CN101955656A - Glass fiber enhanced nylon 6 material for improving transparency - Google Patents
Glass fiber enhanced nylon 6 material for improving transparency Download PDFInfo
- Publication number
- CN101955656A CN101955656A CN 201010507222 CN201010507222A CN101955656A CN 101955656 A CN101955656 A CN 101955656A CN 201010507222 CN201010507222 CN 201010507222 CN 201010507222 A CN201010507222 A CN 201010507222A CN 101955656 A CN101955656 A CN 101955656A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- nylon
- transparency
- glass
- improves
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a glass fiber enhanced nylon 6 material for improving the transparency, comprising the following components in percentage by weight: 38.5-95 percent of nylon 6, 5-60 percent of alkali-free glass fiber, 0.5-6.0 percent of clarifier, 0.1-3.0 percent of glass fiber treating agent and 1.3-5.5 percent of other assistants. The glass fiber enhanced nylon 6 material for improving the transparency has approximate performance to that of the like materials, is convenient to produce and purchase, improves the transparency and also meets all other environment-friendly requirements, so that the material can also be used in places through which the condition can be seen by the shield of products, which increases the application fields, widens the material selecting range of product designers, solves the problem of design limitation of products and improves the competitiveness of the products.
Description
Technical field
The present invention relates to a kind of organic polymer composite, more particularly, relate to a kind of glass fiber reinforced nylon 6 material that improves transparency.The invention still further relates to the method for making this nylon material.
Background technology
Nylon 6 is to use one of maximum several engineering plastics at present, his amide group has polarity, in his structure, has well-set hydrogen bond, make that the fusing point of nylon 6 is higher, have good physical and mechanical property and wear resistance and self lubricity, these comprehensive characteristics are that other plastics are not available.But the heat-drawn wire of pure nylon 6 is lower, and water-absorbent is big, and shock strength is on the low side before the suction, suction back rigidity declines to a great extent again, shortcoming such as size instability simultaneously, thus limited the application of nylon 6, and then dwindled downstream industry design engineer's selection leeway again.Therefore, launched nylon 6 is carried out composite modified research.And improve the comprehensive employed the most universal the most effective method of physical and mechanical property of nylon 6 material, adopt glass fiber reinforced nylon 6 exactly.And glass fiber reinforced nylon 6 material transparency in the market is not high, makes to be difficult for seeing through it behind the goods and to see that it blocks the situation at position, exists sorry in some place.The present technique invention produces in order effectively to improve this phenomenon.
Summary of the invention
The objective of the invention is to, a kind of glass fiber reinforced nylon 6 material that improves transparency is provided, performance is similar with the same type of material of not improvement, and buying is convenient, has improved transparency, also meets other all environmental requirement simultaneously.
Technical scheme provided by the invention is as follows: nylon 6:37.5-95%; Environmental protection glass: 5-60%; Transparent base: 0.5-6.0%; Glass treatment agent: 0.1-3.0%; Other auxiliary agents: 1.3-5.5%.
The preparation method who improves the glass fiber reinforced nylon 6 material of transparency of the present invention, comprise the steps: earlier with nylon 6, transparent base, glass treatment agent, other auxiliary agents proportionally after the weighing in mixer low speed mixing 10 minutes, naturally place after 12 hours and in time under the screw combinations situation that medium tenacity is sheared, add the environmental protection glass in proportion again by the side through twin screw extruder, under vacuum state, with mixing the extruding of 270 degree, the pelletizing of water-cooled tie rod makes the glass fiber reinforced nylon 6 material that improves transparency through screening and dewatering.
The present invention improve transparency glass fiber reinforced nylon 6 material performance with not the improvement same type of material similar, and production procurement is convenient, improved transparency, also meet simultaneously other all environmental requirement, block the place that to see situation at needs through its goods like this and also can use, increased Application Areas, enlarged the selection range of product designer, solve the design limit problem of some product, improved product competitiveness.
Embodiment
Below be the embodiment that improves the glass fiber reinforced nylon 6 material of transparency of the present invention, therefore do not limit protection scope of the present invention.
Embodiment one, and a kind of glass fiber reinforced nylon 6 material that improves transparency is provided, and forms nylon 6:65% by weight by following composition; Environmental protection glass: 30%; Transparent base: 1.5%; Glass treatment agent: 1.0%; Other auxiliary agents: 2.5%.
Earlier with nylon 6, transparent base, glass treatment agent, other auxiliary agents proportionally after the weighing in mixer low speed mixing 10 minutes, mixer adopts low speed mixing, stainless steel, paddle should with the barrel gap less than 0.5 centimetre, the supplementary material mixed effect should visual various particles and powder even substantially, do not have obvious agglomerate or gather, place naturally then and re-use after making its sufficient reacting in 12 hours; Twin screw extruder uses 36 length-to-diameter ratios, and medium tenacity is sheared; The environmental protection glass is added in proportion by the side; Keep vacuum state and 270 the degree condition is mixing extrudes; Adopt water-cooled tie rod pelletizing mode, promptly make the glass fiber reinforced nylon 6 material that improves transparency through screening and dewatering.
The above; it only is the specific embodiment of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the disclosed technical scope of the present invention; variation or the replacement that can expect without creative work all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (2)
1. a glass fiber reinforced nylon 6 material that improves transparency is characterized in that, forms nylon 6:38.5-95% by weight by following composition; Alkali-free glass fiber: 5-60%; Transparent base: 0.5-6.0%; Glass treatment agent: 0.1-3.0%; Other auxiliary agents: 1.3-5.5%.
2. preparation method who improves the glass fiber reinforced nylon 6 material of transparency, it is characterized in that, comprise the steps: earlier with nylon 6, environmental protection glass, transparent base, glass treatment agent, other auxiliary agents proportionally after the weighing in mixer low speed mixing 10 minutes, naturally place after 12 hours and carry out mixing extruding by side adding environmental protection glass through twin screw extruder under the screw combinations situation that medium tenacity is sheared again, the pelletizing of water-cooled tie rod makes a kind of glass fiber reinforced nylon 6 material that improves transparency through screening and dewatering again.