CN102134445A - Qercetin waterproof agent - Google Patents
Qercetin waterproof agent Download PDFInfo
- Publication number
- CN102134445A CN102134445A CN2010100009807A CN201010000980A CN102134445A CN 102134445 A CN102134445 A CN 102134445A CN 2010100009807 A CN2010100009807 A CN 2010100009807A CN 201010000980 A CN201010000980 A CN 201010000980A CN 102134445 A CN102134445 A CN 102134445A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- qercetin
- waterproof agent
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a qercetin waterproof agent and relates to the technical field of building materials. The invention adopts a technical scheme that: the qercetin waterproof agent is prepared from 100 parts of deionized water, 3 part of lotus leaf extract, 8 parts of absolute ethanol, 8 parts of methyl silicic acid and 5 parts of potassium hydroxide. The manufacturing process of the qercetin waterproof agent comprises: uniformly mixing the absolute ethanol and the methyl silicic acid, reacting for 30 minutes in a natural environment, adding the deionized water in a reaction kettle and heating to 50 to 60 DEG C; adding lotus leaf extract and potassium hydroxide, continuously heating to 100 DEG C, adding the reacted methyl silicic acid into a reaction kettle, and reacting at a constant temperature for 50 minutes; pouring the reaction solution into a settling tank for cooling and settling; and pouring clear liquid obtained by settling into a filling machine for filtering, and filling to obtain finished products. The waterproof agent produced by the invention is an environmentally-friendly product and is free from formaldehyde, toxin, pungent odor, flammability, volatilization and steel bar corrosion. The waterproof performance is reliable, the water proof life is long, and the acid resistance, alkali resistance and weather resistance are high. The construction is safe, the operation is simple and convenient, and the price is reasonable.
Description
Technical field
The present invention relates to building material technical field, relate in particular to a kind of high performance water-proof material.
Background technology
At present, the cracking of buildings and various structures and seepage almost become a big common quality defect of current concrete structure, have the saying of " day the moon meets rain all through the night partially ", expressed people the room is leaked the helpless of worry.Cement concrete is usually because water consumption is big, inner and gather materials behind the dry through at cement stone. the slurry interface has formed the pore of a large amount of connections, add volumetric shrinkage in its drying process, the back that suffers restraints easily produces cracking phenomena, has aggravated its seepage harm more.For a long time, people adopt various measures to solve concrete anti-leakage problem, increase cement consumption as adopting, improve aggregate grading etc., but it is limited to produce effects, and the cost increase is more, and crack problem still can not solve.In the past few decades, the measure that people also adopt admixtures such as adding trolamine, iron(ic) chloride to improve concrete permeability resistance, all can not solve the crack on concrete problem, and trolamine improper use, easily concrete performance is caused serious harm, the internal portion of chlorination iron rule reinforcing bar has corrosive nature, has been limited to use.After cement expansive material is succeeded in developing, people begin generally to adopt the measure of swelling agent list blending swelling agent and the compound admixture of water reducer to improve concrete impermeability and splitting resistance, but owing to be too dependent on the swelling property and the fillibility of swelling agent, the example of using failure is also more.
Summary of the invention
At above-mentioned deficiency, the objective of the invention is to provide a kind of Folium Nelumbinis essenc water-resisting agent, this product is to be raw material by the stem of natural nano structure vegetation water lotus, leaf (lotus leaf) extract, with the high molecular polymer with infiltration function is carrier, deionized water and lanolin are miscible agent, by special process, concentrate the collaborative Folium Nelumbinis essenc water-resisting agent of the binary that forms.This product have slight lotus leaf fragrance, transparent (or light green), nontoxic, do not burn, non-volatile, do not change the buildings color after the construction, do not form the surface and be coated with envelope, can stop moisture to be invaded, can make inner moisture again nothing serious and outwards distribute, reaching can water proof anti-seepage, again can gas-pervious magical function.
For achieving the above object, technical scheme that the present invention adopts is: raw material: hydrophobic nature extract, deionized water, potassium hydroxide, methyl siliconic acid, dehydrated alcohol that lotus leaf and stem extract.Equipment: reactor, settling tank, filtration filling machine.
Prescription: 100 parts of deionized waters, 3 parts of Lotus Leafextracts, 8 parts of dehydrated alcohols, 8 parts of methyl siliconic acids, 5 parts in potassium hydroxide.(weight ratio)
Technology: 1. dehydrated alcohol and methyl siliconic acid evenly cooperated in the physical environment of back reaction 30 minutes.
2. deionized water is added in the reactor, heat to 50-60 ℃.
3. add Lotus Leafextract, potassium hydroxide, continue to be warming up to 100 ℃
4. the good methyl siliconic acid of reaction is added reactor, insulation reaction 50 minutes.
5. pour settling tank cooling precipitation into.
6. precipitate limpid liquid pour in the filling machine filter, can is finished product.
Constructional method:
1. after this product being converted 12 times of water and being stirred, directly spray, be applied to exsiccant handled thing surface uniformly, obvious water layer phenomenon be arranged with atomizer or painting brush.
2. according to the perviousness of different building facings, can when the construction first pass is not dried, just continue spraying second time, to reach waterproof effect preferably.
3. if any the crack, use and to spray after cement seccotine water distribution mud that my company produces is filled and led up drying.
4. building constructions accomodation ground waterproof can spray this agent earlier, the elasticity mending-leakage king brushing of producing with the our factory around the upper and lower conduit road, sticking floor brick (or ceramic tile) again.
5. promptly reach waterproof effect after the spraying drying.
Principle: after the construction, the further condensation of Folium Nelumbinis essenc water-resisting agent and with the structured material react with, generate insoluble waterproof macromolecular compound---the netted silicone resin of one deck few molecules thick at substrate surface.This resin molding has advantages such as waterproof, protection against the tide, antiseepage, air permeability, resistance to deterioration, resistance to crocking and weather resisteant, makes buildings not be subjected to weathering or minimizing weathering, thereby prolongs the work-ing life of buildings.
Purposes: 1. between bathe in the lavatory, kitchen, vault, waterproof, antiseepage and old seepage treatment between boiled water room are arranged.
2. the WATER REPELLENT after various sanitary ware are installed.
3. defend the waterproof of wall coating, anticorrosion, mildew-resistant, guarantor's look in.
4. waterproof such as reservoir, water tower, tunnel, hydro project, bridge, harbour, sewage work, agriculture irrigation canals and ditches and underground civil air defense constructions and installations.
5. concrete depositing member and structurally waterproof.
6. salt alkali content height, the buildings that influenced by oceanic climate.
7. efflorescence prevention against corrosion such as gardens, historical relic, ancient building, stone inscription is handled.
8. be used for other to reduce the special purpose of water-absorbent and impervious waterproof
The water-resisting agent characteristics:
The water-resisting agent that the present invention produces is a Green Product, does not contain formaldehyde, and is nontoxic, and non-stimulated flavor is nonflammable, non-volatile, to the reinforcing bar non-corroding.Water resistance is reliable, and the waterproof life-span is permanent, and acid and alkali-resistance, weathering resistance are good.Construction safety, easy and simple to handle, cost is reasonable.The solid content height, extension rate is higher, and cost is cheaper.Alkalinity is low, builds harmless.Produce effects phase section, surface drying promptly produces effect.Effect is obvious, and water presents obvious globule phenomenon on the surface of spraying water-resisting agent.
Specific embodiment
Embodiment 1, outfit 1kg Folium Nelumbinis essenc water-resisting agent, drawing materials is deionized water 806g, Lotus Leafextract 24g, dehydrated alcohol 65g, methyl siliconic acid 65g, potassium hydroxide 40g.But the brushing area is month 10 square meters.
Embodiment 2, outfit 10kg Folium Nelumbinis essenc water-resisting agent, drawing materials is deionized water 8060g, Lotus Leafextract 240g, dehydrated alcohol 650g, methyl siliconic acid 650g, potassium hydroxide 400g.But about 100 square meters of brushing area.
Be used for 1. lavatories bathe between, kitchen, vault, waterproof, antiseepage and old seepage treatment between boiled water room are arranged.2. the WATER REPELLENT after various sanitary ware are installed.3. defend the waterproof of wall coating, anticorrosion, mildew-resistant, guarantor's look in.4. waterproof such as reservoir, water tower, tunnel, hydro project, bridge, harbour, sewage work, agriculture irrigation canals and ditches and underground civil air defense constructions and installations.5. concrete depositing member and structurally waterproof.6. salt alkali content height, the buildings that influenced by oceanic climate.7. efflorescence prevention against corrosion such as gardens, historical relic, ancient building, stone inscription is handled.8. be used for other to reduce the special purpose of water-absorbent and impervious waterproof.
Claims (2)
1. Folium Nelumbinis essenc water-resisting agent, its prescription is: 100 parts of deionized waters, 3 parts of Lotus Leafextracts, 8 parts of dehydrated alcohols, 8 parts of methyl siliconic acids, 5 parts in potassium hydroxide.
2. a kind of Folium Nelumbinis essenc water-resisting agent according to claim 1, its manufacture craft is: dehydrated alcohol and methyl siliconic acid evenly cooperated in the physical environment of back reaction 30 minutes, and deionized water is added in the reactor, heated to 50-60 ℃.Add Lotus Leafextract, potassium hydroxide, continue to be warming up to 100 ℃ the good methyl siliconic acid adding reactor of reaction, insulation reaction 50 minutes.Pour settling tank cooling precipitation into.Precipitate limpid liquid pour in the filling machine filter, can is finished product.