the mixing solutions of polyether-modified poly-two radical siloxanes and poly-two radical siloxanes of polyester modification;
The model of castor oil modified Synolac of the present invention is A631-60S, its shock resistance lastingly;
Ultraviolet absorption auxiliary agent of the present invention, model are UV2, and U.S.'s aerochemistry can absorb the ultraviolet ray of various visible lights lastingly, prevents the accelerated deterioration flavescence that paint film causes because of uviolizing;
Its model of vinyl chloride-vinyl acetate resin of the present invention is VAGH.
The present invention's technology routinely can produce, and as feeding intake in order, casts a kind of material again after every kind of material stirs, and stirs while feeding intake, and the back of waiting to be uniformly dispersed is detected viscosity and can be finished.
In sum, beneficial effect of the present invention:
One, used a kind of modification oil-free alkyd resin in the wood lacquer of the present invention, the solvent release of modification oil-free alkyd resin is very fast, and the oleic acid that uses refines as vegetables oil, thereby has reached the solvent energy snap-out release in the paint film of construction back, causes noresidue solvent odor in the paint film;
Two, added a kind of castor oil modified Synolac in the wood lacquer of the present invention, castor oil modified Synolac can effectively improve the snappiness of paint film lastingly, and to the human body toxicological harmless, thus the paint film impact resistance can effectively be strengthened lastingly, thus reach the shock resistance effect.
Three, formula for a product uniqueness of the present invention, product have functions such as high fullness ratio, chemical resistant properties, anti-bending, high rigidity, superslide feel, paint film be smooth, its ornamental perfect unity.
Embodiment
Below in conjunction with embodiment the present invention is described further:
Embodiment 1
Be equipped with 100kg wood lacquer of the present invention, formulated by the component of following weight:
Modification oil-free alkyd resin 30kg, castor oil modified Synolac 40kg, vinyl chloride-vinyl acetate resin 3kg, the mixture 16.6kg of n-butyl acetate and 1-Methoxy-2-propyl acetate, modified polyurethane dispersion agent 0.5kg, aerosil flatting silica 6.5kg, tetrafluoroethylene wax powder 0.6kg, polyamide wax anti-settling agent 1.0kg, broken bubble polysiloxane solution 0.3kg, the mixing solutions 0.5kg of polyether-modified poly-two radical siloxanes and poly-two radical siloxanes of polyester modification, ultraviolet absorbers 1.0kg.
Prepare wood lacquer of the present invention and in whipping device, drop into the modification oil-free alkyd resin earlier, castor oil modified Synolac, the mixture of n-butyl acetate and 1-Methoxy-2-propyl acetate, vinyl chloride-vinyl acetate resin, the polyamide wax anti-settling agent, middle low speed disperseed 2-3 minute, drop into tetrafluoroethylene wax powder then, the aerosil matting agent is after middling speed disperses to drop into each material down, high speed dispersion 10-15 minute to fineness≤20um then, add other material then, after middling speed disperseed to drop into each material down, high speed was disperseed 5-8 minute then, 200 mesh filter screens filter, and get final product.
Embodiment 2
Be equipped with 100kg wood lacquer of the present invention, formulated by the component of following weight:
Modification oil-free alkyd resin 25kg, castor oil modified Synolac 45kg, vinyl chloride-vinyl acetate resin 3kg, the mixture 15.6kg of n-butyl acetate and 1-Methoxy-2-propyl acetate, modified polyurethane dispersion agent 0.5kg, aerosil flatting silica 7kg, tetrafluoroethylene wax powder 0.6kg, polyamide wax anti-settling agent 1.0kg, broken bubble polysiloxane solution 0.3kg, the mixing solutions 0.5kg of polyether-modified poly-two radical siloxanes and poly-two radical siloxanes of polyester modification, ultraviolet absorbers 1.5kg.
Prepare wood lacquer of the present invention and in whipping device, drop into the modification oil-free alkyd resin earlier, castor oil modified Synolac, the mixture of n-butyl acetate and 1-Methoxy-2-propyl acetate, vinyl chloride-vinyl acetate resin, the polyamide wax anti-settling agent, middle low speed disperseed 2-3 minute, drop into tetrafluoroethylene wax powder then, the aerosil matting agent is after middling speed disperses to drop into each material down, high speed dispersion 10-15 minute to fineness≤20um then, add other material then, after middling speed disperseed to drop into each material down, high speed was disperseed 5-8 minute then, 200 mesh filter screens filter, and get final product.
Embodiment 3
Be equipped with 100kg wood lacquer of the present invention, formulated by the component of following weight:
Modification oil-free alkyd resin 35kg, castor oil modified Synolac 42.6kg, vinyl chloride-vinyl acetate resin 3kg, the mixture 10kg of n-butyl acetate and 1-Methoxy-2-propyl acetate, modified polyurethane dispersion agent 0.7kg, aerosil flatting silica 5kg, tetrafluoroethylene wax powder 1.0kg, polyamide wax anti-settling agent 0.8kg, broken bubble polysiloxane solution 0.3kg, the mixing solutions 0.4kg of polyether-modified poly-two radical siloxanes and poly-two radical siloxanes of polyester modification, ultraviolet absorbers 1.2kg.
Prepare wood lacquer of the present invention and in whipping device, drop into the modification oil-free alkyd resin earlier, castor oil modified Synolac, the mixture of n-butyl acetate and 1-Methoxy-2-propyl acetate, vinyl chloride-vinyl acetate resin, the polyamide wax anti-settling agent, middle low speed disperseed 2-3 minute, drop into tetrafluoroethylene wax powder then, the aerosil matting agent is after middling speed disperses to drop into each material down, high speed dispersion 10-15 minute to fineness≤20um then, add other material then, after middling speed disperseed to drop into each material down, high speed was disperseed 5-8 minute then, 200 mesh filter screens filter, and get final product.
Embodiment 4
Be equipped with 100kg wood lacquer of the present invention, formulated by the component of following weight:
Modification oil-free alkyd resin 28kg, castor oil modified Synolac 38kg, vinyl chloride-vinyl acetate resin 4kg, the mixture 17kg of n-butyl acetate and 1-Methoxy-2-propyl acetate, modified polyurethane dispersion agent 1.0kg, aerosil flatting silica 8kg, tetrafluoroethylene wax powder 1.5kg, polyamide wax anti-settling agent 1.2kg, broken bubble polysiloxane solution 0.4kg, the mixing solutions 0.3kg of polyether-modified poly-two radical siloxanes and poly-two radical siloxanes of polyester modification, ultraviolet absorbers 0.6kg.
Prepare wood lacquer of the present invention and in whipping device, drop into the modification oil-free alkyd resin earlier, castor oil modified Synolac, the mixture of n-butyl acetate and 1-Methoxy-2-propyl acetate, vinyl chloride-vinyl acetate resin, the polyamide wax anti-settling agent, middle low speed disperseed 2-3 minute, drop into tetrafluoroethylene wax powder then, the aerosil matting agent is after middling speed disperses to drop into each material down, high speed dispersion 10-15 minute to fineness≤20um then, add other material then, after middling speed disperseed to drop into each material down, high speed was disperseed 5-8 minute then, 200 mesh filter screens filter, and get final product.
Embodiment 5
Be equipped with 100kg wood lacquer of the present invention, formulated by the component of following weight:
Modification oil-free alkyd resin 34kg, castor oil modified Synolac 45kg, vinyl chloride-vinyl acetate resin 2kg, the mixture 8kg of n-butyl acetate and 1-Methoxy-2-propyl acetate, modified polyurethane dispersion agent 0.6kg, aerosil flatting silica 8kg, tetrafluoroethylene wax powder 0.8kg, polyamide wax anti-settling agent 0.6kg, broken bubble polysiloxane solution 0.2kg, the mixing solutions 0.3kg of polyether-modified poly-two radical siloxanes and poly-two radical siloxanes of polyester modification, ultraviolet absorbers 0.5kg.
Prepare wood lacquer of the present invention and in whipping device, drop into the modification oil-free alkyd resin earlier, castor oil modified Synolac, the mixture of n-butyl acetate and 1-Methoxy-2-propyl acetate, vinyl chloride-vinyl acetate resin, the polyamide wax anti-settling agent, middle low speed disperseed 2-3 minute, drop into tetrafluoroethylene wax powder then, the aerosil matting agent is after middling speed disperses to drop into each material down, high speed dispersion 10-15 minute to fineness≤20um then, add other material then, after middling speed disperseed to drop into each material down, high speed was disperseed 5-8 minute then, 200 mesh filter screens filter, and get final product.
The raw material that the present invention adopts is easy to get, and is convenient to construction, lasting shock resistance, and it is tasteless that paint film is done the back; High fullness ratio, chemical resistant properties, anti-bending, superslide feel, paint film are smooth.
Claims (9)
1. the wood lacquer of a shock resistance plants essential oil is characterized in that being made up of the component of following weight percent:
Synolac 25-35%, castor oil modified Synolac 30-45%,
Vinyl chloride-vinyl acetate resin 2-4%, organic solvent 8-17%,
Dispersion agent 0.5-1.0%, flatting silica 4-8%,
Wax powder 0.6-1.5%, anti-settling agent 0.6-1.2%,
Defoamer 0.2-0.4%, organic silicon surfactant 0.3-0.5%,
Ultraviolet absorbers 0.5-1.5%.
2. the wood lacquer of a kind of shock resistance plants essential oil according to claim 1 is characterized in that described Synolac is the modification oil-free alkyd resin.
3. the wood lacquer of a kind of shock resistance plants essential oil according to claim 1 is characterized in that described organic solvent is the mixture of n-butyl acetate and 1-Methoxy-2-propyl acetate.
4. the wood lacquer of a kind of shock resistance plants essential oil according to claim 1 is characterized in that described dispersion agent is the modified polyurethane dispersion agent.
5. the wood lacquer of a kind of shock resistance plants essential oil according to claim 1 is characterized in that described flatting silica is the aerosil flatting silica.
6. the wood lacquer of a kind of shock resistance plants essential oil according to claim 1 is characterized in that described wax powder is a tetrafluoroethylene wax powder.
7. the wood lacquer of a kind of shock resistance plants essential oil according to claim 1 is characterized in that described anti-settling agent is the polyamide wax anti-settling agent.
8. the defoamer of the wood lacquer of a kind of shock resistance plants essential oil according to claim 1 is broken bubble polysiloxane solution.
9. the wood lacquer of a kind of shock resistance plants essential oil according to claim 1 is characterized in that described organic silicon surfactant is the mixing solutions of polyether-modified poly-two radical siloxanes and poly-two radical siloxanes of polyester modification.