CN101942627A - 一种镀锌钢丝抹拭拭剂 - Google Patents
一种镀锌钢丝抹拭拭剂 Download PDFInfo
- Publication number
- CN101942627A CN101942627A CN 201010503075 CN201010503075A CN101942627A CN 101942627 A CN101942627 A CN 101942627A CN 201010503075 CN201010503075 CN 201010503075 CN 201010503075 A CN201010503075 A CN 201010503075A CN 101942627 A CN101942627 A CN 101942627A
- Authority
- CN
- China
- Prior art keywords
- zinc
- charcoal
- steel wire
- agent
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种镀锌钢丝抹拭拭剂，目前大多数厂家采用油木炭对镀锌后的钢丝进行抹拭，以控制钢丝的上锌量及表面光洁度。由于油木炭容易产生油垢而结块，常需要将壳块去掉并补充新的油木炭，增加了生产成本，且油遇到高温后会产生大量的油烟，影响车间环境。本发明提供了一种节约成本，安全无污染的镀锌钢丝抹拭拭剂，经该拭剂抹拭后的钢丝更清洁光亮。通过以下技术方案来实现：按重量份数计算：将木炭粉末和水按30：(8～12)的比例混合均匀。采用本发明所述的拭剂，节约了能源，大大降低了生产成本，且水遇到高温后只会蒸发出一部分水蒸汽，对车间环境无污染，且最终产品更清洁光亮。
Description
技术领域
本发明涉及对金属材料的镀覆，具体涉及镀覆后使工件达到所需最终状态的拭剂。
背景技术
金属制品的热镀锌是最基本、最有效的防腐工艺之一。可进行热镀锌的金属制品包括钢丝、板材、钢卷、钢管、结构件和紧固件等，其中钢丝是重要的一类。钢丝从锌锅出来后，一般会经过抹拭工艺，以摸平钢丝表面的锌层。目前大多数厂家都采用传统的拭剂进行抹拭，即用混有油的木炭来控制钢丝的上锌量及表面光洁度。用这种抹拭拭剂，由于油木炭容易产生油垢而结块，常需要将壳块去掉并补充新的油木炭，增加了生产成本，且油遇到高温后会产生大量的油烟，影响车间环境；钢丝通过油木炭后，一部分油会粘覆在钢丝上，给后续处理带来一定的麻烦。
发明内容
本发明旨在提供一种节约成本，安全无污染的镀锌钢丝抹拭拭剂，经该拭剂抹拭后的钢丝更清洁光亮。
本发明通过以下技术手段来实现上述目的：
一种镀锌钢丝抹拭拭剂，所用原料为木炭粉末和水，按重量份数计算：将木炭粉末和水按30：（8～12）的比例混合均匀。
优选地，按重量份数计算：将木炭粉末和水按30：（9～11）的比例混合均匀。
所述木炭粉末的粒径为0.8～1.8毫米。
所述木炭为梨炭或机制木炭。
将上述混合均匀后的拭剂直接铺到钢丝出锌锅处的锌液上，拭剂在锌液上的堆积高度为7～9厘米。由于木炭的密度小，与水混合后的混合物能直接漂浮在锌液上方不下沉。钢丝从锌液出来后直接穿过该拭剂，以抹平钢丝表面的锌层。
本发明具有以下有益效果：
①镀锌钢丝工艺中抹拭钢丝的拭剂由油木炭粉末变成了水木炭，节约了能源，大大降低了生产成本，且水遇到高温后只会蒸发出一部分水蒸汽，对车间环境无污染。
②出锌锅的钢丝通过加水的木炭粉末抹拭后，水不会像油一样附在钢丝的表面，使的最终产品更清洁光亮。
③机制木炭具有热值高，无烟、无味、无污染、不爆炸，价格便宜等特点，使用机制木炭作为抹拭镀锌钢丝的试剂，大量节约了成本。
具体实施例
实施例1：一种镀锌钢丝抹拭拭剂，按重量份数计算：将木炭粉末和水按30：8的比例混合，二者混合均匀后，铺在钢丝出锌锅处的锌液上，拭剂堆积高度为7厘米。钢丝从锌液出来后直接穿过该拭剂，以抹平钢丝表面的锌层。
实施例2：一种镀锌钢丝抹拭拭剂，按重量份数计算：将木炭粉末和水按30：12的比例混合，二者混合均匀后，铺在钢丝出锌锅处的锌液上，拭剂堆积高度为8厘米。钢丝从锌液出来后直接穿过该拭剂，以抹平钢丝表面的锌层。
实施例3：一种镀锌钢丝抹拭拭剂，按重量份数计算：将木炭粉末和水按30：9的比例混合，二者混合均匀后，铺在钢丝出锌锅处的锌液上，拭剂堆积高度为9厘米。钢丝从锌液出来后直接穿过该拭剂，以抹平钢丝表面的锌层。
实施例4：一种镀锌钢丝抹拭拭剂，按重量份数计算：将木炭粉末和水按30：11的比例混合，二者混合均匀后，铺在钢丝出锌锅处的锌液上，拭剂堆积高度为7.5厘米。钢丝从锌液出来后直接穿过该拭剂，以抹平钢丝表面的锌层。
实施例5：一种镀锌钢丝抹拭拭剂，按重量份数计算：将木炭粉末和水按30：10的比例混合，二者混合均匀后，铺在钢丝出锌锅处的锌液上，拭剂堆积高度为8厘米。钢丝从锌液出来后直接穿过该拭剂，以抹平钢丝表面的锌层。
Claims (5)
1.一种镀锌钢丝抹拭拭剂，其特征在于，所用原料为木炭粉末和水，按重量份数计算：将木炭粉末和水按30：（8～12）的比例混合均匀。
2.根据权利要求1所述的镀锌钢丝抹拭拭剂，其特征在于，按重量份数计算：将木炭粉末和水按30：（9～11）的比例混合均匀。
3.根据权利要求1或2所述的镀锌钢丝抹拭拭剂，其特征在于，所述木炭粉末的粒径为0.8～1.8毫米。
4.根据权利要求1或2所述的镀锌钢丝抹拭拭剂，其特征在于，所述木炭为梨炭或机制木炭。
5.根据权利要求3所述的镀锌钢丝抹拭拭剂，其特征在于，所述木炭为梨炭或机制木炭。