A kind of aluminium matter pot
Technical field
The present invention relates to the technical field of tableware pot, relate in particular at the bottom of a kind of compound pot of aluminium matter pot.
Background technology
Because aluminium is non-magnet material, therefore traditional aluminium matter pot does not suit on electromagnetic stove, to use, and has occurred to above-mentioned present situation market at the bottom of a kind of compound pot of aluminium matter pot; It is a kind of to be to be in compound last layer stainless steel bottom surface, original aluminium matter the bottom of a pan with it, and the bottom surface and the bottom of a pan are welded, and its defective is that processing technology is complicated; Need steel plate be welded on the bottom of aluminium matter pot; Welding needs special protruding being equipped with, and be easy to have influence on the fineness on surface, the bottom of a pan simultaneously, and the cost of welding is also higher.Be that the Chinese utility model patent " at the bottom of the compound pot of aluminium matter pot " of ZL02217063.4 (notification number is CN2544654Y) has disclosed a kind of such structure also just like a patent No.; It is compound upper steel plate in the bottom in the aluminium matter the bottom of a pan; It is characterized in that stamping out a plurality of hole flangings on the surface of steel plate; Cold extrusion is carried out in the bottom that steel plate is fitted in the aluminium matter the bottom of a pan, is squeezed in the hole flanging on the steel plate after making the aluminum metal distortion in the aluminium matter the bottom of a pan, and the flange of hole flanging is pressed in the aluminum substrate in the aluminum pot the bottom of a pan simultaneously; Tightly embrace with aluminum substrate, steel plate is composite and fixed on the bottom in the aluminium matter the bottom of a pan.Have advantages such as processing is simple, cost is low, connection is more firm at the bottom of this compound pot, still, because magnetic conducting and heating panel is to be composite and fixed at a pot body one side; Causing pot body and magnetic conducting and heating panel is that different materials is made, and under the frequent occasion of expanding with heat and contract with cold, is easy to generate thermal stress; Can cause a lot of hazards after causing the bowl bottom surface to produce the distortion, particularly bowl bottom surface evagination of evagination or indent, as rotate instability; Make the interior blanching object of bowl injure the person, so need further change
This is the disadvantage defective that exists at the bottom of the traditional compound pot, needs further to improve design.
Summary of the invention
Technical problem to be solved by this invention is the aluminium matter pot that a kind of structure practicality is provided to above-mentioned prior art present situation, prevents the multiple end of process that the bottom of a pan is out of shape, security is good.
The present invention solves the problems of the technologies described above the technical scheme that is adopted:
A kind of aluminium matter pot, it includes:
The pot body of one aluminium matter, the lower surface of bottom is to be used for compound surface, is provided with storage tank;
One magnetic conducting and heating panel adopts hole flanging sheet material up;
It is characterized in that:
Other has a metallic interconnect, and its surface distributed has up and upper and lower hole flanging down;
And an aluminium sheet, size shape cooperates with storage tank;
Aluminium sheet and metallic interconnect are filled in the storage tank from descending, and the last hole flanging of metallic interconnect connects the bottom of storage tank, and the following hole flanging of metallic interconnect connect aluminium sheet;
And magnetic conducting and heating panel is bigger than storage tank, makes lower surface that magnetic conducting and heating panel is fastened on aluminium sheet through hole flanging simultaneously like this, and remains with a circle hole flanging at least and be connected with bottom of pot body and fix.
Or,
A kind of aluminium matter pot, it includes:
The pot body of one aluminium matter, the lower surface of bottom is to be used for compound surface, is provided with storage tank;
One magnetic conducting and heating panel;
It is characterized in that:
Other has a metallic interconnect, and its surface distributed has up and upper and lower hole flanging down;
And composite metal plate, the upper strata is an aluminium lamination, the upper strata size shape cooperates with storage tank, and lower floor is the magnetic conducting and heating layer, as magnetic conducting and heating panel;
The aluminium lamination and the metallic interconnect of composite metal plate are filled in the storage tank from descending, and the last hole flanging of metallic interconnect connects the bottom of storage tank, and the following hole flanging of metallic interconnect connect the aluminium lamination of composite metal plate,
And the magnetic conducting and heating layer of composite metal plate remains with a circle hole flanging at least and is connected fixing with bottom of pot body.
Or,
A kind of aluminium matter pot, it includes:
The pot body sheet material of one aluminium matter, the lower surface of bottom is to be used for compound surface, is provided with storage tank;
One magnetic conducting and heating panel adopts hole flanging sheet material up;
It is characterized in that:
Other has a metallic interconnect, and its surface distributed has up and upper and lower hole flanging down;
And an aluminium sheet, size shape cooperates with storage tank;
In the pot body sheet material recombination process, aluminium sheet and metallic interconnect are filled in the storage tank from descending, and the last hole flanging of metallic interconnect connects the bottom of storage tank, and the following hole flanging of metallic interconnect connect aluminium sheet; And magnetic conducting and heating panel is bigger than storage tank, thereby makes lower surface that magnetic conducting and heating panel is fastened on aluminium sheet through hole flanging simultaneously, remains with a circle hole flanging at least and is connected with the position, storage tank outer of pot body sheet material and fixes;
At last, pot body sheet material is pressed into a pot body.
Or,
A kind of aluminium matter pot, it includes:
The pot body sheet material of one aluminium matter, the lower surface of bottom is to be used for compound surface, is provided with storage tank;
One magnetic conducting and heating panel;
It is characterized in that:
Other has a metallic interconnect, and its surface distributed has up and upper and lower hole flanging down;
And composite metal plate, the upper strata is an aluminium lamination, the upper strata size shape cooperates with storage tank, and lower floor is the magnetic conducting and heating layer, as magnetic conducting and heating panel;
In the pot body sheet material recombination process, the aluminium lamination of composite metal plate and metallic interconnect are filled in the storage tank from descending, and the last hole flanging of metallic interconnect connects the bottom of storage tank, and the following hole flanging of metallic interconnect connect the aluminium lamination of composite metal plate; The magnetic conducting and heating layer of composite metal plate is bigger than storage tank, is connected with the position, storage tank outer of pot body sheet material and fixes thereby make the magnetic conducting and heating layer of composite metal plate remain with a circle hole flanging at least;
At last, pot body sheet material is pressed into a pot body.
As preferably, the last hole flanging of described metallic interconnect is spaced apart with following hole flanging.
As preferably, that described hole flanging adopts is circular, square, pentagon or hexagon, is the ring arrangement.
Compared with prior art, the invention has the advantages that: below adopting magnetic conducting and heating panel and the structure of top metallic interconnect positioned opposite, can effectively eliminate the thermal stress that magnetic conducting and heating panel and aluminium matter pot body different materials cause; Reduce the defective of easy deformation behind the bottom high temperature of composite bottom boiler, improved security performance, and; Metallic interconnect also can adopt the magnetic conducting and heating material to make, and has improved heating layer thickness, makes pot body heating effect better; Connect and stablize firmly, structure is practical.
Description of drawings
The cutaway view of 1 pot of body of Fig. 1 examples of implementation;
The partial enlarged drawing of 1 pot of body of Fig. 2 examples of implementation;
The exploded view of 1 pot of body of Fig. 3 examples of implementation;
The cutaway view of 2 pots of bodies of Fig. 4 examples of implementation;
The partial enlarged drawing of 2 pots of bodies of Fig. 5 examples of implementation;
The exploded view of 2 pots of bodies of Fig. 6 examples of implementation;
The cutaway view of 3 pots of bodies of Fig. 7 examples of implementation;
The partial enlarged drawing of 3 pots of bodies of Fig. 8 examples of implementation;
Fig. 9 .1, the 9.2nd, the composite molding procedure chart of 3 pots of body sheet materials of examples of implementation;
The cutaway view of 4 pots of bodies of Figure 10 examples of implementation;
The partial enlarged drawing of 4 pots of bodies of Figure 11 examples of implementation;
Figure 12 .1, the 12.2nd, the composite molding procedure chart of 4 pots of body sheet materials of examples of implementation;
Figure 13 .1 is the vertical view of metallic interconnect;
Figure 13 .2 is the cutaway view of metallic interconnect;
Figure 13 .3 is the partial enlarged drawing of metallic interconnect;
The specific embodiment
Embodiment describes in further detail the present invention below in conjunction with accompanying drawing.
Examples of implementation 1
The lower surface 1.1 of pot body 1 bottom that a kind of aluminium matter pot shown in Fig. 1-3, the crucial part of its invention are is to be used for compound surface, is provided with the adaptive storage tank of shape and thickness 1.3, and is normally circular or square; Other has a metallic interconnect 3, and its surface distributed has last hole flanging 3.1 and following hole flanging 3.2 down up, size and shape and storage tank 1.3 form fit; Can be circular or square; That last hole flanging 3.1 and following hole flanging 3.2 adopt is circular, square, pentagon or hexagon, and last hole flanging 3.1 and following hole flanging 3.2 are spaced apart, can be concentric ring arrangements; Metallic interconnect 3 adopts stainless steel to make; Be an aluminium sheet 4 below metallic interconnect 3, size and shape also with storage tank 1.3 form fit, adopt circular perhaps square; Nethermost is magnetic conducting and heating panel 2, adopts hole flanging stainless steel materials up, and magnetic conducting and heating panel 2 is bigger than storage tank 1.3, remains with a circle hole flanging at least in storage tank 1.3 outsides, and that hole flanging adopts is circular, square, pentagon or hexagon; Through compacting, aluminium sheet 4 and metallic interconnect 3 are from being filled in the storage tank 1.3 down, and the last hole flanging 3.1 of metallic interconnect 3 connects storage tanks 1.3 bottoms, and the following hole flanging 3.2 of metallic interconnect 3 connects aluminium sheets 4; And make the lower surface of aluminium sheet 4 lower surfaces and bottom of pot body concordant basically; Stainless magnetic conducting and heating panel 2 adopts hole flangings to be fastened on the lower surface of aluminium sheet 4, and remains with a circle hole flanging at least and be connected with bottom of pot body 1.2 and fix.
Examples of implementation 2
A kind of aluminium matter pot shown in Fig. 4-6, the crucial part of its invention are that the lower surface 1.1 of pot body 1 bottom of aluminium matter is to be used for compound surface, are provided with the adaptive storage tank of shape and thickness 1.3, and be normally circular or square; Other has a metallic interconnect 3; Its surface distributed has last hole flanging 3.1 and following hole flanging 3.2 down up, and size and shape and storage tank 1.3 form fit can be that circle is perhaps square; Last hole flanging 3.1 is circular, square with following hole flanging 3.2 employings, pentagon or hexagon; Last hole flanging 3.1 is spaced apart with following hole flanging 3.2, can be that concentric ring is arranged, and metallic interconnect 3 adopts stainless steel to make; And nethermost composite metal plate 5, the upper strata is an aluminium lamination 5.1, size and shape also cooperate with storage tank 1.3; And lower floor is a magnetic conducting and heating layer 5.2; As magnetic conducting and heating panel, the magnetic conducting and heating layer 5.2 of composite metal plate is bigger than storage tank 1.3, remains with the outside of a circle hole flanging at storage tank 1.3 at least; At last, the aluminium lamination 5.1 of composite metal plate 5 and metallic interconnect 3 are from being filled in the storage tank 1.3 down, and the last hole flanging 3.1 of metallic interconnect 3 connects the bottom of storage tanks 1.3, and the following hole flanging 3.2 of metallic interconnect 3 connects the aluminium lamination 5.1 of composite metal plates 5; And the magnetic conducting and heating layer of composite metal plate 5 remains with a circle hole flanging 5.3 at least and is connected fixing with bottom of pot body 1.2.
Examples of implementation 3
The lower surface 1.1 of the pot body sheet material A bottom that a kind of aluminium matter pot shown in Fig. 7-9, the crucial part of its invention are is to be used for compound surface, is provided with the adaptive storage tank of shape and thickness 1.3, and is normally circular or square; Other has a metallic interconnect 3, and its surface distributed has last hole flanging 3.1 and following hole flanging 3.2 down up, size and shape and storage tank 1.3 form fit; Can be circular or square; That last hole flanging 3.1 and following hole flanging 3.2 adopt is circular, square, pentagon or hexagon, and last hole flanging 3.1 and following hole flanging 3.2 are spaced apart, can be concentric ring arrangements; Metallic interconnect 3 adopts stainless steel to make; Be an aluminium sheet 4 below metallic interconnect 3, size and shape also with storage tank 1.3 form fit, adopt circular perhaps square; Nethermost is magnetic conducting and heating panel 2, adopts hole flanging stainless steel materials up, and magnetic conducting and heating panel 2 is bigger than storage tank 1.3, remains with a circle hole flanging at least in storage tank 1.3 outsides, and that hole flanging adopts is circular, square, pentagon or hexagon; In the pot body sheet material recombination process, make aluminium sheet 4 and metallic interconnect 3 from being filled in the storage tank 1.3 down, the last hole flanging 3.1 of metallic interconnect 3 connects storage tanks 1.3 bottoms, and the following hole flanging 3.2 of metallic interconnect 3 connects aluminium sheets 4; Stainless magnetic conducting and heating panel 2 adopts hole flangings to be fastened on the lower surface of aluminium sheet 4, and remains with a circle hole flanging 2.2 at least and is connected with position, storage tank 1.3 outer on the pot body sheet material A and fixes, and at last pot body sheet material A ' after compound is pressed into pot body 1.
Examples of implementation 4
A kind of aluminium matter pot shown in Figure 10-12, the crucial part of its invention are that the lower surface 1.1 of the pot body sheet material A bottom of aluminium matter is to be used for compound surface, are provided with the adaptive storage tank of shape and thickness 1.3, and be normally circular or square; Other has a metallic interconnect 3; Its surface distributed has last hole flanging 3.1 and following hole flanging 3.2 down up, and size and shape and storage tank 1.3 form fit can be that circle is perhaps square; Last hole flanging 3.1 is circular, square with following hole flanging 3.2 employings, pentagon or hexagon; Last hole flanging 3.1 is spaced apart with following hole flanging 3.2, can be that concentric ring is arranged, and metallic interconnect 3 adopts stainless steel to make; And nethermost composite metal plate 5, the upper strata is an aluminium lamination 5.1, size and shape also cooperate with storage tank 1.3; And lower floor is a magnetic conducting and heating layer 5.2; As magnetic conducting and heating panel, the magnetic conducting and heating layer 5.2 of composite metal plate is bigger than storage tank 1.3, remains with the outside of a circle hole flanging at storage tank 1.3 at least; In the pot body sheet material recombination process; The aluminium lamination 5.1 of composite metal plate 5 is filled in the storage tank 1.3 from descending with metallic interconnect 3; The last hole flanging 3.1 of metallic interconnect 3 connects the bottom of storage tank 1.3, and the following hole flanging 3.2 of metallic interconnect 3 connects the aluminium lamination 5.1 of composite metal plate 5; And the magnetic conducting and heating layer of composite metal plate 5 remains with a circle hole flanging 5.3 at least and is connected with position, storage tank 1.3 outer on the pot body sheet material and fixes, and at last pot body sheet material A ' after compound is pressed into pot body 1.