CN101955651A - Green, environment-friendly and flexible nylon material for resisting cold and high temperature - Google Patents
Green, environment-friendly and flexible nylon material for resisting cold and high temperature Download PDFInfo
- Publication number
- CN101955651A CN101955651A CN 201010507323 CN201010507323A CN101955651A CN 101955651 A CN101955651 A CN 101955651A CN 201010507323 CN201010507323 CN 201010507323 CN 201010507323 A CN201010507323 A CN 201010507323A CN 101955651 A CN101955651 A CN 101955651A
- Authority
- CN
- China
- Prior art keywords
- nylon
- cold
- high temperature
- percent
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a green, environment-friendly and flexible nylon material for resisting cold and high temperature, comprising the components in percentage by weight: 49.5-90 percent of high-temperature nylon, 1-10 percent of nylon 66, 3-35 percent of cold-resistant agent, 3-35 percent of softener, 1-10 percent of bulking agent, 0.3-1.5 percent of antioxidant, 0.3-3.5 percent of thermal stabilizer and 0.3-5.5 percent of other assistants. The green, environment-friendly and flexible nylon material for resisting cold and high temperature can resist the low temperature of -40DEG C; the impact strength of a cantilever beam notch is near ten times higher than that the general high-temperature nylon; and the material is convenient to produce and purchase, so that the competitiveness is greatly improved.
Description
Technical field
The present invention relates to a kind of organic polymer composite, more particularly, relate to the cold-resistant flexible high temperature resistant nylon material of a kind of environmental protection.The invention still further relates to the method for making the cold-resistant flexible high temperature resistant nylon material of this environmental protection.
Background technology
At present, application with the alternative natural materials of plastics constantly enlarges in the world, scientist all over the world actively seeks new high-performance thermoplastics and comes alternative metals and timber by various tests, and this also becomes enterprise and strives for more families and the important component part of extending volume growth.
It is possible that the development of high temperature plastics changes into more microminiaturized lightweight of industrial or agricultural and civilian installation and powerful.High-temperature resistance plastice can bring higher heat resistance for some parts, or simply having substituted raw material metal produces these parts.The equally also useful high-temperature resistance plastice of the device of novel appts and assembly replaces the trend of metal and thermosetting material.These all will strengthen the demand to the high-temperature resistance plastice material, thereby drive the market requirement.
These high-temperature resistance plastice materials can anti-180 ℃ continuous high temperature, and can also keep good dimensional stability.Have excellent long-term and short term thermal performance, can tolerate infrared (IR) high temperature that reflow ovens produced that uses in the pb-free solder process, and identical intensity is provided under wet environment, remarkable chemical resistant properties.
But the high-temperature resistance plastice material of all kinds all has a common shortcoming in the existing market: impact lowlyer, fragility is obvious, and is especially when the sub-zero temperature environment, crisp more partially.The bigger range of application that has limited high temperature plastics alternative metals and timber of this shortcoming.And these the problem to be solved in the present invention just.
Series product of the present invention fully meet European Union's " waste and old electric electric installation " (WEEE) and " objectionable impurities limits the use of instruction " (RoHS) rules and other environmental regulations, can both use the Application Areas of environmental requirement strictness.
Summary of the invention
The objective of the invention is to, a kind of environmental protection flexible high temperature resistant nylon material that resists cold is provided, can tolerates subzero 40 degree low temperature, the socle girder notched Izod impact strength exceeds about nearly ten times than common high-temperature nylon, and production procurement is convenient, greatly improves the competitiveness like this.
Technical scheme provided by the invention is as follows: high-temperature nylon: 49.5-90%; Nylon 66:1-10%; Cold-resistant agent: 3-35%; Softener: 3-35%; Expanding material: 1-10%; Antioxidant: 0.3-1.5%; Thermo-stabilizer: 0.3-3.5%; Other auxiliary agents: 0.3-5.5%;
The environmental protection of the present invention flexible high temperature resistant nylon preparation methods that resists cold, comprise the steps: earlier with high-temperature nylon, nylon 66 and all auxiliary agents proportionally after the weighing in mixer low speed mixing 10 minutes, after under the screw combinations situation that medium tenacity is sheared, add mixing extruding with the parallel parallel dual-screw extruding machine of cord wood again, the pelletizing of water-cooled tie rod makes the cold-resistant flexible high temperature resistant nylon material of environmental protection through screening and dewatering.
The environmental protection of the present invention flexible high temperature resistant nylon material that resists cold can tolerate subzero 40 degree low temperature, and the socle girder notched Izod impact strength exceeds about nearly ten times than common high-temperature nylon, and production procurement is convenient, greatly improves the competitiveness like this.
Embodiment
Below be the most preferred embodiment of the cold-resistant flexible high temperature resistant nylon material of environmental protection of the present invention, therefore do not limit protection scope of the present invention.
Embodiment one, and a kind of environmental protection flexible high temperature resistant nylon material that resists cold is provided, by following composition by weight forming high-temperature nylon: 60%; Nylon 66:7%; Cold-resistant agent: 7%; Softener: 15%; Expanding material: 8%; Antioxidant: 1.0%; Thermo-stabilizer: 1.5%; Other auxiliary agents: 0.5%;
Earlier with high-temperature nylon, nylon 66, cold-resistant agent and softener, expanding material, antioxidant, thermo-stabilizer, other auxiliary agents proportionally after the weighing in mixer low speed mixing 10 minutes, mixer adopts low speed mixing, paddle should with the barrel gap less than 0.5 centimetre, the supplementary material mixed effect should visual various particles and powder even substantially, do not have obvious agglomerate or gather; Twin screw extruder uses 42 length-to-diameter ratios, the combination of medium tenacity shear screw, mixing extruding; Adopt water-cooled tie rod pelletizing mode, promptly make the cold-resistant flexible high temperature resistant nylon material of environmental protection through screening and dewatering.
The above; it only is the specific embodiment of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the disclosed technical scope of the present invention; variation or the replacement that can expect without creative work all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (2)
1. the cold-resistant flexible high temperature resistant nylon material of environmental protection is characterized in that, forms high-temperature nylon by weight by following composition: 49.5-90%; Nylon 66:1-10%; Cold-resistant agent: 3-35%; Softener: 3-35%; Expanding material: 1-10%; Antioxidant: 0.3-1.5%; Thermo-stabilizer: 0.3-3.5%; Other auxiliary agents: 0.3-5.5%.
2. the cold-resistant flexible high temperature resistant nylon preparation methods of an environmental protection, it is characterized in that, comprise the steps: earlier with high-temperature nylon, every other auxiliary agent proportionally after the weighing in mixer low speed mixing 10 minutes, extrude through twin screw extruder is mixing again, the pelletizing of water-cooled tie rod makes the cold-resistant flexible high temperature resistant nylon material of environmental protection through screening and dewatering again.