CN102140287A - 一种水性云彩涂料 - Google Patents
一种水性云彩涂料 Download PDFInfo
- Publication number
- CN102140287A CN102140287A CN 201110073277 CN201110073277A CN102140287A CN 102140287 A CN102140287 A CN 102140287A CN 201110073277 CN201110073277 CN 201110073277 CN 201110073277 A CN201110073277 A CN 201110073277A CN 102140287 A CN102140287 A CN 102140287A
- Authority
- CN
- China
- Prior art keywords
- water
- film
- urea
- forming material
- coalescence aid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明是一种水性云彩涂料，主要技术特征是它由下列组份（重量百分比）：5~75%的水性成膜材料、0~10%成膜助剂、1~50%尿素、余量的水。所述的水性成膜材料指以水为溶剂在常温下能成膜的材料，其包括但不限于丙烯酸树脂或聚氨酯改性丙烯酸树脂或聚氨酯树脂，所述尿素能溶于水并易结晶，该涂料在施工后随着水的挥发出现云彩状的特殊表面效果，具有好的装饰效果。
Description
技术领域
本发明涉及具有装饰效果的水性涂料，尤其是涉及一种通过加入水溶性材料的尿素，在施工后随着水的挥发出现云彩、绒毛状的特殊效果，并能持久表现的水性云彩涂料。
背景技术
目前，涂装（即指对金属和非金属表面覆盖保护层或装饰层）领域不断追求表面效果的创新，色彩变化、光泽变化、多种配搭等均有出现，本发明能提供一种类似云彩、绒毛状装饰效果的水性涂料，具有较好的花纹与立体效果，使涂装表面多了一种新的选择。
发明内容
本发明的目的在于解决上述现有技术的不足，而提供一种涂装时具有云彩、绒毛状特殊效果的水性涂料，显得柔和且富有立体感，其涂装表面效果与众不同。
本发明解决其技术问题所采用的技术方案是：一种水性云彩涂料，其特征在于，它是由原料水性成膜材料、成膜助剂、尿素和水按照下述重量百分比混合搅拌制备而成：
水性成膜材料 5~75%
成膜助剂 0~10%
尿素 1~50%
水 余量
本发明还可以采用以下技术措施解决：作为更进一步的改进，所述的水性成膜材料包括但不限于丙烯酸树脂或聚氨酯改性丙烯酸树脂或聚氨酯树脂。
所述成膜助剂包括但不限于丙二醇丁醚或乙二醇丁醚或醇酯十二。
本发明的有益效果是：由于本发明选择了尿素，且为溶于水的材料，结合常规的水性成膜材料和成膜助剂，尿素在施工溶解过程中随着水的挥发形成白色结晶体，构成云彩、绒毛状的特殊效果，并能持久表现，具有好的环境保护性能，是符合可持续发展的绿色涂料。
具体实施方式
下面实施例对本发明进一步说明。
实施例1：一种水性云彩涂料，它是由原料水性成膜材料、成膜助剂、尿素和水按照下述重量百分比混合搅拌制备而成，混合搅拌约1个小时至均匀，混合搅拌时间可根据实际情况进行调整：
水性成膜材料 27%
成膜助剂 2%
尿素 3%
水 68%。
所述的水性成膜材料包括但不限于丙烯酸树脂或聚氨酯改性丙烯酸树脂或聚氨酯树脂。
所述成膜助剂包括但不限于丙二醇丁醚或乙二醇丁醚或醇酯十二。
实施例2：搅拌时间和实施例1相似，不同之处在于，所述水性成膜材料、成膜助剂、尿素和水按照下述重量百分比混合搅拌制备而成：
水性成膜材料 23%
成膜助剂 3%
尿素 8%
水 66%。
所述的水性成膜材料包括但不限于丙烯酸树脂或聚氨酯改性丙烯酸树脂或聚氨酯树脂。
所述成膜助剂包括但不限于丙二醇丁醚或乙二醇丁醚或醇酯十二。
实施例3：搅拌时间和实施例1相似，不同之处在于，所述水性成膜材料、成膜助剂、尿素和水按照下述重量百分比混合搅拌制备而成：
水性成膜材料 45%
成膜助剂 5%
尿素 18%
水 32%。
所述的水性成膜材料包括但不限于丙烯酸树脂或聚氨酯改性丙烯酸树脂或聚氨酯树脂。
所述成膜助剂包括但不限于丙二醇丁醚或乙二醇丁醚或醇酯十二。
实施例4：搅拌时间和实施例1相似，不同之处在于，所述水性成膜材料、成膜助剂、尿素和水按照下述重量百分比混合搅拌制备而成：
水性成膜材料 55%
成膜助剂 6%
尿素 33%
水 6%。
所述的水性成膜材料包括但不限于丙烯酸树脂或聚氨酯改性丙烯酸树脂或聚氨酯树脂。
所述成膜助剂包括但不限于丙二醇丁醚或乙二醇丁醚或醇酯十二。
实施例5：搅拌时间和实施例1相似，不同之处在于，所述水性成膜材料、成膜助剂、尿素和水按照下述重量百分比混合搅拌制备而成：
水性成膜材料 50%
成膜助剂 6%
尿素 23%
水 21%。
所述的水性成膜材料包括但不限于丙烯酸树脂或聚氨酯改性丙烯酸树脂或聚氨酯树脂。
所述成膜助剂包括但不限于丙二醇丁醚或乙二醇丁醚或醇酯十二。
本发明的水性云彩涂料，使用时，可按照上述各实施例的配方比进行选择，作为水性涂料按照传统的涂装工艺涂装覆盖在非金属（例如：木器）或金属表面，涂装厚度可根据需要进行喷涂，使基底表面形成具有防护、装饰等功能涂层，特别是本发明的涂料，在涂装过程中尿素在溶解过程中随着水的挥发形成白色结晶体，构成云彩、绒毛状的特殊效果。
Claims (7)
1.一种水性云彩涂料，其特征在于，它是由原料水性成膜材料、成膜剂、尿素和水按照下述重量百分比混合搅拌制备而成：
水性成膜材料 5~75%
成膜助剂 0~10%
尿素 1~50%
水 余量。
2.根据权利要求1水性云彩涂料，其特征在于，所述水性成膜材料、成膜助剂、尿素和水按照下述重量百分比混合搅拌制备而成：
水性成膜材料 27%
成膜助剂 2%
尿素 3%
水 68%。
3.根据权利要求1水性云彩涂料，其特征在于，所述水性成膜材料、成膜助剂、尿素和水按照下述重量百分比混合搅拌制备而成：
水性成膜材料 23%
成膜助剂 3%
尿素 8%
水 66%。
4.根据权利要求1水性云彩涂料，其特征在于，所述水性成膜材料、成膜助剂、尿素和水按照下述重量百分比混合搅拌制备而成：
水性成膜材料 45%
成膜助剂 5%
尿素 18%
水 32%。
5.根据权利要求1水性云彩涂料，其特征在于，所述水性成膜材料、成膜助剂、尿素和水按照下述重量百分比混合搅拌制备而成：
水性成膜材料 55%
成膜助剂 6%
尿素 33%
水 6%。
6.根据权利要求1或2或3或4或5水性云彩涂料，其特征在于，所述的水性成膜材料包括但不限于丙烯酸树脂或聚氨酯改性丙烯酸树脂或聚氨酯树脂。
7.根据权利要求1或2或3或4或5水性云彩涂料，其特征在于，所述成膜助剂包括但不限于丙二醇丁醚或乙二醇丁醚或醇酯十二。