CN101961279B - Double-layer sandwich or multi-layer sandwich multi-latex condom and preparation method thereof - Google Patents
Double-layer sandwich or multi-layer sandwich multi-latex condom and preparation method thereof Download PDFInfo
- Publication number
- CN101961279B CN101961279B CN2010105334710A CN201010533471A CN101961279B CN 101961279 B CN101961279 B CN 101961279B CN 2010105334710 A CN2010105334710 A CN 2010105334710A CN 201010533471 A CN201010533471 A CN 201010533471A CN 101961279 B CN101961279 B CN 101961279B
- Authority
- CN
- China
- Prior art keywords
- heveatex
- condom
- drying
- latex
- promoter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a double-layer sandwich or multi-layer sandwich multi-latex condom and a preparation method thereof. The preparation method of the condom comprises the following steps: vulcanizing natural latex; emulsifying and dispersing polymer materials such as polyurethane or polyisoprene or butyronitrile or other non-natural latex and making the polymer materials into synthetic latex; and dipping a condom die in the natural latex and the synthetic latex respectively and then drying to finally obtain the double-layer sandwich or multi-layer sandwich multi-latex condom the middle layer of which is made from the natural latex or the synthetic latex, wherein, the innermost layer and the outermost layer of the condom can be made from the same material or different materials. The double-layer sandwich or multi-layer sandwich multi-latex condom of the invention has stretch rate and comfortability of the natural latex as well as high compactness of the synthetic latex, thus being applicable to obstructing penetration of small molecules such as hepatitis, AIDS virus and the like.
Description
Technical field
The present invention relates to condom, particularly double-deck sandwich or multilamellar sandwiched high-barrier condom and preparation method thereof.
Background technology
Condom is generally processed by Heveatex at present; This condom has better elastic; Relevant promoter aftershaping is good adding, and suitable men and women wears, but in the molecular structure of Heveatex a fixed gap is arranged; It is the above objects of 4000 nanoscales that these spaces can stop diameter, is the human body sperm etc. of 5000 nanometers like diameter; But for the littler diameter of molecule is the AIDS of 120 nanometers, the hepatitis virus of 40 nanometers etc., and Heveatex lacks the ability of blocking accordingly.Medical experiment proves that natural latex condom can't prevent the infiltration of HIV etc. safely.
Existing science and technology finds, polyurethane, gathers second and defends high molecular synthetic materials such as diene, butyronitrile, and its molecular structure and Heveatex have certain similarity, but compactness greatly improves, and its molecule space can separate the infiltration of AIDS, hepatitis virus etc. fully.
Summary of the invention
The purpose of this invention is to provide a kind of double-deck sandwich or multilamellar sandwiched high-barrier condom and preparation method thereof.The extensibility and the comfort of the existing Heveatex condom of this condom have the good compactness of macromolecular material of synthetic again.
The technical scheme that realizes the object of the invention is:
Utilize condom mold in the synthetic latex (above abbreviation synthetic latex) of Heveatex and synthetic, to flood, process double-deck sandwich or multilamellar sandwiched high-barrier condom.
The method for preparing of double-deck sandwiched high-barrier condom comprises the steps:
(1) Heveatex carry out sulfurization;
(2) with polyurethane or gather macromolecular material that second defends non-natural latex such as diene or butyronitrile and carry out emulsifying and disperse, form emulsion, add compounding ingredients such as Heveatex, promoter, age resistor, zinc oxide, fully stir, form synthetic latex;
(3) Heveatex is injected the first road glue groove and the 3rd road glue groove, synthetic latex is injected the second road groove;
(4) with condom mold behind the first road glue drill traverse glue, form glued membrane, drying, get into the second road glue drill traverse glue after, after drying, get into the 3rd road glue drill traverse glue after, after drying forms the condom of a double-deck sandwich;
(5) water flushing mould dashes condom and to take off from mould, uses the drying machine after drying to be Heveatex, the interlayer double-deck sandwich high-barrier condom as synthetic latex inside and outside processing.
The order of adjustment dipping, can process inside and outside is that synthetic latex, interlayer are the condom of Heveatex; Or increase dipping number of times; Can process multilamellar sandwiched high-barrier condom, inject synthetic latex such as the first road glue groove, the second road glue groove injects Heveatex; The 3rd road glue groove injects synthetic latex; The 4th road glue groove injects natural emulsion, floods in order and opens dry molding, forms multilamellar sandwiched high-barrier condom.Can also use different synthetic latexes and Heveatex to mix utilization by different order, as: inject in the first road glue groove and gather second and defend diene, the second road glue groove injects Heveatex, and the 3rd road glue groove injects polyurethane and processes condom.
Described Heveatex is a prior art.
Described synthetic latex is meant, polyurethane or gather the macromolecular material that second is defended non-natural latex such as diene or butyronitrile adds the relevant raw material that cooperates, fully emulsified dispersion after stirring, the formation emulsion, synthetic latex.Its materials and materials weight part ratio are:
Raw material materials weight part ratio
Polyurethane 5-50
Promoter 0.2-1
Age resistor 0.3-1.5
Zinc oxide 0.2-1
Heveatex 4.3-46.5
Or
Raw material materials weight part ratio
Gather second and defend diene 5-80
Promoter 0.2-1
Age resistor 0.3-1.5
Zinc oxide 0.2-1
Heveatex 4.3-16.5
Or
Raw material materials weight part ratio
Butyronitrile 5-50
Promoter 0.2-1
Age resistor 0.3-1.5
Zinc oxide 0.2-1
Heveatex 4.3-46.5
Advantage of the present invention is: double-deck sandwich of the present invention or multilamellar sandwiched high-barrier condom, the extensibility of existing Heveatex and comfort have high compactness again, can intercept micromolecular infiltrations such as hepatitis, HIV.
Description of drawings
Fig. 1 is the structural representation of embodiment 1;
Fig. 2 is the structural representation of embodiment 2.
The specific embodiment
Embodiment 1:3 layer sandwiched high-barrier condom
The preparation of synthetic latex of the present invention is by polyurethane or gathers the macromolecular material that second is defended non-natural latex such as diene or butyronitrile, adds the relevant raw material that cooperates, fully emulsified dispersion after stirring, the formation emulsion, synthetic latex.Its materials and materials weight part ratio are:
Raw material materials weight part ratio
Polyurethane 5-50
Promoter 0.2-1
Age resistor 0.3-1.5
Zinc oxide 0.2-1
Heveatex 4.3-46.5
Or
Raw material materials weight part ratio
Gather second and defend diene 5-80
Promoter 0.2-1
Age resistor 0.3-1.5
Zinc oxide 0.2-1
Heveatex 4.3-16.5
Or
Raw material materials weight part ratio
Butyronitrile 5-50
Promoter 0.2-1
Age resistor 0.3-1.5
Zinc oxide 0.2-1
Heveatex 4.3-46.5
The method for preparing of 3 layers of sandwiched high-barrier of the present invention condom comprises the steps:
(1) Heveatex carry out sulfurization;
(2) with polyurethane or gather macromolecular material that second defends non-natural latex such as diene or butyronitrile and carry out emulsifying and disperse, form emulsion, add compounding ingredients such as Heveatex, promoter, age resistor, zinc oxide, fully stir, form synthetic latex;
(3) Heveatex is injected the first road glue groove and the 3rd road glue groove, synthetic latex is injected the second road groove;
(4) with condom mold behind the first road glue drill traverse glue, form glued membrane, drying, get into the second road glue drill traverse glue after, after drying, get into the 3rd road glue drill traverse glue after, after drying forms the condom of a double-deck sandwich;
(5) water flushing mould dashes condom and to take off from mould, uses the drying machine after drying to be Heveatex, the interlayer double-deck sandwich high-barrier condom as synthetic latex inside and outside processing.
The order of adjustment dipping, can process inside and outside is that synthetic latex, interlayer are the condom of Heveatex; The synthetic latex layer of ectonexine comprises identical materials or material different.
Embodiment 2:
Increase dipping number of times and order, can process four layers or multilamellar sandwiched high-barrier condom, all the other are with embodiment 1.
Claims (4)
1. the method for preparing of double-deck sandwiched high-barrier condom is characterized in that: comprise the steps:
(1) Heveatex carry out sulfurization;
(2) with polyurethane or gather the second pentadiene or butyronitrile carries out emulsifying and disperses, form emulsion, add Heveatex, promoter, age resistor, zinc oxide, fully stir, form synthetic latex; Its each component materials weight part ratio is:
Polyurethane 5-50, promoter 0.2-1, age resistor 0.3-1.5, zinc oxide 0.2-1, Heveatex 4.3-46.5;
Or
Gather second pentadiene 5-80, promoter 0.2-1, age resistor 0.3-1.5, zinc oxide 0.2-1, Heveatex 4.3-16.5;
Or
Butyronitrile 5-50, promoter 0.2-1, age resistor 0.3-1.5, zinc oxide 0.2-1, Heveatex 4.3-46.5;
(3) Heveatex is injected the first road glue groove and the 3rd road glue groove, synthetic latex is injected the second road glue groove;
(4) with condom mold behind the first road glue drill traverse glue, form glued membrane, drying, get into the second road glue drill traverse glue after, after drying, get into the 3rd road glue drill traverse glue after, after drying forms the condom of a double-deck sandwich;
(5) water flushing mould dashes condom and to take off from mould, uses the drying machine after drying to be Heveatex, the interlayer double-deck sandwich high-barrier condom as synthetic latex inside and outside processing.
2. the method for preparing of multilamellar sandwiched high-barrier condom is characterized in that: comprise the steps:
(1) Heveatex carry out sulfurization;
(2) with polyurethane or gather the second pentadiene or butyronitrile carries out emulsifying and disperses, form emulsion, add Heveatex, promoter, age resistor, zinc oxide, fully stir, form synthetic latex; Its each component materials weight part ratio is:
Polyurethane 5-50, promoter 0.2-1, age resistor 0.3-1.5, zinc oxide 0.2-1, Heveatex 4.3-46.5;
Or
Gather second pentadiene 5-80, promoter 0.2-1, age resistor 0.3-1.5, zinc oxide 0.2-1, Heveatex 4.3-16.5;
Or
Butyronitrile 5-50, promoter 0.2-1, age resistor 0.3-1.5, zinc oxide 0.2-1, Heveatex 4.3-46.5;
(3) synthetic latex is injected the first road glue groove, Heveatex injects the second road glue groove, and synthetic latex injects the 3rd road glue groove, and natural emulsion injects the 4th road glue groove, impregnation and drying and moulding in order; Or different synthetic latexes and Heveatex mixed utilization by different order, impregnation, drying and moulding form a multilamellar sandwiched high-barrier condom;
(4) water flushing mould dashes condom and to take off from mould, uses the drying machine after drying to be Heveatex, the interlayer multilamellar sandwich high-barrier condom as synthetic latex inside and outside processing.
3. the double-deck sandwiched high-barrier condom for preparing with the described method for preparing of claim 1.
4. the multilamellar sandwiched high-barrier condom for preparing with the described method for preparing of claim 2.