CN102126318A - Inflaming retarding fabric - Google Patents
Inflaming retarding fabric Download PDFInfo
- Publication number
- CN102126318A CN102126318A CN2010105171681A CN201010517168A CN102126318A CN 102126318 A CN102126318 A CN 102126318A CN 2010105171681 A CN2010105171681 A CN 2010105171681A CN 201010517168 A CN201010517168 A CN 201010517168A CN 102126318 A CN102126318 A CN 102126318A
- Authority
- CN
- China
- Prior art keywords
- fire
- fabric
- layer
- organic fiber
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an inflaming retarding fabric. The fabric comprises a waterproof layer, a heat-resisting organic fibrous layer, an enhancement layer and a base layer from outside to inside sequentially; all layers are adhered through thermoplastic adhesive fibers; and the heat-resisting organic fibrous layer is compressed. The heat-resisting organic fibrous layer is adhered by the thermoplastic adhesive fibers and keeps compressed in the normal state; when the fabric meets high temperature or flame, the adhesive fibers in the structure become soft, and the compressed crimped fibers are released to ensure that the thickness of the fabric is increased obviously, so that an air bag is formed in the fabric due to the thickness increasing; therefore, heat resistance performance of the fabric is improved.
Description
Technical field
The present invention relates to a kind of fire-retardant lining.
Background technology
In recent years, more and more higher to the fire-retardant requirement of textile in the world, stipulate more and more thinner, and the development of building along with urban modernization, the development of tourism, transportation, flame retardant textiles exists enormous and latent market.Fire-retardant object as Japanese Fire Service Act regulation comprises employed textile in the public buildings such as big or small hotel, theater, hospital; Old man, infant's clothes and bedding; The employed textile of transport facility etc.
The purpose of fire-retardant processing is to make fibre can reduce its combustibility in flame, can slow down the speed that spreads, and does not form the large tracts of land burning, and after leaving flame, can be very fast from putting out, no longer burn or glow.
Summary of the invention
The objective of the invention is to overcome above-mentioned shortcoming of the prior art, a kind of fire-retardant lining is provided.
A kind of fire-retardant lining of the present invention, described lining comprises watertight composition, heatproof organic fiber layer, enhancement layer and basic unit from outside to inside successively, and each layer is by the thermoplastic binder fiber bonding, and described heatproof organic fiber layer is the compression shape.
In a preferred embodiment of the invention, described heatproof organic fiber layer thickness is 20-30 μ m.
In a preferred embodiment of the invention, described heatproof organic fiber is the para-aramid fiber.
In a preferred embodiment of the invention, described groundwork thickness is 20-40 μ m.
In a preferred embodiment of the invention, described basic unit is spunbond thermoplastic nonwoven sheet material.
In a preferred embodiment of the invention, described watertight composition is polyurethane or polyvinyl chloride film.
Fire-retardant principle of the present invention: heatproof organic fiber layer of the present invention is by the thermoplastic binder fiber bonding under normal condition and keeps compressive state, when running into high temperature or flame, adhesive fiber meeting deliquescing in the structure, discharge the crimped fibre of restriction by compression, and make the thickness of lining significantly increase, such increase meeting forms air bag in lining, thereby can increase the hot property of lining.
Description of drawings
Fig. 1 is an embodiment of the present invention structural representation.
Among the figure: 1 is that watertight composition, 2 is that heatproof organic fiber layer, 3 is that enhancement layer, 4 is basic unit.
The specific embodiment
Below in conjunction with accompanying drawing preferred embodiment of the present invention is described in detail, thereby protection scope of the present invention is made more explicit defining so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that.
As shown in Figure 1, present embodiment comprises watertight composition 1, heatproof organic fiber layer 2, enhancement layer 3, basic unit 4, described watertight composition is polyurethane or polyvinyl chloride film, described heatproof organic fiber layer 2 is made up of the mixture of curl heatproof organic fiber and thermoplastic binder fiber, be the compression shape under the normal condition, thickness is 20-30 μ m.Basic unit is spunbond thermoplastic nonwoven sheet material, and thickness is 20-40 μ m.Each layer bonds by thermoplastic binder fiber.
Heatproof organic fiber layer of the present invention is by the thermoplastic binder fiber bonding under normal condition and keeps compressive state, when running into high temperature or flame, adhesive fiber meeting deliquescing in the structure, discharge the crimped fibre of restriction by compression, and make the thickness of lining significantly increase, such increase meeting forms air bag in lining, thereby can increase the hot property of lining.
When present embodiment ran into high temperature or flame, thickness swelling was to more than the twice.
The above; it only is the specific embodiment of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the disclosed technical scope of the present invention; variation or the replacement that can expect without creative work all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (6)
1. a fire-retardant lining is characterized in that, described lining comprises watertight composition, heatproof organic fiber layer, enhancement layer and basic unit from outside to inside successively, and each layer is by the thermoplastic binder fiber bonding, and described heatproof organic fiber layer is the compression shape.
2. a kind of fire-retardant lining according to claim 1 is characterized in that, described heatproof organic fiber layer thickness is 20-30 μ m.
3. a kind of fire-retardant lining according to claim 2 is characterized in that described heatproof organic fiber is the para-aramid fiber.
4. a kind of fire-retardant lining according to claim 1 is characterized in that, described groundwork thickness is 20-40 μ m.
5. a kind of fire-retardant lining according to claim 3 is characterized in that, described basic unit is spunbond thermoplastic nonwoven sheet material.
6. a kind of fire-retardant lining according to claim 1 is characterized in that described watertight composition is polyurethane or polyvinyl chloride film.