CN101993660A - Waterproof paint - Google Patents
Waterproof paint Download PDFInfo
- Publication number
- CN101993660A CN101993660A CN2009100346297A CN200910034629A CN101993660A CN 101993660 A CN101993660 A CN 101993660A CN 2009100346297 A CN2009100346297 A CN 2009100346297A CN 200910034629 A CN200910034629 A CN 200910034629A CN 101993660 A CN101993660 A CN 101993660A
- Authority
- CN
- China
- Prior art keywords
- waterproof paint
- filler
- mass parts
- sebs
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof paint which comprises thermoplastic styrene-butadiene rubber, asphalt and solvent oil. The waterproof paint also comprises drier and filler, wherein the drier is composed of one or more oxides of cobalt, manganese, zinc and calcium; and the filler is talcum powder, fly ash, pulverized asbestos, vermiculite powder, mica powder, heavy calcium carbonate or light calcium carbonate. Due to the adoption of styrene-ethylene-butylene-styrene block copolymer (SEBS), the waterproof paint of the invention has the advantages of excellent elasticity, low-temperature flexibility, low temperature resistance and aging resistance, and does not flow at high temperature, thereby improving the quality of products and widening the use temperature range of the products.
Description
Technical field
The present invention relates to a kind of coating, is a kind of waterproof paint specifically.
Background technology
Waterproof paint is to be main film forming substance by synthesising macromolecule copolymer, high molecular polymer and pitch, high molecular polymer and cement; The coating that adds solvent-borne type, water-latex type or powder-type that various auxiliary agents, material modified, packing material etc. be processed into.Waterproof paint is to use waste rubber and polystyrene foam to asphalt modification at present, concrete technology is for to carry out regenerative sulfur binding with shoddy under the composite regenerant effect, mix with the pitch heated and stirred again, adding waste polystyrene foam and anti-aging agent carry out blend behind the mixing, and then add an amount of solvent and clorafin in sizing material, and the flyash mixing stirring that adds through surface modification gets product.Though this waterproof paint is raw materials used cheap, make that quality product can not get guaranteeing, can only produce the low waterproof paint that waits, and the existing manufacturing technique complexity, make the production cost height.
Summary of the invention
Goal of the invention: the objective of the invention is in order to overcome the deficiencies in the prior art, provide a kind of and can improve the quality of products, ageing-resistant, low temperature flexibility, waterproof paint that elasticity is high.
Technical scheme: in order to solve the problems of the technologies described above, a kind of waterproof paint of the present invention, its component comprises thermoplastic styrene butadiene rubber, pitch, solvent oil.
Thermoplastic styrene butadiene rubber adopts SEBS, SEBS is the hydrogenation thermoplastic styrene butadiene rubber, it promptly is end segment with the polystyrene, the ethylene-butene copolymer that obtains with the polyhutadiene hydrogenation is the linearity three embedding multipolymers of middle elastomeric block, it has ageing-resistant performance, plasticity-, snappiness, weathering resistance, thermotolerance, compression deformability and excellent mechanical property, and need not the sulfuration can process use, scrap stock can heavily use; SEBS comprises line style and star-like, and line style has good processing properties, and star-like have a good modification performance.
For the drying and moulding that quickens to film with improve film quality, described waterproof paint also comprises siccative; Described siccative is one or more in the oxide compound of cobalt, manganese, zinc, calcium.
In order to improve mechanical propertys such as the hardness of filming, viscosity, flexibility, weather resistance, described waterproof paint also comprises filler; Described filler is talcum powder or flyash or asbestos powder or vermiculite power or mica powder or water-ground limestone or light calcium carbonate.
Beneficial effect: compared with prior art, advantage of the present invention is owing to adopted SEBS, make the present invention have excellent elasticity, low temperature flexibility, low temperature resistant, ageing resistance and high temperature non-flowing, thereby can improve the quality of products, enlarge product use temperature scope.
Embodiment
Further illustrate the present invention below in conjunction with specific embodiment, should understand these embodiment only is used to the present invention is described and is not used in and limit the scope of the invention, after having read the present invention, those skilled in the art all fall within the application's claims institute restricted portion to the modification of the various equivalent form of values of the present invention.
Embodiment 1: a kind of waterproof paint of the present invention, its component is: 6 mass parts powdery SEBS, No. 90 pitches of 30 mass parts, 40 mass parts solvent oils, 0.5 mass parts siccative, and siccative is the oxide compound of cobalt, 40 mass parts fillers, filler is a talcum powder, and SEBS adopts line style SEBS.
Embodiment 2: a kind of waterproof paint of the present invention, its component is: 7 mass parts powdery SEBS, No. 90 pitches of 35 mass parts, 45 mass parts solvent oils, 1 mass parts siccative, and siccative is the oxide compound of manganese, zinc, calcium, 32 mass parts fillers, filler is an asbestos powder, and SEBS adopts line style SEBS.
Embodiment 3: a kind of waterproof paint of the present invention, its component is: 8 mass parts powdery SEBS, No. 90 pitches of 40 mass parts, 50 mass parts solvent oils, 1.5 mass parts siccative are the oxide compound of manganese, zinc, 35 mass parts fillers, filler are water-ground limestone, and SEBS adopts star-like SEBS.
Embodiment 4: a kind of waterproof paint of the present invention, its component is: 9 mass parts powdery SEBS, No. 90 pitches of 45 mass parts, 55 mass parts solvent oils, 2 mass parts siccative are the oxide compound of zinc, 38 mass parts fillers, filler are light calcium carbonate, and SEBS adopts line style SEBS.
Embodiment 5: a kind of waterproof paint of the present invention, its component is: 10 mass parts powdery SEBS, No. 90 pitches of 50 mass parts, 60 mass parts solvent oils, 2 mass parts siccative are the oxide compound of zinc, 40 mass parts fillers, filler are light calcium carbonate, and SEBS adopts line style SEBS.
Claims (5)
1. waterproof paint, it is characterized in that: its component comprises thermoplastic styrene butadiene rubber, pitch, solvent oil.
2. waterproof paint according to claim 1 is characterized in that: its component also comprises siccative.
3. waterproof paint according to claim 2 is characterized in that: described siccative is one or more in the oxide compound of cobalt, manganese, zinc, calcium.
4. waterproof paint according to claim 1 is characterized in that: its component also comprises the filler that improves the pitch mechanical property.
5. waterproof paint according to claim 4 is characterized in that: described filler is talcum powder or flyash or asbestos powder or vermiculite power or mica powder or water-ground limestone or light calcium carbonate.