CN101903578B - A cloth for knitting having microfiber - Google Patents
A cloth for knitting having microfiber Download PDFInfo
- Publication number
- CN101903578B CN101903578B CN200880122535.9A CN200880122535A CN101903578B CN 101903578 B CN101903578 B CN 101903578B CN 200880122535 A CN200880122535 A CN 200880122535A CN 101903578 B CN101903578 B CN 101903578B
- Authority
- CN
- China
- Prior art keywords
- area
- knit goods
- yarn
- zone
- microfibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Disclosed are knitted cloth containing microfibers. The knitted cloth comprise ground yarns for shape stability and pile yarns forming unit regions. The unit regions are formed in a repeating manner. Each of the unit regions includes two or three regions composed of different materials. In an exemplary embodiment, each of the unit regions includes at least one region containing mi not crofibers to offer cleaning performance, wiping performance and absorbency and at least one region allowing the knitted fabric to be easily pushed. The microfiber-containing knitted cloth stably pick up dust and impurities and prevent the picked-up dust and impurities from escaping. Therefore, the microfiber-containing knitted cloth exhibit good cleaning performance.
Description
Technical field
The present invention relates to contain the knitted cloth of microfibre, be used for the cleaning element such as cleaning pad.More specifically, the present invention relates to have the knitted cloth that contains microfibre of good clean-up performance, this cloth was easy to promote and does not need user's very large strength and can stably pick up dust and impurity and prevent that the dust and the impurity that are picked up from running away in when cleaning.
Background technology
The cleaning pad that fiber is made and cleaning equipment have been used to clean the purpose of room, floor and the glass of family and office.For example, before cleaning, cleaning pad is connected to the promotion rod and absorbs an amount of water so that cleaning.After the cleaning, with cleaning pad separate from promoting rod, clean, dry and storage.In recent years, they occur in market to have developed many cleaning equipments easy to use and this.Especially, with Velcro cleaning pad is connected to the promotion rod to improve the convenience that uses with being easy to remove.
The cleaning pad of many use microfibres is commercially available at present.Thereby in cleaning pad, use microfibre to increase contact area between cleaning pad and the surface to be cleaned and increased that cleaning pad picks up the ability of dust and dirt and the dust and the dirt that prevent from being picked up are run away the cleaning efficiency that obtains increasing from cleaning pad.Up to now, the NP tearing mode complex yarn that is made of nylon and polyester is used as cleaning microfibre.
Korean Patent No.257806 proposes a kind of method of making cleaning cloth by air mixing and the polyester filament microfibre that interweaves, wherein have the microfibre and the xeothermic inotropic polyester false-twist textured yarn coexistence with 25 to 35% of the multiple fineness of 0.06 to 0.5 DENIER (denier), weave this product that interweaves and produce the long filament microfibre.This cleaning cloth has superiority aspect dust or the dirt removing.Yet because the low-intensity of the microfibre of this cleaning cloth, they are easy to be worn when repeating push-and-pull during cleaning, thereby so that the user is exhausted.
In order to attempt to overcome above-mentioned shortcoming, Korean unexamined patent application No.2003-94342 has proposed a kind of microfibre cleaning cloth that is woven with the pattern that comprises the piqu Weaving pattern.Even this cleaning cloth has reduced the frequency that push-and-pull is moved, but still can show good clean-up performance, yet its shortcoming is the relatively poor durability that produces when using microfibre and uses less power to remove the restriction of long-standing dirt.
Summary of the invention
Technical problem
The objective of the invention is to address the above problem and provide the knitted cloth that contains microfibre with good clean-up performance, this cloth can carry out high-efficiency cleaning by less power.
Technical scheme
According to an embodiment of the invention, a kind of knitted cloth that contains microfibre is provided, it comprises the wire gauze (ground yarn) for shape stability and the suede yarn that forms the unit area, wherein each unit area comprises: 64 to 84% the first area that contains microfibre is to provide clean-up performance, wiping properties and absorbability by weight, by weight 10 to 30% second area with allow pad to be pushed easily and by weight 6 to 16% the 3rd zone be used for cleaning dust or dirt, and these unit areas form with repetitive mode.
Each unit area can have the configuration according to the order setting in first area, second area, first area, second area and the 3rd zone.
In each unit area, first area, second area, first area, second area and the 3rd zone can exist with the weight ratio of 32-42: 5-15: 32-42: 5-15: 6-16.
Each unit area can by braiding forms so that the lint length in first, second, and third zone with the order minimizing of second area＞the 3rd zone＞first area.
The first area can be made of the twist yarn that contains draw-textured yarn, and it is 100 to 400D polyester filament yarn that this draw-textured yarn contains total fineness.
Second area can be made of the twist yarn that contains polyester textured yarn, and this polyester textured yarn has 100 to 200D total fineness.
The 3rd zone can be that 300 to 600D polyolefin draw-textured yarn consists of by having total fineness.
According to another embodiment of the present invention, a kind of knit goods that contains microfibre is provided, it comprises the suede yarn for the wire gauze of shape stability and formation unit area, wherein each unit area comprises: 62 to 75% the split film yarn (split yarns) that contains is used as the regional A of microfibre so that clean-up performance, wiping properties and absorbability to be provided by weight, 25 to 38% regional B is to allow this knit goods easily to be promoted by weight, and this unit area forms with repetitive mode.
Microfibre can be nylon/polyester (NP) split film yarn.
Each unit can by braiding form in case the lint length of regional A greater than the lint length of regional B.
Zone A can be consisted of by having the twist yarn of total fineness by 100 to 400D.
Zone B can be consisted of by containing the twist yarn of total fineness by 100 to 200D polyester textured yarn.
The unit area can form linearity or ripple master drawing case.
Ripple master drawing case can be waveform, impulse wave or z font pattern.
It is 100 to 200D false-twist textured yarn that wire gauze can contain total fineness.
False-twist textured yarn can be selected from spandex, elastomeric yarn, dive crimp property yarn, mechanical crimp property yarn and their combination.
The optional autohemagglutination ammonia of wire gauze ester fiber, polyester fiber, acrylic fiber and their combination.
Knit goods can be under drying regime (moisture＜5%), under 0.50 to 0.55lb pressure and 0.60 to the 0.80lb tension force, on the floor that is 30 ° of inclinations with respect to knit goods by push-and-pull.
When increasing the weight of 3.5lb to knit goods, this knit goods can be under dry or moist state, under the pressure 2.30 to 2.50lb and 4.90 to 5.20lb the tension force, on the floor that is 60 ° of inclinations with respect to knit goods by push-and-pull.
Knit goods can have 99% or higher efficiency of dust collection under moist state.
Another embodiment again according to the present invention, a kind of cleaning pad is provided, it comprises a bed course that is formed by one of described knitted cloth, attach to this bed course rear surface and form to absorb an absorbed layer of moisture or oil by foamable polymer, sponge or bondedfibre fabric net, and attach to the rear surface of this absorbed layer and comprise that velcro Velcro, button, slide fastener or rope are to provide a layer can be removed that cleans convenience.
Beneficial effect
As mentioned above, the knitted cloth that contains microfibre of the present invention is that two or Three regions of the tool difference in functionality by weaving to form linearity or ripple master drawing case makes.Even if reduced the frequency of push-and-pull campaign, the knitted cloth that contains microfibre of the present invention still can be by friction and wiping and is thoroughly removed dust or dirt.In addition, the knitted cloth that contains microfibre of the present invention only needs less cleaning power and is very durable.
In addition, the knitted cloth that contains microfibre of the present invention is easy to clean and can be when water cleans, easily from wherein removing the dust that is picked up.
Description of drawings
Fig. 1 is the plane according to the knit goods that contains microfibre of one embodiment of the present invention;
Fig. 2 is the plane of the knit goods that contains microfibre of another embodiment according to the present invention;
Fig. 3 illustrates the according to the preferred embodiment of the present invention lint pattern (a)-(d) of cleaning pad; With
Fig. 4 is the sectional view of cleaning pad (mat) according to the preferred embodiment of the present invention.
The brief description of＜accompanying drawing critical piece 〉
10: cleaning pad 11: bed course
13: absorbed layer 15: layer can be removed
20: supporter 110: first area
120: 130: the three zones of second area
210: regional A 220: regional B
The specific embodiment
Describe preferred embodiment of the present invention in detail now with reference to accompanying drawing.Be to be noted that as much as possible running through drawing and description will indicate same or analogous parts with identical reference number.When description was of the present invention, the invention basic theme was unclear for fear of causing, and omitted relevant known function or the detailed description of structure.
As used herein, term " about ", " basically " etc. be intended to allow the mathematics accuracy leave some leeway with explain in the industry acceptable error and prevent any irresponsible violator utilize wrongly provided definite or absolute figure to help to understand open text of the present invention.
The knitted cloth that contains microfibre of the present invention is described in connection with cleaning pad, but their purposes is not limited to this.
Be used for microfibre of the present invention and have 0.5 DENIER (D) or less fineness.Microfibre can be selected from filament yarn, sea island yarn, split film yarn such as nylon/polyester (NP) split film yarn and polyester/polypropylene (PP) split film yarn etc.This microfibre can be produced by any suitable technique.
Fig. 1 and 2 is the plane according to the knit goods that contains microfibre of embodiment of the present invention.
Every kind of knitted cloth that contains microfibre comprises for the wire gauze of shape stability and the suede yarn of formation unit area.
As illustrated in fig. 1 and 2, each unit area can comprise the zone that two or three separate.
Unit area shown in Figure 1 forms with repetitive mode, and each unit area comprises the Three regions that is made of different lint materials.Particularly, each unit area can comprise first area 110, second area 120 and the 3rd zone 130.
In each unit area, first area 110 exists take as 64 to 84% amount by weight, and second area 120 exists take as 10 to 30% amount by weight, and the 3rd zone 130 exists with 6 to 16% amount by weight.Each unit area can form by braiding and enclose suede or clipping pattern so that these regional length reduces with the order of second area 120＞130＞first area, the 3rd zone 110.
Each unit area can have the configuration by the order setting in first area 110, second area 120, first area 110, second area 120 and the 3rd zone 130.This unit area forms linearity or ripple master drawing case.In each unit area, first area 110, second area 120, first area 110, second area 120 and the 3rd zone 130 can exist with the weight ratio of 32-42: 5-15: 32-42: 5-15: 6-16.
If first area 110 exists the wiping properties of knit goods or the risk that absorbability may worsen so to exist less than 64% amount by weight.Simultaneously, if first area 110 with when 84% amount exists by weight, may need the durability of extra thrust and knit goods may be very poor so when wiping.
The 3rd zone 130 is made of the polyolefin draw-textured yarn with total fineness of 300 to 600D.Especially optimization polypropylene (PP) twist yarn (450
D/ 15
F).The 3rd zone 130 since its hardness give knit goods with intensity and as broom effectively cleaning and to rub off the dirt, even if therefore the frequency that moves of push-and-pull reduces also and can rub and remove dust and dirt and not need larger power during wiping.In addition, the durability of knit goods is improved in the 3rd zone 130.If use to be lower than by weight 6% amount in the 3rd zone 130, lint strength decreased so, the frequency that causes rubbing increases.The result is to need larger power to clean and cause the reduction of durability.Simultaneously, if the 3rd zone 130 is to use greater than 16% amount by weight, superficial layer is firm so, use this knit goods to the risk of the infringement of cleaning objects thereby increase, and a part dust, dirt or the solution that are picked up still are not removed, thereby increase the risk that the clean-up performance of this knit goods may reduce.
Preferably, the length in first area 110, second area 120 and the 3rd zone 130 reduces with the order of second area 120＞130＞first area, the 3rd zone 110.Because the difference of these zone lengths, second area 120 is so that pad is easily promoted, and dust or oil are collected in the 3rd zone 130, and first area 110 absorbs dust or oil and prevent that the dust or the oil that are picked up from running away.
With reference to figure 2, the knit goods that contains microfibre comprises the unit area that forms with repetitive mode, and each unit area comprises two zones that separate.Particularly, each unit area can comprise regional A 210 and the regional B 220 that is made of the different materials lint.
If regional A 210 exists the wiping properties of knit goods or the risk that absorbability may worsen so to exist less than 62% amount by weight.Simultaneously, if regional A 210 with when 75% amount exists by weight, may need the durability of extra thrust and knit goods may be very poor so when wiping.
It is 100 to 200D false-twist textured yarn that this wire gauze preferably contains total fineness.This false-twist textured yarn can be selected from spandex, elastomeric yarn, dive crimp property yarn, mechanical crimp property yarn and their combination.The optional autohemagglutination ammonia of wire gauze ester fiber, polyester fiber, their combination of acrylic fibers peacekeeping.Particularly preferably this wire gauze contains the polyethylene terephthalate false-twist textured yarn.
This knit goods that contains microfibre under drying regime (moisture＜5%), under 0.50 to 0.55lb pressure and 0.60 to the 0.80lb tension force, on the floor that is 30 ° of inclinations with respect to knit goods by push-and-pull.In addition, when applying the pressure of 3.5lb to knit goods, this knit goods is under dry or moist state, under pressure 2.30 to 2.50lb and 4.90 to 5.20lb the tension force, by push-and-pull, wherein this knit goods contains large 2.00 to 2.50 times of the weight of this knit goods under the weight ratio drying regime of clean solution under the moist state on the floor that is 60 ° of inclinations with respect to knit goods.
This knit goods that contains microfibre has 99% or higher efficiency of dust collection under moist state, wherein this knit goods contains large 2.00 to 2.50 times of the weight of weight ratio this knit goods under drying regime of clean solution under the moist state.
Fig. 3 illustrates the according to the preferred embodiment of the present invention lint pattern (a)-(d) of cleaning pad.
In the linearity pattern of Fig. 3 (a), each zone is set regularly to realize good wiping properties.Fig. 3 (c) and ripple master drawing case (d) can be waveform, impulse wave or z font pattern.Frequency and friction and the wiping required power of contact area between lint increase cleaning pad in the ripple master drawing case and the surface to be cleaned to reduce the push-and-pull campaign, consequently this knit goods wiping properties and clean-up performance significantly improves.
Fig. 4 is the cross sectional view of cleaning pad according to the preferred embodiment of the present invention.With reference to figure 4, cleaning pad 10 is can be with a kind of cleaning article of making according to the knitted cloth that contains microfibre of embodiment of the present invention, and this cleaning pad 10 removably connects supporter 20, and can comprise bed course 11, absorbed layer 13 and layer can be removed 15.Bed course 11 is directly with floor to be cleaned or regionally contact and can be made of a kind of knitted cloth that contains microfibre according to embodiment of the present invention.Bed course 11 can form circle suede or clipping pattern to optimize the clean-up performance of cleaning pad 10.The lint pattern is useful for clean-up performance.In addition, another advantage of lint pattern is high elasticity, and this allows lint to be swelled and provide good flexibility and sense of touch texture.
Absorbed layer 13 can form on a surface of layer can be removed 15.Absorbed layer 13 can form to absorb moisture or oil by foamable polymer, sponge or bondedfibre fabric net.Layer can be removed 15 can form on a surface of absorbed layer 13 and can comprise that Velcro, button, slide fastener or rope are for connecting/separating so that the convenience of cleaning to be provided.
Each contains the knit goods of microfibre under drying regime (moisture＜5%), under 0.50 to 0.55lb pressure and 0.60 to the 0.80lb tension force, on the floor that is 30 ° of inclinations with respect to knit goods by push-and-pull.In addition, when applying the pressure of 3.5lb to knit goods, this knit goods is under dry or moist state, under pressure 2.30 to 2.50lb and 4.90 to 5.20lb the tension force, by push-and-pull, wherein this knit goods contains large 2.00 to 2.50 times of the weight of this knit goods under the weight ratio drying regime of clean solution under the moist state on the floor that is 60 ° of inclinations with respect to knit goods.
Each knitted cloth that contains microfibre has 99% or higher efficiency of dust collection under moist state, wherein this knit goods contains large 2.00 to 2.50 times of the weight of weight ratio this knit goods under drying regime of clean solution under the moist state.
Embodiment
Below, more specifically explain the present invention with reference to following embodiment.
Embodiment 1
Bed course is made of the knit goods that contains microfibre.Rear surface at bed course forms absorbed layer.Absorbed layer is formed by three-dimensional low-density bondedfibre fabric net.Velcro Velcro layer is formed on the absorbed layer rear surface as layer can be removed.This sandwich be sewn as a whole and with its edge finish to finish the manufacturing of rectangle cleaning pad.This knit goods that contains microfibre forms the unit area by wire gauze and suede yarn and is formed.In wire gauze, comprise high-elastic PET draw-textured yarn (150
D/ 48
F).Comprise by weight 66% first area, by weight 22% second area and 12% the 3rd zone by weight in each unit area.The first area is made of twist yarn, and each twist yarn is by with two strands of PET filament draw textured yarns (170
D/ 72
F) as microfibre and one PET twist yarn (150
D/ 288
F) phase twisting and making.Second area is made of twist yarn, and each twist yarn passes through three strands of PET draw-textured yarns (150
D/ 48
F) phase twisting and making.The 3rd zone is by PP twist yarn (450
D/ 15
F) consist of.Each unit area forms circle suede pattern by braiding.In each unit area, the first area has six row, and second area has two row, and the 3rd zone has two row.That is to say the first area: second area: the first area: second area: the weight ratio in the 3rd zone=33.5: 11: 33.5: 11: 11.The unit area forms z font pattern by braiding with repetitive mode so that the lint length in first, second, and third zone reduces with the order of second area＞the 3rd zone＞first area.The weight of final knit goods is 590g/sm.
Embodiment 2
Bed course is made of the knit goods that contains microfibre.Rear surface at bed course forms absorbed layer.Absorbed layer is formed by three-dimensional low-density bondedfibre fabric net.The Velcro layer is formed on the absorbed layer rear surface as layer can be removed.This sandwich be sewn as a whole and with its edge finish to finish the manufacturing of rectangle cleaning pad.This knit goods that contains microfibre forms the unit area by wire gauze and suede yarn and is formed.In wire gauze, comprise high-elastic PET draw-textured yarn (150
D/ 48
F).Comprise by weight 72% regional A and 28% regional B by weight in each unit area.Zone A is made of twist yarn, and each twist yarn is by with two bursts of nylon/polyester (NP) draw-textured yarn (150
D/ 72
F) make as the twisting of microfibre phase.Zone B is made of twist yarn, and each twist yarn passes through three strands of PET draw-textured yarns (150
D/ 48
F) phase twisting and making.The unit area forms z font circle suede pattern as shown in Figure 2 so that the lint length of the lint Length Ratio of regional A zone B is larger by braiding with repetitive mode.The weight of final knit goods is 570g/sm.
Comparative example 1
Repeat the method for embodiment 1, just this bed course is to be made of and wire gauze is polyester yarn the PP split film yarn.
Comparative example 2
Repeat the method for embodiment 1, just this bed course is by nylon/PET split film yarn (80
D/ 20
F) consist of and wire gauze is polyester yarn as microfibre.
Comparative example 3
Use microfibre pad (3M).
Comparative example 4
Use microfibre pad (Johnson Diversity).
Comparative example 5
Use microfibre pad (Tuway).
* detection method
1, resistance measurement
At first, the dry sample of cleaning pad is originally weighed.The mixed solution (Quat, 3M 2oz./l gallons water) that thing is cleaned in chlorination is coated on vinyl floor and wipes out with the supporting wiper of tower husband (tuff matewiper).Wipe out remaining water and dust with the microfibre pad.After dry sample is connected to the cleaning supporter with each, in a user two step scopes, make cleaning pad be under the state that is 30 ° of overturning angles with respect to the floor on the floor repeatedly this cleaning pad of push-and-pull.Maximum pressure on the recording gauge measuring device and tension force.Simultaneously, the weight of 3.5lb is applied to the cleaning supporter so that cleaning pad with respect to 60 ° of angles of floor tilt.With in the solution of this immersion of dry sample chlorination cleaning thing until the final weight of this sample greater than about 2.26 times of original weight.Wet sample is weighed.After this, under being the state of 60 ° of overturning angles, cleaning pad carries out identical test.In this test case, three samples of each sample are carried out three tests.Get the mean value of the numerical value of acquisition.
Table 1
2, dedusting test
At first, the dry sample of cleaning pad is originally weighed.The zone of the vinyl floor that mark is to be tested.The mixed solution (Quat, 3M 2oz./l gallons water) that thing is cleaned in chlorination is coated on the test zone on floor and falls with the supporting wiper wipes of tower husband.Wipe out remaining moisture and dust with the microfibre pad.After one ounce dust is placed on the middle part of test zone, scatter case at the outside dust of installing of this test zone.Compressed air hose and nozzle are connected to this dust distribution case, and scatter air so that dust is distributed on the test zone equably towards the dust heap downwards.
After dust is distributed after deposit on the floor about 5 minutes, measure the dust density on the test zone.After this, will separate and be placed on the floor from the dust detector as the test sample book (adhesive with rear surface of the test sample book of being connected to) of standard sample.Use roller to make the surface smoothing of test sample book so that dust is attached to this test sample book equably.This test sample book separated from the floor and put into the dust detector.Measure the weight differential (%) of this test sample book before and after cleaning.Simultaneously, each dry sample is immersed in the solution of chlorination cleaning thing until the final weight of sample greater than about 2.26 times of original weight.After weighing, wet sample is installed on the supporter, and applies the weight of 3.5lb to it.In the horizontal direction, spur this sample with the wiping floor along floor surface.Do not apply normal load to sample.The dust density of record test zone.After having set the new concentration of dust, repeat identical test.The numerical value that obtains is as shown in table 2.
Table 2
3, Contamination measurement
At first, the dry sample of cleaning pad is originally weighed.The mixed solution (Quat, 3M 2oz./l gallons water) that thing is cleaned in chlorination is coated on vinyl floor and falls with the supporting wiper wipes of tower husband.Wipe out remaining moisture and dust with the microfibre pad.Obtain to pollute spot by following method.With three milk with in a straight line and one of the dropping position at 6 inches at interval connect a ground and be added drop-wise on the floor.Cleaning pad is of a size of 18 inches, and this is within user's a step.Can happy catsup drip with the regular interval of dripping 1 inch apart from milk.With dry 4 hours of these stains.Simultaneously, each dry sample is immersed in the solution of chlorination cleaning thing until the final weight of sample greater than about 2.26 times of original weight.After weighing, wet sample is installed on the supporter, and applies the weight of 3.5lb to it.Within user's a step, along floor surface in the horizontal direction before and after push-and-pull this sample with the wiping floor.Do not apply normal load to sample.Calculate the frequency of push-and-pull campaign until the stain disappearance.
Table 3
4, absorbability test
At first, the dry sample of cleaning pad is originally weighed.Each sample is immersed in the water receptacle.When sample is stretched at ordinary times, it is taken out from container.Sample is kept smooth until there is not water to fall from sample above water receptacle, then weigh.In addition, sample is remained the edge above water receptacle until there is not water to fall from sample, then weigh.
Table 4
The result of table 1-4 discloses the knitted cloth (embodiment 1 and 2) that contains microfibre of the present invention and demonstrates than the better clean-up performance characteristic of conventional products (comparative example 1-5).Therefore, the knitted cloth that contains microfibre of the present invention can be used for the place that any needs also can utilize outstanding sanitary characteristics.
Although described the present invention at this embodiment and accompanying drawing with reference to the front, scope of the present invention is limited by following claim.Therefore, it will be appreciated by those skilled in the art that multiplely substitute, modifications and variations are possible, and do not deviate from such as the disclosed spirit of the present invention of claims.
Claims (12)
1. knit goods that contains microfibre, comprise for the wire gauze of shape stability and the suede yarn of formation unit area, wherein each unit area comprises: 64 to 84% contain the first area of microfibre so that clean-up performance to be provided by weight, wiping properties and absorbability, by weight 10 to 30% second area with allow pad to be pushed easily and by weight 6 to 16% the 3rd zone be used for cleaning dust and dirt, and this unit area forms with repetitive mode, and wherein each unit area forms consequently first by braiding, the lint length in the second and the 3rd zone is with second area〉the 3rd zone〉order of first area reduces.
2. the knit goods of claim 1, wherein each unit area has the configuration that the order according to first area, second area, first area, second area and the 3rd zone arranges.
3. the knit goods of claim 2, wherein in each unit area, first area, second area, first area, second area and the 3rd zone exist with the weight ratio of 32-42:5-15:32-42:5-15:6-16.
4. the knit goods of claim 1, wherein the first area is made of the twist yarn that contains draw-textured yarn, and it is 100 to 400D polyester filament yarn that this draw-textured yarn contains total fineness.
5. the knit goods of claim 1, wherein second area is made of the twist yarn that contains polyester textured yarn, and this polyester textured yarn has 100 to 200D total fineness.
6. the knit goods of claim 1, wherein the 3rd zone is that 300 to 600D polyolefin draw-textured yarn consists of by total fineness.
7. the knit goods of claim 1, wherein the unit area forms linearity or ripple master drawing case.
8. the knit goods of claim 7, its medium wave master drawing case is waveform or z font pattern.
9. the knit goods of claim 1, wherein to contain total fineness be 100 to 200D false-twist textured yarn to wire gauze.
10. the knit goods of claim 9, wherein false-twist textured yarn is elastomeric yarn.
11. the knit goods of claim 1, wherein wire gauze is selected from polyurethane fiber, polyester fiber, acrylic fiber, and their combination.
12. a cleaning pad comprises:
One bed course, this bed course is formed by the knit goods of claim 1;
One absorbed layer, this absorbed layer is attached to the rear surface of this bed course, and is to be formed by foamable polymer or bondedfibre fabric net, to absorb moisture or oil; With
One layer can be removed, this layer can be removed is attached to the rear surface of this absorbed layer, and it comprises that velcro, button, slide fastener or rope are to provide the cleaning convenience.