CN102090382B - Method for improving strength of nylon fishing line after being knotted - Google Patents
Method for improving strength of nylon fishing line after being knotted Download PDFInfo
- Publication number
- CN102090382B CN102090382B CN2010105940848A CN201010594084A CN102090382B CN 102090382 B CN102090382 B CN 102090382B CN 2010105940848 A CN2010105940848 A CN 2010105940848A CN 201010594084 A CN201010594084 A CN 201010594084A CN 102090382 B CN102090382 B CN 102090382B
- Authority
- CN
- China
- Prior art keywords
- nylon
- raw material
- improving
- raw materials
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a method for improving the strength of a nylon fishing line after being knotted, and the method comprises the following steps: adding 0.1-2% stearic amide and 0.1-2% ethylene bis(stearamide) into raw materials, respectively processing into white powder, uniformly mixing, and then processing based on original process steps and process conditions, namely sequentially carrying out the steps of drying of the raw materials, melting of the raw materials, spinning, cooling and molding, drawing, oiling and moistening, stretching and shaping, and final winding. By utilizing the stearic amide and the ethylidene bis(stearamide), wherein the stearic amide can be used for improving the softness and toughness of nylon yarn and improving the strength of the nylon yarn when the yarnis knotted; the ethylene bis(stearamide) have functions of demoulding, improving the resistance to bond, improving the antistatic role, improving the lubrication of nylon chips in a screw rod and assisting flow; after the additives are added, the knot strength of the fishing line is improved to 0.72-0.8 compared with the linear strength ratio, thus requirements are met, and the problem that the strength of a nylon single filament serving as the fishing line after being knotted is reduced is solved.
Description
Technical field
The present invention relates to the setline product technical field, relate in particular to a kind of setline of making by nylon yarn.
Background technology
Along with expanding economy and growth in the living standard, people's life and operating pressure are also in quick increase, and this pressure continues to increase and can produce harmful effect to health, and therefore, people need adopt various ways to come release pressure.Past people is often loosened body and mind through modes such as having a dinner party, play Karaoka, play card, and afterwards, it also was not too healthy that these methods are proved to be, modes such as present popular mode joins into sports, climbs the mountain, goes on a tour, fishing.Wherein fishing receives vast social personage's on the middle and senior level welcome deeply, and its cost is low, can enjoy than higher sense of accomplishment again, is popular activity, therefore becomes more and more popular.At present; The silkworm gut of fishing usefulness mainly contains: nylon wire, carbon element line, wire, cloth litzendraht wire, synthetic thread, ceramic thread etc.; Wherein, nylon yarn is that application is maximum, and nylon yarn is through drying, fusion, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting with polyamide; Reeling at last forms, and its advantage is to have good ductility and elasticity.At present, nylon monofilament as the major defect of setline is: the powerful powerful ratio when not tiing a knot in nylon yarn knotting back is below 0.5, that is to say that the intensity of knotting back setline can reduce a lot.
Summary of the invention
The technical problem that the present invention will solve provides a kind of method that can effectively solve the problem of setline knotting back intensity decline.
For solving the problems of the technologies described above; The present invention adopts following technical scheme: a kind of method that improves nylon setline knotting back intensity; Production process may further comprise the steps: raw material drying, raw materials melt, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting; Reel at last; It is characterized in that: in raw material, add the stearmide that can improve nylon yarn softness, toughness, and the ethylenebisstearamide that can improve resistance to bond, antistatic property, and mix; According to original processing step and process conditions mixed raw materials is processed the step of promptly get into raw material drying, raw materials melt, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting successively, reeling at last then.
Further, earlier stearmide and ethylenebisstearamide are processed into white powder respectively, and then mix with raw material.
Further, the addition of stearmide is the 0.01-2% of raw material total amount, and the addition of ethylenebisstearamide is the 0.01-2% of raw material total amount.
The present invention is through adding stearmide and ethylenebisstearamide, and wherein the effect of stearmide is softness, a toughness of improving nylon yarn, and the intensity of nylon yarn is improved when making the silk knotting; The function of ethylenebisstearamide has been the demoulding effect, improves resistance to bond, improves antistatic property; Improve the lubricity of nylon chips in screw rod; Play and help the stream effect, add the knot strength and the powerful ratio of straight line of setline behind the above-mentioned auxiliary agent and bring up to 0.72-0.8, the knot strength that is about to setline improves about 30%; Can meet the demands fully, solve nylon monofilament as the powerful problem that descends in setline knotting back.
Embodiment
Below in conjunction with specific embodiment the present invention is further specified:
Embodiment 1; The production process of this nylon setline may further comprise the steps: raw material drying, raw materials melt, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting; Reel at last; In raw material, add the stearmide that can improve nylon yarn softness, toughness, and the ethylenebisstearamide that can improve resistance to bond, antistatic property, and mix; According to original processing step and process conditions mixed raw materials is processed the step of promptly get into raw material drying, raw materials melt, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting successively, reeling at last then.Earlier stearmide and ethylenebisstearamide are processed into white powder respectively during interpolation, and then mix with raw material.The addition of stearmide is 0.01% of a raw material total amount, and the addition of ethylenebisstearamide is 0.01% of a raw material total amount.
[0009]Embodiment 2; The production process of this nylon setline may further comprise the steps: raw material drying, raw materials melt, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting; Reel at last; In raw material, add the stearmide that can improve nylon yarn softness, toughness, and the ethylenebisstearamide that can improve resistance to bond, antistatic property, and mix; According to original processing step and process conditions mixed raw materials is processed the step of promptly get into raw material drying, raw materials melt, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting successively, reeling at last then.Earlier stearmide and ethylenebisstearamide are processed into white powder respectively during interpolation, and then mix with raw material.The addition of stearmide is 1% of a raw material total amount, and the addition of ethylenebisstearamide is 1% of a raw material total amount.
Embodiment 3; The production process of this nylon setline may further comprise the steps: raw material drying, raw materials melt, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting; Reel at last; In raw material, add the stearmide that can improve nylon yarn softness, toughness, and the ethylenebisstearamide that can improve resistance to bond, antistatic property, and mix; According to original processing step and process conditions mixed raw materials is processed the step of promptly get into raw material drying, raw materials melt, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting successively, reeling at last then.Earlier stearmide and ethylenebisstearamide are processed into white powder respectively during interpolation, and then mix with raw material.The addition of stearmide is 2% of a raw material total amount, and the addition of ethylenebisstearamide is 2% of a raw material total amount.
The powerful powerful ratio when not tiing a knot in conventional nylon single line setline knotting back is below 0.5, and the setline of making according to embodiment 1, and the powerful powerful ratio when not tiing a knot in its knotting back is 0.73; According to the setline that embodiment 2 makes, the powerful powerful ratio when not tiing a knot in its knotting back is 0.77; According to the setline that embodiment 3 makes, the powerful powerful ratio when not tiing a knot in its knotting back is 0.73.
Below the present invention is done a detailed description, the above is merely the present invention's preferred embodiment, when can not limiting practical range of the present invention, promptly allly does impartially to change and modify according to the application's scope, all should still belong in the covering scope of the present invention.
Claims (2)
1. one kind is improved the nylon setline knotting method of intensity afterwards; Production process may further comprise the steps: raw material drying, raw materials melt, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting; Reel at last; It is characterized in that: in raw material, add the stearmide that can improve nylon yarn softness, toughness, and the ethylenebisstearamide that can improve resistance to bond, antistatic property, and mix; According to original processing step and process conditions mixed raw materials is processed the step of promptly get into raw material drying, raw materials melt, spray silk, cooling forming, drawing-off, oil supply dewing, drawing and setting successively, reeling at last then; Wherein, the addition of stearmide is the 0.01-2% of raw material total amount, and the addition of ethylenebisstearamide is the 0.01-2% of raw material total amount.
2. the method for raising nylon setline knotting according to claim 1 back intensity is characterized in that: earlier stearmide and ethylenebisstearamide are processed into white powder respectively, and then mix with raw material.