CN102092009A - Ceramic bond diamond finishing wheel - Google Patents
Ceramic bond diamond finishing wheel Download PDFInfo
- Publication number
- CN102092009A CN102092009A CN 201010583049 CN201010583049A CN102092009A CN 102092009 A CN102092009 A CN 102092009A CN 201010583049 CN201010583049 CN 201010583049 CN 201010583049 A CN201010583049 A CN 201010583049A CN 102092009 A CN102092009 A CN 102092009A
- Authority
- CN
- China
- Prior art keywords
- ceramic bond
- diamond
- bond diamond
- percent
- grinding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a ceramic bond diamond finishing wheel consisting of a metal core, a binding layer and a ceramic bond diamond working layer. The ceramic bond diamond working layer comprises the following raw material components in percentage by weight: 25 to 40 percent of the ceramic bond, and 60 to 75 percent of diamond grinding material, wherein the ceramic bond comprises the following raw material components in percentage by weight: 45 to 60 percent of SiO2, 0 to 3 percent of Al2O3, 30 to 45 percent of B2O3, 2 to 5 percent of ZnO, 3 to 5 percent of P2O5, and 1 to 4 percent of Li2O. The ceramic bond diamond finishing wheel provided by the invention has the advantages of high hardness, high self-sharpening performance, adjustable thickness and hardness of the working layer, and greatly improved service life and finishing efficiency; and the ceramic bond diamond finishing wheel can be used for finishing grinding manufacture tools used in various grinding machines.
Description
Technical field
The invention relates to the abrasive machining tool that all kinds of grinding machines use, relate in particular to the roll dresser of abrasive machining tool.
Background technology
Grinding Technology is the key areas in the advanced manufacturing technology, is to realize High-speed machining, Precision Machining, the most effective, the most widely used basic technology technology of ultraprecise processing in the modern mechanical manufacturing.The grinding amount accounts for 30% ~ 40% of machining total amount.What rely in grinding is that grinding tool (emery wheel) is realized grinding and finished requirement on machining accuracy workpiece, the Grinding Process medium plain emery wheel is through abrasion wearing and tearing, abrasive wear, after wearing and tearing three cycles that come off, can form sand grains on its surface degrade not sharp, and stay many grinding particles obstruction emery wheel pores, so just be difficult to workpiece is carried out grinding.So, will be constantly in the process of grinding emery wheel be carried out surfacing or to the finishing of formed grinding wheel shape, reaches and remove the passivation abrasive particle, guarantee to have effective cutting edge of new abrasive particle and sufficient amount, thereby guarantee the dimensional accuracy of workpiece and the roughness on surface.The dresser that each special purpose grinder all can have a cover that emery wheel own is repaired, and trimmer is finished finishing by freeing wheel (roller) to emery wheel.
On the other hand, different grinding machines, different processing work shapes, dimensional accuracy etc., require the emery wheel of different specification size and shape, therefore in emery wheel preparation technology, great majority before being applied to grinding machine, the grinding wheel shape that emery wheel manufacturing firm all will provide according to the grinding user, size etc. to emery wheel repair, correction of the flank shape and dressing, and these all will be realized by freeing wheel.
Along with working (machining) efficiency, improving constantly of requirement on machining accuracy and continuing to bring out of difficult-to-machine material, the application of superhard material (diamond or cubic boron nitride) emery wheel in grinding more and more widely, and extra hard material grinding wheel is because of its material hardness characteristics, to its correction of the flank shape, the finishing difficulty is bigger, most widely used in the market is electroplated diamond roller (as: ZL 200520029838.X rotary diamond dresser, CN101663133A internal tooth colyliform diamond truer), and the diamond that plays the finishing effect in the plating roller has only skim, so it is limited that be durability its service time, when especially diamond or cubic boron nitride superhard material emery wheel being repaired, the wearing and tearing of roller and consumption are more obvious, need several electroplated diamond rollers just can finish the finishing of an extra hard material grinding wheel sometimes.Simultaneously, electroplate roller and can not carry out performance adjustment such as hardness according to processing object to reach best dressing efficiency.
Summary of the invention
The objective of the invention is service life and working (machining) efficiency, a kind of adjustable ceramic bond diamond freeing wheel of good self-sharpening, working lining hardness and thickness that has is provided in order to improve freeing wheel.
Diamond dressing wheel of the present invention is by metal-cored (metallic matrix) and ceramic bond diamond working lining and tack coat 31
Part is formed, its specification can be according to the specification requirement of grinding machine and trimmer, the thickness of its working lining can be regulated arbitrarily, be far longer than the working lining thickness of the electroplated diamond roller of prior art, and vitrified bond itself has characteristics such as hardness height, great thermotolerance, self-sharpening be good, sharp, therefore, can frequently change freeing wheel and improve the service life and the working (machining) efficiency of freeing wheel greatly.The working lining of diamond dressing wheel by vitrified bond and diamond is complex sintered forms.
The present invention is achieved by following technical solution.
Ceramic bond diamond freeing wheel of the present invention is made up of metal-cored, tack coat and ceramic bond diamond working lining; It is characterized in that the raw material components of described ceramic bond diamond working lining and weight percent content thereof are: 25～40% vitrified bonds and 60～75% diamond abrasives; The raw material components of described vitrified bond and weight percent content thereof are: 45～60% SiO
2, 0～3% Al
2O
3, 30～45% B
2O
3, 2～5% ZnO, 3～5% P
2O
5, 1～4% Li
2O.
Described diamond abrasive granularity is arbitrary granularity or the arbitrary combination grain between 50～300mm.
Described metal-cored be steel or Al-alloy metal core.
The thickness and the hardness of described ceramic bond diamond working lining are adjustable.
The specification of described ceramic bond diamond freeing wheel is not limit.
The sintering temperature of described ceramic bond diamond freeing wheel is lower than 800 ℃.
Freeing wheel interacts with grinding tool when work, in the time of its finishing grinding tool, self also can be subjected to blunt or produce under the stress effect coming off, and influence finishing effect or ineffective.For the electroplated diamond freeing wheel of prior art, it has only the skim diamond, is easy to come off fully, and is ineffective; And for the ceramic bond diamond freeing wheel, vitrified bond itself belongs to crisp hard material, its outer blunt particle is easy to come off, the not new sharper diamond abrasive grain of wearing and tearing that can expose internal layer in the time of the blunt particle detachment, make it remain good finishing effect and efficient, and so forth, up to the working lining of using up the whole freeing wheel of diamond.Therefore, good self-sharpening that itself has and thicker working lining thickness make it have good dressing efficiency and service life, can reach 10～30 times of electroplated diamond freeing wheel its service life.In addition, for adapting to the development of grinding machine and continuing to bring out of new material, the performance of grinding tool is more and more abundanter, the performance of dressing tool also will constantly change naturally to adapt to the demand of grinding tool development, and the hardness of electroplated diamond layer in the electroplated diamond freeing wheel, tissue, pore, diamond concentrations etc. are nonadjustable, but the working lining hardness of ceramic bond diamond freeing wheel, tissue, pore, diamond concentrations etc. all can design and adjust as required, can be at the hardness and the performance characteristics of different grinding tools, carry out preparing targetedly personalizedly and regulating, also make it can be more effectively, carry out the finishing of grinding tool targetedly.
The invention has the beneficial effects as follows that a kind of adjustable ceramic bond diamond freeing wheel of good self-sharpening, working lining hardness and thickness that has is provided, and its durability than the prior art freeing wheel (service life) and dressing efficiency improve greatly.
Description of drawings
Fig. 1 is the front view of ceramic bond diamond freeing wheel schematic diagram.
Description of reference numerals is as follows:
2
1-ceramic bond diamond working lining, 2-tack coat 3-metal-cored
The specific embodiment
Below in conjunction with specific embodiment the present invention is further described.
Development along with manufacturing technology, require more and more higher to the dimensional accuracy of various parts, geometric accuracy, surface state etc., and grinding is to realize the high accurately machined a kind of important machining process of various parts, especially in recent years the raising that requires along with grinding machine Development of Preparation Technology and machined, grinding is applied to field of machining more and more widely.Grinding generally is the later process that belongs to part, i.e. the fine finishining of part.Be stranded dimensional accuracy and the positional precision of correlation surface and the form accuracy and the surface smoothness on relevant surface of this part, all will in grinding, must control to the end and guarantee.And these guarantee except the performance of grinding machine itself, most critical be exactly shape and size precision and the surface state that is used for realizing the emery wheel of grinding.Emery wheel self also is squeezed in the grinding workpiece, wearing and tearing, fire damage etc., the wheel face abrasive particle also can come off, passivation, and the accumulation scrap stops up pore etc., therefore, need carry out surfacings such as correction of the flank shape, dressing termly to wheel face according to different emery wheels and grinding condition.
Diamond is the present industrial the hardest material of being used, and has therefore born the finishing task to various abrasive grinding wheels duty-boundly.But itself belongs to ridgity material diamond abrasive, rely on other material to mutually combine and finalize the design and guarantee certain bond strength, owing to technical reason, past all is to electroplate one deck diamond as freeing wheel at metal base surface, and electrodeposited coating is very thin, the hardness that is easy to attrition and can not regulates working lining effectively at different finishing objects.Along with the ripe and development of ceramic bond diamond goods technology of preparing, can adopt the ceramic bond diamond roller fully as freeing wheel.The ceramic bond diamond freeing wheel combines ceramic material and diamond advantage separately, and can regulate the hardness of diamond dressing wheel working lining as required, to reach best dressing efficiency and effect, and the thickness of diamond working layers is far longer than the prior art thickness of plating layer, and ceramic bond diamond working lining thickness is adjustable as required, the service life of having improved freeing wheel greatly.
The specific embodiment is:
Step (1) is at first according to proportion of composing, the density of tissue, diamond and the bond of the material of trimming wheel and hardness design freeing wheel (roller).
Step (2) is calculated the moulding substance of diamond roller according to the specification of freeing wheel.
Step (3) according to the prescription of step (1), (2) prepare burden, batch mixing and moulding.
The specific embodiment of the working lining of preparation ceramic bond diamond correction wheel sees table 1 for details.
Table 1
| № | Diamond abrasive (%) | Vitrified bond (%) |
| Embodiment 1 | 75 | 25 |
| Embodiment 2 | 65 | 35 |
| Embodiment 3 | 60 | 40 |
3
In order to make composition in the vitrified bond carry out fully, interact equably, in the hope of can more effectively controlling the structural homogenity of ceramic bond diamond freeing wheel, the raw material that will take by weighing by proportioning at first, through mix, 1200 ℃ of meltings, quenching,
Pulverize and make the vitrified bond powder.The vitrified bond raw material is conventional industrial chemicals, and specific embodiment sees table 2 for details
Table 2
| № | SiO 2 | Al 2O 3 | B 2O 3 | ZnO | P 2O 5 | Li 2O |
| Embodiment 1 | 45 | 1.5 | 45 | 2.5 | 5 | 1 |
| Embodiment 2 | 51 | 3 | 35 | 5 | 3 | 3 |
| Embodiment 3 | 60 | 0 | 30 | 2 | 4 | 4 |
Step (4): the blank of step (3) moulding is being carried out sintering below 800 ℃.
Step (5): the processing metal core, and guarantee metal-cored within the mechanical connection of hole dimension precision and trimmer, outside in footpath and step (4) sintered body through just identical.
Step (6) is embedded in the metal-cored bonding of step (5) processing in the sintered body of step (4), and tack coat adopts the epoxy organic adhesion agent.Tack coat to guarantee the ceramic bond diamond freeing wheel and metal-cored between do not have big slit, pressurize then, solidify.
Step (7) is carried out the finishing of removing surface and outward appearance with the freeing wheel release that is cured.
The present invention is not limited to the foregoing description, and the variation of a lot of details is possible, but therefore this do not run counter to scope and spirit of the present invention.
Claims (6)
1. ceramic bond diamond freeing wheel is made up of metal-cored, tack coat and ceramic bond diamond working lining; It is characterized in that the raw material components of described ceramic bond diamond working lining and weight percent content thereof are: 25～40% vitrified bonds and 60～75% diamond abrasives; The raw material components of described vitrified bond and weight percent content thereof are: 45～60% SiO
2, 0～3% Al
2O
3, 30～45% B
2O
3, 2～5% ZnO, 3～5% P
2O
5, 1～4% Li
2O.
2. ceramic bond diamond freeing wheel according to claim 1 is characterized in that, described diamond abrasive granularity is arbitrary granularity or the arbitrary combination grain between 50～300mm.
3. ceramic bond diamond freeing wheel according to claim 1 is characterized in that, described metal-cored be steel or Al-alloy metal core.
4. ceramic bond diamond freeing wheel according to claim 1 is characterized in that, the thickness and the hardness of described ceramic bond diamond working lining are adjustable.
5. ceramic bond diamond freeing wheel according to claim 1 is characterized in that the specification of described ceramic bond diamond freeing wheel is not limit.
6. ceramic bond diamond freeing wheel according to claim 1 is characterized in that, the sintering temperature of described ceramic bond diamond freeing wheel is lower than 800 ℃.