CN102092718A - Method for preparing solar-grade polycrystalline silicon - Google Patents
Method for preparing solar-grade polycrystalline silicon Download PDFInfo
- Publication number
- CN102092718A CN102092718A CN2009102019355A CN200910201935A CN102092718A CN 102092718 A CN102092718 A CN 102092718A CN 2009102019355 A CN2009102019355 A CN 2009102019355A CN 200910201935 A CN200910201935 A CN 200910201935A CN 102092718 A CN102092718 A CN 102092718A
- Authority
- CN
- China
- Prior art keywords
- silicon
- polycrystalline silicon
- solar energy
- grade polycrystalline
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing solar-grade polycrystalline silicon. 3N-grade silicon metal is adopted as a raw material, and is purified through slagging and directional solidification in a vacuum smelting furnace, so that the silicon metal is purified into the solar-grade polycrystalline silicon with the purity of 99.9999 percent. Through the vacuum smelting furnace, the content of boron in the silicon metal is reduced to 0.5ppm from 5ppm, the content of phosphorus is reduce to 0.8ppm from 15pm, and the total impurities of the metal are reduced to less than 0.1ppm from 1,000ppm. The process flow is short, electricity consumption is low, the emission is avoided, the investment cost and production cost for polycrystalline silicon production can be greatly reduced, and the method is suitable for large-scale production.
Description
Technical field
The present invention relates to vacuum metallurgy material purification engineering field, especially relate to a kind of preparation method of solar energy grade polycrystalline silicon.
Background technology
Existing the most sophisticated polysilicon purifying technique is a Siemens Method.This method is to mix metallurgical grade silicon and hydrogen chloride gas in fluidized-bed reactor, and by described metallurgical grade silicon and hydrogenchloride generation chemical reaction, obtaining boiling point at last only has 31 ℃ trichlorosilicane, and described chemical equation is:
Si (solid)+3HCl (gas)=SiHCl3 (gas)+H2 (gas) (heat release).
To pass through in the vapor deposition reaction stove together with the silicon rod that is heated to 1100 ℃ again behind the mixture distillation of trichlorosilicane and hydrogen subsequently, thereby remove hydrogen, separate out solid-state silicon simultaneously, just become chunk polysilicon after smashing.So just can obtain purity and be 99.9999999% silicon.
The present cost of this method is generally more than 400 yuan/kilogram.Along with the formation of solar energy industry chain, the cost of photovoltaic generation has become the biggest factor that the restriction photovoltaic generation is promoted.Reduce the cost of photovoltaic generation, new mode must be arranged, therefore, exploring new solar energy level silicon production technique becomes focus.
The metallurgy method purifying polycrystalline silicon is not because chemical reaction takes place in silicon itself, only be to be undertaken by the mode of the high-temperature vacuum melting and the degassing at the impurity in the silicon, therefore, energy consumption is low, polluting for a short time, is the most promising a kind of method that reduces the solar energy polycrystalline silicon cost for purification.
Summary of the invention
Technical problem to be solved by this invention provides a kind of preparation method of solar energy grade polycrystalline silicon, technical process is short, simple to operate, the chemical reaction amount is little, current consumption is little, and non-pollution discharge, can reduce the cost of investment and the production cost of production of polysilicon significantly, can also carry out scale operation.
In order to achieve the above object, the preparation method of solar energy grade polycrystalline silicon provided by the invention comprises following steps:
Step 1, be that the Pure Silicon Metal fragmentation of 3N becomes granularity at 20～80 millimeters bulk silicon material, clean the pollution of removing described silicon material surface, put into vacuum melting furnace purity; The boron content of described Pure Silicon Metal less than 5ppm, phosphorus content less than 15ppm, metallic impurity total content less than 1000ppm; After the cleaning, described silicon material is dried;
Step 2, put into the reagent of 25ppm in described vacuum melting furnace, this reagent is made up of silicon-dioxide, calcium oxide and barium oxide, and the mass ratio of described three kinds of components is 3: 3: 4; Described reagent should be clipped in the described silicon material equably.
Step 3, to described vacuum melting stove evacuation, arrive after the vacuum reheat and heat up and make described silicon material fusing, follow-up continuous 1600 degree that are warmed up to of described silicon material fusing; Wherein said vacuum melting furnace begins heat temperature raising when its vacuum pressure is 100 handkerchiefs, during the fusing of described silicon material and the vacuum pressure in the follow-up temperature-rise period be less than 1 handkerchief.
Step 4, in described vacuum melting furnace, feed purity greater than 99.999% hydrogen, gas flow be per minute 2 to be raised to 20 liters, air pressure be normal pressure, aeration time is 2 hours;
Step 5, described vacuum melting furnace is progressively lowered the temperature, make described fused silicon material begin cooling from the bottom, and upwards carry out solidification and crystallization from the bottom, the crystallization velocity of described silicon material forms silicon ingot at last between 6～20 millimeters/hour;
Described silicon ingot is taken out in step 6, blow-on, and bottom, the top of excising described silicon ingot reach part all around, and the remainder of resulting described silicon ingot is the solar-grade polysilicon silicon ingot just; Excise described silicon ingot bottom, top and around during part, carry out resistivity measurement to described silicon ingot, resistivity is excised less than the part of 0.5 ohmcm.
By above-mentioned steps, can obtain purity at the solar-grade polysilicon of 5N to 6N; The content of boron in the Pure Silicon Metal can be reduced to 0.5ppm from 5ppm, the content of phosphorus is reduced to 0.8ppm from 15ppm, total metal content impurity is reduced to below the 0.1ppm from 1000ppm.By the selection of the chemical additive in above steps, can also obtain P type or N type polysilicon respectively, wherein can be controlled at respectively in the scope that helps most making the opto-electronic conversion behind the battery as the content that the phosphorus of electronics or hole carrier and boron are provided.
The preparation method's of solar energy grade polycrystalline silicon provided by the invention technical process is short, and simple to operate, the chemical reaction amount is little, and current consumption is little, and non-pollution discharge, can reduce the cost of investment and the production cost of production of polysilicon significantly; Compare existing chemical method, physics and chemistry method of the present invention makes production of polysilicon technology simpler, and facility investment is little, cost of investment have only existing chemical method 10% less than, production cost has only 1/3 of existing chemical method; Compare with the method for existing physics method purifying polycrystalline silicon, technology of the present invention is simple, and cost of investment is low, and production cost has only 60% of existing physics method, and yield rate improves greatly.Preparation method of the present invention can also carry out scale operation.
Description of drawings
The present invention is further detailed explanation below in conjunction with the drawings and specific embodiments:
Fig. 1 is the preparation method's of a solar energy grade polycrystalline silicon of the present invention schema.
Embodiment
Be the preparation method's of solar energy grade polycrystalline silicon of the present invention schema as shown in Figure 1, a preferred embodiment of the present invention comprises the steps:
Step 1, be that the Pure Silicon Metal fragmentation of 3N becomes granularity at 20～80 millimeters bulk silicon material with purity, the boron content of described Pure Silicon Metal be 0.5ppm, phosphorus content less than 1ppm, metallic impurity total content less than 800ppm; Clean the pollution of removing described silicon material surface, after the cleaning, described silicon material is dried, bake out temperature is 200 degree; Described silicon material is put into vacuum melting furnace, method is described silicon material to be put into the quartz crucible of described vacuum melting furnace, lay successively from bottom to top, note during blowing the described silicon material size of different size is separated lay, reduce gap between the silicon material as far as possible, and when filling with substance is handled with care, and does not damage crucible;
Step 2, put into the reagent of 25ppm in described vacuum melting furnace, this reagent is made up of silicon-dioxide, calcium oxide and barium oxide, and the mass ratio of described three kinds of components is 3: 3: 4; Described reagent will be clipped in the described silicon material equably;
Step 3, the fire door of closing described vacuum melting furnace, the body of heater of following described vacuum melting furnace vacuumize, beginning heating during less than 100 handkerchiefs at described body of heater pressure heats up described body of heater gradually, after described body of heater pressure is less than 10 handkerchiefs, described body of heater is warmed up to makes described silicon material fusing, follow-up continuous 1600 degree that are warmed up to of described silicon material fusing;
Step 4, feed purity greater than 99.999% hydrogen in described vacuum melting furnace, gas flow is that 20 liters of per minutes, air pressure are normal pressure, and aeration time is 2 hours; Because hydrogen at high temperature is easy to generate blast, when feeding hydrogen, must take required measure, prevent that blast from taking place;
Step 5, progressively reduce the heating power of described vacuum melting furnace and make described fused silicon material begin from the bottom cooling, make described silicon material begin to solidify from the bottom of described crucible, form columnar grain, and upwards growth gradually, the whole solidification and crystallizations of described silicon material in whole crucible, the crystallization velocity of described silicon material is controlled between 6～20 millimeters/hour, forms silicon ingot at last;
Step 6, described silicon ingot is lowered the temperature, when the temperature of described silicon ingot was lower than 100 degrees centigrade, described silicon ingot was taken out in blow-on; Bottom, the top of excising described silicon ingot reach part all around, and the remainder of resulting described silicon ingot is the solar-grade polysilicon silicon ingot just; Excise described silicon ingot bottom, top and around during part, carry out resistivity measurement to described silicon ingot, the silicon ingot of resistivity less than 0.5 ohmcm partly excised.
By implementing the above-mentioned steps of the embodiment of the invention, can obtain the solar-grade polysilicon that purity is 5.8N, this solar-grade polysilicon can directly carry out the microsection manufacture solar cell, and the solar cell photoelectric efficiency of conversion of made can reach more than 14%.
By the selection of the chemical additive in above steps, can obtain P type or N type polysilicon respectively, wherein can be controlled at respectively in the scope that helps most making the opto-electronic conversion behind the battery as the content that the phosphorus of electronics or hole carrier and boron are provided.
More than by specific embodiment the present invention is had been described in detail, but these are not to be construed as limiting the invention.Under the situation that does not break away from the principle of the invention, those skilled in the art also can make many distortion and improvement, and these also should be considered as protection scope of the present invention.
Claims (6)
1. the preparation method of a solar energy grade polycrystalline silicon is characterized in that, comprises following steps:
Step 1, be that the Pure Silicon Metal fragmentation of 3N becomes granularity at 20～80 millimeters bulk silicon material, clean the pollution of removing described silicon material surface, put into vacuum melting furnace purity;
Step 2, put into the reagent of 25ppm in described vacuum melting furnace, this reagent is made up of silicon-dioxide, calcium oxide and barium oxide, and the mass ratio of described three kinds of components is 3: 3: 4;
Step 3, to described vacuum melting stove evacuation, arrive after the vacuum reheat and heat up and make described silicon material fusing, follow-up continuous 1600 degree that are warmed up to of described silicon material fusing;
Step 4, in described vacuum melting furnace, feed hydrogen, gas flow be per minute 2 to be raised to 20 liters, air pressure be normal pressure, aeration time is 2 hours;
Step 5, described vacuum melting furnace is progressively lowered the temperature, make described fused silicon material begin cooling from the bottom, and upwards solidify, form silicon ingot at last from the bottom;
Described silicon ingot is taken out in step 6, blow-on, and bottom, the top of excising described silicon ingot reach part all around, and the remainder of resulting described silicon ingot is the solar energy grade polycrystalline silicon silicon ingot just.
2. the preparation method of solar energy grade polycrystalline silicon as claimed in claim 1 is characterized in that:
The boron content of Pure Silicon Metal described in the step 1 less than 5ppm, phosphorus content less than 15ppm, metallic impurity total content less than 1000ppm.
3. the preparation method of solar energy grade polycrystalline silicon as claimed in claim 1 is characterized in that:
Reagent described in the step 2 is clipped in the described silicon material equably.
4. the preparation method of solar energy grade polycrystalline silicon as claimed in claim 1 is characterized in that:
Vacuum melting furnace described in the step 3 begins heat temperature raising when its vacuum pressure is 100 handkerchiefs, during the fusing of described silicon material and the vacuum pressure in the follow-up temperature-rise period be less than 1 handkerchief.
5. the preparation method of solar energy grade polycrystalline silicon as claimed in claim 1 is characterized in that:
The purity of the hydrogen that feeds in the step 4 is greater than 99.999%.
6. the preparation method of solar energy grade polycrystalline silicon as claimed in claim 1 is characterized in that:
The speed of directional freeze is per hour 6～20 millimeters in the step 5.