CN102074619A - 一种非晶硅电池的简便绝缘处理方法 - Google Patents

一种非晶硅电池的简便绝缘处理方法 Download PDF

Info

Publication number
CN102074619A
CN102074619A CN2010105835752A CN201010583575A CN102074619A CN 102074619 A CN102074619 A CN 102074619A CN 2010105835752 A CN2010105835752 A CN 2010105835752A CN 201010583575 A CN201010583575 A CN 201010583575A CN 102074619 A CN102074619 A CN 102074619A
Authority
CN
China
Prior art keywords
battery
beaker
deionized water
aqueous solution
battery sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2010105835752A
Other languages
English (en)
Other versions
CN102074619B (zh
Inventor
赵宗芳
崔兆娜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN JINNENG SOLAR CELL CO Ltd
Original Assignee
TIANJIN JINNENG SOLAR CELL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN JINNENG SOLAR CELL CO Ltd filed Critical TIANJIN JINNENG SOLAR CELL CO Ltd
Priority to CN2010105835752A priority Critical patent/CN102074619B/zh
Publication of CN102074619A publication Critical patent/CN102074619A/zh
Application granted granted Critical
Publication of CN102074619B publication Critical patent/CN102074619B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种非晶硅电池的简便绝缘处理方法，处理方法的步骤是：(1)原材料准备；(2)溶液配制：称取于烧杯中，将去离子水倒入含有的烧杯中，再向烧杯中滴加15-20滴稀盐酸，即形成水溶液；(3)样品绝缘处理：室温条件下，将待绝缘电池片放置于平整的操作台上，并将其固定；(4)绝缘处理：取配制好的水溶液，沿一定的宽度将其均匀涂抹在电池板的铝膜上，2-3min之后，用去离子水将电池片上残留的溶液清除掉，并用丝布将电池片擦拭干净，防止电池片被深度腐蚀。本发明通过一种较为简便的方式实现了对非晶硅太阳电池片进行边绝缘处理，具有较好的绝缘效果、简易的操作方式和低成本等优势，对非常规电池板的研发生产具有极大优势。

Description

一种非晶硅电池的简便绝缘处理方法
技术领域
本发明属于光伏发电应用技术领域，尤其是一种非晶硅电池的简便绝缘处理方法。
背景技术
对于非晶硅太阳电池而言，边上绝缘电阻很重要。通常的绝缘方法为采用喷砂的方式将电池边缘一定区域内的薄膜清除掉，使之形成一个绝缘区域。目前应用较为前沿的是采用激光刻划设备对电池板进行边绝缘，此方法可以大大提高非晶硅薄膜太阳能电池的生产效率与自动化程度，适用于大规模的生产。但对于日常实验用电池板或非常规电池板而言，此两种方法均显不够简便。
发明内容
本发明的目的在于克服现有技术的不足之处，提供一种非晶硅电池的简便绝缘处理方法，该方法方便快捷，能够快速实现非常规电池板的边绝缘处理。
本发明解决其技术问题是采取以下技术方案实现的：
一种非晶硅电池的简便绝缘处理方法，处理方法的步骤是：
(1)原材料准备：电池片、FeCl3.6H2O、稀盐酸、去离子水、量筒、烧杯；
(2)溶液配制：称取于烧杯中，将去离子水倒入含有的烧杯中，再向烧杯中滴加15-20滴稀盐酸，即形成水溶液；
(3)样品绝缘处理：室温条件下，将待绝缘电池片放置于平整的操作台上，并将其固定；
(4)绝缘处理：取配制好的水溶液，沿一定的宽度将其均匀涂抹在电池板的铝膜上，2-3min之后，用去离子水将电池片上残留的溶液清除掉，并用丝布将电池片擦拭干净，防止电池片被深度腐蚀。
而且，所述FeCl3.6H2O与去离子水的质量比为1∶3-4。
本发明的优点和积极效果是：
1、本发明采用FeCl3水溶液作为太阳电池片的边缘绝缘处理物质，能够确保非晶硅太阳电池片的边绝缘效果，且在该溶液中添加H+以防水解。
2、本发明通过一种较为简便的方式实现了对非晶硅太阳电池片进行边绝缘处理，具有较好的绝缘效果、简易的操作方式和低成本等优势，对非常规电池板的研发生产具有极大优势。
具体实施方式
下面通过具体实施例对本发明作进一步详述，以下实施例只是描述性的，不是限定性的，不能以此限定本发明的保护范围。
一种非晶硅电池的简便绝缘处理方法，步骤是：
(1)原材料准备：电池片、FeCl3.6H2O、稀盐酸、去离子水、250ml量筒、2000ml烧杯、天平、手套、刷子、玻璃棒、胶头滴管。
(2)溶液配制：称取135.3g的FeCl3.6H2O置于2000ml的烧杯中，用量筒量取500ml去离子水，倒入含有FeCl3.6H2O的烧杯中。由于Fe3+离子在水溶液中极不稳定，因此需要在溶液的配制过程中加入相应的酸来抑制该离子的水解，针对本方案，加入的酸为盐酸，具体措施为向FeCl3水溶液中滴加15-20滴稀盐酸，所配成的溶液即为盐酸稳定的FeCl3水溶液。
(3)样品绝缘处理：室温条件下，将待绝缘电池片放置于平整的操作台上，并将其固定。
(4)取配制好的FeCl3水溶液，沿一定的宽度将其均匀涂抹在电池板的铝膜上，2-3min之后，用去离子水将电池片上残留的溶液清除掉，并用丝布将电池片擦拭干净，防止电池片被深度腐蚀。

Claims (2)

1.一种非晶硅电池的简便绝缘处理方法，其特征在于：处理方法的步骤是：
(1)原材料准备：电池片、FeCl3.6H2O、稀盐酸、去离子水、量筒、烧杯；
(2)溶液配制：称取于烧杯中，将去离子水倒入含有的烧杯中，再向烧杯中滴加15-20滴稀盐酸，即形成水溶液；
(3)样品绝缘处理：室温条件下，将待绝缘电池片放置于平整的操作台上，并将其固定；
(4)绝缘处理：取配制好的水溶液，沿一定的宽度将其均匀涂抹在电池板的铝膜上，2-3min之后，用去离子水将电池片上残留的溶液清除掉，并用丝布将电池片擦拭干净，防止电池片被深度腐蚀。
2.根据权利要求1所述的非晶硅电池的简便绝缘处理方法，其特征在于：所述FeCl3.6H2O与去离子水的质量比为1∶3-4。
CN2010105835752A 2010-12-14 2010-12-14 一种非晶硅电池的绝缘处理方法 Expired - Fee Related CN102074619B (zh)