CN101921520A - Anti-asphalt paint, composite polyester resin and preparation methods thereof - Google Patents
Anti-asphalt paint, composite polyester resin and preparation methods thereof Download PDFInfo
- Publication number
- CN101921520A CN101921520A CN2009100529847A CN200910052984A CN101921520A CN 101921520 A CN101921520 A CN 101921520A CN 2009100529847 A CN2009100529847 A CN 2009100529847A CN 200910052984 A CN200910052984 A CN 200910052984A CN 101921520 A CN101921520 A CN 101921520A
- Authority
- CN
- China
- Prior art keywords
- parts
- asphalt paint
- solution
- aminoresin
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an anti-asphalt paint and a preparation method thereof. The anti-asphalt paint comprises the following raw materials in parts by weight: 0-65 parts of acrylic resin, 0-65 parts of polyester resin, 8-20 parts of amino resin, 0-12 parts of polyurethane resin, 3 parts of TSP, 5 parts of dimethylbenzene, 5 parts of butyl acetate, 4 parts of MIBK and 4 parts of PMA. The invention also discloses a formula of the polyester resin and preparation methods of the anti-asphalt paint and the polyester resin; the invention utilizes D2 polyurethane resin to increase the reaction cross-link points and the cross-link density, and has lower surface tension; the polyester resin enhances the cross-link density, and improves the compactness of a paint film; and the TSP reduces the surface tension of the paint film. The invention has compact structure and sufficiently low surface tension, and has the advantage of resisting pollution by.
Description
Technical field
The present invention relates to a kind of coating, be specifically related to a kind of anti-asphalt paint, also relate to the composite polyester resin for preparing this anti-asphalt paint, the invention still further relates to the preparation method of anti-asphalt paint and composite polyester resin, belong to the technical field of coating.
Background technology
Still there is not the sophisticated coating products of anti-the bituminous on the market now.Existing coating mainly comprises acrylic resin and aminoresin, and the inflexible acrylic resin can not be fully and the aminoresin reaction, and cross-linking density is low, and the compactness of paint film is poor, and surface tension is low inadequately, so anti-bituminous effect is undesirable.
Summary of the invention
One of technical problem to be solved by this invention is to provide a kind of anti-asphalt paint, and this anti-asphalt paint is applicable to that the wheel hub surfacecti proteon of automobile light metal and other need the application of high dirt resistance.
Two of technical problem to be solved by this invention is to provide the above-mentioned anti-asphalt paint of preparation used composite polyester resin.
Three of technical problem to be solved by this invention is to provide the preparation method of above-mentioned composite polyester resin.
Four of technical problem to be solved by this invention is to provide the preparation method of above-mentioned anti-asphalt paint.
As the anti-asphalt paint of first aspect present invention, form by the feedstock production of following parts by weight:
0~65 part of acrylic resin
0~65 part in vibrin
8~20 parts in aminoresin
0~12 part of urethane resin
3 parts of TSP
5 parts of dimethylbenzene
5 parts of N-BUTYL ACETATEs
4 parts of MIBK
4 parts of PMA.
The proportion relation of the preferred weight umber of above-mentioned anti-asphalt paint is as follows:
60 parts of acrylic resins
5 parts in vibrin
15 parts in aminoresin
5 parts of urethane resins
3 parts of TSP
5 parts of dimethylbenzene
5 parts of N-BUTYL ACETATEs
4 parts of MIBK
4 parts of PMA.
Form as the composite polyester resin of second aspect present invention feedstock production by following parts by weight:
Phthalic anhydride 20-25 part
Hexanodioic acid 10-15 part
TriMethylolPropane(TMP) 10-15 part
Neopentyl glycol 15-20 part
Dimethylbenzene 10-15 part
1-Methoxy-2-propyl acetate 5-10 part
N-BUTYL ACETATE 15-20 part.
Preparation method as the composite polyester resin of third aspect present invention, be made up of following steps:
(1) phthalic anhydride that will take by weighing in proportion, hexanodioic acid, TriMethylolPropane(TMP), neopentyl glycol and dimethylbenzene input have in the reactor of water trap and are warming up to about 110 ℃, start stirring after thing melts substantially in the described reactor, are warming up to 130-140 ℃ and begin to reflux;
(2) constantly emit the water and the weighing of generation, continue to heat up, stopping to discharge water to 190 ° begins insulation, and temperature control is between 190-210 ℃;
(3) treat that the water trap solvent is clear, polyester resin solution acid number in the measured reaction pot, until reaching acid number 15-20, reaction terminating is cooled to 50 ℃ with 1-Methoxy-2-propyl acetate and N-BUTYL ACETATE latting drown;
(4) sampling, by the technical indicator test performance qualified after, filter discharging.
Preparation method as the anti-asphalt paint of fourth aspect present invention, be made up of following steps:
(1) at room temperature, acrylic resin and the vibrin for preparing are added in the paint cylinder, whipped state adds dimethylbenzene and N-BUTYL ACETATE down, dissolving evenly, tested viscosity behind 25-30s (being coated with-4 glasss) homogeneous solution A is stand-by;
(2) add urethane resin in step (1) gained homogeneous solution, at room temperature, middling speed stirs and got solution B in 2 hours;
(3) stirring at low speed is transferred in stirring, in step (2) gained solution B, is added aminoresin, stirred 10 minutes; With the aminoresin homodisperse open solution C,
(4) in step (3) gained solution C, add PMA and TSP, continue stirring at low speed and got solution D in 10 minutes;
(5) in step (4) gained solution D, add MIBK, regulate viscosity, by the qualified back discharging of technical indicator test performance to 25-35s (being coated with-4 glasss).
Described acrylic resin adopts high 4050 acrylic resins that chemical industry company limited produces of putting; 138 aminoresin that described aminoresin adopts Aksu company to produce; The D2 urethane resin that described urethane resin adopts Degussa company to produce;
Described TSP is the modest company of a moral product.
The rotating speed that described middling speed stirs is 800r/s, and churning time is 2 hours; The middling speed mixing speed is fast, produces heat energy and improves temperature, and urethane resin is dissolved in the short period of time.
Described stirring at low speed rotating speed is 400r/s, and churning time is 10 minutes; Stirring at low speed is opened the aminoresin homodisperse.
Anti-contamination mechanism of the present invention:
The mechanism of the anti-contamination of anti-asphalt paint of the present invention is its fine and close structure and enough low surface tension, the present invention uses an amount of D2 urethane resin, the D2 urethane resin promptly can react with the acrylic resin or the vibrin of hydroxyl again with the aminoresin reaction, effectively increase the cross-linking reaction point, increased cross-linking density.The D2 resin is compared with aminoresin simultaneously, and lower surface tension is arranged.
The principle that the present invention adds the small amount of polyester resin is, the easier rotation of the vibrin of line style, and can well remedy can not be fully than inflexible vinylformic acid and the problem of aminoresin reaction, thereby increase cross-linking density, improves the compactness of paint film.
It is a kind of high molecular weight solvent that contains tensio-active agent that the present invention adds a small amount of TSP, and the adding of TSP can effectively reduce the surface tension of paint film.
Like product compares: color special dragon: 006/010808/01; Bright Ke Weize: RF20-0000/1; Ippon: SP110DK coating varnish; PPG:DCC62009.The present invention has improved contamination resistance, erosion resistance and the hardness of paint film greatly under the situation that does not reduce sticking power, weathering resistance, gloss and condition of surface.
Owing to adopted technique scheme, anti-asphalt paint of the present invention to have fine and close structure and enough low capillary characteristics, because have the advantage that preferable anti-pitch stains.
Description of drawings
Further specify the present invention below in conjunction with the drawings and specific embodiments.
Fig. 1 is the experiment effect of the anti-pitch figure of a kind of prescription 1 of the present invention.
Fig. 2 is the experiment effect of the anti-pitch figure of a kind of prescription 2 of the present invention.
Fig. 3 is the experiment effect of the anti-pitch figure of a kind of prescription 3 of the present invention.
Fig. 4 is the experiment effect of the anti-pitch figure of a kind of prescription 4 of the present invention.
Fig. 5 is the experiment effect of the anti-pitch figure of a kind of prescription 5 of the present invention.
Fig. 6 is the experiment effect of the anti-pitch figure of a kind of prescription 6 of the present invention.
Fig. 7 is the experiment effect of the anti-pitch figure of a kind of prescription 7 of the present invention.
Fig. 8 is the experiment effect of the anti-pitch figure of a kind of prescription 8 of the present invention.
Fig. 9 is the experiment effect of the anti-pitch figure of a kind of prescription 9 of the present invention.
Figure 10 is the experiment effect of the anti-pitch figure of a kind of prescription 10 of the present invention.
Figure 11 is the experiment effect of the anti-pitch figure of a kind of prescription 11 of the present invention.
Figure 12 is the experiment effect of the anti-pitch figure of a kind of prescription 12 of the present invention.
Figure 13 is the experiment effect of the anti-pitch figure of contrast.
Figure 14 is the experiment effect of the anti-pitch figure of contrast.
Figure 15 is the experiment effect of the anti-pitch figure of contrast.
Figure 16 is the experiment effect of the anti-pitch figure of contrast.
Embodiment
In order to make technique means of the present invention, creation characteristic, to reach purpose and effect is easy to understand,, further set forth the present invention below in conjunction with concrete diagram.
One, the preparation of vibrin
The prescription of 9510 vibrin, ratio of weight and number:
Phthalic anhydride 20-25 part
Hexanodioic acid 10-15 part
TriMethylolPropane(TMP) 10-15 part
Neopentyl glycol 15-20 part
Dimethylbenzene 10-15 part
1-Methoxy-2-propyl acetate 5-10 part
N-BUTYL ACETATE 15-20 part.
The formulation weight umber of table 1 vibrin is in parts by weight
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | |
Phthalic anhydride | 20 | 21 | 23 | 24 | 25 |
Hexanodioic acid | 15 | 14 | 12 | 11 | 10 |
TriMethylolPropane(TMP) | 10 | 12 | 11 | 13 | 15 |
Neopentyl glycol | 20 | 18 | 16 | 17 | 15 |
Dimethylbenzene | 10 | 15 | 11 | 12 | 13 |
1-Methoxy-2-propyl acetate | 5 | 6 | 10 | 8 | 7 |
N-BUTYL ACETATE | 20 | 19 | 17 | 15 | 15 |
The preparation method of vibrin:
(1) with reference to the proportion relation of each embodiment of table 1, have in the reactor of water trap and be warming up to about 110 ℃ taking by weighing phthalic anhydride, hexanodioic acid, TriMethylolPropane(TMP), neopentyl glycol and dimethylbenzene input, start stirring after thing melts substantially in the described reactor, be warming up to 130-140 ℃ and begin to reflux;
(2) constantly emit the water and the weighing of generation, continue to heat up, stopping to discharge water to 190 ° begins insulation, and temperature control is between 190-210 ℃;
(3) treat that the water trap solvent is clear, survey in the described reactor tree polyester lipoprotein solution acid number,, be cooled to 50 ℃ with 1-Methoxy-2-propyl acetate, N-BUTYL ACETATE latting drown until reaching in acid number 15-20 requires;
(4) sampling, by the technical indicator test performance qualified after, filter discharging.Polyester liposoluble inspection technology index sees Table 2.
Table 2 vibrin inspection technology index
Sequence number | Project | Index | The method of inspection |
1 | Outward appearance | Colourless or yellowish, Clear ﹠ Transparent | Range estimation |
2 | Fineness μ m | ≤10 | GB/T1724 |
3 | Viscosity S | 60-150 | GB/T1723 |
4 | Solids content % | 60±2 | GB/T6751 |
5 | Acid number | 15-20 | GB/T6743 |
Two, the making of anti-asphalt paint
A kind of anti-asphalt paint, its prescription comprises following raw material, ratio of weight and number:
0~65 part of 4050 acrylic resin (the high chemical industry company limited of putting)
0~65 part in vibrin
8~20 parts in 138 aminoresin (Aksu company)
0~12 part of D2 urethane resin (Degussa company)
3 parts of TSP (the modest company of moral)
5 parts of dimethylbenzene
5 parts of N-BUTYL ACETATEs
4 parts of MIBK
4 parts of PMA.
The preparation method of described anti-asphalt paint may further comprise the steps:
(1) at room temperature, 4050 acrylic resins and the vibrin for preparing are added in the paint cylinder, whipped state adds dimethylbenzene and N-BUTYL ACETATE down, and dissolving is even, and tested viscosity is stand-by in 25-30s (being coated with-4 glasss) back;
(2) add the D2 urethane resin in (1) gained homogeneous solution, at room temperature, middling speed stirred 800r/s 2 hours;
(3) stirring is transferred to the 400r/s stirring at low speed, in (2) gained solution, is added 138 aminoresin, stirred 10 minutes;
(4) in (3) gained solution, add PMA and TSP, continue to stir 10 minutes;
(5) in (4) gained solution, add MIBK, regulate viscosity, by the qualified back discharging of technical indicator test performance to 25-35s (being coated with-4 glasss).
The inspection technology index of anti-asphalt paint is referring to table 3.
Make the anti-asphalt paint of 12 kinds of prescriptions, prescription is referring to table 4.
Table 3 anti-asphalt paint inspection technology index
Sequence number | Project | Index | The method of inspection |
1 | Former lacquer outward appearance | Clear ﹠ Transparent, there is not mechanical impurity | Range estimation |
2 | Viscosity S | 25-35 | GB/T1723 |
3 | Solids content % | ≥45 | GB/T6751 |
4 | Drying conditions | 140℃/20min |
5 | Hardness | ≥H | GB/T6739 |
6 | The sticking power level | ≤1 | GB/T9286 |
7 | Shock strength kg.cm | 50 | GB/T1732 |
8 | Snappiness mm | ?≤1 | GB/T1731 |
9 | 60 ° of gloss | ?≥95 | GB/T9754 |
10 | Water tolerance | Room temperature, 240 hours, outward appearance did not have considerable change | GB/T1733 |
11 | Petrol-resistance (90#) | Room temperature, 24 hours, outward appearance did not have considerable change | GB/T1734 |
12 | Artificial accelerated aging | 1000 hours, Comprehensive Assessment≤2 grade | GB1865 |
13 | The acid salt-fog test | 240 hours, Wb≤2mm | TL-239 |
14 | Stone hits the load simulation test | Maximum performance number is 4, and does not have bubble | PV1213 method C |
15 | Anti-asphalt test | 1 hour, no change | TL-239 |
Three, pitch stains experiment
Adopt the anti-asphalt paint of 12 kinds of prescriptions of above-mentioned making, prescription is referring to table 4.
The like product contrast is adopted:
Color special dragon: 006/010808/01;
Bright Ke Weize: RF20-0000/1;
Ippon: SP110DK coating varnish;
PPG:DCC62009。
Test material is: panmex pitch, solvent is washing gasoline.
Touchstone:
Group of Shanghai Volkswagen Automotive Company Ltd standard: the surfacecti proteon of TL239 light metal wheel hub, chemically-resistant thing corrodibility, test by VDA621-412: the Panmex (model 85/25) that 5 gram Esso companies produce adds 5 milliliters of washings and stirs into pasty state with gasoline.Again muddle is about at a diameter on the test block surface of 30mm, acts on after 1 hour should the surface will sticking with paste and know that the painted surface achromatization changes with coal tar scavenger (model 000.096.052C).
The prescription of table 4 anti-asphalt paint and pitch stain experiment in parts by weight
The experimental result of the anti-asphalt paint of 12 kinds of prescriptions is referring to Fig. 1~12;
Color special dragon: 006/010808/01, referring to Figure 13;
Bright Ke Weize: RF20-0000/1 is referring to Figure 14;
Ippon: the SP110DK coating varnish, referring to Figure 15;
PPG:DCC62009 is referring to Figure 16.
The result shows, more than 4 kinds of state's over lacquers commonly used, all do not reach anti-pitch standard.
Result's contrast, the anti-pitch effect of prescription 5 is preferable.
More than show and described ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that describes in the foregoing description and the specification sheets just illustrates principle of the present invention; the present invention also has various changes and modifications without departing from the spirit and scope of the present invention, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (7)
1. anti-asphalt paint is formed by the feedstock production of following parts by weight:
0~65 part of acrylic resin
0~65 part in vibrin
8~20 parts in aminoresin
0~12 part of urethane resin
3 parts of TSP
5 parts of dimethylbenzene
5 parts of N-BUTYL ACETATEs
4 parts of MIBK
4 parts of PMA.
2. anti-asphalt paint according to claim 1 is characterized in that, the proportion relation of the parts by weight of described anti-asphalt paint is as follows:
60 parts of acrylic resins
5 parts in vibrin
15 parts in aminoresin
5 parts of urethane resins
3 parts of TSP
5 parts of dimethylbenzene
5 parts of N-BUTYL ACETATEs
4 parts of MIBK
4 parts of PMA.
3. prescription for preparing the composite polyester resin of the described anti-asphalt paint of claim 1 is formed by the feedstock production of following parts by weight:
Phthalic anhydride 20-25 part
Hexanodioic acid 10-15 part
TriMethylolPropane(TMP) 10-15 part
Neopentyl glycol 15-20 part
Dimethylbenzene 10-15 part
1-Methoxy-2-propyl acetate 5-10 part
N-BUTYL ACETATE 15-20 part.
4. the preparation method of the described composite polyester resin of claim 3:
(1) phthalic anhydride that will take by weighing in proportion, hexanodioic acid, TriMethylolPropane(TMP), neopentyl glycol and dimethylbenzene input have in the reactor of water trap and are warming up to about 110 ℃, start stirring after thing melts substantially in the described reactor, are warming up to 130-140 ℃ and begin to reflux;
(2) constantly emit the water and the weighing of generation, continue to heat up, stopping to discharge water to 190 ° begins insulation, and temperature control is between 190-210 ℃;
(3) treat that the water trap solvent is clear, survey polyester liposoluble solution acid number in the described reactor,, illustrate that reaction process reaches terminal point, be cooled to 50 ℃ with 1-Methoxy-2-propyl acetate and N-BUTYL ACETATE latting drown until reaching acid number 15-20;
(4) sampling, by the technical indicator test performance qualified after, filter discharging.
5. the preparation method of the described anti-asphalt paint of claim 1-4, be made up of following steps:
(1) at room temperature, acrylic resin and the vibrin for preparing are added in the paint cylinder, whipped state adds dimethylbenzene and N-BUTYL ACETATE down, dissolving evenly, tested viscosity behind 25-30s homogeneous solution A is stand-by;
(2) add urethane resin in step (1) gained homogeneous solution, at room temperature, middling speed stirs and got solution B in 2 hours;
(3) stirring at low speed is transferred in stirring, in step (2) gained solution B, is added aminoresin, stirred 10 minutes; With the aminoresin homodisperse open solution C,
(4) add PMA and TSP in step (3) gained solution C, stirring at low speed got solution D in 10 minutes;
(5) in step (4) gained solution D, add MIBK, regulate viscosity, by the qualified back discharging of technical indicator test performance to 25-35s.
6. the preparation method of anti-asphalt paint according to claim 5 is characterized in that, middling speed described in the described step (2) stirs and is 800r/s, and churning time is 2 hours; The middling speed mixing speed is fast, produces heat energy and improves temperature, and urethane resin is dissolved in the short period of time.
7. the preparation method of anti-asphalt paint according to claim 5 is characterized in that, stirring at low speed is 400r/s described in the described step (3), and churning time is 10 minutes; Stirring at low speed is opened the aminoresin homodisperse.