CN101898206B - Surface processing method for metal plate - Google Patents
Surface processing method for metal plate Download PDFInfo
- Publication number
- CN101898206B CN101898206B CN2009100338197A CN200910033819A CN101898206B CN 101898206 B CN101898206 B CN 101898206B CN 2009100338197 A CN2009100338197 A CN 2009100338197A CN 200910033819 A CN200910033819 A CN 200910033819A CN 101898206 B CN101898206 B CN 101898206B
- Authority
- CN
- China
- Prior art keywords
- groups
- rolls
- group
- rollers
- roller
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a surface processing method for a metal plate, which consists of three processing steps of flattening, polishing and drying. For the flattening step, the metal plate to be processed is put on a flattener consisting of a plurality of rollers which are parallel up and down and is subjected to assembly line operation such as flattening, polishing, drying and the like, wherein five groups (1, 3, 5, 7 and 9) of rollers are transmission rollers; a group 2 of upper roller, a group 4 of lower roller, a group 6 of upper roller and a group 8 of lower roller are grinding rollers; a group 2 of lower roller and a group 6 of lower roller are carrier rollers; a group 4 of upper roller and a group 8 of upper roller are compression rollers; and three groups (10, 11 and 12) of rollers are water sucking rollers. The processed metal plate has the advantages of shortening the operating time, improving operating efficiency, along with no brush marks, water spots and colored patches on the surface, uniform color and no pollution on atmosphere.
Description
Technical field: the method for surface finish that the present invention relates to a kind of sheet metal.
Background technology: traditional metal surface processing method generally adopts pickling, clear water rinsing, water wiper, oven dry, dried wiper, finish rolling.Product after the processing because wire brush surface silking is darker, is easy to generate sour spot after generating water spots, pickling easily; Also can produce phenomenons such as baking is not passed through, oxidation; Manufacturing procedure is loaded down with trivial details in addition, and the turnover flow process is many, can't overcome scuffing, the pressure point phenomenon on surface; Dried simultaneously wiper is prone to produce dust, and environment is polluted.
Summary of the invention: the object of the invention is exactly the method for surface finish that a kind of sheet metal will be provided, existing defective when it can overcome above design effectively.The objective of the invention is to realize like this; A kind of method of surface finish of sheet metal; It is made up of straight, polishing, three processing portion branch of oven dry, it is characterized in that: described straight, and be the sheet metal of being processed to be put into adopt on the some flatteners that parallel roll is formed up and down; Frequency control makes top and bottom rolls adjust synchronously; Described polishing; Be that the sanding machine that adopts 12 groups of upper and lower rolls to form polishes sheet material, wherein, 1,3,5,7,9 totally 5 groups be live-roller; 2 groups of top rolls, 4 groups of lower rolls, 6 groups of top rolls, 8 groups of lower rolls are set to mixing roll; 2 groups of lower rolls, 6 groups of lower rolls are set to carrying roller, and 4 groups of top rolls, 8 groups of top rolls are set to pressure roller, 10,11,12 totally 3 groups be set to suction roll; Described oven dry adopts heating tube to heat, and according to the thickness of sheet material temperature is controlled in 300～400 ℃ of scopes.Processing method of the present invention, after handling metal material, fine and smooth bright and clean, the no brush mark in surface, no water spots, color spot, color even is consistent, can any pollution not arranged to atmosphere, has shortened the working time, has improved operating efficiency.
The specific embodiment: the method for surface finish of a kind of sheet metal of the present invention; It is made up of straight, polishing, three processing portion branch of oven dry; It is characterized in that: described straight; Be the sheet metal of being processed to be put into adopt on the some flatteners that parallel roll is formed up and down, frequency control makes top and bottom rolls adjust synchronously; Described polishing; Be that the sanding machine that adopts 12 groups of upper and lower rolls to form polishes sheet material, wherein, 1,3,5,7,9 totally 5 groups be live-roller; 2 groups of top rolls, 4 groups of lower rolls, 6 groups of top rolls, 8 groups of lower rolls are set to mixing roll; 2 groups of lower rolls, 6 groups of lower rolls are set to carrying roller, and 4 groups of top rolls, 8 groups of top rolls are set to pressure roller, 10,11,12 totally 3 groups be set to suction roll; Described oven dry adopts heating tube to heat, and according to the thickness of sheet material temperature is controlled in 300～400 ℃ of scopes.During practical implementation, straight is to adopt top 6, following 7 totally 13 straight sheet metals of flattener that the roll that is parallel to each other is formed, frequency control; The assurance up-down rollers is adjusted synchronously; Polishing is to adopt special-purpose sanding machine, and sanding machine is that 12 groups of up-down rollers are formed, 1,3,5,7,9 totally 5 groups be live-roller; 2 groups of top rolls, 4 groups of lower rolls, 6 groups of top rolls, 8 groups of lower rolls are set to mixing roll; 2 groups of lower rolls, 6 groups of lower rolls are set to carrying roller, and 4 groups of top rolls, 8 groups of top rolls are set to pressure roller, 10,11,12 totally 3 groups be set to suction roll.Can carry out the gap of frequency control and control live-roller according to the thickness of sheet metal, it is consistent to guarantee that sheet material is handled color and luster, and transmission mechanism adopts run-in synchronism, and mixing roll adopts single driving.Grinder grinds brush roll and adopts nylon yarn adding corundum composite to process, and can not cause scratch to metal material, can thoroughly remove the oxide on surface of metal material.Suction roll adopts the foaming engineering material, can fully absorb the water mark of plate surface.Oven dry is to adopt energy saving and environment friendly heating tube to replace old-fashioned resistance wire heating, and temperature is controlled in 300～400 ℃ of scopes, and transmission has adopted pig iron roller to drive, and frequency control as required.
Claims (1)
1. the method for surface finish of a sheet metal; It is made up of straight, polishing, three processing portion branch of oven dry; It is characterized in that: described straight; Be the sheet metal of being processed to be put into adopt on the some flatteners that parallel roll is formed up and down, frequency control makes top and bottom rolls adjust synchronously; Described polishing; Be that the sanding machine that adopts 12 groups of upper and lower rolls to form polishes sheet material, wherein, 1,3,5,7,9 totally 5 groups be live-roller; 2 groups of top rolls, 4 groups of lower rolls, 6 groups of top rolls, 8 groups of lower rolls are set to mixing roll; 2 groups of lower rolls, 6 groups of lower rolls are set to carrying roller, and 4 groups of top rolls, 8 groups of top rolls are set to pressure roller, 10,11,12 totally 3 groups be set to suction roll; Described oven dry adopts heating tube to heat, and according to the thickness of sheet material temperature is controlled in 300～400 ℃ of scopes.