CN102016960A - Retroreflector label sheet and article to which retroreflector label sheet is bonded - Google Patents
Retroreflector label sheet and article to which retroreflector label sheet is bonded Download PDFInfo
- Publication number
- CN102016960A CN102016960A CN2009801152032A CN200980115203A CN102016960A CN 102016960 A CN102016960 A CN 102016960A CN 2009801152032 A CN2009801152032 A CN 2009801152032A CN 200980115203 A CN200980115203 A CN 200980115203A CN 102016960 A CN102016960 A CN 102016960A
- Authority
- CN
- China
- Prior art keywords
- layer
- labei sheet
- mentioned
- retroeflection
- article
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Provided is a retroreflector label sheet and an article to which a retroreflector label sheet is boded wherein a judgment can be made whether a label sheet has been re-stuck or not by observing the conditions on the surface, unsealing can be confirmed, and forgery and camouflage can be inspected. The retroreflector label sheet (1) consists of a base layer (10), a retroreflective layer (20) that is laminated on one surface of the base layer (10) and can retroreflect a detection light, that has entered from a fixed direction, in the same direction, an adhesive layer (30) laminated on the other surface of the base layer (10) and adhering to an article, an easy-to-destroy layer (40) provided at least partially on the front surface of the retroreflective layer (20), and background information (50) consisting of designs or characters formed on the front surface of the base layer (10) on the side of the adhesive layer (30) by printing.
Description
Technical field
The present invention relates to retroeflection body labei sheet, for example the retroeflection body labei sheet of the style of opening that exposes of beaded glass (below be referred to as the anaclasis body) and the article that fixedly are pasted with this retroeflection body labei sheet.
Background technology
The retroeflection body is to have utilized to incide the reflex returned to incident direction once more as the light in for example beaded glass of reflecting body, and it is by constituting as the glass bead layer of anaclasis body and the reflection horizon that is provided with thereunder.The retroeflection body has the enclosed type that forms water white resin system clad and form on beaded glass, the style of opening that reaches the exposure beaded glass.
Disclose a kind of retroeflection body and hologram are combined in the patent documentation 1 and sought to strengthen false proof technology.This retroeflection body utilizes following character to be usually used in traffic mark, armband, working cloth etc.: under the such natural light of sunshine and illumination light from all directions, and for example the such direction unanimity of automobile lamp light next time the tone of beam seem different to some extent such character.In addition, on bank note, certificate etc. false proof, also use the retroeflection body that has special reflecting light.This is used for false proof retroeflection body and adopts the case type retroeflection body of printing easily mostly.
A kind of technology that is used to be easy to destroy glass bead layer, reflection horizon and it can't be re-used is disclosed in the patent documentation 2.This retroeflection body is, utilizes glass bead layer, the reflection horizon of retroeflection body in a single day destroyed with regard to the principle that is difficult to recover and as confirming sheet in Kaifeng, is that purpose is to affirmations that breaks a seal such as casings to prevent to palm off, forge, distort etc. thus.
Patent documentation 1: TOHKEMY 2000-272300 communique
Patent documentation 2: TOHKEMY 2003-29012 communique
About the disclosed retroeflection body of patent documentation 2, peel off and will destroy glass bead layer in case will stick on retroreflection sheet on the casing etc. etc., therefore can't re-use., if use organic solvent such as alcohol or heat when peeling off, then the bonding force of the bonding coat of retroeflection body weakens, and can peel off under the situation of not destroying glass bead layer, reflection horizon, might re-use.
Summary of the invention
The present invention puts in view of the above problems and finds out, its purpose is to provide a kind of retroeflection body labei sheet to reach the article that fixedly are pasted with this retroeflection body labei sheet, this retroeflection body labei sheet is not the destruction of check as for example glass bead layer, the reflection horizon etc. of retroeflection body, distinguish and pasted labei sheet whether again but can be applied to printed layers situation on the retroeflection surface by observation, the situation that the result can not break a seal or break a seal is confirmed, thereby can be judged to there is no need to check whether article have been carried out forgery, personation.
What the inventor etc. furtherd investigate in order to achieve the above object found that: when being provided with the destructible layer that is formed by the material that friction force is had destructible on the beaded glass exposure at the retroeflection body, very little power will make the destructible layer peel off.Thereby finished the present invention.
That is, retroeflection body labei sheet of the present invention comprises: substrate layer; Retroreflective layer, it is laminated on the face of substrate layer, and can make this detection light to the equidirectional retroeflection when detecting light from prescribed direction incident; Bonding coat, it is laminated on another face of substrate layer, and is adhered to article; And the destructible layer, it is arranged at least a portion on the surface of retroreflective layer; Retroreflective layer comprises: anaclasis body layer; Keep layer, anaclasis body layer is remained the surface element exposed state and the reflection horizon of this anaclasis body layer, be laminated on the face of a side opposite with surface element of anaclasis body layer or the inside that keeps layer, the destructible layer is formed by the material that friction force is had destructible.
The object lesson of anaclasis body layer is a plurality of beaded glasses, and these a plurality of beaded glasses are retained as a part and imbed the state on the surface that keeps layer and the state that is paved with, and this maintenance is pressed on substrate layer layer by layer and is made of thermoplastic resin.
According to above-mentioned structure, so that the release backing paper bending does not make the mode of retroeflection body labei sheet bending peel off, and the mode that at all can not run into the destructible layer with hand sticks on retroeflection body labei sheet on the article.When so pasting retroeflection body labei sheet, only otherwise the destructible layer that is formed by the material that friction force is had destructible is applied the power that can not apply usually, the destructible layer just can not be destroyed.
At this,, might desire and the devious conduct of forging the article replacing for show no sign of the article that ruined state is pasted with the article of retroeflection body labei sheet or is contained in article inside with the destructible layer.
If change the devious conduct of the article that are pasted with retroeflection body labei sheet, then retroeflection body labei sheet is peeled and it is sticked on the forgery article again from authentic articles.In addition, for in container body, holding ROM etc. and closing the lid, cover the article that are pasted with retroeflection body labei sheet at the faying face of container body and lid, if change the devious conduct of ROM etc., then retroeflection body labei sheet is peeled and it is sticked on again from authentic articles and forge on the article.At this moment, in case the retroeflection body is applied careless power, perhaps careless the wiping rubbed the destructible layer with the hands, and the destructible layer will be from the surfacial spalling of retroreflective layer.
Dig when peeling off will sticking on retroeflection body labei sheet on the article, the destructible layer of retroeflection body labei sheet is applied bending force, and this destructible layer forms by the material that friction force is had destructible, so this destructible layer is destroyed locally and peeled off.Particularly, when having applied the power of the anaclasis body laminar surface of wiping stranding retroeflection body, the destructible layer will be peeled off.
Therefore, for authentic articles, if exist forge, distort, during the suspicion of personation etc., can stick on the situation of the destructible layer of the retroeflection body labei sheet on the article by observation, the situation that does not break a seal or broken a seal is confirmed, thereby can be waited to detect whether carried out forgery, personation according to the destruction of destructible layer or the state of coming off.When the destructible layer shows no sign of when take place destroying, provablely do not dig retroeflection body labei sheet, promptly do not paste retroeflection body labei sheet again.In addition, when the destructible layer has taken place even when little by little destroying, provablely dug retroeflection body labei sheet, promptly pasted retroeflection body labei sheet again.Thereby whether the destructible layer on labei sheet surface exists or its state that comes off by inquiry, confirms whether retroeflection body labei sheet of the present invention have been applied power, and article has been implemented the operation that makes a stab.
According to above-mentioned structure, be not the destruction of glass bead layer, reflection horizon etc. by detecting retroeflection body labei sheet, but can be applied to the situation of the destructible layer on the retroeflection surface by observation, the situation that does not break a seal or broken a seal is confirmed, can be detected thus and whether article carried out forgery, personation.
The retroeflection body labei sheet of above-mentioned structure preferably, the destructible layer is by transparent under natural light or have and the transparency material that is difficult under the situation that color forms with the color of this color discrimination in the reflection horizon and form.According to this structure, the devious conduct of the article replacing of retroeflection body labei sheet will be pasted with even desire to carry out, owing to can't discern the situation that is formed with the destructible layer, therefore when peeling off retroeflection body labei sheet, use nail and finger tip mostly and wipe the destructible layer of rubbing the sheet surface with the hands.Owing to the power that the sheet surface is applied nail, finger tip, to compare with the situation of digging retroeflection body labei sheet with not contacting the destructible layer, the destruction of destructible layer can be obviously.Thereby, the destruction of destructible layer, come off more obviously, therefore can confirm to paste again the situation of retroeflection body labei sheet more significantly.
For whether the destructible layer of investigating the labei sheet surface exists or its state that comes off, to retroeflection body labei sheet irradiation high light, for example via the light of the light behind the optical lens, direction unanimity.So, in the part that does not cover the destructible layer of anaclasis body layer, incide the anaclasis of this anaclasis body layer and return, so the color in reflection horizon strengthens, compare with the color of under natural light, seeing, can see distinct more color.On the other hand, if the destructible layer exists, then the light that returns in the refraction of anaclasis body layer and in reflective layer reflects is because of the deflection of destructible layer.Therefore, in the zone that has the destructible layer with do not exist between the zone of destructible layer and can produce contrast.Like this, investigate whether there is the destructible layer,, can judge whether to have carried out re-using behavior according to its result to retroeflection body labei sheet irradiation high light.
Thereby, according to the present invention, utilize the reader of radiation detection light to scan detection light, image show transparency material pattern or be contained in pattern in the reader in advance and compare and discern, thereby need not take to judge at the destructible layer whether such inspection method has taken place to destroy, just can whether exist or its state that comes off by the simple more destructible layer of investigating the labei sheet surface of checking.
The retroeflection body labei sheet of above-mentioned structure preferably has the stripping damage layer between substrate layer and bonding coat, this stripping damage layer autoadhesion is peeled off to be stripped from the state of article and destroyed and remain at least a portion of article.According to this structure, the devious conduct of changing at the article that will attempt to be pasted with retroeflection body labei sheet and peel moment of retroeflection body labei sheet, the stripping damage layer just is stripped from destruction, retroeflection body labei sheet can't be recovered again, and the retroeflection body labei sheet of having carried out pasting again is that a glance just can be found out and unsmooth and have a concavo-convex situation.Especially owing to there is retroreflective layer, so the labei sheet hardening, for peel off need be bigger power.Thereby the stripping damage layer also is stripped from destruction easily.That is, the affirmation that does not break a seal or broken a seal also can easily be distinguished by the smoothness of visual inspection retroeflection body labei sheet except detecting the destructible layer.In addition, in structure,, therefore be difficult to bending, can not peel off simply because the gross thickness of labei sheet becomes big with stripping damage layer.Therefore, want to peel off retroeflection body labei sheet, need apply bigger power, when this masterpiece had been used in the destructible layer, the destructible layer can destroyedly reliably come off.Therefore, prevent that the effect of forging, palming off is higher.
The retroeflection body labei sheet of above-mentioned structure preferably, the reflection horizon produces schemochrome by the interference of light effect.Schemochrome is meant the light and the light interference of reflecting at lower surface in the upper surface reflection of the film of light wavelength degree, and produces the color of the phenomenon of various colors according to the angle of watching.Make the reflection horizon that produces schemochrome, for example can list, (1) metallic compound is made the light wavelength (single thin film of degree of 390nm～770nm), (2) metallic compound is made the multilayer film of light wavelength degree, (3) utilize fine groove, projection, particulate that light is produced to interfere, scattering.According to this structure, background color becomes camouflage color, is difficult to see the destructible layer, and the people who desires to carry out devious conduct that the article that are pasted with retroeflection body labei sheet are changed is difficult to notice the existence of destructible layer more.Therefore, prevent that the effect of forging, palming off is higher.
The retroeflection body labei sheet of above-mentioned structure preferably is provided with otch at the side of retroreflective layer.According to this structure, when with the mode of residual retroeflection body labei sheet on the release backing paper with the labei sheet remainder when release backing paper peels, can disperse the power that retroeflection body labei sheet applies, the drying of the solvent that further promotes bonding agent and contained by otch, sheet is adhered to stripping film more firmly, therefore can prevent with rising.In addition, in order to carry out retroeflection body labei sheet that the devious conduct desire will be pasted on article when peeling, torn from otch, propagate into the stripping damage layer and can't recover again, therefore can not paste retroeflection body labei sheet with no damage again, thereby prevent that the effect of forging, palming off is higher.
The retroeflection body labei sheet of above-mentioned structure preferably, retroreflective layer is transparent, is formed with background information on any surface of substrate layer, this background information has pattern or literal.According to this structure, retroeflection body labei sheet can be seen background information under natural light, therefore be difficult to know have the destructible layer on the surface, therefore when desiring to carry out devious conduct, wipe the probability rising of rubbing lip-deep destructible layer with the hands and making its destruction, thereby prevent that the effect of forging, palming off is higher.
According to the present invention, be not the destruction of check as for example glass bead layer, the reflection horizon etc. of retroeflection body, distinguish and pasted labei sheet whether again but can be applied to printed layers situation on the retroeflection surface by observation.The result, can provide a kind of retroeflection body labei sheet to reach the article that fixedly are pasted with this retroeflection body labei sheet, the situation that this retroeflection body labei sheet can not break a seal or break a seal is confirmed, thereby can be judged to there is no need to check whether article have been carried out forgery, personation.In addition, according to the present invention,, prevent the effect of forging, palming off so have because be difficult to make the counterfeit of retroeflection body labei sheet.
Description of drawings
Fig. 1 is the concise and to the point cut-open view of the retroeflection body labei sheet of expression the 1st embodiment;
Fig. 2 is the concise and to the point cut-open view of the retroeflection body labei sheet of expression the 2nd embodiment;
Fig. 3 is the concise and to the point cut-open view of the retroeflection body labei sheet of expression the 3rd embodiment;
Fig. 4 is the concise and to the point cut-open view of the retroeflection body labei sheet of expression the 4th embodiment;
Fig. 5 is the concise and to the point cut-open view of the retroeflection body labei sheet of expression the 5th embodiment;
Fig. 6 is the concise and to the point cut-open view of the retroeflection body labei sheet of expression the 6th embodiment;
Fig. 7 is the concise and to the point cut-open view of the retroeflection body labei sheet of expression the 7th embodiment;
Fig. 8 is the concise and to the point cut-open view of the retroeflection body labei sheet of expression the 8th embodiment;
Fig. 9 is the vertical view of the retroeflection body labei sheet of the 9th embodiment;
Figure 10 is concise and to the point cut-open view expression the 9th embodiment, that a mode of printing protective seam is set on the retroeflection body labei sheet corresponding with the 1st embodiment;
Figure 11 is concise and to the point cut-open view expression the 9th embodiment, that the another way of printing protective seam is set on the retroeflection body labei sheet corresponding with the 1st embodiment;
Figure 12 is that expression applies circular hemisect and arranges the vertical view that forms retroeflection body labei sheet of the present invention and peeling label sheet remainder sheet state before the retroeflection body label lamella that lamination is formed on the release backing paper;
Figure 13 is the schematic cross sectional views of the state after the expression peeling label sheet remainder;
Figure 14 is that expression is with the figure of labei sheet as the state of sealing of the certificate on the case that sticks on the control part;
Figure 15 is the figure of expression state that labei sheet is used so that the mode of the mating surface of the case main body of its coverage control part and lid is sealed;
Figure 16 is the figure that expression sticks on labei sheet the state on control basal plate, the housing side such as CPU.
Embodiment
Below, describe the embodiment of retroeflection body labei sheet of the present invention in detail with reference to accompanying drawing.
The 1st embodiment
As shown in Figure 1, the retroeflection body labei sheet 1 of the 1st embodiment comprises: substrate layer 10; Retroreflective layer 20, it is laminated on the face of substrate layer 10, and can make this detection light to the equidirectional retroeflection when detecting light from prescribed direction incident; Bonding coat 30, it is laminated on another face of substrate layer 10, and is bonded in article; Destructible layer 40, it is arranged on lip-deep at least a portion of retroreflective layer 20; And background information 50, it is made of pattern that forms by printing or literal etc. on the surface of bonding coat 30 sides of substrate layer 10.In this embodiment, constitute and to see background information 50 from the face side of retroeflection body labei sheet 1.That is, retroreflective layer 20, destructible layer 40 and substrate layer 10 constitute transparent.In addition, background information 50 also can be arranged on the surface of retroreflective layer 20 sides of substrate layer 10.If will make retroeflection body labei sheet 1 have originality, then on background information 50, use specific design, trade mark, house sign to get final product.
In this embodiment, anaclasis body layer 21 adopts beaded glass to form.Beaded glass 21 is imbedded in the mode that its part is exposed to the face side that keeps layer 22.In this embodiment, reflection horizon 23 is water white transparency or colored transparent.Beaded glass 21 is the balls that are used to make the anaclasis of incident, and its latter half is the state that buries to keeping in the layer 22 substantially, and remaining the first half is for being exposed to airborne state.The raw material of beaded glass 21 is not special to be limited, and can adopt BaO-SiO
2-TiO
2Class glass, BaO-ZnO-TiO
2Class glass.Refractive index is in 1.9～2.2 the scope of common employing and gets final product.In the present embodiment, the refractive index of beaded glass 21 is about 1.9.Preferably, the particle diameter of beaded glass 21 is 38 μ m～50 μ m or 45 μ m～90 μ m.Preferably beaded glass 21 is paved with ordered state with abutting one another, but beaded glass 21 is separated to each other a little.Also can have originality, on circular or heart-shaped area, remove beaded glass 21 with constant space in order to make reflecting body labei sheet 1.
Keeping layer 22 to keep beaded glasses 21, is to be used for the layer that bonding substrate layer 10 and beaded glass 21 keep this beaded glass 21.About keeping layer 22, preferably, use good and transparent higher resin, for example thermoplastic resins such as polystyrene resins, polyester resin, propylene resin, silicones, fluororesin, polyamide-based resin, polyvinyl alcohol resin, polyurethanes resin, polyolefin resin, polycarbonate resin, polysulfone resin with the cohesiveness of beaded glass 21.
For example, can make the reflection horizon 23 that can produce schemochrome by the optical index in the alternatively laminated viewing area shown below higher metallic compound and lower compound.
[metallic compound that optical index is higher]
Zinc sulphide (ZnS): 2.40
Titanium dioxide (TiO
2): 2.71 (rutile structure bodies), 2.52 (anatase structured bodies)
Indium oxide (In
2O, In
2O
3): 2.00
Tin oxide (SnO, SnO
2): 1.90
Zirconia (ZrO
2): 2.40
Aluminium oxide (Al
2O
3): 1.76
Magnesium oxide (MgO): 1.74
[metallic compound that optical index is higher]
Calcium fluoride (CaF
2): 1.44
Magnesium fluoride (MgF
2): 1.38
Sodium fluoride (NaF): 1.29
Monox (SiO
2): 1.46
Preferably, the bed thickness in reflection horizon 23 is at the light of the upper surface of film reflection with in the scope of the light interference of lower surface reflection, selects in 300～600nm when multilayer.If total bed thickness of multilayer is less than 300nm then the interference light dimness, if gross thickness is greater than 600nm then can't obtain desired results look or appearance color gonorrhoea.Preferably, the thickness of a layer is in the scope of 100～200nm.In addition, preferably, in the scope of a bed thickness, has level.Want in individual layer, to present schemochrome, adopt the film of above-mentioned metallic compound to get final product.Under the situation of individual layer, thickness is preferably the scope of 100～600nm, has level and get final product in the scope of this bed thickness.
Preferably, adopt the higher bonding agent of the transparency to form bonding coat 30.For example, can enumerate polyesters bonding agent, acrylic adhesives, polyurethane binding, ethylene oxide class bonding agent.In addition, also can be on the lower surface of bonding coat 30 also paste the stripping film (not shown) that peels before using and bonding coat 30 is exposed.
The retroreflective layer of background information 50 is transparent, and its any surface at substrate layer 10 has pattern or literal forms.Under natural light, be the structure that can see background information 50, therefore can adopt the pattern that is difficult to see destructible layer 40, perhaps adopt mark, trade mark with proof function.In case to the stronger light of retroeflection body labei sheet 1 irradiation, then transparent retroreflective layer 20 is utilized whole reflection of retroeflection function, at this moment, can't see this background information 50.Thereby, if remove the part in the reflection horizon 23 of retroreflective layer 20, then can see background information 50 in the part of from whole reflection, missing in the mode that has the little pattern that beaded glass is not set, can be used as concealed advertisement, other mark.
According to above-mentioned structure, only otherwise the destructible layer that is formed by the China ink that friction force is had destructible is applied the power that can not apply usually, destructible layer 40 just can not be destroyed.So that the release backing paper bending does not make the mode of retroeflection body labei sheet bending peel off, and, can not wipe the mode of rubbing the destructible layer with the hands strongly retroeflection body labei sheet is sticked on the article.When desiring to carry out the devious conduct that the article that are pasted with retroeflection body labei sheet are changed, can peel retroeflection body labei sheet and it is sticked on again from authentic articles and forge on the article, when peeling, the destructible layer can be peeled off.Therefore, by observing the situation of destructible layer, the situation that just can not break a seal or break a seal is confirmed, can be detected thus and whether carry out forgery, personation.
The retroeflection body labei sheet 1 of above-mentioned the 1st embodiment is can see through destructible layer 40, retroreflective layer 20 and substrate layer 10 to see background information 50 under natural light, but also reflection horizon 23 can be made as opaque structure, in this case, background information 50 is not set.In addition, formed destructible layer 40, but also can form destructible layer 40 by opaque ink by transparent China ink.In this case, preferably, with reflection horizon 23 color, and form destructible layer 40 by having the transparent China ink that is difficult to the color of this color discrimination.
The 2nd embodiment
As shown in Figure 2, the retroeflection body labei sheet 1A of the 2nd embodiment comprises: substrate layer 10; Retroreflective layer 20A, it is laminated on the face of substrate layer 10, and transparent, and can make this detection light to the equidirectional retroeflection when detecting light from prescribed direction incident; Bonding coat 30, it is laminated on another face of substrate layer 10, and is bonded in article; Destructible layer 40, it is arranged on the lip-deep part of retroreflective layer 20A; And background information 50, it is formed by pattern or literal etc. on the surface of bonding coat 30 sides of substrate layer 10.
About other structures, identical with the 1st embodiment, the therefore Reference numeral of the constitutive requirements that mark is corresponding and omit its explanation.Effect, effect is also identical with the 1st embodiment.
The 3rd embodiment
As shown in Figure 3, the retroeflection body labei sheet 1B of the 3rd embodiment comprises: substrate layer 10; Retroreflective layer 20, it is laminated on the face of substrate layer 10, and transparent, and can make this detection light to the equidirectional retroeflection when detecting light from prescribed direction incident; Bonding coat 30, it is laminated on another face of substrate layer 10, and is bonded in article; Stripping damage layer 60, it is formed between substrate layer 10 and the bonding coat 30; Destructible layer 40, it is arranged on the lip-deep part of retroreflective layer 20; And background information 50, it is formed by pattern or literal etc. on the surface of bonding coat 30 sides of substrate layer 10.Retroreflective layer 20 is structures same with the 1st embodiment, and it comprises beaded glass is paved with the anaclasis body layer 21 that forms, anaclasis body layer 21 is remained the maintenance layer 22 of its surface element exposed state and is laminated on the face of a side opposite with surface element of anaclasis body layer 21 or is laminated to the reflection horizon 23 that keeps layer 22 inside.
The difference of this retroeflection body labei sheet 1B and the 1st embodiment is to have stripping damage layer 60.Stripping damage layer 60 is formed with more weak bonding force lamination by a plurality of film layers, in case it is to apply the layer that causes dissociating between tunic with regard to being easy to interface peel takes place from horizontal shearing force.At this, the part that dissociates between tunic is present in the part except that periphery of labei sheet.
About his structure, identical with the 1st embodiment, the therefore Reference numeral of the constitutive requirements that mark is corresponding and omit its explanation.Effect, effect is also identical with the 1st embodiment.
Stripping damage layer 60 is to peel off the layer of being stripped from least a portion of destroying and remaining in article (not shown) in the state of article (not shown) by retroeflection body labei sheet 1B autoadhesion.
According to this structure, following as can be known situation: when desiring to carry out the devious conduct that the article that are pasted with retroeflection body labei sheet are changed, in the moment that peels retroeflection body labei sheet, retroeflection body labei sheet just becomes and can't recover.Carrying out under the situation of pasting again, not only destructible layer 40 is understood destroyed coming off, the surface of retroeflection body labei sheet 1B is also unsmooth and present can obviously recognize concavo-convex, therefore by observing the situation of destructible layer 40 and stripping damage layer 60, can be confirmed to be the situation that has still broken a seal in Kaifeng not, can detect thus and whether carry out forgery, personation.
The 4th embodiment
As shown in Figure 4, the retroeflection body labei sheet 1C of the 4th embodiment comprises: substrate layer 10; Retroreflective layer 20A, it is laminated on the face of substrate layer 10, and transparent, and can make this detection light to the equidirectional retroeflection when detecting light from prescribed direction incident; Bonding coat 30, it is laminated on another face of substrate layer 10, and is bonded in article; Stripping damage layer 60, it is formed between substrate layer 10 and the bonding coat 30; Destructible layer 40, it is arranged on the lip-deep part of retroreflective layer 20A; And background information 50, it is formed by pattern or literal etc. on the surface of bonding coat 30 sides of substrate layer 10.
The difference of this retroeflection body labei sheet 1C and the 2nd embodiment is to have stripping damage layer 60.About other structures, identical with the 2nd embodiment, the therefore Reference numeral of the constitutive requirements that mark is corresponding and omit its explanation.Effect, effect is also identical with the 3rd embodiment.
The the 5th～the 8th embodiment
Fig. 5～Fig. 8 represents the 5th～the 8th embodiment.Anaclasis body layer 21D and the 1st embodiment of the retroreflective layer 20D of the retroeflection body labei sheet 1D of the 5th embodiment shown in Figure 5 are different.Anaclasis body layer 21E and the 2nd embodiment of the retroreflective layer 20E of the retroeflection body labei sheet 1E of the 6th embodiment shown in Figure 6 are different.Anaclasis body layer 21F and the 3rd embodiment of the retroreflective layer 20F of the retroeflection body labei sheet 1F of the 7th embodiment shown in Figure 7 are different.Anaclasis body layer 21G and the 4th embodiment of the retroreflective layer 20G of the retroeflection body labei sheet 1G of the 8th embodiment shown in Figure 8 are different.
These anaclasis body layers 21D～21G is not beaded glass, but is arranged with the optical forming body of convex sphere on its two sides, can obtain in fact and is paved with the retroreflective layer identical functions that beaded glass forms to arrange shape.About other structures, identical with corresponding embodiment, therefore mark identical Reference numeral and omit its explanation.
The 9th embodiment
Fig. 9 represents the vertical view of the retroeflection body labei sheet of the 9th embodiment, and this retroeflection body labei sheet is provided with printing protective seam 70 at retroeflection body labei sheet 1, the 1A～1G of above-mentioned the 1st～the 8th embodiment around the surface of retroreflective layer.Figure 10 represents that the destructible layer 40 of the retroeflection body labei sheet 1 of the 1st embodiment shown in Figure 1 is formed into the situation of labei sheet periphery, in this retroeflection body labei sheet 1, and printing protective seam 70 overlapping being arranged on the destructible layer 40.Figure 11 represents the situation that the destructible layer 40 of the retroeflection body labei sheet 1 of the 1st embodiment shown in Figure 1 forms away from the labei sheet periphery, in this retroeflection body labei sheet 1, and printing protective seam 70 overlapping being arranged on the retroreflective layer 20.Printing protective seam 70 also can similarly be provided with at retroeflection body labei sheet 1, the 1A～1G of the 1st～the 8th embodiment.
Printing protective seam 70 helps to prevent that thin slice in the retroeflection body labei sheet that comprises ordered state on the release backing paper is overlapping and the power that is applied in etc. cause destructible layer 40 destroyed when carrying waits.By forming printing protective seam 70, can avoid proper operator to touch destructible layer 40 because of carelessness in operating aspect, therefore can improve the precision of finding forgery behavior, personation.
Preferably, printing protective seam 70 is printing-ink or thermoplastic resin.As for thermoplastic resin, polystyrene resins, polyester resin, propylene resin, silicones, fluororesin, polyamide-based resin, polyvinyl alcohol resin, polyurethanes resin, polyolefin resin, polycarbonate resin, polysulfone resin etc. are for example arranged.By printing protective seam 70 is set, makes the thickness increase of destructible layer 40 and make it be difficult for declining.Preferably, printing protective seam 70 is added up with destructible layer 40 and is had the above thickness of 5 μ m.
Use by Toyo Ink (East ocean イ Application キ in that tone that the reflective layer reflects light time can see is gone up for the surface (exposure of beaded glass) of red retroeflection body) transparent ink that constitutes of system FDKARTON ACE MAT OP NISU (FD カ Le ト Application ACE マ Star ト OP ニ ス) and form light transmission literal " Sample " destructible layer by typographic printing.It is 3 μ m and 5 μ m these two kinds that the destructible layer is made thickness.
The retroeflection body layer that will have the destructible layer that bed thickness has nothing in common with each other is die-cut into the circle of diameter 1cm, and it is sticked on the casing as retroeflection body labei sheet.The literal " Sample " of this retroeflection body labei sheet is difficult to see under natural light, but when having shone high light, literal " Sample " appears in one's mind and can see.Then, peel thin slice from casing, once more it is sticked on the casing, the irradiation high light has been observed thin slice.Under the situation of the thin slice of the destructible layer with thickness 3 μ m, the literal of " Sample " is reamed, and in having been reamed the zone of literal, the literal of " Sample " appears in one's mind with the state of reading basically not come out and can see.On the other hand, under the situation of the thin slice of the destructible layer with thickness 5 μ m, the literal of " Sample " clearly appears in one's mind and can see.In addition, this observation has been carried out 20 times repeatedly, all is identical results.
Embodiment 2
On the beaded glass of retroeflection body (tone seen of reflective layer reflects light time is for red), use the colored transparent printing ink (Toyo Ink system FD KARTON ACE MAT OP NISU+ cherry palace chemistry (Sakurai Palace chemistry) of the different tones of seeing with the reflective layer reflects light time of tone to make MICROLITH BLUE (マ イ Network ロ リ ス Block Le one) (total weight 3%)) printed literal " Sample ".
The retroeflection body with coloured destructible layer that obtains is die-cut into the circle of diameter 1cm, it is sticked on the casing as retroeflection body labei sheet.
Similarly to Example 1, carry out the disbonded test of the scraps of paper.The situation that reams " Sample " literal is the degree that can confirm a little under natural light, but when the irradiation high light, the color in reflection horizon is strengthened, and, can confirm clearly that " Sample " literal is destroyed.In addition, this observation has been carried out 20 times repeatedly, all is identical results.
Embodiment 3
On the surface (exposure of beaded glass) of retroeflection body (reflective layer reflects light time see tone become iris according to viewing angle, be so-called schemochrome), using warm colour is colored transparent printing ink and the destructible layer that forms literal " Sample " by typographic printing with thickness 3 μ m.
The retroeflection body that will have the destructible layer is die-cut into the circle of diameter 1cm, and it is sticked on the casing as retroeflection body labei sheet.The literal of this retroeflection body " Sample " is the degree that can confirm a little under natural light.When irradiation during high light, when the schemochrome in the reflection horizon of retroeflection body saw that warm colour is, literal " Sample " just can't confirm, when tone except that warm colour is was seen in the reflection horizon in that the retroeflection body is tilted, literal " Sample " just can be confirmed.Then, carry out the disbonded test of the scraps of paper, when the irradiation high light and when observing thin slice, in the zone that has reamed " Sample " literal, when the schemochrome in reflection horizon was seen tone removing warm colour is, literal appeared in one's mind with ruined state and can see.In addition, this observation has been carried out 20 times repeatedly, all is identical results.
Embodiment 4
On the beaded glass of the retroeflection body of embodiment 3, using warm colour is colored transparent printing ink (Toyo Ink system FD KARTON ACE MAT OP NISU+ cherry palace chemistry system MICROLITH RED (マ イ Network ロ リ ス レ Star De) (total weight 3%)) with thickness 3 μ m printing spider lable, and the transparent ink by employing in embodiment 1 is with thickness 3 μ m printing words " Sample ".
The retroeflection body with two kinds of printings that obtains is die-cut into the circle of diameter 1cm, it is sticked on the casing as retroeflection body labei sheet.This retroeflection body labei sheet only can be seen spider lable under natural light.Then, carried out the disbonded test of thin slice.
When observing thin slice when the irradiation high light, schemochrome is strengthened, and in having been reamed the zone of " Sample " literal, " Sample " literal appears in one's mind with the collapse state of reading basically not come out and can see.In addition, when the schemochrome in reflection horizon was seen tone except that warm colour system, spider lable appeared in one's mind with ruined state and can see.In addition, this observation has been carried out 20 times repeatedly, all is identical results.
Then, the manufacture method of simple declaration retroeflection body of the present invention labei sheet.At this, the situation of the retroeflection body labei sheet that has the destructible layer on beaded glass is described.
The manufacturing process of retroeflection body labei sheet comprises fixedly operation, the formation operation in reflection horizon, the stickup operation of substrate layer, the film stripping process of beaded glass substantially.Below, concrete manufacture method is described.
(1) reflection horizon is the manufacturing of the retroeflection body labei sheet of individual layer
At the upper surface coating polyvinyl resin of films such as PET film, scatter beaded glass and carry out drying to arrange shape thereon.Thus, make the lower semisphere of beaded glass bury in polyvinyl resin (the fixedly operation of beaded glass).Then, at the upper surface of the beaded glass that exposes, with the film (the formation operation in reflection horizon) of evaporation metal compound in the scope of 100～600nm.Then, on the substrate layer that is laminated to by bonding coat on the stripping film, apply polyvinyl resin, it is as keeping layer and substrate layer and this maintenance layer being sticked on (substrate layer stickup operation) on the above-mentioned reflection horizon, last, peel off film and polyvinyl resins (film stripping process) such as PET film.
Concavo-convex owing to existing on the surface of beaded glass, so the film thickness change of metallic compound, have level.
(2) reflection horizon is the retroeflection body labei sheet of multilayer
Upper surface coating polyvinyl resin at films such as PET films scatters beaded glass thereon and carries out drying, makes the lower semisphere of beaded glass bury in polyvinyl resin (the fixedly operation of beaded glass).Then, in the film (scope of 100～200nm) of a plurality of metallic compounds of upper surface evaporation of the beaded glass that exposes, the reflection horizon (the formation operation in reflection horizon) of making multilayer.Then, on the substrate layer that is laminated to by bonding coat on the stripping film, apply polyvinyl resin, it is as keeping layer and substrate layer and this maintenance layer being sticked on (substrate layer stickup operation) on the above-mentioned reflection horizon, last, peel off film and polyvinyl resins (film stripping process) such as PET film.
When the retroeflection body labei sheet that on beaded glass, has the destructible layer that will obtain make given shape, for example during circular labei sheet, making only has circular labei sheet 1 to be arranged in the thin slice (with reference to Figure 12) that forms on the stripping film 80.The retroeflection body labei sheet 1 that only has labei sheet to remain in to form on the stripping film 80 can be by applying the otch 91 of labei sheet shape on beaded glass 21, and only peel off circular labei sheet remainder 93 and obtain.
But, when peeling label sheet remainder 93 (removing the sheet slag), the situation that labei sheet remainder 93 and labei sheet 1 are peeled off (below be called " with rise ") together can take place.In order to prevent with rising, as shown in figure 12, at the side setting of labei sheet 1 otch 91 across labei sheet remainder 93.Otch 91 is set to periphery in labei sheet 1 each other in the diagonal angle.This otch 91 is the hemisects that are applied to retroreflective layer 20 from the surface of retroeflection body labei sheet.
By this otch 91 across retroeflection body labei sheet 1 and labei sheet remainder 93 is set, promote the drying of the solvent that bonding agent contained by otch, when release backing paper 80 peels labei sheet remainder 93, the power that is applied to retroeflection body labei sheet 1 can be disperseed, retroeflection body labei sheet 1 is adhered to release backing paper 80 securely, therefore can prevent with rising.And otch 91 has tearability with respect to the stickup again of retroeflection body labei sheet 1, does not have restoratively for pasting again, therefore having Kaifeng and confirming effect.
About being used to apply the cutter of otch 91 and the die-cut scarfing 92 die-cut retroeflection body labei sheet 1 of label, for example can use Thomson cutter, rotating knife etc.
Then, any article that fixedly are pasted with in above-mentioned the 1st～the 9th retroeflection body labei sheet are described.
About fixedly being pasted with the article of retroeflection body labei sheet, what can list false proof article or accommodate these false proof article holds the body article.For example, in game machines such as pinball game or Slot Machine, the probability that goes out ball is written among PROM etc., and this PROM etc. is contained in the case and can't touches simply.In order to improve the devious conduct that the ball probability and to prevent, at PROM etc. self or accommodate on the case of PROM etc. retroeflection body labei sheet is set, thereby can judge to there is no need to check whether carried out forgery, personation to changing PROM.
When at PROM etc. when having pasted retroeflection body labei sheet on one's body, need change with wrongful PROM etc., and paste retroeflection body labei sheet again.In addition, when the mode of the mating surface of box main body that contains PROM etc. with covering and lid has been pasted retroeflection body labei sheet, need peel retroeflection body labei sheet, open lid and come to change, paste retroeflection body labei sheet in the mode of the mating surface that covers box main body and lid once more with wrongful PROM etc.
In a single day retroeflection body labei sheet of the present invention pastes again, and the destructible layer will be destroyed.In addition, if there is the stripping damage layer, then the stripping damage layer also can be stripped from destruction, therefore can distinguish the situation of pasting again of having carried out immediately.Thereby, can be confirmed to be the situation that has still broken a seal in Kaifeng not, perhaps can confirm whether to have changed article.
As for the article of pasting retroeflection body labei sheet, can list electronic components such as control basal plate in the substrate housing that is contained in game machine control basal plate unit, substrate housing, PROM, to sealing of the certificate that is pasted on housing etc.
Figure 14 represents to be provided with 102 the situation sealed to certificate 101, and this certificate 101 sticks on the housing 100 that holds as the control part of improper replacing object.About sealing 102, adopt retroeflection body labei sheet 102.In addition, shown in this example, also the background information 50 of retroeflection body labei sheet 102 can be made proof information, seal 102 and adopt common seal.
Figure 15 represent mode with covering shell main body 104 and the mating surface of lid 105 with retroeflection body labei sheet 106 as sealing the situation of pasting, this housing body 104 is held the control part as improper replacing object.
Figure 16 represents following situation: paste the 1st retroeflection body labei sheet 110 on the control basal plate 109 with CPU 107, ROM 108 etc. as improper replacing object, mounting control basal plate 109 on lower house 111, cover the upper shell 113 that the side is pasted with the 2nd retroeflection body labei sheet 112, and lower house 111 and upper shell 113 are linked up with bolt.In this example, the 2nd retroeflection body labei sheet 112 under assembled state between the side of the side of lower house 111 and upper shell 113.In addition, in this example, also can on CPU107, paste the 1st retroeflection body labei sheet 110.
Industrial applicibility
Owing to have the retroeflection body labei sheet of easy breakable layer as the anti-Kaifeng sealing part of the substrate housing case of for example game machine with of the present invention, as long as break a seal wrongly, therefore will stay its vestige, can effectively utilize in that devious conduct is taken precautions against in aspect the possible trouble.
Description of reference numerals
1,1A～1G retroeflection body labei sheet; 10 substrate layers; 20,20A～20G retroreflective layer; 21 beades; 21D～21G anaclasis body layer; 22 retaining layers; 23,23A reflecting layer; 30 bonding layers; 40 easy breakable layers; 50 background informations; 60 stripping damage layers; 70 printing protective layers; 80 release backing papers; 91 otch; The die-cut scarfing of 92 labels; 93 labei sheet remainders.
Claims (11)
1. retroeflection body labei sheet comprises:
Substrate layer;
Retroreflective layer, it is laminated on the face of above-mentioned substrate layer, and can make this detection light to the equidirectional retroeflection when detecting light from prescribed direction incident;
Bonding coat, it is laminated on another face of above-mentioned substrate layer, and is adhered to article; And
The destructible layer, it is arranged at least a portion on the surface of above-mentioned retroreflective layer;
Above-mentioned retroreflective layer comprises: anaclasis body layer; Keep layer, above-mentioned anaclasis body layer is remained the surface element exposed state of this anaclasis body layer; And the reflection horizon, be laminated on the face of a side opposite of above-mentioned anaclasis body layer or the inside of above-mentioned maintenance layer with surface element;
Above-mentioned destructible layer is formed by the material that friction force is had destructible.
2. retroeflection body labei sheet according to claim 1, wherein,
Above-mentioned destructible layer is by transparent under natural light or have and the transparency material that is difficult under the situation that color forms with the color of this color discrimination in above-mentioned reflection horizon and form.
3. retroeflection body labei sheet according to claim 1, wherein,
Have the stripping damage layer between above-mentioned substrate layer and above-mentioned bonding coat, this stripping damage layer autoadhesion is peeled off to be stripped from the state of above-mentioned article and is destroyed and remain at least a portion of above-mentioned article.
4. according to each described retroeflection body labei sheet in the claim 1 to 3, wherein,
Above-mentioned reflection horizon produces schemochrome by the interference of light effect.
5. according to each described retroeflection body labei sheet in the claim 1 to 4, wherein,
Side in above-mentioned retroreflective layer is provided with otch.
6. according to each described retroeflection body labei sheet in the claim 1 to 5, wherein,
Above-mentioned anaclasis body layer is made of a plurality of beaded glasses, and these a plurality of beaded glasses are retained as a part and imbed the state on the surface that keeps layer and the state that is paved with, and above-mentioned maintenance is pressed on above-mentioned substrate layer layer by layer and is made of thermoplastic resin.
7. according to each described retroeflection body labei sheet in the claim 1 to 6, wherein,
Above-mentioned retroreflective layer is transparent, is formed with background information on any surface of above-mentioned substrate layer, and this background information has pattern or literal.
8. according to each described retroeflection body labei sheet in the claim 1 to 7, wherein,
Above-mentioned retroeflection body labei sheet is false proof sealing.
9. article fixedly are pasted with each described retroeflection body labei sheet in the claim 1 to 8.
10. article according to claim 9, wherein,
Above-mentioned article be false proof article or accommodate these false proof article hold the body article, and fixedly be pasted with above-mentioned retroeflection body labei sheet.
11. article according to claim 9, wherein,
Above-mentioned article are article that a plurality of members of combination form, and fixedly are pasted with above-mentioned retroeflection body labei sheet in the mode that covers closure seam on these a plurality of members.