CN102070840A - Plastic material with weighted quality - Google Patents
Plastic material with weighted quality Download PDFInfo
- Publication number
- CN102070840A CN102070840A CN2011100048967A CN201110004896A CN102070840A CN 102070840 A CN102070840 A CN 102070840A CN 2011100048967 A CN2011100048967 A CN 2011100048967A CN 201110004896 A CN201110004896 A CN 201110004896A CN 102070840 A CN102070840 A CN 102070840A
- Authority
- CN
- China
- Prior art keywords
- plastic material
- weight
- powder
- percent
- texture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plastic material with weighted quality, which comprises the following components in percentage by weight: 10 to 20 percent of plastic material, 30 to 60 percent of barium sulfate, 20 to 50 percent of metal powder, 0.5 to 2 percent of compatilizer, 0.5 to 2 percent of lubricant, 0.3 to 1.5 percent of dispersing agent, and 0.5 to 1 percent of coupling agent. In the invention, the plastic material is polypropylene (PP), or nylon (PA6 and PA66) or polybutylene terephthalate (PBT), and the metal powder is iron powder, copper powder, lead powder, zinc powder or metal lead oxide and metal zinc oxide. In the invention, different weighting metal powder materials are added into the conventional plastic material, the mixture is uniformly mixed with other additives to form a new plastic material with weighted quality, and the new plastic material is used to make objects or appliances with different qualities; meanwhile, the new material is favorable for forming articles in complex shapes, and the articles or appliances meet different use needs of customers.
Description
Technical field
The invention belongs to technical field of composite materials, relate to a kind of special plastic composite material, be specifically related to a kind of plastic material that increases the weight of texture that has.
Background technology
Along with the develop rapidly of science and technology, the improving constantly of material life, people are also more and more exquisite to the requirement of daily necessities.The many daily necessities that use in the daily life or the making material of vessel are substituted by plastic material, and be not only handsome in appearance, beautiful in colour, and saved a large amount of timber, pottery, glass or metallic substance.This new type plastic material with environmental protection, excellent property in succession substituting existing various material, saved resource, reduced cost.But because plastic material proportion is lighter, so it does not possess the weight and the texture of replaced material, is therefore always feeling to exist some to use defectives.
Summary of the invention
The purpose of this invention is to provide a kind of plastic material that increases the weight of texture that has, it can be according to the texture demand of different articles for use or utensil, in plastic rubber material, add the different heavy metal powder that adds, mix with other additive again, make a kind of new plastic material that increases the weight of texture that has, make it have different texture, remedied the sensory defect when using, solved problems of the prior art.
The technical solution adopted in the present invention is, a kind of have a plastic material that increases the weight of texture, and the composition that material is formed is: plastic rubber material, barium sulfate, metal powder, compatilizer, lubricant, dispersion agent, coupling agent;
Wherein the weight proportion of each component is: plastic rubber material 10-20%, barium sulfate 30-60%, metal powder 20-50%, compatilizer 0.5-2%, lubricant 0.5-2%, dispersion agent 0,3-1.5%, coupling agent 0,5-1%.
Of the present invention have a plastic material that increases the weight of texture, and its feature also is,
Described plastic rubber material is polypropylene (PP), or nylon (PA6, PA66), or polybutylene terephthalate (PBT).
Described metal powder is: iron powder, copper powder, lead powder, zinc powder, or burning lead, metal zinc oxide.
Described compatilizer is: maleic anhydride graft PP, maleic anhydride graft PE;
Described lubricant is: PP wax, stearic acid, calcium stearate;
Described dispersion agent is: vinyl bis-stearamides (EBS);
Described coupling agent is: silane resin acceptor kh-550, KH-560.
The present invention has the plastic material that increases the weight of texture, it adopts and add the different metal powder materials that increases the weight of in original plastic rubber material, again with other additive uniform mixing, make a kind of new plastic material that increases the weight of texture that has, has different texture after making article or utensil again, this novel material also helps the moulding of complex model articles for use simultaneously, and different articles for use of making or utensil have satisfied the different user demand of human consumer.
Embodiment
The present invention is described in detail below in conjunction with embodiment.
A kind of have a plastic material that increases the weight of texture, and the composition that material is formed is: plastic rubber material, barium sulfate, metal powder, compatilizer, lubricant, dispersion agent, coupling agent;
Wherein the weight proportion of each component is: plastic rubber material 10-20%, barium sulfate 30-60%, metal powder 20-50%, compatilizer 0.5-2%, lubricant 0.5-2%, dispersion agent 0,3-1.5%, coupling agent 0,5-1%.
Of the present invention have a plastic material that increases the weight of texture, and described plastic rubber material is polypropylene (PP), or nylon (PA6, PA66), or polybutylene terephthalate (PBT).
Of the present invention have a plastic material that increases the weight of texture, and described metal powder is: iron powder, copper powder, lead powder, zinc powder, or burning lead, metal zinc oxide.
Of the present invention have a plastic material that increases the weight of texture, and described compatilizer is: maleic anhydride graft PP, maleic anhydride graft PE;
Described lubricant is: PP wax, stearic acid, calcium stearate;
Described dispersion agent is: vinyl bis-stearamides (EBS);
Described coupling agent is: silane resin acceptor kh-550, KH-560.
The present invention adopts and add the different metal powder materials that increases the weight of in original plastic rubber material; as iron powder, copper powder, burning lead, zinc; again with other additive uniform mixing; pour prepared mixture into twin screw extruder then; in temperature is that 220-260 ℃, rotating speed are under the 300-450r/min condition; extrude the back by the tank tie rod, be cut into particle by dicing machine then, can obtain having the plastic material of various metal-likes.
Embodiment
Embodiment one,
It with weight 20% polybutylene terephthalate (PBT); weight is 50% barium sulfate; weight is 25% iron powder; weight is 1.5% maleic anhydride graft PP; weight is 1.7% whiteruss; weight is 0.8% vinyl bis-stearamides (EBS); weight is that 1% silane resin acceptor kh-550 mixes; pour prepared mixture into twin screw extruder then; in temperature is 220 ℃; rotating speed is under the 350r/min condition; extrude the back by the tank tie rod; be cut into particle by dicing machine then, can obtain having the plastic material of ironware texture.
Embodiment two
With weight is that 30% polypropylene (PP), weight are that 50% barium sulfate, weight are that 15% copper powder, weight are that 1% maleic anhydride graft PP, weight are that 1.5% stearic acid, weight are that 2% vinyl bis-stearamides (EBS), weight are that 0.5% silane coupling agent KH-560 mixes; pour prepared mixture into twin screw extruder then; in temperature is that 240 ℃, rotating speed are under the 400r/min condition; extrude the back by the tank tie rod; be cut into particle by dicing machine then, can obtain having the plastic material of bronze, brass or copper ware texture.
Embodiment three
With weight is that 20% polypropylene (PP), weight are that 45% barium sulfate, weight are that 30% burning lead, weight are that 1% maleic anhydride graft PE, weight are that 1.5% calcium stearate, weight are that 1.5% vinyl bis-stearamides (EBS), weight are that 1% silane resin acceptor kh-550 mixes; pour prepared mixture into twin screw extruder then; in temperature is that 260 ℃, rotating speed are under the 450r/min condition; extrude the back by the tank tie rod; be cut into particle by dicing machine then, can obtain having the plastic material of plumbery texture.
The present invention has the plastic material that increases the weight of texture, it adopts and add the different metal powder materials that increases the weight of in original plastic rubber material, as iron powder, copper powder, burning lead, zinc, with other additive uniform mixing, make a kind of new plastic material again, increase the weight of metal powder material owing to added with metal-like, make this novel material help the moulding of complex model articles for use more, have different texture after making article or utensil again, satisfied the various user demand of human consumer
Above-mentioned embodiment is several example of the present invention, is not to be used for limiting enforcement of the present invention and interest field, and all equivalences of making according to the described content of the present patent application scope of patent protection change and modify, and all should be included in the present patent application claim.
Claims (4)
1. one kind has the plastic material that increases the weight of texture, makes through extrusion, it is characterized in that, the composition that material is formed is: plastic rubber material, barium sulfate, metal powder, compatilizer, lubricant, dispersion agent, coupling agent;
Wherein the weight proportion of each component is: plastic rubber material 10-20%, barium sulfate 30-60%, metal powder 20-50%, compatilizer 0.5-2%, lubricant 0.5-2%, dispersion agent 0,3-1.5%, coupling agent 0,5-1%.
2. according to claim 1 have a plastic material that increases the weight of texture, it is characterized in that described plastic rubber material is polypropylene (PP), or nylon (PA6, PA66), or polybutylene terephthalate (PBT).
3. according to claim 1 have a plastic material that increases the weight of texture, it is characterized in that described metal powder is: iron powder, copper powder, lead powder, zinc powder, or burning lead, metal zinc oxide.
4. according to claim 1 have a plastic material that increases the weight of texture, it is characterized in that described compatilizer is: maleic anhydride graft PP, maleic anhydride graft PE;
Described lubricant is: PP wax, stearic acid, calcium stearate;
Described dispersion agent is: vinyl bis-stearamides (EBS);
Described coupling agent is: silane resin acceptor kh-550, KH-560.