CN102093790A - Polyvinyl chloride powder coating - Google Patents
Polyvinyl chloride powder coating Download PDFInfo
- Publication number
- CN102093790A CN102093790A CN200910263339XA CN200910263339A CN102093790A CN 102093790 A CN102093790 A CN 102093790A CN 200910263339X A CN200910263339X A CN 200910263339XA CN 200910263339 A CN200910263339 A CN 200910263339A CN 102093790 A CN102093790 A CN 102093790A
- Authority
- CN
- China
- Prior art keywords
- kilograms
- polyvinyl
- chloride powder
- polyvinyl chloride
- stablizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a polyvinyl chloride powder coating, which comprises the following components in part by weight: 100 parts of polyvinyl chloride resin, 3 to 9 parts of stabilizing agent, 35 to 100 parts of plasticizer, 2 to 10 parts of chalking agent and 2 to 20 parts of antistatic agent. The powder coating is prepared from readily available raw materials, has the characteristics of low cost, high finished product flowability, high stability and the like, and can be applied to a product with a high requirement on corrosion resistance and weather resistance.
Description
Technical field
The present invention relates to a kind of coating, particularly a kind of polyvinyl-chloride powder paint.
Background technology
Polyvinyl-chloride powder paint has good chemicals-resistant and water tolerance, and also some is soft and pliable and tough, glossy for outstanding shock strength, rebound resilience, resistance to salt(spray)fog and weathering resistance, polyvinyl chloride powder coating.By adjusting special dimension such as the frozen product frame and the machine barrel that washes the dishes that its prescription can be applicable to U.S. food and FAD (FDA) approval.The general applications of pvc coating comprises the electrical isolation occasion, can be used for the covering with paint of Chain Link Fence, outdoor furniture and related occasion.At present external adopt with polyvinyl chloride batching back high temperature happy and harmoniously extrude, wire drawing, granulation, the technology that degree of depth cooling is pulverized then, but this technical process is long, cost is high and can only be applied to the fluidized-bed processing method, can not be applied in the electrostatic spraying processing.
Summary of the invention
The object of the present invention is to provide a kind of high-quality polyvinyl-chloride powder paint, solve above-mentioned deficiency.
The technical scheme that realizes the object of the invention is: the present invention includes a kind of polyvinyl-chloride powder paint, its each composition and weight ratio are as follows:
100 parts of polyvinyl chloride (PVC) RESINS;
Stablizer 3-9 part;
Softening agent 35-100 part;
Powdering agent 2-10 part;
Static inhibitor 2-20 part.
Above-mentioned polyvinyl-chloride powder paint, described stablizer are the organic tin stablizer.
Above-mentioned polyvinyl-chloride powder paint, described stablizer are a kind of in octyl mercaptan tin, the Methyl stannum mercaptide.
Above-mentioned polyvinyl-chloride powder paint, described softening agent are phthalate.
Above-mentioned polyvinyl-chloride powder paint, described softening agent are one or more in Phthalic acid, diallyl ester, dioctyl phthalate (DOP), the dioctyl terephthalate.
The present invention has following characteristics: (1) raw material be simple and easy to, cost is low; (2) add powdering agent and electrostatic agent and effectively eliminate resin and mix the back by the phenomenon of swelling and cohesion and caking, and eliminate generation of static electricity with softening agent.
Embodiment
(embodiment 1)
Prescription: the polymerization degree is 100 kilograms of 300 polyvinyl chloride (PVC) RESINS; 5 kilograms in stablizer octyl mercaptan tin; 40 kilograms of Phthalic acid, diallyl esters; 4 kilograms of powdering agents; 6 kilograms in static inhibitor.
Technology: with the polymerization degree is that 100 kilograms of polyvinyl chloride (PVC) RESINS, 5 kilograms of mixing of stablizer octyl mercaptan tin of 300 are warming up to 90 degree and add 40 kilograms of Phthalic acid, diallyl esters, stirred 30 minutes, be cooled to about 55 degree, add powdering agent and add 6 kilograms in static inhibitor again for 4 kilograms, evenly stir after 45 minutes and filter out qualified coating.
(embodiment 2)
Prescription: the polymerization degree is 100 kilograms of 300 polyvinyl chloride (PVC) RESINS; 3 kilograms in stablizer octyl mercaptan tin; 35 kilograms of dioctyl terephthalates; 2 kilograms of powdering agents; 2 kilograms in static inhibitor.
Technology: with the polymerization degree is that 100 kilograms of polyvinyl chloride (PVC) RESINS, 3 kilograms of mixing of stablizer octyl mercaptan tin of 300 are warming up to 90 degree and add 35 kilograms of dioctyl terephthalates, stirred 30 minutes, be cooled to about 55 degree, add powdering agent and add 2 kilograms in static inhibitor again for 2 kilograms, evenly stir after 45 minutes and filter out qualified coating.
(embodiment 3)
Prescription: the polymerization degree is 100 kilograms of 300 polyvinyl chloride (PVC) RESINS; 5 kilograms of stablizer Methyl stannum mercaptides; 40 kilograms of dioctyl phthalate (DOP)s; 4 kilograms of powdering agents; 6 kilograms in static inhibitor.
Technology: with the polymerization degree is that 5 kilograms of mixing of 100 kilograms of polyvinyl chloride (PVC) RESINS, stablizer Methyl stannum mercaptide of 300 are warming up to 90 degree and add 40 kilograms of dioctyl phthalate (DOP)s, stirred 30 minutes, be cooled to about 55 degree, add powdering agent and add 6 kilograms in static inhibitor again for 4 kilograms, evenly stir after 45 minutes and filter out qualified coating.
(embodiment 4)
Prescription: the polymerization degree is 100 kilograms of 300 polyvinyl chloride (PVC) RESINS; 9 kilograms of stablizer Methyl stannum mercaptides; 100 kilograms of Phthalic acid, diallyl esters; 10 kilograms of powdering agents; 20 kilograms in static inhibitor.
Technology: with the polymerization degree is that 5 kilograms of mixing of 100 kilograms of polyvinyl chloride (PVC) RESINS, stablizer Methyl stannum mercaptide of 300 are warming up to 90 degree and add 100 kilograms of Phthalic acid, diallyl esters, stirred 30 minutes, be cooled to about 55 degree, add powdering agent and add 20 kilograms in static inhibitor again for 10 kilograms, evenly stir after 45 minutes and filter out qualified coating.
Claims (5)
1. polyvinyl-chloride powder paint, it is characterized in that by form and weight ratio as follows: 100 parts of polyvinyl chloride (PVC) RESINS; Stablizer 3-9 part; Softening agent 35-100 part; Powdering agent 2-10 part; Static inhibitor 2-20 part.
2. polyvinyl-chloride powder paint according to claim 1 is characterized in that: described stablizer is the organic tin stablizer.
3. polyvinyl-chloride powder paint according to claim 1 is characterized in that: described stablizer is a kind of in octyl mercaptan tin, the Methyl stannum mercaptide.
4. polyvinyl-chloride powder paint according to claim 1 is characterized in that: described softening agent is a phthalate.
5. polyvinyl-chloride powder paint according to claim 1 is characterized in that: described softening agent is one or more in Phthalic acid, diallyl ester, dioctyl phthalate (DOP), the dioctyl terephthalate.