CN102079644B - 砂浆胶 - Google Patents
砂浆胶 Download PDFInfo
- Publication number
- CN102079644B CN102079644B CN201010604336A CN201010604336A CN102079644B CN 102079644 B CN102079644 B CN 102079644B CN 201010604336 A CN201010604336 A CN 201010604336A CN 201010604336 A CN201010604336 A CN 201010604336A CN 102079644 B CN102079644 B CN 102079644B
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- mortar glue
- mortar
- water reducer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种砂浆胶,本砂浆胶中各组分的重量份分别为:醋酸乙烯胶粉或丙烯酸胶粉17.5份~32.5份、羟丙甲基纤维素/或瓜耳胶3.5份~6.5份、矿物油和/或有机硅0.35份~0.65份、碳酸钙和/或石英砂48.3份~89.7份、减水剂0.35份~0.65份。本发明的砂浆胶可解决现有技术中水泥砂浆铺贴瓷砖等建筑材料时粘结不牢、空鼓、开裂、脱落、性能不稳定等难题。本发明的砂浆胶加入水泥砂浆中后使得水泥砂浆的施工性能好,水泥砂浆不下垂、不流挂、晾置调整时间长。加入本发明砂浆胶的水泥砂浆在施工过程中不用浸砖湿墙,施工连贯,提高了施工效率。本发明砂浆胶无毒、无异味,属于环保产品。
Description
技术领域
本发明属于建筑用水泥砂浆技术领域,具体的说是涉及一种砂浆胶。
背景技术
水泥砂浆是建筑工程中最常用的建筑材料,并且在建筑材料中占有很大的比重,是不可或缺的建筑材料之一。
中国发明专利(专利号为200610009998.7)公开了一种建筑砂浆胶凝材,其重量百分比组成为粉煤灰60-70%、水泥熟料25-35%和添加剂4-6%,其中,添加剂的重量百分比组成为羟甲基纤维素15-25%、三萜皂甙10-20%、木质素磺酸钙30-40%、甲基苯肼盐酸盐15-25%和磷酸盐7-13%。该建筑砂浆胶凝材用于工业、民用建筑中的砌筑、内墙抹灰的砂浆中。
然而,在铺贴时,上述建筑砂浆胶凝材由于气候温差太大,长期热胀冷缩,往往会出现粘结不牢、空鼓、开裂、脱落和水泥砂浆性能不稳定等缺陷,这些缺陷给建筑施工的技术人员带来很多难题。同时,上述建筑砂浆胶凝材的缺陷也给消费者带来很大的困扰。
因此,现有技术中亟需出现一种能够克服水泥砂浆上述缺陷,粘结牢、不易空鼓、不易开裂、不易脱落和性能稳定的砂浆胶。
发明内容
本发明的目的在于克服现有技术中的缺陷,提供一种能够使水泥砂浆粘结牢固、性能稳定的砂浆胶。
本发明的目的是通过以下方案来实现的:一种砂浆胶,本砂浆胶中各组分的重量份分别为:醋酸乙烯胶粉或丙烯酸胶粉17.5份~32.5份、羟丙甲基纤维素和/或瓜耳胶3.5份~6.5份、矿物油和/或有机硅0.35份~0.65份、碳酸钙和/或石英砂48.3份~89.7份、减水剂0.35份~0.65份。
作为本发明优选的实施方式,本砂浆胶各组分的重量份分别为:醋酸乙烯胶粉或丙烯酸胶粉20份~30份、羟丙甲基纤维素和/或瓜耳胶4~6份、矿物油和/或有机硅0.4份~0.6份、碳酸钙和/或石英砂55份~80份、减水剂0.4份~0.6份。
作为本发明的最佳实施方式,本砂浆胶各组分的重量份分别为:醋酸乙烯胶粉或丙烯酸胶粉25份、羟丙甲基纤维素和/或瓜耳胶5份、矿物油和/或有机硅0.5份、碳酸钙和/或石英砂69份、减水剂0.5份。
所述减水剂为聚羧酸系减水剂。
所述减水剂为密胺系减水剂。
本发明的优点在于:本发明的砂浆胶是由改性的聚合物优质胶粉和多种添加剂配制而成的单组份粉状水泥砂浆改良添加剂,本发明的砂浆胶加入后既保留了水泥砂浆的特性,又结合有机聚合物优质胶粉高粘结度的特点,可解决现有技术中水泥砂浆铺贴瓷砖等建筑材料时粘结不牢、空鼓、开裂、脱落、性能不稳定等难题。加入本发明砂浆胶的水泥柔韧性好,适应基材和瓷砖的变形,耐候性强。
表一:砂浆胶与纯水泥膏、普通水泥砂浆铺贴瓷砖时的粘结强度对比:
表二:砂浆胶与普通瓷砖胶的经济性能对比:
由表一可知,加入本发明砂浆胶的水泥砂浆的粘结强度最高。
由表二可知,加入砂浆胶的水泥砂浆不但粘结强度高,而且单位面积成本相比于普通瓷砖胶更低,真正实现了粘结效果好、成本低廉的有益效果,更加有利于大规模推广应用,更加经济实惠。表二中的施工方法为厚层施工法,砂浆胶是一种浓缩型瓷砖胶添加剂,1千克砂浆胶可制成25千克瓷砖胶,运输成本可降低90%以上,桶装砂浆胶贮存和搬运中可降低包装补损率和仓库使用率。
具体实施方式
下面结合具体实施例对本发明做进一步说明。
实施例1:一种砂浆胶,本砂浆胶中各组分的重量份分别为:醋酸乙烯胶粉或丙烯酸胶粉25份、羟丙甲基纤维素5份、矿物油0.5碳酸钙69份、聚羧酸系减水剂0.5份。将本发明的砂浆胶添加到水泥砂浆中,用于瓷砖铺贴:把本发明的砂浆胶用量杯装平顶2杯共计1千克倒入包装桶内,加清水至6升,用电动工具搅拌5分钟,让砂浆胶和清水充分融合,根据工程用量需要,直接和水泥、细砂搅拌混合即可使用。
实施例2:一种砂浆胶,本砂浆胶中各组分的重量份分别为:丙烯酸胶粉50份、瓜耳胶10份、有机硅1份、石英砂138份、聚羧酸系减水剂1份。将本发明的砂浆胶添加到水泥砂浆中,用于大理石和天然石材的铺贴:把本发明的砂浆胶用量杯装平顶4杯共计2千克倒入包装桶内,加清水至12升,用电动工具搅拌5分钟,让砂浆胶和清水充分融合,根据工程用量需要,直接和水泥、细砂搅拌混合即可使用。
实施例3:一种砂浆胶,本砂浆胶中各组分的重量份分别为:醋酸乙烯胶粉20份、羟丙甲基纤维素和瓜耳胶4份、矿物油和有机硅0.4份、碳酸钙和石英砂55份、密胺系减水剂0.4份。将本发明的砂浆胶添加到水泥膏中,用于界面拉毛:本发明的砂浆胶加水后,再与水泥混合搅拌成浆糊状,用工具抹到界面上即可。
实施例4: 一种砂浆胶,本砂浆胶各组分的重量份分别为:醋酸乙烯胶粉25份、羟丙四基纤维素5份、有机硅0.5份、石英砂60份、密胺系减水剂0.5份。本发明的砂浆胶应按砂浆胶:水:水泥:砂=1:6:12:12的配比使用,并且按照本发明的具体使用方法使用,即可得到最佳使用效果。
本发明的砂浆胶适宜在5℃~40℃的环境下使用,并且应避免高温、低温和室外阴雨天气。本发明的砂浆胶在粘贴瓷砖时,按规定混合后的液体不可再加水。本发明的砂浆胶用于薄层施工,每公斤砂浆胶可作业8平方;本发明砂浆胶用于厚层施工,每公斤砂浆胶可作业2.5平方。
综上所述,以上实施例不过是本发明砂浆胶的最佳实施方案,不可理解为对本发明保护范围的限定,对于该领域的技术工作人员根据本发明的实施例所做的不超出本发明技术方案的调整和改动,应认为落在本发明的保护范围内。
Claims (4)
1.一种砂浆胶,其特征在于:本砂浆胶中各组分的重量份分别为:醋酸乙烯胶粉或丙烯酸胶粉20份~30份、瓜耳胶4份~6份、矿物油和/或有机硅0.4份~0.6份、碳酸钙和/或石英砂55份~80份、减水剂0.4份~0.5份。
2.按照权利要求1所述的砂浆胶,其特征在于:各组分的重量份分别为:醋酸乙烯胶粉或丙烯酸胶粉25份、瓜耳胶5份、矿物油和/或有机硅0.5份、碳酸钙和/或石英砂69份、减水剂0.5份。
3.按照权利要求1或2所述的砂浆胶,其特征在于:所述减水剂为聚羧酸系减水剂。
4.按照权利要求1或2所述的砂浆胶,其特征在于:所述减水剂为密胺系减水剂。