CN101903541B - Method for manufacturing binderless briquettes and apparatus for manufacturing the same - Google Patents
Method for manufacturing binderless briquettes and apparatus for manufacturing the same Download PDFInfo
- Publication number
- CN101903541B CN101903541B CN2008801211500A CN200880121150A CN101903541B CN 101903541 B CN101903541 B CN 101903541B CN 2008801211500 A CN2008801211500 A CN 2008801211500A CN 200880121150 A CN200880121150 A CN 200880121150A CN 101903541 B CN101903541 B CN 101903541B
- Authority
- CN
- China
- Prior art keywords
- iron ore
- reducing iron
- sludge
- equipment
- dust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a method of manufacturing a binderless briquette and an apparatus for performing the same. The method of manufacturing the binderless briquette includes providing a dust gathered by using a dry collection manner from an offgas discharged when an iron ore is dried, providing a reduced iron ore discharged from an apparatus for manufacturing a molten iron including a reduction furnace providing a reduced iron obtained by reducing the dried iron ore and a melter-gasifier manufacturing the molten iron by melting the reduced iron, providing a sludge discharged from the apparatus for manufacturing the molten iron, providing a mixture formed by drying and mixing at least two sources selected from the group consisting of the dust, the reduced iron ore and the sludge and forming the binderless briquette by molding the mixture without adding a binder.
Description
Technical field
The present invention relates to a kind of equipment of making the method for binder free agglomerate and making the binder free agglomerate.More particularly, the present invention relates to a kind of equipment that the dust, sludge or the reduced iron that produce when forming molten iron are made the method for binder free agglomerate and made the binder free agglomerate that is utilized in.
Background technology
When making molten iron, produce various sub products.Under the situation that reclaims sub product, because sub product comprises carbon or iron, so the cost that can economize in raw materials greatly.Sub product can be dust, sludge or reducing iron ore.
Can when making molten iron, reclaim dust to form pellet as sticker through utilizing cement.Yet, because cement is used as sticker, so need burn till (maturing) technology to pellet.In addition, if pellet is used for blast furnace, can produce a large amount of slags.
Summary of the invention
Technical problem
Embodiments of the invention relate to a kind of method that the dust, sludge or the reduced iron that produce when forming molten iron are made the binder free agglomerate that is utilized in.
Embodiments of the invention provide a kind of equipment of carrying out aforesaid method.
Technical scheme
According to embodiments of the invention, a kind of method of making the binder free agglomerate is provided.This method may further comprise the steps: provide to utilize and do the dust that collection method is collected from exhaust gas discharged when iron ore is dried; Provide from the reducing iron ore of the equipment exhausting that is used to make molten iron, the equipment that is used to make molten iron comprises reduction furnace that the reduced iron that obtains through the exsiccant iron ore through reduction is provided and makes the melting Gas-making Furnace of molten iron through smelting reduction iron; The sludge that is used to make the equipment exhausting of molten iron from said is provided; Provide through drying and mix the mixture that at least two kinds of raw materials from the group of being made up of said dust, said reducing iron ore and said sludge, selecting form; Make mixture forming form the binder free agglomerate through not adding sticker.
In the step of reducing iron ore is provided, reducing iron ore is being carried out after drying and the size separation reducing iron ore being provided.Before reducing iron ore was carried out drying and size separation, reducing iron ore comprised about 10wt% to the interior moisture of the scope of about 30wt%.The reduction ratio of reducing iron ore is about 30% to about 60%.Reducing iron ore is carried out size separation,, thick reducing iron ore is filled into the melting Gas-making Furnace reducing iron ore is divided into thick reducing iron ore and smart reducing iron ore.The diameter of thick reducing iron ore is greater than about 8mm.
In the step that forms the binder free agglomerate, when making mixture forming, forming pressure is that about 6t/cm is to about 10t/cm.In the step of mixture was provided, the amount of the moisture in the reducing iron ore was about 0 to about 6wt%.In the step of mixture was provided, the diameter of reducing iron ore was that about 1mm is to about 5mm.
In the step of mixture was provided, the amount of mixing the dust of species was about 0 to about 50wt%.In the step of reducing iron ore is provided, reducing iron ore is provided from reduction furnace.In the step of reducing iron ore is provided; The equipment that is used to make molten iron comprises that also foundary weight forms device; Foundary weight formation device is with reduction furnace and the melting Gas-making Furnace is connected to each other and will be fed to the melting Gas-making Furnace through pushing the foundary weight that forms from the reduced iron of reduction furnace discharging, forms the device provisioning reducing iron ore from foundary weight.
In the step that forms the binder free agglomerate, the intensity of binder free agglomerate is that about 80kgf/p is to about 100kgf/p.In the step of sludge is provided, after sludge is dried and is broken, sludge is provided.Before sludge was dried also fragmentation, sludge comprised the moisture of about 30wt% to about 40wt%.
In the step of mixture is provided, form mixture through mixing dust, reducing iron ore and sludge, the amount of sludge is about 0 to about 55wt% in the mixture.The amount of reducing iron ore and the amount of dust are basic identical.
In the step of mixture is provided, form mixture through mixing dust and sludge, the content of dust is that about 70wt% is to about 100wt% in the mixture.In the step of mixture is provided, form mixture through mixing reducing iron ore and sludge, the content of reducing iron ore is that about 70wt% is to about 100wt% in the mixture.In the step of mixture is provided, mixture is heat-treated to about 400 ℃ temperature with about 350 ℃.
According to embodiments of the invention, a kind of equipment that is used to make the binder free agglomerate is provided.This equipment comprises: the dust hopper, collect the dust of dust and store collected from exhaust gas discharged when the dry iron ore through utilizing dried collection mode; The reducing iron ore hopper; Storage is from the reducing iron ore of the equipment exhausting that is used to make molten iron, and the said equipment that is used to make molten iron comprises reduction furnace that the reduced iron that obtains through the exsiccant iron ore through reduction is provided and makes the melting Gas-making Furnace of molten iron through smelting reduction iron; The sludge hopper stores the sludge that is used to make the equipment exhausting of molten iron from said; Mixing tank is connected to dust hopper, reducing iron ore hopper and sludge hopper, and dry at least two kinds of raw materials from the group of being made up of said dust, said reducing iron ore and said sludge, selecting with mixing form mixture; A pair of forming roll forms the binder free agglomerate to mixture forming.
Mixing tank comprises housing and the rotating member that in housing, rotates.Rotating member is to extend the spiral member in housing, to rotate along pre-determined direction.
Said equipment also comprises: moisture eliminator, dry sludge; Destroyer is connected to each other moisture eliminator and sludge warehouse and broken sludge.Moisture eliminator is a rotary kiln.
Said equipment also comprises: moisture eliminator, dry reducing iron ore; The size separation device is connected to each other moisture eliminator and reducing iron ore hopper, and to carrying out size separation through the exsiccant reducing iron ore being divided into smart reducing iron ore and thick reducing iron ore through the exsiccant reducing iron ore.Moisture eliminator is a rotary kiln.
Thick reducing iron ore is filled into the melting Gas-making Furnace.Reduction furnace is fed to the reducing iron ore hopper with reducing iron ore.
Mixture is heat-treated to about 400 ℃ temperature with about 350 ℃.The equipment that is used to make molten iron comprises also reduction furnace and melting Gas-making Furnace foundary weight connected to one another is formed device that reducing iron ore forms device provisioning to the reducing iron ore hopper from foundary weight.
Said a pair of forming roll makes said mixture forming with the forming pressure of the extremely about 10t/cm of about 6t/cm.Reduction furnace is fluid bed reduction reactor drum or packed-bed reactor.
Beneficial effect
Can be recovered in the sub product (for example, dust, sludge or reducing iron ore) that produces when making molten iron.Therefore, raw materials cost is minimized.In addition, the agglomerate that utilizes dust, sludge or reducing iron ore to form can at high temperature have higher intensity, makes agglomerate can be filled into effectively in the melting Gas-making Furnace to make molten iron.
Description of drawings
Fig. 1 schematically shows the equipment that is used to make the binder free agglomerate according to first embodiment of the invention.
Fig. 2 schematically shows the equipment that is used to make the binder free agglomerate according to second embodiment of the invention.
Fig. 3 shows the equipment that is used to make molten iron, and wherein, this equipment exhausting is fed to being used among Fig. 1 and Fig. 2 and makes the raw material of the equipment of binder free agglomerate.
Fig. 4 schematically shows the ore drying installation of discharging dust.
Fig. 5 schematically shows the fluid bed reduction reactor drum of discharging reduced iron ore and sludge.
The foundary weight (compacted iron) that Fig. 6 schematically shows the discharging reduced iron ore forms device.
Fig. 7 schematically shows the hold-up vessel of discharging sludge.
Fig. 8 schematically shows the equipment that is used to make molten iron of discharging reduced iron ore and sludge.
Fig. 9 to Figure 17 is the graphic representation that illustrates according to the variation of the ultimate compression strength of the binder free agglomerate of example 1 to example 12.
Embodiment
To the present invention be described more fully with reference to accompanying drawing hereinafter, embodiments of the invention shown in the drawings.Yet the present invention can implement with different forms, and should not be construed as the embodiment that is confined in this elaboration.On the contrary, provide these embodiment to make that the disclosure will be sufficient with completely, and will convey to those skilled in the art to scope of the present invention fully.Identical label is represented components identical all the time.
The whole terms that comprise T.T. and scientific terminology used herein have the meaning equivalent in meaning with those skilled in the art institute common sense.It will also be appreciated that these terms (term that for example in universaling dictionary, defines) should be understood that to have the meaning of the aggregatio mentium in the context with the disclosure and association area, and should be not ideally or too formally explain their meaning.
The binder free agglomerate is need not add the agglomerate that sticker forms.Therefore, when forming agglomerate, can not need optionally to add sticker.
Fig. 1 schematically shows the equipment 10 according to the manufacturing binder free agglomerate of first embodiment of the invention.
As shown in Figure 1, the equipment 10 that is used to make the binder free agglomerate comprises: reducing iron ore hopper 101, dust hopper 102, mixing tank 108 and former 110.In addition, the equipment 10 that is used to make the binder free agglomerate also can comprise size separation device 105 and warehouse 106 and 107.
To be fed to reducing iron ore hopper 101 by the reducing iron ore of the equipment 1000 (see figure 3)s discharging that is used to make molten iron.Reducing iron ore is stored in the reducing iron ore hopper 101.Reducing iron ore can be remet.Can form reducing iron ore through making reduction of iron ore.Reducing iron ore can comprise the iron ore of complete reductive iron ore and partial reduction.
The reduction ratio of reducing iron ore can be about 30% to about 60%.When the reduction ratio of reducing iron ore less than about 30% or 60% the time, can effectively not form the binder free agglomerate greater than about.When making molten iron, can when making reduction of iron ore or when the extruding dri, form reducing iron ore.Reducing iron ore can be by partly reduction and reductive ore can again be oxidized when molten iron cools off subsequently when making molten iron.Therefore, reduced iron can have above-mentioned reduction ratio.
Reducing iron ore can be from the discharging of the different piece equipment 1000 (see figure 3)s of making molten iron.Because reducing iron ore is from different partial discharges and mix subsequently, thus the size of reducing iron ore is irregular and reduced iron in moisture content big relatively.Therefore, reducing iron ore cannot be directly as the raw material of making the binder free agglomerate.Therefore, before reduced iron is used to make the binder free agglomerate, but can be with the dry also size of sorting reduced iron of reducing iron ore.
Dust is fed to dust hopper 102.Dust is stored in the dust hopper 102 subsequently.When dry iron ore or when carrying iron ore, form dust.Specifically, dried collection process capable of using is collected dust from exhaust gas discharged when the dry iron ore.To be fed to dust hopper 102 through the dust that dried collection process is collected subsequently.Can dust be fed to dust warehouse 107 from dust hopper 102.Dust is stored in the dust warehouse 107 subsequently.
As stated; Can directly be used to be manufactured on the binder free agglomerate that the equipment 1000 that is used to make molten iron uses from the reducing iron ore of the equipment 1000 (see figure 3)s discharging that is used for making molten iron or dust; Make and compare that raw material efficient can maximize with the situation that stack reducing iron ore or dust ground on the scene.
As shown in Figure 1, can be with rotary kiln as moisture eliminator 104.Alternatively, can use the moisture eliminator of other type.Moisture eliminator 104 hot blasts capable of using come drying to fill into the reducing iron ore of moisture eliminator 104.That is, moisture eliminator 104 can arrive moisture eliminator 104 inside along direction of arrow rotation and with hot blast feeding.Reducing iron ore is filled in the moisture eliminator 104.Fill into reducing iron ore in the moisture eliminator 104 by warm air drying, then from moisture eliminator 104 dischargings.
The temperature moisture content of regulating reducing iron ore through the control hot blast.Before the equipment 1000 (see figure 3)s discharging that is used to make molten iron, reducing iron ore can have about 10wt% to the about moisture content of 30wt% at reducing iron ore.Under the relatively little situation of the moisture content of reducing iron ore, the intensity of agglomerate is relatively little, makes that agglomerate can be damaged easily.On the other hand, under the big relatively situation of the moisture content of reducing iron ore, reducing iron ore can become pulpous state, thereby can not form agglomerate effectively.Therefore, the moisture eliminator 104 capable of using moisture content of suitably regulating reducing iron ore.
As shown in Figure 1, will be transported to size separation device 105 through the exsiccant reducing iron ore.Size separation device 105 is connected to the size (for example, diameter) of moisture eliminator 104 with the sorting reducing iron ore.Irregular from the size of the reducing iron ore of the equipment 1000 (see figure 3)s discharging that is used to make molten iron.Therefore, size separation device 105 capable of using is regulated the size of reducing iron ore, makes the size of reducing iron ore become even relatively.
As shown in Figure 1, smart reducing iron ore is supplied to reducing iron ore warehouse 106, and reducing iron ore is stored in the reducing iron ore warehouse 106 subsequently.Reducing iron ore and dust can discharge from reducing iron ore warehouse 106 and dust warehouse 107 respectively, and are transported to mixing tank 108 subsequently.
As shown in Figure 1, mixing tank 108 comprises housing 1081 and spiral member 1083.Spiral member 1083 can extend with rotation along pre-determined direction in housing 1081.Therefore, spiral member 1083 can be with carrying to former 110 mixing from the reducing iron ore and the dust of reducing iron ore warehouse 106 and 107 dischargings of dust warehouse respectively.Mixing tank 108 capable of using makes reducing iron ore and dust drying.
As shown in Figure 1, will and mix reducing iron ore and the mixture of dust gained is transported to former 110 through drying.Former 110 can comprise hopper 1100, screw rod 1102 and a pair of forming roll 1104.Former 110 also can comprise hydraulicefficiency plant (not shown) and the load unit (not shown) that is installed to a pair of forming roll 1104, to make mixture forming under the constant compression force relatively.
Mixture is transported in the hopper 1100 and mixture is temporarily stored subsequently in hopper 1100.Screw rod 1102 along direction of arrow rotation will temporarily be stored in mixture forced discharge in the hopper 1100 in the gap between a pair of forming roll 1104.A pair of forming roll 1104 can rotate in opposite direction.A pair of forming roll 1104 can be made agglomerate through cold formation technology.
Fig. 2 schematically shows the equipment according to the manufacturing binder free agglomerate of second embodiment of the invention.The structure of the equipment 12 of the manufacturing binder free agglomerate among Fig. 2 is similar with the equipment 10 of the manufacturing binder free agglomerate of Fig. 1.Therefore, indicate identical parts and will omit any further explanation with identical label.
As shown in Figure 2, the equipment 12 of making the binder free agglomerate comprises sludge hopper 103, moisture eliminator 114, warehouse 108 and destroyer 116.In addition, the equipment 12 of making the binder free agglomerate comprise with Fig. 1 in the different mixing tank 109 of mixing tank 108 structures.The parts that comprise in the equipment 10 of other parts that comprise in the equipment 12 of manufacturing binder free agglomerate and the manufacturing binder free agglomerate of Fig. 1 are basic identical.
The sludge of collecting from fluid bed reduction reactor drum 20 (see figure 3) exhaust gas discharged is supplied to sludge hopper 103.Sludge is stored in the sludge hopper 103 subsequently.Sludge can have and is lower than 5% reduction ratio.Sludge can comprise a certain amount of carbon.Carbon can be used as the lubricant of making in the binder free agglomerate process, to reduce the intensity of binder free agglomerate.The part of iron ore changes magnetite into from rhombohedral iron ore in the fluid bed reduction reactor drum.The part of iron ore is discharged to become the source of sludge with the form of dust.Therefore, the dust that comprises in the sludge can comprise crackle and cause volumetric expansion.Therefore, the volume density of sludge is lower than the volume density of dust.
Sludge be dried with fragmentation before, sludge has the moisture that content is 30wt% to 40wt%.Comprise at sludge under the situation of moisture of relatively small amount, the intensity of the binder free agglomerate that is formed by subsequent technique is too little, makes that the binder free agglomerate can be frangible relatively.On the other hand, comprise at sludge under the situation of a large amount of relatively moisture, can not form the binder free agglomerate effectively.Therefore, moisture eliminator 114 capable of using is suitably regulated the content of the moisture in the sludge.
Moisture eliminator 114 can be a rotary kiln.Alternatively, can use other moisture eliminator to substitute rotary kiln.Moisture eliminator 114 hot blasts capable of using make the sludge that fills in the moisture eliminator 114 dry.Moisture eliminator 114 can rotate along the direction of arrow.Inside to moisture eliminator 114 provides hot blast.The temperature of may command hot blast is regulated the content of the moisture in the sludge.Sludge is filled in the moisture eliminator 114.Fill into sludge in the moisture eliminator 114 by warm air drying, then from moisture eliminator 114 dischargings.
Destroyer 116 is broken through the exsiccant sludge.Can make the sludge drying to have block shape.Therefore, need utilize destroyer 116 to make the sludge fragmentation so that sludge has the predetermined size that is suitable for making the binder free agglomerate.The sludge of fragmentation is fed to sludge warehouse 108, and the sludge with fragmentation is stored in the sludge warehouse 108 then.
As stated; Can the reducing iron ore, dust or the sludge that discharge from equipment 1000 (see figure 3)s of making molten iron directly be used for being manufactured on the binder free agglomerate of equipment 1000 uses of making molten iron; Thereby compare with the situation that reducing iron ore, dust or sludge are piled up in the place, can make the raw material maximizing efficiency.Reducing iron ore, dust and sludge discharge from reduced iron warehouse 106, dust warehouse 107 and sludge warehouse 108 respectively, and are transported to mixing tank 109.
Here, need be with reducing iron ore, dust and sludge all as the raw material of making the binder free agglomerate.As an example, can use reducing iron ore and dust to make the binder free agglomerate.As another example, can use dust and sludge to make the binder free agglomerate.As another example, can use sludge and reducing iron ore to make the binder free agglomerate.
As shown in Figure 2, mixing tank 109 comprises housing 1091 and rotating member 1093.Rotating member 1093 extends in housing 1091 with rotation vertically.Therefore, rotating member 1093 can mix and heat reducing iron ore, dust and the sludge that discharges from reducing iron ore warehouse, dust warehouse and sludge warehouse respectively.In addition, rotating member 1093 can be carried reducing iron ore, dust and sludge in the process of mixing and heating reducing iron ore, dust and sludge to former 110.
As shown in Figure 2, be transported to former 110 through the mixture that mixes and heating reducing iron ore, dust and sludge obtain.Mixture is filled in the hopper 1100 and is temporarily stored subsequently in hopper 1100.The screw feeder 1102 that is installed in the hopper 1100 can be forced to fill in the gap between a pair of forming roll 1104 along direction of arrow rotation and with mixture.A pair of forming roll 1104 can rotate in opposite direction.A pair of forming roll 1104 can be made agglomerate through cold formation technology.Hereinafter, show forming process with reference to Fig. 3 to Fig. 8 as reducing iron ore, dust and the sludge of the raw material of binder free agglomerate.
Fig. 3 shows the equipment 1000 that is used to make molten iron, is fed to the raw material of equipment that is used to make the binder free agglomerate of equipment and Fig. 2 that being used among Fig. 1 make the binder free agglomerate from being used to make equipment 1000 dischargings of molten iron.
As shown in Figure 3, the equipment 1000 that is used to make molten iron comprises that fluid bed reduction reactor drum 20, foundary weight form device 30, melting Gas-making Furnace 60, reducing gas supply line 70 and ore drying installation 80.In addition, the equipment 1000 that is used to make molten iron also comprises hot pressing equilibrator 40 and hold-up vessel 50.The equipment 1000 that is used to make molten iron also can comprise required device.
As shown in Figure 3, ore drying installation 80 can dry fill into the iron ore of fluid bed reduction reactor drum 20.Under the big relatively situation of moisture content in iron ore, iron ore can be in fluid bed reduction reactor drum 20 fluidisation and be attached to the inboard of fluid bed reduction reactor drum 20.Therefore, can make iron ore fluidisation effectively in fluid bed reduction reactor drum 20 through predrying iron ore in ore drying installation 80.
As shown in Figure 3, fluid bed reduction reactor drum 20 can comprise first fluidized bed 20a, the second fluidized-bed 20b, the 3rd fluidized-bed 20c and the 4th fluidized-bed 20d.First fluidized bed 20a, the second fluidized-bed 20b, the 3rd fluidized-bed 20c and the 4th fluidized-bed 20d sequentially are connected.Fluid bed reduction reactor drum 20 receives reducing gas and makes reduction of iron ore from melting Gas-making Furnace 60 through reducing gas supply line 70.First fluidized bed 20a receives through the exsiccant iron ore and utilizes reducing gas preheating iron ore from ore drying installation 80.But the second fluidized-bed 20b and the 3rd fluidized-bed 20c prereduction are through the iron ore of preheating.The 4th fluidized-bed 20d can finally reduce iron ore through prereduction to form meticulous dri.
Fluid bed reduction reactor drum 20 can be transferred to meticulous dri foundary weight and form device 30.Foundary weight forms device 30 can push meticulous dri.Meticulous dri is directly being filled under the situation of melting Gas-making Furnace 60, meticulous dri can outwards be disperseed by the reducing gas in the melting Gas-making Furnace 60.In addition, meticulous dri is directly filled in the melting Gas-making Furnace 60, can make the air cycle deterioration in the melting Gas-making Furnace 60.Therefore, utilize foundary weight to form device 30 meticulous dri is formed foundary weight.Then foundary weight is fed to melting Gas-making Furnace 60.
As shown in Figure 3, foundary weight forms device 30 and comprises hold-up vessel 301, pair of rolls 302, destroyer 304 and foundary weight hold-up vessel 306.But the dri that hold-up vessel 301 temporarily storeds are meticulous.Meticulous dri can discharge and utilize pair of rolls 302 to convert into from hold-up vessel 301 has the foundary weight of being with the shape shape.Destroyer 304 can broken foundary weight so that have the fixed size through broken foundary weight.Foundary weight through broken is stored in the foundary weight hold-up vessel 306.
Hot pressing equilibrator 40 can make foundary weight form device 30 and be connected to each other with hold-up vessel 50.Hot pressing equilibrator 40 adjustable foundary weight form the pressure between device 30 and the hold-up vessel 50, are delivered to hold-up vessel 50 by the strong hand so that foundary weight is formed device 30 from foundary weight.Hold-up vessel 50 stores foundary weight and foundary weight is fed to melting Gas-making Furnace 60.
Foundary weight is filled in the melting Gas-making Furnace 60 and fusing subsequently.The carbon material of caking is filled in the melting Gas-making Furnace 60, thus can be at the melting Gas-making Furnace 60 inner coal packed beds that form.Here, the carbon material of caking can be lump coal or coal agglomerate (coal briquette).With oxygen injection in melting Gas-making Furnace 60 so that coal packed bed burning.Foundary weight is by the heat melts that obtains through the coal combustion packed bed.Foundary weight is melted to form molten iron, and molten iron is by outwards discharging subsequently.To be fed to fluid bed reduction reactor drum 20 from the reducing gas that the coal packed bed produces through reducing gas supply line 70.
As shown in Figure 3, through dust supply line 90 dust is fed to the equipment 10 that is used to make the binder free agglomerate from ore drying installation 80., iron ore done collection to assemble dust when being dried from ore drying installation 80 exhaust gas discharged.The dust of collecting by the way is supplied to the equipment 10 that is used to make the binder free agglomerate through dust supply line 90.In addition, the reducing iron ore that produces from the equipment 1000 that is used to make molten iron is collected and is supplied to the equipment 10 that is used to make the binder free agglomerate through reducing iron ore supply line 85 subsequently.The sludge that produces from the equipment 1000 that is used to make molten iron is collected and is supplied to the equipment 10 that is used to make the binder free agglomerate through sludge supply line 95 subsequently.Hereinafter, describe from the process of equipment 1000 discharging reduced iron ores, dust and the sludge that is used to make molten iron with reference to Fig. 3 to Fig. 8.
Fig. 4 schematically shows the ore drying installation 80 among Fig. 3, and dust is from 80 dischargings of ore drying installation.Discharge process among Fig. 4 is not limit example of the present invention.Therefore, dust can be through another discharge process discharging.
As shown in Figure 4, ore drying installation 80 can comprise ore moisture eliminator 801, tornado dust collector 804, rear portion strainer 808, burner 809 etc.Can provide coke-oven gas (COG) and air with dry iron ore to ore moisture eliminator 801.Be delivered to warehouse 802 through the exsiccant iron ore from moisture eliminator 801, and be stored in the warehouse 802 through the exsiccant iron ore.With being stored in ferrolite supply in the warehouse 802 to fluid bed reduction reactor drum 20 (see figure 3)s.
Burn through burner 809 from ore moisture eliminator 801 exhaust gas discharged.Therefore, the removal fine powder ore deposit thereby burnt in the fine powder ore deposit.Yet unburned fine powder ore deposit also is included in the waste gas and it is supplied in the tornado dust collector 804 with waste gas.Here, for example, the fine powder ore deposit that can utilize gravity to make diameter surpass about 1.5 μ m is separated to the bottom of tornado dust collector 804.Isolating fine powder ore deposit utilizes travelling belt 806 to carry to be stored in the warehouse 802 along the direction of arrow.
Be transported to rear portion strainer 808 from tornado dust collector 804 exhaust gas discharged.The dust of not collected by tornado dust collector 804 that is included in the waste gas can be collected in rear portion strainer 808.For example, dust can have the diameter less than about 1.5 μ m.The dust of collecting in the rear portion strainer 808 can be collected and be transported to the equipment that is used to make the binder free agglomerate through second travelling belt 807 subsequently.Therefore, be used to make the equipment 10 dust manufacturing agglomerates capable of using of binder free agglomerate.
Fig. 5 schematically shows the fluid bed reduction reactor drum 20 among Fig. 3, and reducing iron ore and sludge are from 20 dischargings of fluid bed reduction reactor drum.
Can reducing iron ore be provided from fluid bed reduction reactor drum 20.Fluid bed reduction reactor drum 20 can make reduction of iron ore.Under the situation of maintenance fluid bed reduction reactor drum 20, the operation of fluid bed reduction reactor drum 20 stops and can being emitted on accumulative reducing iron ore in the fluid bed reduction reactor drum 20.
For example, as shown in Figure 5, the 4th fluid bed reduction reactor drum 20d bellows that are positioned at the 4th fluid bed reduction reactor drum 20d below capable of using come the discharging reduced iron ore.Reducing iron ore is stored in the temporarily stored jar 200 and utilizes water cooling.Reducing iron ore is fed to the equipment that is used to make the binder free agglomerate through reducing iron ore supply line 85 then.
Waste gas discharges from first fluidized bed reduction reactor 20a through offgas line 22.Waste gas comprises a certain amount of dust, thereby at offgas line 22 places scrubber 24 is installed, and scrubber 24 is to exhaust blast water, to remove dust.With the waste gas of having removed dust outwards discharging or once more with it as reducing gas.Under the situation of scrubber 24 injection waters, the water that has absorbed dust can be used as sludge and outwards discharges.Can sludge be fed to the equipment 10 that is used to make the binder free agglomerate through sludge supply line 95.
The foundary weight that Fig. 6 schematically shows Fig. 3 forms device 30, and reducing iron ore forms device 30 dischargings from foundary weight.
As shown in Figure 6, under the situation of utilizing destroyer 304 broken foundary weight, foundary weight is broken to produce dust, that is, and and reducing iron ore.Therefore, can reducing iron ore be fed to the equipment 10 that is used to make the binder free agglomerate from destroyer 304 through reducing iron ore supply line 85.
Because meticulous dri is filled into hold-up vessel 301, can outwards discharge from hold-up vessel 301 so comprise the waste gas of a certain amount of dust.Therefore, utilize from the water of washer 32 supplies and remove dust, can waste gas outwards be discharged then.The water that comprises dust can become sludge in washer 32.Can sludge be fed to the equipment 10 that is used to make the binder free agglomerate through sludge supply line 95.
In addition, meticulous dri is pushed also moulding to produce waste gas by pair of rolls 302.Here, waste gas can comprise a certain amount of dust.Therefore, scrubber 34 can eject water to waste gas to remove dust from waste gas.The water that comprises dust becomes sludge.Sludge is fed to the equipment 10 that is used to make the binder free agglomerate through sludge supply line 95 then.
The discharging reduced iron ore among Fig. 5 and Fig. 6 and the process of sludge are not limit example of the present invention.Therefore, can adopt another process to come discharging reduced iron ore and sludge.
Fig. 7 schematically shows the hold-up vessel 50 among Fig. 3, and sludge is from hold-up vessel 50 dischargings.
As shown in Figure 7, filled under the situation in the hold-up vessel 50 at foundary weight, can in hold-up vessel 50, produce waste gas owing to foundary weight.Waste gas outwards discharges through the offgas line 52 that is connected to hold-up vessel 50.Waste gas comprises dust.Therefore, come to remove dust from washer 54 supplied water from waste gas.The water that comprises dust is collected as sludge.Sludge is fed to the equipment 10 that is used to make the binder free agglomerate through sludge supply line 95.
Fig. 8 schematically shows the equipment 2000 that is used to make molten iron, and reducing iron ore and sludge are from being used to make equipment 2000 dischargings of molten iron.Be used for making the structural similitude of equipment 1000 that is used to make molten iron of structure and Fig. 3 of the equipment 2000 of molten iron.Therefore, with using the identical parts of identical label indication and will omitting any further explanation.
As shown in Figure 8, the equipment 2000 that is used to make molten iron comprises packed bed reactor 58.Though not shown in Fig. 8, the equipment 2000 that is used to make molten iron can comprise packed bed reactor and fluid bed reduction reactor drum simultaneously.In addition, the equipment 2000 that is used to make molten iron can comprise a plurality of packed bed reactors.
As shown in Figure 8, the reducing gas that produces from melting Gas-making Furnace 60 is fed to packed bed reactor 58 through reducing gas supply line 71.Iron ore is filled into packed bed reactor 58 change iron ore into reduced iron to utilize reducing gas.Reduced iron is filled into melting Gas-making Furnace 60 also to be melted to form molten iron.
The waste gas that produces from packed bed reactor 58 outwards discharges through offgas line 59.Washer 57 is installed in offgas line 59 places and washer 57 can eject water to waste gas.Comprise a certain amount of dust in the waste gas.Water can be collected dust, makes that dust can be from the form discharging of scrubber 57 with sludge.Sludge is fed to the equipment 10 that is used to make the binder free agglomerate through sludge supply line 95.
In addition, under the situation of maintenance packed bed reactor 58, packed bed reactor 58 becomes empty.Therefore, the reducing iron ore in the packed bed reactor 58 is outwards discharged.Reducing iron ore is fed to the equipment 10 that is used to make the binder free agglomerate through reducing iron ore supply line 85.Therefore, be used to make the equipment 10 reducing iron ores manufacturing binder free agglomerates capable of using of binder free agglomerate.
Hereinafter, will the present invention be described more fully with reference to example.Providing these examples will make the disclosure is completely and completely, and the present invention should not be understood that to be confined to the example in this elaboration.
Example
Utilize reducing iron ore and dust to make the experiment of binder free agglomerate as raw material
Analysis being used in Fig. 1 made the composition that comprises in dust that the equipment of binder free agglomerate uses and the reducing iron ore.List in the composition table 1 below of dust and reducing iron ore.
Table 1
[table 1]
[table]
Disclosed like table 1, because reducing iron ore is by partly reduction, so the iron level of reducing iron ore is higher.On the other hand, owing to when iron ore is dried, collect dust, the composition of dust is basic identical with the composition that is included in the iron ore.
Having carried out various experiments utilizes dust and reducing iron ore to make good binder free agglomerate.Here, the binder free agglomerate can at high temperature have HS, thereby when the binder free agglomerate was filled into the melting Gas-making Furnace, the binder free agglomerate can not separate by reduced gas.
Example 1
The mixture that a pair of forming roll 1104 essentially identical a pair of forming roll extruding among utilization and Fig. 1 and moulding comprise dust and reducing iron ore.Here, the diameter of reducing iron ore is less than about 5mm.Controlling the moment of said a pair of forming roll to change changeably forming pressure and makes the binder free agglomerate.Measure the ultimate compression strength of binder free agglomerate.When making the binder free agglomerate, variable forming pressure is 4t/cm, 6t/cm, 8t/cm and 10t/cm.Measure the ultimate compression strength of the binder free agglomerate of each forming pressure relatively.
The result of example 1
Fig. 9 shows the variation according to the ultimate compression strength of the binder free agglomerate of example 1.The ultimate compression strength of in Fig. 9, representing the binder free agglomerate corresponding with each forming pressure with black circles or white circle.In addition, in Fig. 9 through utilizing least square method that the ultimate compression strength of binder free agglomerate is expressed as dotted line.
As shown in Figure 9, when moulding pressure when 4t/cm increases to 10t/cm, the ultimate compression strength of binder free agglomerate can linearly increase.Carrying the minimum value of the required ultimate compression strength of binder free agglomerate is about 50kgf/p.In addition, filled at the binder free agglomerate under the situation of melting Gas-making Furnace, when the ultimate compression strength of binder free agglomerate surpassed about 80kgf/p, separation rate reduced.Therefore, when the ultimate compression strength of binder free agglomerate surpasses about 80kgf/p, can the binder free agglomerate be filled into the melting Gas-making Furnace.That is, the ultimate compression strength of binder free agglomerate can be about 80kgf/p to about 100kgf/p.Under the big situation of the ultimate compression strength of binder free agglomerate, need big forming pressure, thereby the load that is applied to said a pair of forming roll can be excessive.
With reference to the dotted line among Fig. 9, the ultimate compression strength of 80kgf/p is corresponding with the forming pressure of 6t/cm.Therefore, forming pressure can be 6t/cm to 10t/cm.Under the too small situation of forming pressure, the ultimate compression strength of binder free agglomerate is too small, thereby the binder free agglomerate can not be filled into the melting Gas-making Furnace.On the other hand, under the excessive situation of forming pressure, thereby the load that is applied to said a pair of forming roll can excessively possibly damage forming roll.
Example 2
The mixture that a pair of forming roll 1104 essentially identical a pair of forming roll extruding among utilization and Fig. 1 and moulding comprise dust and reducing iron ore.Here, the forming pressure of said a pair of forming roll is about 6t/cm.The reducing iron ore that has different diameter through utilization is made the binder free agglomerate.Measure the ultimate compression strength of binder free agglomerate.Through utilizing diameter less than about 1mm, make the binder free agglomerate less than about 5mm with less than the about reducing iron ore of 10mm.
Example 3
The mixture that a pair of forming roll 1104 essentially identical a pair of forming roll extruding among utilization and Fig. 1 and moulding comprise dust and reducing iron ore.Here, the forming pressure of said a pair of forming roll is about 10t/cm.Utilization has the reducing iron ore of different diameter and makes the binder free agglomerate.Measure the ultimate compression strength of binder free agglomerate.Utilize diameter less than about 1mm, make the binder free agglomerate less than about 5mm with less than the about reducing iron ore of 10mm.
The result of example 2 and example 3
Figure 10 is the graphic representation that illustrates according to the variation of the ultimate compression strength of the binder free agglomerate of example 2 and example 3.Square among Figure 10 is represented example 2.Circle among Figure 10 is represented example 3.In addition, in Figure 10 through utilizing least square method that the ultimate compression strength of binder free agglomerate is expressed as dotted line.The dotted line of below is represented example 2.The dotted line of top is represented example 3.
Shown in figure 10, when the diameter of reducing iron ore increased, the ultimate compression strength of binder free agglomerate reduced.In addition, when example 2 and example 3 were compared, the ultimate compression strength of the binder free agglomerate of the comparable example 3 of degree that the ultimate compression strength of the binder free agglomerate of example 2 reduces according to the increase of diameter was little according to the degree that the increase of diameter reduces.Therefore, under the little situation of forming pressure, the influence of the diameter of reducing iron ore is received in the not conference of ultimate compression strength of binder free agglomerate.
The diameter of reducing iron ore can be that about 1mm is to about 5mm.Under the situation of the diameter at reducing iron ore too small (for example, less than about 1mm), though the ultimate compression strength of binder free agglomerate is high, the efficient of the diameter of sorting reducing iron ore reduces.In addition, consume lot of energy.On the other hand, under the excessive situation of diameter, the filling ratio step-down of the mixture when making the binder free agglomerate in the recessed portion of forming roll.Therefore, the technology of manufacturing binder free agglomerate becomes unstable.
Example 4
The mixture that comprises dust and reducing iron ore through 1104 essentially identical a pair of forming roll extruding of a pair of forming roll among utilization and Fig. 1 and moulding.Here, the moisture content change in the reducing iron ore.The content of the moisture that changes is 0wt%, 3wt%, 6wt%, 9wt%, 12wt% and 17.5wt%.Measure the ultimate compression strength of binder free agglomerate.
Example 5
The mixture that comprises dust and reducing iron ore through 1104 essentially identical a pair of forming roll extruding of a pair of forming roll among utilization and Fig. 1 and moulding.Here, the moisture content change in the reducing iron ore.The content of the moisture that changes is 0wt%, 3wt%, 6wt%, 9wt%, 12wt% and 17.5wt%.Measure the ultimate compression strength of binder free agglomerate.In example 5, use with example 4 in the different reducing iron ore of reducing iron ore.
The result of example 4 and example 5
Figure 11 is the graphic representation that illustrates according to the variation of the ultimate compression strength of the binder free agglomerate of example 4 and example 5.Circle among Figure 11 is represented example 4.Square among Figure 11 is represented example 5.In addition, in Figure 11, utilize least square method that the ultimate compression strength of binder free agglomerate is expressed as dotted line.
Shown in figure 11, when the moisture content in the reducing iron ore increased, the ultimate compression strength of binder free agglomerate is linear to be reduced.When the moisture content in the reducing iron ore increased, mixture was attached to the surface of a pair of forming roll to reduce shaping characteristic.Therefore, moisture content is controlled to be is lower than about 6wt%.During greater than about 6wt%, the ultimate compression strength of binder free agglomerate reduces greatly in moisture content.
Example 6
The mixture that comprises dust and reducing iron ore through 1104 essentially identical a pair of forming roll extruding of a pair of forming roll among utilization and Fig. 1 and moulding.Here, the moisture content in the reducing iron ore is about 0wt%.Increase with the content of reducing iron ore blended dust.The content of the dust that increases is 0wt%, 20wt%, 40wt%, 60wt%, 80wt% and 100wt%.Measure the ultimate compression strength of binder free agglomerate.
Example 7
The mixture that a pair of forming roll 1104 essentially identical a pair of forming roll extruding among utilization and Fig. 1 and moulding comprise dust and reducing iron ore.Here, the dust content in the reducing iron ore is about 3wt%.Increase with the content of reducing iron ore blended dust.The content of the moisture that increases is 0wt%, 20wt%, 40wt%, 60wt%, 80wt% and 100wt%.Measure the ultimate compression strength of binder free agglomerate.
The result of example 6 and example 7
Figure 12 is the graphic representation that illustrates according to the variation of the ultimate compression strength of the binder free agglomerate of example 6 and example 7.Circle among Figure 12 is represented example 6.Square among Figure 12 is represented example 7.In addition, in Figure 12 through utilizing least square method that the ultimate compression strength of binder free agglomerate is expressed as dotted line.
Shown in figure 12, when the content of dust increased, the ultimate compression strength of binder free agglomerate can reduce.Content at dust is lower than under the situation of about 50wt%, the ultimate compression strength of the binder free agglomerate that can obtain to suit.Under the situation of content greater than about 50wt% of dust, the ultimate compression strength of binder free agglomerate can reduce greatly.Therefore, be not suitable for this binder free agglomerate is applied to the melting Gas-making Furnace.
utilize sludge to make the experiment of binder free agglomerate as raw material.
Analysis being used in Fig. 2 made the composition that comprises in sludge, dust and the reducing iron ore that the equipment of binder free agglomerate uses.The composition of sludge, dust and reducing iron ore is disclosed in the table 2 below.
Table 2
[table 2]
[table]
A small amount of sludge is reduced in the fluid bed reduction reactor drum.Reducing iron ore is by partly reduction.The composition of sludge is similar basically with the composition of reducing iron ore.The iron level of sludge and reducing iron ore is higher.Specifically, as shown in table 2, the iron level of sludge and reducing iron ore is respectively about 50.03wt% and about 73.39wt%.Owing to when iron ore is dried, collect dust, so dust can comprise and the essentially identical composition of the composition of iron ore.
As shown in table 2, sludge comprises the carbon of about 10.3wt%.Therefore, when under the state of cooling, making the binder free agglomerate, can in the binder free agglomerate, produce the crackle that causes by carbon.Therefore, the binder free agglomerate can have the relatively low ultimate compression strength of about 20kgf/p to about kgf/p.Therefore, sludge, dust and reducing iron ore are heated and mix, to make the binder free agglomerate.That is, the mixture that comprises sludge, dust and reducing iron ore is pushed and moulding, thereby make binder free agglomerate with suitable ultimate compression strength through a pair of forming roll 1104 essentially identical a pair of forming roll among utilization and Fig. 2.
Example 8
Manufacturing comprises the mixture of sludge, dust and reducing iron ore.Here, make the binder free agglomerate through the amount that changes the sludge that comprises in the mixture.Specifically, in the scope of the extremely about 80wt% of about 50wt%, change the amount of sludge, to make the binder free agglomerate.Measure the ultimate compression strength of binder free agglomerate.
The result of example 8
Figure 13 shows the variation according to the ultimate compression strength of the binder free agglomerate of the amount of the sludge in the example 8.
Shown in figure 13, when the amount of the sludge in being included in mixture increased, the ultimate compression strength of binder free agglomerate reduced gradually.Filled under the situation in the melting Gas-making Furnace at the binder free agglomerate, need suitably keep the ultimate compression strength of binder free agglomerate under comparatively high temps, to separate to prevent the binder free agglomerate.Therefore, the amount of the sludge in the mixture is retained as and is lower than about 55wt%.Amount at sludge is higher than under the situation of about 55wt%, and the ultimate compression strength of agglomerate can reduce, thereby agglomerate can be inappropriate in the melting Gas-making Furnace and using.
Example 9
Manufacturing comprises the mixture of sludge, dust and reducing iron ore.Here, the ratio of amount that is included in amount and the dust of the reducing iron ore in the mixture through change is made the binder free agglomerate.Specifically, when making the binder free agglomerate, the ratio of amount that is included in amount and the dust of the reducing iron ore in the mixture changes to about 1/2 scope about 1/4.Measure the ultimate compression strength of binder free agglomerate.
The result of example 9
Figure 14 is the graphic representation that illustrates according to the variation of the ultimate compression strength of the binder free agglomerate of the ratio of the amount of amount that is included in the reducing iron ore in the mixture in the example 9 and dust.Surplus is the sludge in the example 9.
Shown in figure 14, when the ratio of the relative dust of reducing iron ore increased, the ultimate compression strength of binder free agglomerate increased.Fill at the binder free agglomerate under the situation of melting Gas-making Furnace, need suitably keep the ultimate compression strength of binder free agglomerate under comparatively high temps, to separate to prevent the binder free agglomerate.The ultimate compression strength of binder free agglomerate can be not less than about 80kgf/p.Therefore, can keep the amount of reducing iron ore so that the amount of the amount of reducing iron ore and dust is basic identical.That is, the ratio with the amount of reducing iron ore and dust remains about 1.
Example 10
Manufacturing comprises the mixture of sludge, dust and reducing iron ore.Heating temperature through changing mixture is made the binder free agglomerate.Specifically, change Heating temperature to about 400 ℃ scope at about 170 ℃ and make the binder free agglomerate.Measure the ultimate compression strength of binder free agglomerate.
The result of example 10
Figure 15 is the graphic representation that illustrates according to the variation of the ultimate compression strength of the binder free agglomerate of the Heating temperature of the mixture in the mixing tank in the example 10.
Shown in figure 15, the ultimate compression strength of binder free agglomerate increases.Fill under the situation in the melting Gas-making Furnace at the binder free agglomerate, then need suitably keep the ultimate compression strength of binder free agglomerate under comparatively high temps, to separate to prevent the binder free agglomerate.Therefore, can be through obtaining suitable ultimate compression strength to about 400 ℃ temperature heated mixt with about 350 ℃.Under being lower than about 350 ℃ temperature during thermally treated mixture, owing to enough cohesive forces are not provided from mixture, so the ultimate compression strength of binder free agglomerate is less.In addition, under with the situation that is higher than about 400 ℃ of thermally treated mixtures, because mixture is attached to a pair of forming roll, so can not form the binder free agglomerate.
Example 11
Manufacturing comprises the mixture of dust and sludge.The mixture that a pair of forming roll 1104 essentially identical a pair of forming roll extruding among utilization and Fig. 2 and moulding comprise dust and sludge.Here, the forming pressure of said a pair of forming roll is about 10t/cm, and mold temperature is about 400 ℃.When making mixture, the amount that changes dust makes that the amount of dust is about 80wt%, 60wt%, 40wt% and 0wt%.The amount of the sludge corresponding with the amount of dust is controlled as and makes the amount of sludge become 20wt%, 40wt%, 60wt% and 100wt%.Utilize this mixture forming binder free agglomerate.Measure the ultimate compression strength of binder free agglomerate.
The result of example 11
Figure 16 is the graphic representation that illustrates according to the variation of the ultimate compression strength of the binder free agglomerate of the amount of the amount of the dust in the example 11 and sludge.
Shown in figure 16, when the amount of dust reduced, the ultimate compression strength of binder free agglomerate reduced.Yet when the amount of sludge was higher than about 60wt%, the ultimate compression strength of binder free agglomerate raise again.The ultimate compression strength of binder free agglomerate is no more than 100kgf/p.
Filled under the situation in the melting Gas-making Furnace at the binder free agglomerate, need suitably keep the ultimate compression strength of binder free agglomerate under comparatively high temps, to separate to prevent the binder free agglomerate.The ultimate compression strength of binder free agglomerate can surpass about 80kgf/p.Therefore, like with dashed lines indication, the amount of the dust in the mixture at about 70wt% to the about scope between the 100wt%.Amount at dust is lower than under the situation of about 70wt%, and the ultimate compression strength of binder free agglomerate meeting deterioration makes the binder free agglomerate to be inappropriate for and is used for the melting Gas-making Furnace.
Example 12
Manufacturing comprises the mixture of reducing iron ore and sludge.The mixture that a pair of forming roll 1104 essentially identical a pair of forming roll extruding among utilization and Fig. 2 and moulding comprise reducing iron ore and sludge.Here, the forming pressure of said a pair of forming roll is about 10t/cm, and mold temperature is about 400 ℃.When making mixture, the amount that changes reducing iron ore makes that the amount of reducing iron ore is about 100wt%, 80wt%, 60wt%, 40wt%, 20wt% and 0wt%.The amount of the sludge corresponding with the amount of reducing iron ore is controlled as and makes the amount of sludge become 0wt%, 20wt%, 40wt%, 60wt%, 80wt% and 100wt%.Utilize this mixture forming binder free agglomerate.Measure the ultimate compression strength of binder free agglomerate.
The result of example 12
Figure 17 is the graphic representation that illustrates according to the variation of the ultimate compression strength of the binder free agglomerate of the amount of the amount of the reducing iron ore in the example 12 and sludge.
Shown in figure 17, when the amount of reducing iron ore reduced, the ultimate compression strength of binder free agglomerate reduced.In addition, be lower than under the situation of about 60wt% in the amount of reducing iron ore, the ultimate compression strength of binder free agglomerate is similar basically.Filled under the situation in the melting Gas-making Furnace at the binder free agglomerate, need suitably keep the ultimate compression strength of binder free agglomerate under comparatively high temps, to separate to prevent the binder free agglomerate.The ultimate compression strength of binder free agglomerate can be higher than about 80kgf/p.Therefore, like with dashed lines indication, the amount of the reducing iron ore in the mixture can be at about 70wt% to the about scope between the 100wt%.Amount at reducing iron ore is lower than under the situation of about 70wt%, and the ultimate compression strength of binder free agglomerate meeting deterioration makes the binder free agglomerate to be inappropriate for and is used for the melting Gas-making Furnace.
Aforementioned is to explanation of the present invention, and should not be understood that to limit the present invention.Though described some embodiments of the present invention, do not break away from itself under the situation of novel teachings of the present invention and advantage, those skilled in the art expect the possible many modifications to embodiment easily.Therefore, these are revised and also are intended to be included in as in the scope of the present invention that limits in claims.Therefore, it should be understood that aforementioned is to explanation of the present invention, is confined to disclosed specific embodiment and should not be construed as, and the modification of disclosed embodiment and other embodiment intention are included in the scope of claims.The present invention is defined by the claims, and the equivalent of claims comprises therewith.
Claims (33)
1. method of making the binder free agglomerate, this method may further comprise the steps:
Provide through utilizing and do the dust that collection method is collected from exhaust gas discharged when iron ore is dried;
Provide from the reducing iron ore of the equipment exhausting that is used to make molten iron, the equipment that is used to make molten iron comprises reduction furnace that the reduced iron that obtains through the exsiccant iron ore through reduction is provided and makes the melting Gas-making Furnace of molten iron through smelting reduction iron;
The sludge that is used to make the equipment exhausting of molten iron from said is provided;
Provide through drying and mix the mixture that at least two kinds of raw materials from the group of being made up of said dust, said reducing iron ore and said sludge, selecting form;
Make mixture forming form the binder free agglomerate through not adding sticker.
2. the method for claim 1, wherein in the step of reducing iron ore is provided, reducing iron ore is being carried out after drying and the size separation reducing iron ore being provided.
3. method as claimed in claim 2, wherein, before reducing iron ore was carried out drying and size separation, reducing iron ore comprised the moisture in the scope of 10wt% to 30wt%.
4. method as claimed in claim 2, wherein, the reduction ratio of reducing iron ore is 30% to 60%.
5. method as claimed in claim 4 wherein, is carried out size separation to reducing iron ore, reducing iron ore is divided into thick reducing iron ore and smart reducing iron ore, thick reducing iron ore is filled into the melting Gas-making Furnace.
6. method as claimed in claim 5, wherein, the diameter of thick reducing iron ore is greater than 8mm.
7. the method for claim 1, wherein in the step that forms the binder free agglomerate, when making mixture forming, forming pressure is 6t/cm to 10t/cm.
8. the method for claim 1, wherein in the step of mixture is provided, the amount of the moisture in the reducing iron ore is 0 to 6wt%.
9. the method for claim 1, wherein in the step of mixture is provided, the diameter of reducing iron ore is 1mm to 5mm.
10. the method for claim 1, wherein in the step of mixture is provided, the amount of mixing the dust of species is 0 to 50 wt%.
11. the method for claim 1, wherein in the step of reducing iron ore is provided, reducing iron ore is provided from reduction furnace.
12. the method for claim 1; Wherein, In the step of reducing iron ore is provided; The equipment that is used to make molten iron comprises that also foundary weight forms device, foundary weight form device with reduction furnace with the melting Gas-making Furnace is connected to each other and will be fed to the melting Gas-making Furnace from the foundary weight that the reduced iron of reduction furnace discharging forms through extruding, from foundary weight formation device provisioning reducing iron ore.
13. the method for claim 1, wherein in the step that forms the binder free agglomerate, the ultimate compression strength of binder free agglomerate is 80kgf/p to 100kgf/p.
14. the method for claim 1, wherein in the step of sludge is provided, after sludge is dried and is broken, sludge is provided.
15. method as claimed in claim 14, wherein, before sludge was dried also fragmentation, sludge comprised the moisture of 30wt% to 40wt%.
16. the method for claim 1, wherein in the step of mixture is provided, form mixture through mixing dust, reducing iron ore and sludge, the amount of sludge is 0 to 55wt% in the mixture.
17. method as claimed in claim 16, wherein, the amount of reducing iron ore is identical with the amount of dust.
18. the method for claim 1, wherein in the step of mixture is provided, form mixture through mixing dust and sludge, the content of dust is between 70wt% to 100wt% in the mixture.
19. the method for claim 1, wherein in the step of mixture is provided, form mixture through mixing reducing iron ore and sludge, the content of reducing iron ore is between 70wt% to 100wt% in the mixture.
20. the method for claim 1, wherein in the step of mixture is provided, mixture is heat-treated with 350 ℃ to 400 ℃ temperature.
21. an equipment that is used to make the binder free agglomerate, this equipment comprises:
The dust hopper is collected the dust of dust and store collected through utilizing dried collection mode from exhaust gas discharged when the dry iron ore;
The reducing iron ore hopper; Storage is from the reducing iron ore of the equipment exhausting that is used to make molten iron, and the said equipment that is used to make molten iron comprises reduction furnace that the reduced iron that obtains through the exsiccant iron ore through reduction is provided and makes the melting Gas-making Furnace of molten iron through smelting reduction iron;
The sludge hopper stores the sludge that is used to make the equipment exhausting of molten iron from said;
Mixing tank is connected to dust hopper, reducing iron ore hopper and sludge hopper, and dry at least two kinds of raw materials from the group of being made up of said dust, said reducing iron ore and said sludge, selecting with mixing form mixture;
A pair of forming roll makes mixture forming form the binder free agglomerate.
22. equipment as claimed in claim 21, wherein, mixing tank comprises:
Housing;
Rotating member rotates in housing.
23. equipment as claimed in claim 22, wherein, rotating member is to extend the spiral member in housing, to rotate along pre-determined direction.
24. equipment as claimed in claim 21, said equipment also comprises:
Moisture eliminator, dry sludge;
Destroyer is connected to each other moisture eliminator and sludge warehouse and broken sludge, and wherein, the sludge warehouse stores broken sludge.
25. equipment as claimed in claim 24, wherein, moisture eliminator is a rotary kiln.
26. equipment as claimed in claim 21, said equipment also comprises:
Moisture eliminator, dry reducing iron ore;
The size separation device; Moisture eliminator and reducing iron ore warehouse are connected to each other; And to carrying out size separation through the exsiccant reducing iron ore being divided into smart reducing iron ore and thick reducing iron ore through the exsiccant reducing iron ore, wherein, former iron ore warehouse stores smart reducing iron ore.
27. equipment as claimed in claim 26, wherein, moisture eliminator is a rotary kiln.
28. equipment as claimed in claim 26 wherein, fills into the melting Gas-making Furnace with thick reducing iron ore.
29. equipment as claimed in claim 21, wherein, reduction furnace is fed to the reducing iron ore hopper with reducing iron ore.
30. equipment as claimed in claim 21 wherein, is heat-treated mixture with 350 ℃ to 400 ℃ temperature.
31. equipment as claimed in claim 21, wherein, the equipment that is used to make molten iron comprises also reduction furnace and melting Gas-making Furnace foundary weight connected to one another is formed device that reducing iron ore forms device provisioning to the reducing iron ore hopper from foundary weight.
32. equipment as claimed in claim 21, wherein, said a pair of forming roll makes said mixture forming with the forming pressure of 6t/cm to 10t/cm.
33. equipment as claimed in claim 30, wherein, reduction furnace is fluid bed reduction reactor drum or packed-bed reactor.