CN102029718A - Agate-jade artificial composite material decorating plate and processing method - Google Patents
Agate-jade artificial composite material decorating plate and processing method Download PDFInfo
- Publication number
- CN102029718A CN102029718A CN200910246577XA CN200910246577A CN102029718A CN 102029718 A CN102029718 A CN 102029718A CN 200910246577X A CN200910246577X A CN 200910246577XA CN 200910246577 A CN200910246577 A CN 200910246577A CN 102029718 A CN102029718 A CN 102029718A
- Authority
- CN
- China
- Prior art keywords
- kilograms
- unsaturated polyester
- kilogram
- polyester resin
- agate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an agate-jade artificial composite material decorating plate and a processing method. The surface of the conventional decorating plate is not provided with emulational pattern, the surface finish is undesirable and certain decorating plates contain toxic and harmful substances and cause great damage to the using environment. The processing method of the agate-jade artificial composite material decorating plate comprises the following steps of: preparing 1 kilogram of unsaturated polyester resin and color paste based on a square meter of finished product, wherein the using amount of the color paste is determined according to the color desired by a user; preparing 1 kilogram of unsaturated polyester resin fine powder, 1.3 kilograms of aluminum hydroxide fine powder and white paste, wherein the using amount of the white paste is determined according to field condition; and preparing 6.5 to 6 kilograms of unsaturated polyester resin, 6 to 5.5 kilograms of aluminum hydroxide coarse powder, 5.5 to 6 kilograms of aluminum hydroxide fine powder, 5 to 2.8 grams of methyl ethyl ketone peroxide and 5 to 2.8 grams of cobalt naphthenate, wherein processing temperature is between 5 and 2.8 DEG C. The product is applied to interior decoration.
Description
Technical field:
The present invention relates to imitative agate jade artificial compounded material dalle and processing method that a kind of resin composite materials is made.
Background technology:
Decorative panel is as the important materials widespread usage of house decoration.According to the complaint of house ornamentation industry statistics, the 70%th, about decoration panel, case hardness is low, fineness is also undesirable, bulk strength is poor, does not often reach user's satisfaction, and some decorative panel is owing to added harmful substance such as benzene, contain poisonous, harmful substance, environment for use is caused very big harm.
Summary of the invention:
The artificial compounded material decorative panel and the processing method that the purpose of this invention is to provide the imitative agate jade material of height that a kind of, fine powder thick by unsaturated polyester resin and Aluminium Hydroxide Powder(to make Alum.Sulfate) powder be composited.
Above-mentioned purpose realizes by following technical scheme:
Agate jade artificial compounded material decorative panel processing method:
The first step: getting 1 kilogram of unsaturated polyester resin, want color to add the mill base amount of supporting color according to the user, evenly mix, is first kind of material, and described first kind of material is spread out on the off-the-shelf workbench equably, leaves standstill 1-5 minute;
Second step: get the unsaturated polyester resin fine powder and add 1.3 kilograms of aluminium hydroxide powder and fine powders for 1 kilogram, adding stock white is second kind of material, with the even pattern that mixes by every capable diamond block of described second kind of material, is arranged in order cast and finishes, and leaves standstill 3-8 minute;
The 3rd step: get unsaturated polyester resin 6.5---6 kilogram, each 6---5.5 kilogram of aluminium hydroxide meal and fine powder is poured in the mixer and is stirred, and is the third material;
The third material is cast on second kind of material, left standstill 10-30 minute;
Add man-hour, temperature on mounted workbench, is reserved temperature between 5 ℃-28 ℃, gives above three kinds to treat to add in proportion in the materials cobalt naphthenate 5---2.8 gram and peroxidating first and second bronze medal 5---2.8 gram;
The 4th step: towards the direction of workbench,, form unique decorative pattern naturally, leave standstill 5-10 hour coagulation forming as leaf by extruding.Play platform, check the quality of the products, treat up-to-standard after, pack, dispatch from the factory.
The agate jade artificial compounded material decorative panel that a kind of above-mentioned method is processed, its composition comprises: base plate, with the described base plate of said method making with by the very high surface layer that has decorative pattern of the compound fineness of said method.
Beneficial effect of the present invention:
1. the hardness of artificial compounded material decorative panel of the present invention is good, surface smoothness is very high, and the decorative pattern uniqueness is fit to various decoration occasions and uses.
2. the surface color of artificial compounded material decorative panel of the present invention is soft, the color warmth, and clear transparent brings the people warming sense.
3. artificial compounded material decorative panel waterproof of the present invention, protection against the tide, can according to, can bore, can glue, processing technology is simple.
4. nontoxic, tasteless, the environmental protection, harmless of artificial compounded material decorative panel of the present invention.
Description of drawings:
Accompanying drawing 1 is a structural representation of the present invention.
The specific embodiment:
Embodiment 1:
Agate jade artificial compounded material decorative panel, its composition comprises: base plate is compounded with the very high surface layer that has decorative pattern of fineness on the described base plate.
Embodiment 2:
At first, consumption is 1 kilogram of unsaturated polyester resin and a mill base, and the consumption of mill base wants color to decide according to the user.
Secondly, consumption is 1 kilogram of unsaturated polyester resin fine powder, 1.3 kilograms of aluminium hydroxide powder and fine powders, stock white, and the consumption of stock white according to the situation.
Then, following consumption is decided by variations in temperature:
When processing temperature during at 7 ℃-8 ℃, 6.5 kilograms of unsaturated polyester resins, 6 kilograms of aluminium hydroxide meal, 5.5 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 4.8 grams, cobalt naphthenate (purple water) 4.8 grams;
When processing temperature during at 9 ℃-10 ℃, 6.5 kilograms of unsaturated polyester resins, 6 kilograms of aluminium hydroxide meal, 5.5 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 4.6 grams, cobalt naphthenate (purple water) 4.6 grams;
When processing temperature during at 11 ℃-12 ℃, 6.5 kilograms of unsaturated polyester resins, 6 kilograms of aluminium hydroxide meal, 5.5 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 4.4 grams, cobalt naphthenate (purple water) 4.4 grams;
When processing temperature during at 13 ℃-14 ℃, 6.5 kilograms of unsaturated polyester resins, 6 kilograms of aluminium hydroxide meal, 5.5 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 4.7 grams, cobalt naphthenate (purple water) 4.7 grams;
When processing temperature during at 15 ℃-16 ℃, 6 kilograms of unsaturated polyester resins, 6 kilograms of aluminium hydroxide meal, 6 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 4 grams, cobalt naphthenate (purple water) 4 grams;
When processing temperature during at 17 ℃-18 ℃, 6 kilograms of unsaturated polyester resins, 6 kilograms of aluminium hydroxide meal, 6 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 3.8 grams, cobalt naphthenate (purple water) 3.8 grams;
When processing temperature during at 19 ℃-20 ℃, 6 kilograms of unsaturated polyester resins, 5.5 kilograms of aluminium hydroxide meal, 6 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 3.6 grams, cobalt naphthenate (purple water) 3.6 grams;
When processing temperature during at 21 ℃-22 ℃, 6 kilograms of unsaturated polyester resins, 5.5 kilograms of aluminium hydroxide meal, 6 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 3.5 grams, cobalt naphthenate (purple water) 3.5 grams;
When processing temperature during at 23 ℃-24 ℃, 6 kilograms of unsaturated polyester resins, 5.5 kilograms of aluminium hydroxide meal, 6 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 3.1 grams, cobalt naphthenate (purple water) 3.1 grams;
When processing temperature during at 25 ℃-26 ℃, 6 kilograms of unsaturated polyester resins, 5.5 kilograms of aluminium hydroxide meal, 6 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 3 grams, cobalt naphthenate (purple water) 3 grams.
When processing temperature during at 27 ℃-28 ℃, 6 kilograms of unsaturated polyester resins, 5.5 kilograms of aluminium hydroxide meal, 6 kilograms of aluminium hydroxide fine powders, peroxidating first and second bronze medals (plain boiled water) 2.8 grams, cobalt naphthenate (purple water) 2.8 grams.
Embodiment 3:
Agate jade artificial compounded material decorative panel processing method is characterized in that:
The first step: getting 1 kilogram of unsaturated polyester resin, want color to add the mill base amount that cover mixes colours according to the user, evenly mix, is first kind of material, and described first kind of material is spread out on the off-the-shelf workbench equably, leaves standstill 1-5 minute;
Second step: get the unsaturated polyester resin fine powder and add 1.3 kilograms of aluminium hydroxide powder and fine powders for 1 kilogram, adding stock white is second kind of material, with the even pattern that mixes by every capable diamond block of described second kind of material, is arranged in order cast and finishes, and leaves standstill 3-8 minute;
The 3rd step: get unsaturated polyester resin 6.5---6 kilogram, each 6---5.5 kilogram of aluminium hydroxide meal and fine powder is poured in the mixer and is stirred, and is the third material;
The third material is cast on second kind of material, left standstill 10-30 minute;
Add man-hour, temperature on mounted workbench, is reserved temperature between 5 ℃-28 ℃, gives above three kinds to treat to add in proportion in the materials cobalt naphthenate 5---2.8 gram and peroxidating first and second bronze medal 5---2.8 gram;
The 4th step: towards the direction of workbench,, form unique decorative pattern naturally, leave standstill 5-10 hour coagulation forming as leaf by extruding.
Claims (2)
1. agate jade artificial compounded material decorative panel processing method is characterized in that:
The first step: getting 1 kilogram of unsaturated polyester resin, want color to add the mill base amount of supporting color according to the user, evenly mix, is first kind of material, and described first kind of material is spread out on the off-the-shelf workbench equably, leaves standstill 1-5 minute;
Second step: get the unsaturated polyester resin fine powder and add 1.3 kilograms of aluminium hydroxide powder and fine powders for 1 kilogram, adding stock white is second kind of material, with the even pattern that mixes by every capable diamond block of described second kind of material, is arranged in order cast and finishes, and leaves standstill 3-8 minute;
The 3rd step: get unsaturated polyester resin 6.5---6 kilogram, each 6---5.5 kilogram of aluminium hydroxide meal and fine powder is poured in the mixer and is stirred, and is the third material;
The third material is cast on second kind of material, left standstill 10-30 minute;
Add man-hour, temperature on mounted workbench, is reserved temperature between 5 ℃-28 ℃, gives above three kinds to treat to add in proportion in the materials cobalt naphthenate 5---2.8 gram and peroxidating first and second bronze medal 5---2.8 gram;
The 4th step: towards the direction of workbench,, form unique decorative pattern naturally, leave standstill 5-10 hour coagulation forming as leaf by extruding.
2. agate jade artificial compounded material decorative panel, its composition comprises: base plate is characterized in that: the described base plate made from said method and by the very high surface layer that has decorative pattern of the compound fineness of said method.