CN101913834A - Quarry stone building material decorating plate and manufacturing method - Google Patents

Quarry stone building material decorating plate and manufacturing method Download PDF

Info

Publication number
CN101913834A
CN101913834A CN 201010258614 CN201010258614A CN101913834A CN 101913834 A CN101913834 A CN 101913834A CN 201010258614 CN201010258614 CN 201010258614 CN 201010258614 A CN201010258614 A CN 201010258614A CN 101913834 A CN101913834 A CN 101913834A
Authority
CN
China
Prior art keywords
agitator
charging basket
percent
stir
type high
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010258614
Other languages
Chinese (zh)
Other versions
CN101913834B (en
Inventor
文流学
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201010258614 priority Critical patent/CN101913834B/en
Publication of CN101913834A publication Critical patent/CN101913834A/en
Application granted granted Critical
Publication of CN101913834B publication Critical patent/CN101913834B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a quarry stone building material decorating plate. The decorating plate consists of the following components in percentage by weight: 48 to 60 percent of alpha-type high-strength gypsum powder, 6 to 8 percent of quartz sand, 6 to 9 percent of vermiculite grains, 0.8 to 1.5 percent of toning powder, 2.8 to 5 percent of glass fiber, 2.5 to 3.5 percent of acrylic polymer emulsion, 1.9 to 2.5 percent of galvanized round steel and 20 to 28 percent of clear water. The decorating plate has the characteristics of high strength, shock resistance, maximal breaking load of up to 1,800N, high flexibility, capacity of being made into various sizes, shapes and design models to be utilized in a building decoration project, high density, light weight, capacity of reducing main building weight and component load, water absorption rate within 25 percent, capacity of protecting moisture when used in a place filled with moisture, adoption of pollution-free environmental-friendly raw materials, no odor, no radioactive nuclide and capacity of regeneration and utilization, and belongs to an environmental-friendly material.

Description

A kind of quarry stone building material decorating plate and making method
Technical field
The present invention relates to a kind of building dalle and making method.
Background technology
Decorated gypsum board is to be a kind of material that main raw material is made with the plaster of Paris.It is a kind of in light weight, intensity is higher, thinner thickness, easy to process and sound insulation is adiabatic and the material of construction of better performances such as fire prevention, is one of novel light sheet material of current development emphatically.Plasterboard has been widely used in internal partition wall, body of wall cladding boards (replacing the wall plastering layer), top ceiling, acoustic panel, surface based laminate and the various decorative sheets etc. of various buildingss such as dwelling house, office building, shop, hotel and industrial premises.
Though decorated gypsum board of the prior art has obtained improving greatly, the breaking load of decorated gypsum board is not high, about general 300N; Snappiness is relatively poor, easy fracture, and work-ing life is not long; Humidity resistance is poor, and water-intake rate is generally within 3.5%; And more or less contain radionuclide, as formaldehyde etc.
Summary of the invention
At above shortcomings in the prior art, it is higher to the purpose of this invention is to provide a kind of breaking load, and snappiness is better, humidity resistance the best, and the quarry stone building material decorating plate of environmental protection and making method.
A kind of quarry stone building material decorating plate provided by the invention is grouped into by following by weight percentage: alpha type high-strength gypsum powder 48～60%; Quartz sand 6～8%; Vermiculite granule 6～9%; Chromatic timing powder 0.8～1.5%; Glass fibre 2.8～5%; Acrylate polymer emulsion 2.5～3.5%; Zinc-plated round steel 1.9～2.5%; Clear water 20%～28%.
Simultaneously, the present invention also provides a kind of method of making this quarry stone building material decorating plate, comprises the steps:
1) makes top layer compound and bottom compound
1.1) making top layer compound;
1.1.1) cleaning agitator charging basket;
1.1.2) water is poured in the charging basket, and add acrylate polymer emulsion, stir;
1.1.3) chromatic timing powder is added in the charging basket, and stir with sticking plaster;
1.1.4) the alpha type high-strength gypsum powder is added in the charging basket, turn on agitator, the blade rotational speed of agitator is controlled at 45～50 rev/mins, makes water-soaked alpha type high-strength gypsum powder, leaves standstill 1 fen kind; The blade rotational speed of agitator is controlled at 50～60 rev/mins, restir 3 minutes;
1.1.5) add quartz sand and vermiculite granule again, and stir;
1.2) making bottom compound;
1.2.1) cleaning agitator charging basket;
1.2.2) water is poured in the charging basket, and add acrylate polymer emulsion, stir;
1.2.3) chromatic timing powder is added in the charging basket, and stir with sticking plaster;
1.2.4) the alpha type high-strength gypsum powder is added in the charging basket, turn on agitator, the blade rotational speed of agitator is controlled at 45～50 rev/mins, makes water-soaked alpha type high-strength gypsum powder, leaves standstill 1 fen kind; The blade rotational speed of agitator is controlled at 50～60 rev/mins, restir 3 minutes;
2) coat releasing agent in the casting mold inboard, the top layer mixed solution was poured in the casting mold in 25 minutes, make its surface that covers mould equably, and exert pressure;
3) shop triplex glass fiber and zinc-plated round steel, and extruding makes it be fitted in the surface of top layer mixed solution;
4) pour the bottom mixed solution at last in casting mold, fluid injection to be poured is solidified;
5) make the product behind the casting break away from mould with heat gun blowing, and place it in the ventilation and dry;
6) send the barn oven dry at last, the temperature of barn is controlled at the 50-60 degree, toasts 12 hours.
Adopt quarry stone building material decorating plate that component of the present invention and making method make compared with prior art, have following advantage:
1, intensity height, shock resistance: maximum breaking load can reach 1800N(thickness at 12mm), can be uniform and stable bear resistance to compression, shock resistance, and product is indeformable, do not sink, not crooked, expanded by heating not.
2, snappiness: the snappiness height, can make various size, shape and design model, because relatively be easy to use, thus be used in complicated metope, post, door-window opening, furred ceiling and the decoration, (such as: embossment, garden carving, lines, flat board etc.).
3, density height and light weight: density can reach 1900kg/m 3(standard thickness is 8mm to 12mm), every weight per square meter can alleviate main building weight and member load only 5 to 8.8kg.
4, fire resistance: this material belongs to A1 level fire-retardant material, and when fire took place, it itself can also discharge the moisture that is equivalent to own wt 15% to 18% except energy is fire-retardant, can reduce the surface temperature that catches fire significantly, reduced fire losses.
5, humidity resistance: water-intake rate within 25%, be used for humid local time can be moistureproof.
6, environmental protection: all adopt free of contamination environmental protection raw material, do not have any smell, inflammable and biography smoke index is 0, and radionuclide is limited the quantity of and met and surmount the standard of the category-A finishing material of stipulating among the GB6566-2001, and can carry out regeneration, belongs to green material.
Embodiment
Quarry stone building material decorating plate is made up of following component: alpha type high-strength gypsum powder 48～60% by weight percentage; Quartz sand 6～8%; Vermiculite granule 6～9%; Chromatic timing powder 0.8～1.5%; Glass fibre 2.8～5%; Acrylate polymer emulsion 2.5～3.5%; Zinc-plated round steel 1.9～2.5%; Clear water 20%～28%.
Make the following embodiment of concrete steps of this quarry stone building material decorating plate, each component all adds by weight percentage among the embodiment.
Embodiment 1
Make the method for this quarry stone building material decorating plate, mainly comprise the steps:
1) makes top layer compound and bottom compound
1.1) making top layer compound;
1.1.1) cleaning agitator charging basket;
1.1.2) water 15% is poured in the charging basket, and add acrylate polymer emulsion 2%, stir;
1.1.3) with in chromatic timing powder (white use titanium dioxide, and is black, red, Huang, palm fibre, green, indigo plant is the ferric oxide toner entirely) the 0.8% adding charging basket, and stir with sticking plaster;
1.1.4) alpha type high-strength gypsum powder 25% is added in the charging basket, turn on agitator, the blade rotational speed of agitator is controlled at 45 rev/mins, makes water-soaked alpha type high-strength gypsum powder, leaves standstill 1 fen kind; The blade rotational speed of agitator is controlled at 50 rev/mins, restir 3 minutes;
1.1.5) add quartz sand 6% and vermiculite granule 6% again, and stir;
1.2) making bottom compound;
1.2.1) cleaning agitator charging basket;
1.2.2) water 13% is poured in the charging basket, and add acrylate polymer emulsion 1.5%, stir;
1.2.3) chromatic timing powder 0.7% is added in the charging basket, and stir with sticking plaster;
1.2.4) alpha type high-strength gypsum powder 23% is added in the charging basket, turn on agitator, the blade rotational speed of agitator is controlled at 45 rev/mins, makes water-soaked alpha type high-strength gypsum powder, leaves standstill 1 fen kind; The blade rotational speed of agitator is controlled at 50 rev/mins, restir 3 minutes;
2) coat releasing agent in the casting mold inboard, the top layer mixed solution was poured in the casting mold in 25 minutes, make its surface that covers mould equably, and exert pressure;
3) shop triplex glass fiber 4.5% and the zinc-plated round steel 2.5% of diameter 6mm, and extruding makes it be fitted in the surface of top layer mixed solution;
4) pour the bottom mixed solution at last in casting mold, fluid injection to be poured is solidified;
5) make the product behind the casting break away from mould with heat gun blowing, and place it in the ventilation and dry;
6) send the barn oven dry at last, the temperature of barn is controlled at the 50-53 degree, toasts 12 hours.
Detect the quarry stone building material decorating plate of above-mentioned making, breaking load can reach 1790N(thickness at 10mm), density reaches 1880kg/m 3(thickness is 8mm), every weight per square meter is 5kg only, and has snappiness and fire resistance well.
Embodiment 2
Make the method for this quarry stone building material decorating plate, mainly comprise the steps:
1) makes top layer compound and bottom compound
1.1) making top layer compound;
1.1.1) cleaning agitator charging basket;
1.1.2) water 12.9% is poured in the charging basket, and add acrylate polymer emulsion 1.3%, stir;
1.1.3) with in chromatic timing powder (white use titanium dioxide, and is black, red, Huang, palm fibre, green, indigo plant is the ferric oxide toner entirely) the 0.4% adding charging basket, and stir with sticking plaster;
1.1.4) alpha type high-strength gypsum powder 26% is added in the charging basket, turn on agitator, the blade rotational speed of agitator is controlled at 48 rev/mins, makes water-soaked alpha type high-strength gypsum powder, leaves standstill 1 fen kind; The blade rotational speed of agitator is controlled at 55 rev/mins, restir 3 minutes;
1.1.5) add quartz sand 8% and vermiculite granule 9% again, and stir;
1.2) making bottom compound;
1.2.1) cleaning agitator charging basket;
1.2.2) water 12% is poured in the charging basket, and add acrylate polymer emulsion 1.2%, stir;
1.2.3) chromatic timing powder 0.4% is added in the charging basket, and stir with sticking plaster;
1.2.4) alpha type high-strength gypsum powder 24% is added in the charging basket, turn on agitator, the blade rotational speed of agitator is controlled at 48 rev/mins, makes water-soaked alpha type high-strength gypsum powder, leaves standstill 1 fen kind; The blade rotational speed of agitator is controlled at 55 rev/mins, restir 3 minutes;
2) coat releasing agent in the casting mold inboard, the top layer mixed solution was poured in the casting mold in 25 minutes, make its surface that covers mould equably, and exert pressure;
3) shop triplex glass fiber 2.8% and the zinc-plated round steel 2% of diameter 6mm, and extruding makes it be fitted in the surface of top layer mixed solution;
4) pour the bottom mixed solution at last in casting mold, fluid injection to be poured is solidified;
5) make the product behind the casting break away from mould with heat gun blowing, and place it in the ventilation and dry;
6) send the barn oven dry at last, the temperature of barn is controlled at the 54-56 degree, toasts 12 hours.
Detect the quarry stone building material decorating plate of above-mentioned making, breaking load can reach 1780N(thickness at 12mm), density reaches 1900kg/m 3(thickness is 10mm), every weight per square meter is 8kg only, and has snappiness and fire resistance well.
Embodiment 3
Make the method for this quarry stone building material decorating plate, mainly comprise the steps:
1) makes top layer compound and bottom compound
1.1) making top layer compound;
1.1.1) cleaning agitator charging basket;
1.1.2) water 10% is poured in the charging basket, and add acrylate polymer emulsion 1.3%, stir;
1.1.3) with in chromatic timing powder (white use titanium dioxide, and is black, red, Huang, palm fibre, green, indigo plant is the ferric oxide toner entirely) the 0.4% adding charging basket, and stir with sticking plaster;
1.1.4) alpha type high-strength gypsum powder 32% is added in the charging basket, turn on agitator, the blade rotational speed of agitator is controlled at 50 rev/mins, makes water-soaked alpha type high-strength gypsum powder, leaves standstill 1 fen kind; The blade rotational speed of agitator is controlled at 60 rev/mins, restir 3 minutes;
1.1.5) add quartz sand 6% and vermiculite granule 6% again, and stir;
1.2) making bottom compound;
1.2.1) cleaning agitator charging basket;
1.2.2) water 10% is poured in the charging basket, and add acrylate polymer emulsion 1.2%, stir;
1.2.3) chromatic timing powder 0.4% is added in the charging basket, and stir with sticking plaster;
1.2.4) alpha type high-strength gypsum powder 28% is added in the charging basket, turn on agitator, the blade rotational speed of agitator is controlled at 50 rev/mins, makes water-soaked alpha type high-strength gypsum powder, leaves standstill 1 fen kind; The blade rotational speed of agitator is controlled at 60 rev/mins, restir 3 minutes;
2) coat releasing agent in the casting mold inboard, the top layer mixed solution was poured in the casting mold in 25 minutes, make its surface that covers mould equably, and exert pressure;
3) shop triplex glass fiber 2.8% and the zinc-plated round steel 1.9% of diameter 6mm, and extruding makes it be fitted in the surface of top layer mixed solution;
4) pour the bottom mixed solution at last in casting mold, fluid injection to be poured is solidified;
5) make the product behind the casting break away from mould with heat gun blowing, and place it in the ventilation and dry;
6) send the barn oven dry at last, the temperature of barn is controlled at the 58-60 degree, toasts 12 hours.
Detect the quarry stone building material decorating plate of above-mentioned making, breaking load can reach 1790N(thickness at 12mm), density reaches 1890kg/m 3(thickness is 10mm), every weight per square meter is 8.8kg only, and has snappiness and fire resistance well.
Quarry stone building material decorating plate of the present invention is not limited to a kind of flat board, also can make solid pattern or various plane patterns such as various embossments, garden carving on flat board, and various solids or plane pattern all can be formed by mould.
Explanation is at last, above embodiment is only unrestricted in order to technical scheme of the present invention to be described, although the present invention is had been described in detail with reference to preferred embodiment, those of ordinary skill in the art is to be understood that, can make amendment or be equal to replacement technical scheme of the present invention, and not breaking away from the aim and the scope of technical solution of the present invention, it all should be encompassed in the middle of the claim scope of the present invention.

Claims (2)

1. a quarry stone building material decorating plate is characterized in that: be made up of following component by weight percentage: alpha type high-strength gypsum powder 48～60%; Quartz sand 6～8%; Vermiculite granule 6～9%; Chromatic timing powder 0.8～1.5%; Glass fibre 2.8～5%; Acrylate polymer emulsion 2.5～3.5%; Zinc-plated round steel 1.9～2.5%; Clear water 20%～28%.
2. a method of making the described quarry stone building material decorating plate of claim 1 is characterized in that, comprises the steps:
1) makes top layer compound and bottom compound
1.1) making top layer compound;
1.1.1) cleaning agitator charging basket;
1.1.2) water is poured in the charging basket, and add acrylate polymer emulsion, stir;
1.1.3) chromatic timing powder is added in the charging basket, and stir with sticking plaster;
1.1.4) the alpha type high-strength gypsum powder is added in the charging basket, turn on agitator, the blade rotational speed of agitator is controlled at 45～50 rev/mins, makes water-soaked alpha type high-strength gypsum powder, leaves standstill 1 fen kind; The blade rotational speed of agitator is controlled at 50～60 rev/mins, restir 3 minutes;
1.1.5) add quartz sand and vermiculite granule again, and stir;
1.2) making bottom compound;
1.2.1) cleaning agitator charging basket;
1.2.2) water is poured in the charging basket, and add acrylate polymer emulsion, stir;
1.2.3) chromatic timing powder is added in the charging basket, and stir with sticking plaster;
1.2.4) the alpha type high-strength gypsum powder is added in the charging basket, turn on agitator, the blade rotational speed of agitator is controlled at 45～50 rev/mins, makes water-soaked alpha type high-strength gypsum powder, leaves standstill 1 fen kind; The blade rotational speed of agitator is controlled at 50～60 rev/mins, restir 3 minutes;
2) coat releasing agent in the casting mold inboard, the top layer mixed solution was poured in the casting mold in 25 minutes, make its surface that covers mould equably, and exert pressure;
3) shop triplex glass fiber and zinc-plated round steel, and extruding makes it be fitted in the surface of top layer mixed solution;
4) pour the bottom mixed solution at last in casting mold, fluid injection to be poured is solidified;
5) make the product behind the casting break away from mould with heat gun blowing, and place it in the ventilation and dry;
6) send the barn oven dry at last, the temperature of barn is controlled at the 50-60 degree, toasts 12 hours.
CN 201010258614 2010-08-20 2010-08-20 Quarry stone building material decorating plate and manufacturing method Active CN101913834B (en)