CN102091636A - Catalyst and preparation method thereof - Google Patents
Catalyst and preparation method thereof Download PDFInfo
- Publication number
- CN102091636A CN102091636A CN2010102776714A CN201010277671A CN102091636A CN 102091636 A CN102091636 A CN 102091636A CN 2010102776714 A CN2010102776714 A CN 2010102776714A CN 201010277671 A CN201010277671 A CN 201010277671A CN 102091636 A CN102091636 A CN 102091636A
- Authority
- CN
- China
- Prior art keywords
- nitrate
- active carbon
- preparation
- weighing
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a catalyst and a preparation method thereof. The preparation method comprises the following steps of: weighing 1kg of carrier active carbon; removing impurities and dust with clear water; weighing 20g of copper nitrate, 150g of ferric nitrate, 80g of nickel nitrate, 30g of manganous nitrate, 20g of potassium nitrate, 1ml of titanium tetrachloride, 5g of sodium metavanadate and 15g of cobalt nitrate and mixing and dissolving; then charging the cleaned active carbon into a prepared solution and soaking for 48 hours; fully adsorbing metal salt by the active carbon; after completely soaking, drying in the sun; after drying in the sun, charging the metal salt into an oven for curing at high temperature; after curing, discharging and naturally cooling; and then screening and packaging a finished product for storage. The invention has the advantage of effectively removing heavy metal ions and organic matter enriched in sewage treatment.
Description
[technical field]
The present invention relates to a kind of sewage catalyst technical field, be specifically related to a kind of technical field of Catalysts and its preparation method.
[background technology]
Well-known water pollutes the pollutant that is mainly produced by mankind's activity to be caused, and it comprises industrial pollution source, agricultural pollution source and domestic pollution source three parts.Characteristics such as industrial wastewater is the important pollution sources in waters, and the amount of having is big, wide, complicated component, toxicity big, be difficult for purifying, difficult.Show according to water resources in china communique data in 1998: this year, totally 539 hundred million tons of national wastewater emission amounts (not comprising fiery constant current cooling water), wherein, 40,900,000,000 tons of discharged volume of industrial waste water account for 69%.In fact, water amount of blowdown is considerably beyond this number, because many township enterprises trade effluent discharge capacity is difficult to statistics.Agricultural pollution source comprises excrement of animals, agricultural chemicals, chemical fertilizer etc.In the pesticide sewage, the one, organic matter, plant nutrient and pathogenic microorganism content height, the 2nd, agricultural chemicals, chemical fertilizer content height.China does not carry out the monitoring on the agriculture face at present, shows according to interrelated data, and on 100,000,000 hectares of arable lands and 2,200,000 hectares of grassland, annual 110.49 ten thousand tons in the agricultural chemicals that uses.China is one of country of punishing severely most of soil erosion in the world, about 5,000,000,000 tons of the native number of dropouts of annual table, cause a large amount of agricultural chemicals, chemical fertilizer to flow into river, river, lake, storehouse with table soil, the nitrogen of Liu Shiing, phosphorus, potassium nutrition element thereupon, make 2/3 lake be subjected to the harm of eutrophication pollution in various degree, cause algae and other biological to breed unusually, cause the variation of water transparency and dissolved oxygen, thereby cause water quality deterioration.Domestic pollution source mainly is the various washing agent that use in the urban life and sewage, rubbish, ight soil etc., mostly is nontoxic inorganic salts, and nitrogenous in the sanitary sewage, phosphorus, sulphur are many, and malignant bacteria is many.According to investigations, China's sanitary sewage discharge capacity in 1998 is 18,400,000,000 tons.China has 1/3 industrial wastewater and the 90% above unprocessed waters that just enters of sanitary sewage every year approximately, the whole nation has in more than 1200 river of monitoring, present more than 850 are polluted, urban waters more than 90% is also polluted, cause the disappearance of many sections fishes and shrimps, meet country-level and the river secondary water standard only accounts for 32.2%.Pollute and just developed to deep layer by shallow-layer, underground water and territory, coastal waters seawater are also polluted, and the water that we can drink and use reduces unawares.And along with the level of urbanization of China improves and industrial expansion, trade effluent and city domestic sewage are more and more serious.
And traditional sewage disposal is generally drawn sewage toward collecting-tank, to collecting-tank end one style joint pH, rise to the first class pressure dissolving with one-level dissolved air water pump, suck air and coacervation decolorizer simultaneously, will be discharged into the one-level flotation tank at the one-level saturated dissolved gas water in the first class pressure dissolving suddenly and form one-level processing water; One-level is handled water and is overflowed into Buffer Pool, one-level being handled water at control pH with secondary dissolved air water pump again is promoted in the secondary pressure dissolving, suck air and coacervation decolorizer simultaneously, the secondary saturated dissolved gas water in the secondary pressure dissolving is discharged into the secondary air-floatation pond suddenly forms secondary treated wastewater and discharge from overflowing to the sedimentation basin post precipitation; Mud scum in the I and II flotation tank is gone into the mud scum pond, and press filtration becomes filter cake, and filtrate returning causes collecting-tank.This processing method often needs long time and more complicated flow process just can reach discharging standards water quality.
[summary of the invention]
For solving above deficiency, the invention provides a kind of a kind of Catalysts and its preparation method that is applicable to sewage disposal, catalyst by the preparation of this method can be effectively and the heavy metal ion in the sewage and its reaction of organic matter, and clean effect is obvious, has very strong practical function.
The problem to be solved in the present invention is how to add a kind of catalyst can effectively remove heavy metal ion and the organic matter that is rich in the sewage in sewage, making sewage reach discharging standards enters natural environment and does not make water system ecological deterioration and this method for preparing catalyst.
A kind of Catalysts and its preparation method takes by weighing the 1KG carrier active carbon, remove impurity and dust with clear water, take by weighing copper nitrate 20G, ferric nitrate 150G, nickel nitrate 80G, manganese nitrate 30G, potassium nitrate 20G, titanium tetrachloride 1ML, sodium metavanadate 5G, cobalt nitrate 15G mixed dissolution, then cleaned active carbon being put into the solution for preparing flooded 48 hours, slaine is fully absorbed by active carbon, dry after dipping is good, put into the baking oven hot setting after drying, the nature cooling of coming out of the stove that solidifying finishes, the finished product that sieves then is packaged into the storehouse.
Described a kind of Catalysts and its preparation method is characterized in that described molten metal dip time is 36 hours-48 hours.
The temperature that described a kind of Catalysts and its preparation method is characterized in that putting into the baking oven hot setting is 280 degree-320 degree, and the time of hot setting is 12-15 hour.
Metal ion and organic matter course of reaction in this catalyst and the sewage,
C
mHn+O
3--→CO
2↑+H
2O
Fe+2H
2--→Fe
3++H
2↑ Fe
3++3OH
---→Fe(OH)
3↓
Fe+CU
2+--→ Fe
2++ Cu ↓ Fe+Zn
2+--→ Fe
2++ Zn ↓ (other heavy metal courses of reaction are identical)
Get the above-mentioned catalyst for preparing, with dioxygen water level oxidant, the waste water of the waste water of certain pigment factory is carried out catalytic oxidation treatment, 32 times of water inlet CODcr (725mg/l), colourities, CODcr after the water outlet (89mg/l), CODcr clearance 90.6%, colourity extraction efficiency are 97.8%.
Beneficial effect of the present invention: the present invention effectively removes heavy metal ion and the organic matter that sewage disposal is rich in.
Further understand feature of the present invention and technology contents for making, see embodiment of the present invention for details, yet the embodiment of institute is only for reference and explanation usefulness, and the present invention is limited.
[specific embodiment]
The invention will be further described below in conjunction with embodiment.
Embodiment 1 takes by weighing the 1KG carrier active carbon, remove impurity and dust with clear water, take by weighing copper nitrate 20G, ferric nitrate 150G, nickel nitrate 80G, manganese nitrate 30G, potassium nitrate 20G, titanium tetrachloride 1ML, sodium metavanadate 5G, cobalt nitrate 15G mixed dissolution, then cleaned active carbon being put into the solution for preparing flooded 48 hours, slaine is fully absorbed by active carbon, dip time is 36-48 hour, dry after dipping is good, put into the baking oven hot setting after drying, the temperature of hot setting is the 280-320 degree, the time of hot setting is 12-15 hour, the nature cooling of coming out of the stove that solidifying finishes, and the finished product that sieves then is packaged into the storehouse.
Embodiment 2 takes by weighing the 1KG carrier active carbon, remove impurity and dust with clear water, take by weighing copper nitrate 20G, ferric nitrate 120G, nickel nitrate 100G, manganese nitrate 40G, potassium nitrate 20G, titanium tetrachloride 1ML, sodium metavanadate 5G, cobalt nitrate 15G mixed dissolution, then cleaned active carbon being put into the solution for preparing flooded 48 hours, slaine is fully absorbed by active carbon, dip time is 36 hours, dry after dipping is good, put into the baking oven hot setting after drying, the temperature of hot setting is 280 degree, the time of hot setting is 12 hours, the nature cooling of coming out of the stove that solidifying finishes, and the finished product that sieves then is packaged into the storehouse.
Embodiment 3 takes by weighing the 1KG carrier active carbon, remove impurity and dust with clear water, take by weighing copper nitrate 20G, ferric nitrate 150G, nickel nitrate 90G, manganese nitrate 25G, potassium nitrate 15G, titanium tetrachloride 1ML, sodium metavanadate 5G, cobalt nitrate 15G mixed dissolution, then cleaned active carbon being put into the solution for preparing flooded 48 hours, slaine is fully absorbed by active carbon, dip time is 36-48 hour, dry after dipping is good, put into the baking oven hot setting after drying, the temperature of hot setting is the 280-320 degree, the time of hot setting is 12-15 hour, the nature cooling of coming out of the stove that solidifying finishes, and the finished product that sieves then is packaged into the storehouse.
Embodiment 4 takes by weighing the 1KG carrier active carbon, remove impurity and dust with clear water, take by weighing copper nitrate 20G, ferric nitrate 130G, nickel nitrate 90G, manganese nitrate 35G, potassium nitrate 25G, titanium tetrachloride 1ML, sodium metavanadate 5G, cobalt nitrate 15G mixed dissolution, then cleaned active carbon being put into the solution for preparing flooded 48 hours, slaine is fully absorbed by active carbon, dip time is 36-48 hour, dry after dipping is good, put into the baking oven hot setting after drying, the temperature of hot setting is the 280-320 degree, the time of hot setting is 12-15 hour, the nature cooling of coming out of the stove that solidifying finishes, and the finished product that sieves then is packaged into the storehouse.
Yet the preferable feasible embodiment of above-mentioned only the present invention, non-so limitation protection domain of the present invention is done various distortion or is applied mechanically all within this technical scheme protection domain according to the foregoing description.
Claims (3)
1. a Catalysts and its preparation method takes by weighing the 1KG carrier active carbon, remove impurity and dust with clear water, take by weighing copper nitrate 20G, ferric nitrate 150G, nickel nitrate 80G, manganese nitrate 30G, potassium nitrate 20G, titanium tetrachloride 1ML, sodium metavanadate 5G, cobalt nitrate 15G mixed dissolution, then cleaned active carbon being put into the solution for preparing flooded 48 hours, slaine is fully absorbed by active carbon, dry after dipping is good, put into the baking oven hot setting after drying, the nature cooling of coming out of the stove that solidifying finishes, the finished product that sieves then is packaged into the storehouse.
2. a kind of Catalysts and its preparation method according to claim 1 is characterized in that described molten metal dip time is 36 hours-48 hours.
3. the temperature that a kind of Catalysts and its preparation method according to claim 1 is characterized in that putting into the baking oven hot setting is 280 degree-320 degree, and the time of hot setting is 12-15 hour.