CN101955563A - Emulsion for low-surface energy coating and preparation method - Google Patents
Emulsion for low-surface energy coating and preparation method Download PDFInfo
- Publication number
- CN101955563A CN101955563A CN 200910016789 CN200910016789A CN101955563A CN 101955563 A CN101955563 A CN 101955563A CN 200910016789 CN200910016789 CN 200910016789 CN 200910016789 A CN200910016789 A CN 200910016789A CN 101955563 A CN101955563 A CN 101955563A
- Authority
- CN
- China
- Prior art keywords
- surface energy
- acrylate
- emulsion
- value
- low surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses emulsion for a low-surface energy coating and a preparation method. The emulsion is characterized in that: the emulsion is prepared by copolymerizing fluorine-containing acrylate, fluorine-silicon macormonomers, alkyl methacrylate, alkyl acrylate and hydroxyalkyl acrylamide under the action of water, an emulsifier, an initiator, a pH value buffering agent and a pH value conditioning agent. The preparation method is characterized by comprising the following steps of: adding the water, the initiator, the emulsifier and the pH value buffering agent into a reaction kettle according to proportion; adding dropwise the mixed solution of the alkyl methacrylate, the alkyl acrylate, the hydroxyalkyl acrylamide, the fluorine-containing acrylate and the fluorine-silicon macormonomers into the reaction kettle for reaction according to proportion; and finally adding the pH value conditioning agent into the reaction kettle to condition a pH value to prepare the emulsion for the low-surface energy coating. The emulsion for the low-surface energy coating prepared by the preparation method has the characteristics of stable reaction process, relatively higher product stability, high scrubbing resistance, high saltwater resistance, high salt fog resistance, high acid and alkali resistance, high ageing resistance, high paste-resistant persistence and the like. The coating produced by using the emulsion for the low-surface energy coating has relatively lower surface energy and long-lasting effect, forms the contact angle of more than 100 degrees with the water and forms the contact angle of more than 70 degrees with diiodomethane.
Description
Technical field:
The present invention relates to coating with emulsion and production technical field, be specially a kind of low surface energy coatings with emulsion and preparation method.
Background technology:
Low surface energy coatings has hydrophobic, oleophobic property is widely used in the protection of materials such as Architectural Equipment, bridge, boats and ships, offshore platform, terminal facilities, electronic product, engineering machinery, historical relic's protection, leather, woodenware and prevents that the unrest of communal facility from the field such as pasting, scrawling.Especially in recent years " city psoriasis " phenomenon is day by day serious, develops the water-based anti-sticking dope of a kind of difficult adhesion glue, paste and pressure sensitive adhesive, is used for the appearance protection and the decoration of urban architecture engineering, helps the modern city civilization construction.Because low surface energy coatings has hydrophobic, oleophobic property, glue, paste, pressure sensitive adhesive etc. are very poor to its sticking power of filming, and the small advertisement of pasting on it has certain " sticking up property certainly ", Exposure to Sunlight, wind, drench with rain or the effect of other external force under can come off easily; Ink, the oil pen, the coating of low surface energy coatings being filmed from spraying paint is also very poor, be sprayed on above it from spraying paint and be " two-layer skin " state, be easy to remove, so a lot of departments are all at the research and development low surface energy coatings, but owing to lack this water-soluble low surface energy paint emulsion on the current market, therefore, many researchs are to rely on to add low surface energy auxiliary agent (wax class, the silicon class, fluorine class etc.) realize the low surface energy anti-adhesion effects with coating main film forming substance (being emulsion) by physical blending, this class low surface energy coatings is because the low surface energy auxiliary agent that adds can not lump together or combine insufficient with chemical bonded refractory with filmogen, therefore a series of shortcomings of this class coating have been caused, easily dirty such as some " bellding ", some anti-adhesion effects is poor, after pasting repeatedly, some can lose non-stick property, some short-term is exposed to the sun and rain and is just lost non-stick property etc., some homemade and imported product expensive etc.
Summary of the invention:
The objective of the invention is to overcome above-mentioned the deficiencies in the prior art, provide can ambient self-crosslinking a kind of low surface energy coatings with emulsion and preparation method.
The present invention can reach by following measure:
A kind of low surface energy coatings emulsion, it is characterized in that by fluorinated monomer, the big monomer of fluorine silicon, alkyl methacrylate, alkyl acrylate, the hydroxyalkyl acrylamide is at water, emulsifying agent, initiator, copolymerization forms under the effect of pH value buffer reagent, and the mass percent of each composition is: fluorinated acrylate 1～30%, the big monomer 1～20% of fluorine silicon, alkyl methacrylate 10～40%, alkyl acrylate 5～35%, hydroxyalkyl acrylamide 0.5～5%, water 40～50%, initiator 0.05～1%, emulsifying agent 0.1～4%, pH value buffer reagent 0.1～1%.
The present invention can add an amount of PH conditioning agent, to regulate the pH value of emulsion.
The big monomeric general formula of fluorine silicon of the present invention is:
R1 wherein, R2, R4 are any one in methyl, ethyl, propyl group, butyl, isobutyl-, the phenyl etc.; The general formula of R3 is CF3 (CF2) m (CH2) n-or H (CF2) x (CH2) n-, wherein m 〉=0, n=2～8, x 〉=2; A=2～8 in the big monomer of fluorine silicon, b 〉=3, c 〉=3.
Fluorinated acrylate of the present invention is a kind of or any several mixture in trifluoroethyl methacrylate, vinylformic acid trifluoro ethyl ester, vinylformic acid hexafluoro butyl ester, methacrylic acid hexafluoro butyl ester, dodecafluorhe-ptylacrylate, methacrylic acid ten difluoro heptyl esters, vinylformic acid octafluoro pentyl ester, methacrylic acid octafluoro pentyl ester, vinylformic acid 19 fluorine esters, the vinylformic acid perfluoro capryl ethyl ester etc.
Alkyl methacrylate of the present invention is a kind of or several arbitrarily in methyl methacrylate, Jia Jibingxisuanyizhi, n-BMA, Propenoic acid, 2-methyl, isobutyl ester, methacrylic acid (different) monooctyl ester, methacrylic acid 2-ethylhexyl, lauryl methacrylate(LMA), stearyl methacrylate, 2-hydroxyethyl methacrylate, methacrylic acid 2～hydroxy propyl ester, the methacrylic acid hydroxy butyl ester etc.
Alkyl acrylate of the present invention is a kind of or several arbitrarily in methyl acrylate, ethyl propenoate, n-butyl acrylate, isobutyl acrylate, vinylformic acid (different) monooctyl ester, 2-EHA, lauryl acrylate, octadecyl acrylate, vinylformic acid 2-hydroxy methacrylate, vinylformic acid 2-hydroxy propyl ester, the vinylformic acid hydroxy butyl ester etc.
PH value buffer reagent of the present invention is any one in yellow soda ash, sodium bicarbonate, sodium phosphate, SODIUM PHOSPHATE, MONOBASIC, Sodium phosphate dibasic, bicarbonate of ammonia, the ammoniacal liquor etc.
Emulsifying agent of the present invention is non-reactive emulsifier, contains any several composition in the reactive emulsifier of unsaturated double-bond.
Initiator of the present invention is a kind of in Potassium Persulphate, the ammonium persulphate.
The present invention is with fluorinated acrylate, the big monomer of fluorine silicon, alkyl methacrylate, alkyl acrylate, monomers such as hydroxyalkyl acrylamide are at water, emulsifying agent, initiator, the effect of pH value buffer reagent is carried out letex polymerization and is formed, make fluorine, silicon is combined on the acrylate side chain with the chemical bond form, utilize organic fluorine, the excellent performance of silicon realizes modification to acrylate resin, obtained a kind of low surface energy coatings emulsion, it films hydrophobic strong with the oleophobic ability, the surface energy of filming is lower, effect is lasting, with the contact angle of water greater than 100 °, with the contact angle of methylene iodide greater than 70 °.
A kind of low surface energy coatings preparation method of emulsion is characterized in that step is:
The 1st step joined water, initiator, emulsifying agent, pH value buffer reagent in the reactor in proportion, was warming up to 60～80 ℃,
Second step, react to reactor dropping alkyl methacrylate, alkyl acrylate, hydroxyalkyl acrylamide, fluorinated acrylate, the big monomeric mixed solution of fluorine silicon in proportion, lower the temperature behind reaction times 4～12h,
The 3rd step, survey pH value, pH value is 7.0～9.0 get final product, can add an amount of pH value conditioning agent in reactor, with the accent pH value.
The low surface energy coatings that the present invention produces is stable with the emulsion reaction process, and product stability is better, and the surface energy of filming is lower, effect lasting, excellent scrubbing resistance is arranged, salt water resistance salt fog, acid and alkali-resistance, performance such as ageing-resistant
Description of drawings:
Fig. 1 is the synoptic diagram of 106.2 ° of the contact angles of water.
Fig. 2 is the synoptic diagram of 115.4 ° of the contact angles of water.
Fig. 3 is 75.1 ° of synoptic diagram of contact angle of methylene iodide.
Fig. 4 is 83.5 ° of synoptic diagram of contact angle of methylene iodide.
Embodiment:
Below in conjunction with embodiment the present invention is further described,
Embodiment 1:
The mass percent of composition and composition:
1. the big monomer 6.0g of fluorine silicon
2. fluorinated acrylate 5.5g
3. alkyl methacrylate 17.1g
4. alkyl acrylate 15.0g
5. hydroxyalkyl acrylamide 3.5g
6. emulsifying agent 4.3g
7.PH value buffer reagent 0.2g
8. initiator 0.4g
9. water 48.0
10.PH the value conditioning agent is an amount of
Preparation process is:
The 1st step joined water, initiator, emulsifying agent, pH value buffer reagent in the reactor, was warming up to 60 ℃,
In second step, reactor adding alkyl methacrylate, alkyl acrylate, hydroxyalkyl acrylamide, fluorinated acrylate, the big monomeric mixed solution of fluorine silicon react, lower the temperature behind the reaction times 4h,
The 3rd step, survey pH value, pH value is 7.0 get final product, can add an amount of pH value conditioning agent in reactor, with the accent pH value.
Embodiment 2:
The mass percent of composition and composition:
1. the big monomer 6.5g of fluorine silicon
2. fluorinated acrylate 9.0g
3. alkyl methacrylate 17.8g
4. alkyl acrylate 15.1g
5. hydroxyalkyl acrylamide 1.8g
8. emulsifying agent 4.2g
10.PH value buffer reagent 0.3g
11. initiator 0.4g
12. water 48.0
10.PH the value conditioning agent is an amount of
Preparation process is:
The 1st step joined water, initiator, emulsifying agent, pH value buffer reagent in the reactor, was warming up to 80 ℃,
In second step, reactor adding alkyl methacrylate, alkyl acrylate, hydroxyalkyl acrylamide, fluorinated acrylate, the big monomeric mixed solution of fluorine silicon react, lower the temperature behind the reaction times 4h,
The 3rd step, survey pH value, pH value is 7.0 get final product, can add an amount of pH value conditioning agent in reactor, with the accent pH value.
Embodiment 3:
The mass percent of composition and composition:
1. the big monomer 8.0g of fluorine silicon
2. fluorinated acrylate 7.0g
3. alkyl methacrylate 16.1g
4. alkyl acrylate 13.5g
5. hydroxyalkyl acrylamide 2.8g
6. emulsifying agent 3.8g
7.PH value buffer reagent 0.3g
8. initiator 0.5g
9. water 48.0
10.PH the value conditioning agent is an amount of
Preparation process is:
The 1st step joined water, initiator, emulsifying agent, pH value buffer reagent in the reactor, was warming up to 70 ℃,
In second step, reactor adding alkyl methacrylate, alkyl acrylate, hydroxyalkyl acrylamide, fluorinated acrylate, the big monomeric mixed solution of fluorine silicon react, lower the temperature behind the reaction times 10h,
The 3rd step, survey pH value, pH value is 8.0 get final product, can add an amount of pH value conditioning agent in reactor, with the accent pH value.
Embodiment 4:
The mass percent of composition and composition:
1. the big monomer 8.8g of fluorine silicon
2. fluorinated acrylate 10.0g
3. alkyl methacrylate 16.6g
4. alkyl acrylate 11.4g
5. hydroxyalkyl acrylamide 1.0g
6. emulsifying agent 3.5g
7.PH value buffer reagent 0.3g
8. initiator 0.4g
9. water 48.0
10.PH the value conditioning agent is an amount of
Preparation process is:
The 1st step joined water, initiator, emulsifying agent, pH value buffer reagent in the reactor, was warming up to 80 ℃,
In second step, reactor adding alkyl methacrylate, alkyl acrylate, hydroxyalkyl acrylamide, fluorinated acrylate, the big monomeric mixed solution of fluorine silicon react, and are cooled to room temperature behind the reaction times 12h,
The 3rd step, survey pH value, pH value is 9.0 get final product, can add an amount of pH value conditioning agent in reactor, with the accent pH value.
The foregoing description emulsion property is as follows:
With the emulsion dilute with water in the foregoing description, add room temperature film-forming behind an amount of film coalescence aid, test performance is as follows after the maintenance:
The present invention is combined in organic fluorine and organosilicon on the acrylate side chain with the chemical bond form, utilize the excellent performance of fluorine, silicon that acrylate is carried out modification, obtained a kind of hydrophobic and strong low surface energy coatings emulsion of oleophobic ability, the low surface energy coatings that the present invention produces is stable with the emulsion reaction process, product stability is better, and performances such as excellent scrubbing resistance, salt water resistance salt fog, acid and alkali-resistance, ageing-resistant, anti-stick subsides persistence are arranged.The low surface energy coatings that the present invention produces is lower with the surface energy of emulsion film, effect is lasting, with the contact angle of water greater than 100 °, with the contact angle of methylene iodide greater than 70 °.
Claims (10)
1. low surface energy coatings emulsion, it is characterized in that by fluorinated monomer, the big monomer of fluorine silicon, alkyl methacrylate, alkyl acrylate, the hydroxyalkyl acrylamide is at water, emulsifying agent, initiator, copolymerization forms under the effect of pH value buffer reagent, and the mass percent of each composition is: fluorinated acrylate 1～30%, the big monomer 1～20% of fluorine silicon, alkyl methacrylate 10～40%, alkyl acrylate 5～35%, hydroxyalkyl acrylamide 0.5～5%, water 40～50%, initiator 0.05～1%, emulsifying agent 0.1～4%, pH value buffer reagent 0.1～1%.
2. a kind of low surface energy coatings emulsion according to claim 1 is characterized in that the big monomeric general formula of fluorine silicon is:
R1 wherein, R2, R4 are any one in methyl, ethyl, propyl group, butyl, isobutyl-, the phenyl etc.; The general formula of R3 is CF3 (CF2) m (CH2) n-or H (CF2) x (CH2) n-, wherein m 〉=0, n=2～8, x 〉=2; A=2～8 in the big monomer of fluorine silicon, b 〉=3, c 〉=3.
3. a kind of low surface energy coatings emulsion according to claim 1 is characterized in that fluorinated monomer is a kind of or any several mixture in trifluoroethyl methacrylate, vinylformic acid trifluoro ethyl ester, vinylformic acid hexafluoro butyl ester, methacrylic acid hexafluoro butyl ester, dodecafluorhe-ptylacrylate, methacrylic acid ten difluoro heptyl esters, vinylformic acid octafluoro pentyl ester, methacrylic acid octafluoro pentyl ester, vinylformic acid 19 fluorine esters, the vinylformic acid perfluoro capryl ethyl ester etc.
4. a kind of low surface energy coatings emulsion according to claim 1 is characterized in that alkyl methacrylate is a kind of or several arbitrarily in methyl methacrylate, Jia Jibingxisuanyizhi, n-BMA, Propenoic acid, 2-methyl, isobutyl ester, methacrylic acid (different) monooctyl ester, methacrylic acid 2-ethylhexyl, lauryl methacrylate(LMA), stearyl methacrylate, 2-hydroxyethyl methacrylate, methacrylic acid 2-hydroxy propyl ester, the methacrylic acid hydroxy butyl ester etc.
5. a kind of low surface energy coatings emulsion according to claim 1 is characterized in that alkyl acrylate is a kind of or several arbitrarily in methyl acrylate, ethyl propenoate, n-butyl acrylate, isobutyl acrylate, vinylformic acid (different) monooctyl ester, 2-EHA, lauryl acrylate, octadecyl acrylate, vinylformic acid 2-hydroxy methacrylate, vinylformic acid 2-hydroxy propyl ester, the vinylformic acid hydroxy butyl ester etc.
6. a kind of low surface energy coatings emulsion according to claim 1 is characterized in that the pH value buffer reagent is any one in yellow soda ash, sodium bicarbonate, sodium phosphate, SODIUM PHOSPHATE, MONOBASIC, Sodium phosphate dibasic, bicarbonate of ammonia, the ammoniacal liquor etc.
7. a kind of low surface energy coatings emulsion according to claim 1 is characterized in that emulsifying agent is any several composition that contains in the reactive emulsifier of unsaturated double-bond.
8. a kind of low surface energy coatings emulsion according to claim 1 is characterized in that initiator is a kind of in Potassium Persulphate, the ammonium persulphate.
9. a low surface energy coatings is characterized in that step is with the preparation method of emulsion:
The 1st step joined water, initiator, emulsifying agent, pH value buffer reagent in the reactor in proportion, was warming up to 60～80 ℃,
Second step, react to reactor dropping alkyl methacrylate, alkyl acrylate, hydroxyalkyl acrylamide, fluorinated acrylate, the big monomeric mixed solution of fluorine silicon in proportion, lower the temperature behind reaction times 4～12h,
The 3rd step, survey pH value, pH value is 7.0～9.0 to get final product.
10. a kind of low surface energy coatings according to claim 9 with emulsion the preparation method, it is characterized in that in reactor, adding an amount of pH value conditioning agent, regulate pH value to 7.0～9.0.