CN101993572A - High-elastic environment-friendly rubber sheet for teaching head and manufacturing process thereof - Google Patents
High-elastic environment-friendly rubber sheet for teaching head and manufacturing process thereof Download PDFInfo
- Publication number
- CN101993572A CN101993572A CN2009101682295A CN200910168229A CN101993572A CN 101993572 A CN101993572 A CN 101993572A CN 2009101682295 A CN2009101682295 A CN 2009101682295A CN 200910168229 A CN200910168229 A CN 200910168229A CN 101993572 A CN101993572 A CN 101993572A
- Authority
- CN
- China
- Prior art keywords
- mold
- environmental protection
- toner
- slurry
- teacher
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-elastic environment-friendly rubber sheet for a teaching head and a manufacturing process thereof, which relates to a product in the plastic field. The product comprises 80-100 parts of imported polyvinyl chloride (PVC) paste resin raw material, 100-150 parts of dioctyl phthalate, 2-4 parts of composite liquid stabilizer and 0.1-1 part of environment-friendly toner, and is molded by adopting a slush molding process. The manufacturing process comprises the following steps: grinding the toner; stirring; filtering; carrying out vacuum defoamation; and carrying out slush molding treatment. The slush molding treatment mainly comprises the following steps: putting a mold into a rubber heating furnace at 260-280 DEG C to be heated for 5-10s; then, taking out the mold, filling slurry, and standing for 10-15s; pouring the non-gelatinous slurry into a recovery tank; putting the mold into the rubber heating furnace again to be heated for 30-40s; taking out the mold, putting the mold into cooling water, and standing for 20-30s; and after the mold is cooled, taking the mold out of the water, and taking out burrs. The product integrates the characteristics of environment protection, flexibility, high elasticity and is convenient to use, uses more elastic materials, has stronger self-regulating property and wide application range, and can be used by a user conveniently.
Description
Technical field
The present invention relates to plastic cement field product, is a kind of hair dressing and beauty training aid, particularly a kind of novel high-elastic shape of face teacher head of cutting.
Background technology
Teacher's head in the market mainly contains following several, and a kind of is combination teacher head, and combination teacher head is look to be sent out be inserted on the plastic mold, the inner filled and process of plastic mold, and outside surface is made up, and the drawback of this combination teacher head is the cost height, and handiness is little.Hair style can only be arranged in pairs or groups with a kind of shape of face, and the colour of skin is made up or the like, and various elements all can not mutual alternative change, and purposes is single.Second kind is to cut ear teacher head, cuts ear teacher head itself and has shape of face and cosmetic, can wear different shaven heads and use, but because its shape of face and cosmetic have been itself to carry, still have certain limitation.The third is to cut face teacher head, and this teacher's head only is fixed together hair and rubber, can be worn on the different shaven heads as cap, is combined as a whole with the shape of face of shaven head, the colour of skin, cosmetic etc.Can better show the effect of hairdressing.
But in the market cut a face teacher used not environmental protection of rubber, more stiff and poor flexibility, difficulty was big when itself and shaven head were worn, and did not shrink to stretch, and can not well coincide together with shaven head.At this drawback, we have developed a kind of environmental protection and the strong high-elastic rubber of teacher's head of screen resilience.
Summary of the invention
The purpose of this invention is to provide a kind of high-elastic rubber of teacher's head that integrates environmental protection, softness, characteristics high-elastic, easy to use, this novel rubber has more used resilient material, and self-regulatory is bigger, and is applied widely, and the user is easy to use.
For achieving the above object, the technical scheme that the present invention takes is: a kind of teacher's head is made up of import PVC paste resin raw material 80-100 part, dioctyl phthalate (DOP) 100-150 part, composite liquid stabilizing agent 2-4 part, environmental protection toner 0.1-1 part with high-elastic environmental protection rubber, adopts roto casting to make type.
Concrete operations technology is:
One, grinds toner: the environmental protection toner was put into grinding machine for grinding 4-6 hour for 1 part by above proportioning and dioctyl phthalate (DOP).Above raw material by proportioning, is added in the stirrer, and stirring at normal temperature is even.
Two, stir: will grind uniform toner and import PVC and stick with paste the evenly stirring in 2-3 hour in hollander of resin, dioctyl phthalate (DOP), composite liquid stabilizing agent.
Three, filter: use the nylon net filter slurry, leach impurity, be stored in the slurry pool.
Four, vacuum defoamation: will filter good slurry and be extracted in the vacuum defoamation machine, and slough bubble.
Five, slush moulding: mould is put into 260-280 ℃ of boiling hot glue stove internal heating, time 5-10 second, take out mould then, fill slurry, stop 10-15 second, the slurry of gel is not poured in the accumulator tank, once more mould is put into and scalded glue stove internal heating 30-40 after second, take out mould and put into water coolant, stop 20-30 second, treat from water, to take out after mould cools off, draw out scalp and get final product.
This its soft durometer of processing method products made thereby, resilience degree can both well satisfy the production of teacher's product and the use of teacher's product.
The present invention compared with prior art has following advantage:
1, the used resin raw material of the present invention is the import high quality raw material.
2, the pliability of this rubber more approaches true man's skin;
3, this rubber is anti-extrusion, not modification;
4, this rubber adopts environment-friendly materials to make.
Embodiment
Below in conjunction with specific embodiment the present invention is described in further detail.
With 0.04 part of red toner, 0.6 part of white toner, 0.1 part of mixing of yellow toner, putting into the toner shredder with 1 part of dioctyl phthalate (DOP) evenly ground 5 hours, uniform toner and import PVC be will grind and 100 parts of resins, 120 parts of dioctyl phthalate (DOP)s, 3 parts of even stirrings 3 hours in hollander of composite liquid stabilizing agent stuck with paste, go out impurity with nylon net filter, be stored in the slurry pool, deaeration is stand-by in the suction vacuum defoamation machine.Adopt roto casting to make high resilience glue scalp: mould is put into 270 ℃ of boiling hot glue stove internal heating, 7 seconds time, take out mould then, fill slurry, stopped 12 seconds, the slurry of gel is not poured in the accumulator tank, once more mould is put into and scalded glue stove internal heating after 3040 seconds, take out mould and put into water coolant, stop 20-30 second, treat from water, to take out after mould cools off, draw out scalp and get final product.
The present invention has adopted the high-quality resin raw material of import on raw material, strengthened the pliability and the elasticity of rubber, and feel and true man's skin are approaching.Be easy to just can be worn on the shaven head, with shaven head coincide fine, the outward appearance nature, use properties also has more superiority than before like product, and material is the feature of environmental protection.
More than be preferred embodiment of the present invention, all changes of doing according to technical solution of the present invention when the function that is produced does not exceed the scope of technical solution of the present invention, all belong to protection scope of the present invention.
Claims (3)
1. teacher's head is with high-elastic environmental protection rubber, it is characterized in that: this teacher's head is made up of import PVC paste resin raw material 80-100 part, dioctyl phthalate (DOP) 100-150 part, composite liquid stabilizing agent 2-4 part, environmental protection toner 0.1-1 part with high resilience environmental protection rubber, adopts roto casting to make type.
2. a kind of teacher's head according to claim 1 is with high-elastic environmental protection rubber, and it is characterized in that: manufacture craft is a roto casting.
According to claim 1 and 2 described a kind of teacher's heads with high-elastic environmental protection rubber and manufacture craft thereof, it is characterized in that: may further comprise the steps:
(1) grind toner: the environmental protection toner was put into grinding machine for grinding 4-6 hour for 1 part by above proportioning and dioctyl phthalate (DOP), above raw material by proportioning, is added in the stirrer, stirring at normal temperature is even.
(2) stir: will grind uniform toner and import PVC and stick with paste the evenly stirring in 2-3 hour in hollander of resin, dioctyl phthalate (DOP), composite liquid stabilizing agent.
(3) filter: use the nylon net filter slurry, leach impurity, be stored in the slurry pool.
(4) vacuum defoamation: will filter good slurry and be extracted in the vacuum defoamation machine, and slough bubble.
(5) slush moulding: mould is put into 260-280 ℃ of boiling hot glue stove internal heating, time 5-10 second, take out mould then, fill slurry, stop 10-15 second, the slurry of gel is not poured in the accumulator tank, once more mould is put into and scalded glue stove internal heating 30-40 after second, take out mould and put into water coolant, stop 20-30 second, treat from water, to take out after mould cools off, draw out scalp and get final product.