CN101884323A - Oxygen reduction and humidity control curing agent for tobacco leaf storage - Google Patents
Oxygen reduction and humidity control curing agent for tobacco leaf storage Download PDFInfo
- Publication number
- CN101884323A CN101884323A CN2010101050156A CN201010105015A CN101884323A CN 101884323 A CN101884323 A CN 101884323A CN 2010101050156 A CN2010101050156 A CN 2010101050156A CN 201010105015 A CN201010105015 A CN 201010105015A CN 101884323 A CN101884323 A CN 101884323A
- Authority
- CN
- China
- Prior art keywords
- curing agent
- agent
- wet curing
- controlled atmosphere
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an oxygen reduction and humidity control curing agent for tobacco leaf storage, comprising a controlled-atmosphere curing agent and a humidity controlled curing agent which are in coordinated use with a use ratio range of (2-10):1. The controlled-atmosphere curing agent comprises the following components: 40-80% of reduced iron powder or pyrite powder, 1-8% of calcium oxide, 0.1-2% of mould proof assistant, 10-21% of activated carbon, 0-12% of sodium chloride, 1-15% of water absorbent, 3-15% of pearlite, 0.1-5% of first water retaining agent, 2-10% of diatomite and 0-10% of water. The humidity controlled curing agent comprises the following components: 30-60% of drier, 2-30% of second water retaining agent and 5-30% of pearlite. The curing agent for tobacco leaf storage can enable the oxygen reduction process to be mild and simultaneously improve dehumidification speed. The invention also provides a manufacturing method of the oxygen reduction and humidity control curing agent for tobacco leaf storage.
Description
Technical field
The invention belongs to the tobacco storage technical field, relate to a kind of tobacco leaf storage sealing compound.
Background technology
Seal ultralow oxygen (Ultra low-oxygen ULO) storage practice and come from Britain, the principle of this storage method is meant by the oxygen under the storage environment is controlled at below 2%, thereby the respiratory activity of stored article is suppressed, substantially be in resting state, breathe the nutriment consumed and reduce, so the nutrient component of article and quality can be kept preferably.The environment of ultralow oxygen also can suppress and kill microorganism and the plant pest in the storage environment simultaneously.
Seal ultralow oxygen storage practice and be widely used in fields such as the article that need store in a warehouse such as fruit, grain, tobacco.In the tobacco field, because need being deposited in by certain requirement, tobacco leaf carries out natural alcoholization in the warehouse, by control temperature, humidity, under hypoxia, refine, the alcoholization time is generally 1-3, at present main what use is that iron is that oxygen falls in oxygen absorbent, but this oxygen absorbent seals in the ultralow oxygen storage at tobacco leaf, has following problem:
1. it is too fast to fall oxygen.Present tobacco leaf air conditioning agent all is to adopt efficiently iron system to fall the oxygen agent to fall oxygen, and this principle of falling the oxygen agent is to utilize reduced iron powder oxidized and consume oxygen, thereby reaches the purpose of falling oxygen.This oxygen mode of falling belongs to an exothermic reaction on thermodynamics, owing to fall oxygen excessive velocities (generally oxygen concentration just drops to below 2% within 15 days), liberated heat makes that the interior local temperature of cigarette buttress is too high, can cause the temperature at tobacco leaf center can not distributed when serious, phenomenons such as tobacco leaf goes rancid, heartburn, knot plate occur, make tobacco leaf forfeiture use value.
2. it is slow to fall wet speed.Tobacco leaf storage has an optimal spatial relative moisture scope usually, and general requirement of cigar mill remains on the relative moisture in tobacco leaf storage space in the scope of 50%-65% at present, and existing air conditioning agent can not be controlled the relative moisture of environment.If tobacco leaf is in the environment of high humidity high temperature (such as southern summer) for a long time, owing to have mould in the tobacco leaf, and mould very easily growth under the condition of high humidity high temperature, thereby cause tobacco mildew, forfeiture use value.And that wet speed falls in the medicament that uses at present is slow, therefore probably causes tobacco mildew.Because existing tobacco leaf air conditioning agent all is will have the material that falls oxygen, falls wet function simultaneously to mix and make, this makes air conditioning agent fall wet slow-footed shortcoming and becomes more obvious.
3. tobacco leaf the dewfall phenomenon occurs in the sealing storage.If the phenomenon of dewfall appears in tobacco leaf, then illustrate in the local local humidity of dewfall too high, thereby improved the probability that tobacco leaf goes mouldy, the musty that tobacco mildew produced can influence whole cigarette buttress, and the quality of whole cigarette buttress is descended.
4. the CO of existing tobacco leaf air conditioning agent to producing in the tobacco mellowing process
2Absorb less, CO
2Excessive concentration the alcoholization of tobacco leaf is suppressed (with CO
2The rising of concentration, the alcoholization reaction balance is destroyed, and alcoholization is suppressed), thereby the continuation that is unfavorable for tobacco leaf is refined.
The packing of existing controlled atmosphere sealing compound mainly contains following two kinds of forms: a kind of is to adopt the brown paper packaging bag, and another kind is to adopt plastic film to pack, and irregularly has several holes on the plastic film.For the air conditioning agent of packing with brown paper, it falls the oxygen excessive velocities, and the dewfall phenomenon easily takes place.And for the controlled atmosphere sealing compound of the plastic film packaging with random punching number, it falls oxygen speed may be too fast, also may be slow excessively: it falls the oxygen excessive velocities more for a long time when the punching number, easily dewfall; And the punching number more after a little while, and it is slow excessively to fall oxygen speed, can not in 30 days oxygen concentration be reduced to below 2%, and these all might damage the quality of tobacco leaf.
Summary of the invention
Technical problem to be solved by this invention is at the above-mentioned deficiency of existing in prior technology, provide a kind of making to fall the oxygen process and tend towards stability, and improve the tobacco leaf storage fall wet speed simultaneously and fall oxygen, control wet curing agent and preparation method thereof, be used for tobacco leaf storage, make tobacco mellowing stablize, reduce tobacco mildew, improve quality of tobacco.
Solving the technical scheme that problem of the present invention adopted is that oxygen falls in this tobacco leaf storage, control wet curing agent comprises controlled atmosphere sealing compound and the control wet curing agent that cooperatively interacts and use, and both operating weight proportions are (2-10): 1,
The component of controlled atmosphere sealing compound comprises:
Reduced iron powder or pyrite dust 40-70%
Mildew-resistant auxiliary agent 0.1-5%
Active carbon 10-21%
Sodium chloride 0-12%
Water absorbing agent 1-15%
Calcium oxide 1-8%
Perlite or wood chip or carbonization rice hulls 3-15%
The first water-loss reducer 0.1-5%
Diatomite 2-10%
Water 0-10%
More than each components contents be weight percent content;
Be divided into two kinds of compositions for the control wet curing agent that is used with the controlled atmosphere sealing compound, i.e. A type composition and Type B composition, the both can be used with the controlled atmosphere sealing compound respectively,
The component of control wet curing agent is an A type composition, comprising:
Desiccant 30-60%
The second water-loss reducer 2-30%
Perlite 5-30%
Perhaps control the component or the Type B composition of wet curing agent, comprising:
Powder 60-70%
Coupling agent 3-5%
Low density polyethylene (LDPE) 15-20%
The solid moisture absorbent 10-15% of microporosity silica gel
Described powder is: polyacrylic acid-marine alga sodium macromolecule resin
Described coupling agent is: starch
More than each components contents be weight percent content.
Wherein, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound can adopt the fumaric acid methyl esters, perhaps adopts sodium sulphite; Water absorbing agent can adopt calcium chloride, calcium sulphate, anhydrous magnesium sulfate, anhydrous sodium sulfate, silica gel or zinc chloride; First water-loss reducer can adopt polyacrylacid ester compounds.
In the controlled atmosphere sealing compound, reduced iron powder or pyrite dust are the main medicaments that carries out oxygen uptake, adopt 80-120 order reduced iron powder or pyrite dust; Active carbon is as electrode material; The steam that water absorbing agent is used for absorbing environmental offers medicament (being reduced iron powder or pyrite dust) and carries out oxidation reaction; Calcium oxide is as suction and inhale CO
2With; Anhydrous magnesium sulfate is also as water absorbing agent usefulness, and perlite or wood chip or carbonization rice hulls, first water-loss reducer, diatomite three are mixed for preserving moisture, and help the absorption of oxygen simultaneously.The water that adds 0-10% is to help reduced iron powder and oxygen reacts.If tobacco leaf is in the higher space of relative moisture, also can not add entry, utilize the moisture in space that oxidation reaction can take place.
Preferably, the calcium oxide that also comprises 10-50% in the control wet curing agent A type composition.
Preferably, in the controlled atmosphere sealing compound,, can add the sodium chloride of 0-12% in order to improve electrical conductivity because sodium chloride can improve the electrical conductivity of whole controlled atmosphere sealing compound, thereby strengthened the controlled atmosphere sealing compound the oxygen effect falls.
Desiccant in the control wet curing agent A type composition can be alkaline earth metal salt desiccant or silica, anhydrous cupric sulfate, anhydrous zinc sulfate or anhydrous sodium sulfate, and alkaline earth metal salt desiccant is calcium chloride, calcium sulphate, anhydrous magnesium sulfate; Second water-loss reducer is the agent of solid constant humidity, adopts the special-purpose constant humidity agent of commercially available tobacco, for the magnesium sulfate that will have equilibrium humidity is mediated the product that makes in the polyacrylamide, can buy on the market, has the effect of regulating relative moisture.
The desiccant and second water-loss reducer play regulation and control relative moisture jointly; Perlite plays retaining, flows out after desiccant from forming saturated solution preventing; Calcium oxide is used for suction and absorbs CO
2, to help the continuation alcoholization of tobacco leaf.
Powder is as the moisture usefulness that absorbs the space in the control wet curing agent Type B composition, and coupling agent plays adhesive effect, prevents to scatter after the powder suction, and the solid moisture absorbent of low density polyethylene (LDPE), microporosity silica gel is used as the water absorbing properties that increases medicament.
The preparation method of oxygen, control wet curing agent falls in tobacco leaf storage of the present invention, be earlier controlled atmosphere sealing compound and control wet curing agent to be made separately respectively, again with controlled atmosphere sealing compound and control wet curing agent in (2-10): 1 part by weight scope comes into operation or directly is respectively charged in the packaging bag in this ratio, is convenient to the user and directly uses.
The preparation method of controlled atmosphere sealing compound preparation method and control wet curing agent is as described below respectively:
A kind of preparation method of controlled atmosphere sealing compound, it comprises the following steps:
(1) reduced iron powder, mildew-resistant auxiliary agent, active carbon, water absorbing agent, calcium oxide, perlite or wood chip or carbonization rice hulls, first water-loss reducer, diatomite, sodium chloride pressed column weight amount ratio take by weighing after, mix:
Reduced iron powder or pyrite dust 40-80%
Mildew-resistant auxiliary agent 0.1-5%
Active carbon 10-21%
Water absorbing agent 1-15%
Calcium oxide 1-8%
Perlite or wood chip or carbonization rice hulls 3-15%
The first water-loss reducer 0.1-5%
Diatomite 2-10%
Sodium chloride 0-12%
(2) above-mentioned each mixture is stirred.
Preferably, in step (1), described mildew-resistant auxiliary agent can adopt fumaric acid methyl esters or sodium sulphite.
Preferably, in step (2), after each mixture is stirred, can add the water of 0-10% again, and then stir.
Further preferably, also include step (3) in the preparation method of controlled atmosphere sealing compound, promptly
(3) the A type controlled atmosphere sealing compound for preparing is loaded in the inner wrapping PE plastic film bag of a size for the mm of (100-180) mm * (150-250), punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, and the punching number is 100-1500, seals again; Then, 6-15 small package bag is loaded in the big packing PE plastic film bag, sealing is preserved.
A kind of preparation method of controlling the wet curing agent: be divided into two kinds of compositions for the control wet curing agent that is used with the controlled atmosphere sealing compound, be A type composition and Type B composition, both can be used with the controlled atmosphere sealing compound respectively, and the preparation method of therefore controlling the wet curing agent comprises the following steps:
(1) A type composition material being pressed column weight amount ratio takes by weighing:
Desiccant 30-60%
The second water-loss reducer 2-40%
Perlite 5-40%
Described second water-loss reducer is the agent of solid constant humidity, adopts the special-purpose constant humidity agent of commercially available tobacco, for the magnesium sulfate that will have equilibrium humidity is mediated the product that makes in the polyacrylamide, can buy on the market, has the effect of regulating relative moisture.
Or the Type B composition material pressed column weight amount ratio take by weighing:
Powder 60-70%
Coupling agent 3-5%
Low density polyethylene (LDPE) 15-20%
The solid moisture absorbent 10-15% of microporosity silica gel
Described powder is: polyacrylic acid-marine alga sodium macromolecule resin
Described coupling agent is: starch
(2) said mixture is mixed.
Preferably, also can include the calcium oxide of 10-50% in the control wet curing agent A type composition.
Preferably, also include step (3) in the preparation method of control wet curing agent, that is: (3) the control wet curing agent that will prepare is contained in size in the small package bag that (150-250) mm * (250-350) nonwoven of mm is made, again small package bag is sealed, then 7-15 small package bag is loaded in the big packing PE plastic film bag, it is to lose efficacy because of absorbing airborne moisture for the control wet curing agent that prevents to prepare that small package bag is packed in the big packing PE plastic film bag, preserves to help sealing.
The plastic film packaging bag that the permeability of the small package bag that nonwoven is made is better than punching, thereby more help controlling the wet curing agent and bring into play its hygroscopic effect.
When controlled atmosphere sealing compound and control wet curing agent are used, controlled atmosphere sealing compound and control wet curing agent be the form with small package bag be interspersed on the smoke box or the slit of smoke box and smoke box in.
In use, can with the controlled atmosphere sealing compound of small package bag packing and control wet curing agent by weight proportion scope be (2-10): 1 together is placed in the tobacco leaf storage space, evenly puts to get final product.
Wherein, the controlled atmosphere sealing compound mainly is to fall oxygen, fall wet process at the tobacco leaf that needs the long period to store maintenance under closed environment, thus by tobacco leaf is carried out insect protected, the alcoholization that helps tobacco leaf is handled in mildew-resistant; Control wet curing agent is at needing the long-time tobacco leaf that stores maintenance to carry out humidity regulation under closed environment in maintenance processes, and is mouldy in maintenance processes, rotten to prevent tobacco leaf, can also absorb the CO that produces in the tobacco mellowing process with time control wet curing agent
2, eliminate CO
2To the negative interaction of tobacco mellowing generation, to help the alcoholization of remaining valid of tobacco leaf.
Controlled atmosphere sealing compound of the prior art generally just dropped to concentration of oxygen below 2% within 15 days, and use tobacco leaf storage of the present invention to fall oxygen, control wet curing agent, in 15-30 days scope, oxygen concentration is dropped to below 2%, it is mild to fall the oxygen process, can not produce the rapid rising of temperature, this has positive effect to promoting quality of tobacco.
Oxygen falls in tobacco leaf storage of the present invention, control wet curing agent can make the oxygen concentration under the tobacco leaf storage environment reduce to below 2% in 15-30 days, the relative moisture of environment can be controlled in 7-15 days in the scope of 50%-65% of appointment, the problem of solved tobacco leaf easily insect pest in storage, going mouldy, the while also helps improving the quality of tobacco leaf.
The present invention separately makes and packing by the controlled atmosphere sealing compound and the control wet curing agent of tobacco leaf storage being fallen in oxygen, the control wet curing agent, be about to fall oxygen and fall wet function separately, make and fall the oxygen process and tend towards stability more, it is higher to fall wet efficient, thereby has further improved the quality of tobacco leaf in storage.
The advantage that oxygen, control wet curing agent fall in tobacco leaf storage of the present invention is as follows:
1. fall oxygen, fall wet process and separate: the present invention separately makes controlled atmosphere sealing compound (falling the oxygen agent) and control wet curing agent (falling humectant) and packing, makes to fall oxygen, fall wet operating process and become more flexible, and falls oxygen and fall the process of wetting and do not disturb mutually.Adjust the usage ratio of controlled atmosphere sealing compound and control wet curing agent easily, to help the tobacco leaf of different alcoholization phase: the initial stage tobacco leaf that the new cigarette of coming in for firm purchase promptly refines, because the aqueous vapor that the tobacco leaf respiration produces is bigger, the consumption of control wet curing agent wants big; For the tobacco leaf that is used for takeing in two to three months, because the relative stage of stable development of tobacco mellowing, the consumption of control wet curing agent can be slightly little, and the ratio of regulating control wet curing agent is to reach the purpose of maintenance tobacco leaf better.
2. wet efficient height falls: can in the short period of time the relative moisture in the cigarette buttress be reduced to 50%-65%.
3. packing method uniqueness: at present, existing controlled atmosphere sealing compound mainly is the packaging bag of adopting brown paper to make, or adopt the plastic film bag of unqualified concrete punching quantity, the oxygen speed of falling can not be effectively controlled in this class packaging bag, and the employing of controlled atmosphere sealing compound has the PE plastic foil of strict punching quantity to make small package bag among the present invention, with the oxygen speed of falling of effective control controlled atmosphere sealing compound, greatly reduce the possibility of steam dewfall in the cigarette buttress.And test result proves do not have the dewfall phenomenon to take place in the cigarette buttress in the experimental test phase.
4. environmental protection: with respect to existing phosphine fumigation killing method, oxygen falls in tobacco leaf storage of the present invention, control wet curing agent can not produce virulent material in the process of carrying out desinsection and mildew-resistant, therefore falling oxygen, falling in the wet process and can not pollute tobacco leaf, can not cause environmental pollution.
5. the impairment of guaranteeing the quality: can suppress microbial reproduction in the tobacco leaf, slow down the oxidation reaction in the tobacco leaf, reduce water loss, keep the quality of tobacco leaf, thereby guarantee the quality safety of tobacco leaf.
6. oxygen falls, to fall wet effective duration long: for the new tobacco leaf of 1000kg (refining the initial stage tobacco leaf), the usage amount scope that needs storage to fall the controlled atmosphere sealing compound of oxygen is 5-10kg, control wet curing agent usage amount scope is 0.5-2.5kg, the general sustainable 1.5-2 year of the term of validity, if this tobacco leaf need continue storage, then need replenish tobacco leaf storage and fall oxygen, control wet curing agent, prolong curing period.
Oxygen falls in tobacco leaf storage of the present invention, control wet curing agent can also be used to preserve the material that traditional Chinese medicine, grain, fruit etc. need be stored in a warehouse.
Embodiment
Below in conjunction with embodiment and accompanying drawing, the present invention is described in further detail.
Following embodiment is non-limiting embodiment of the present invention.
Embodiment 1:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts the fumaric acid methyl esters, and water absorbing agent adopts calcium chloride, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Desiccant in the control wet curing agent adopts calcium chloride, and second water-loss reducer adopts the special-purpose constant humidity agent of commercially available tobacco.
Earlier reduced iron powder, fumaric acid methyl esters, active carbon, sodium chloride, calcium chloride, calcium oxide, perlite, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, after stirring, the water of part by weight stirs then and promptly makes the controlled atmosphere sealing compound below adding again.
80 order reduced iron powders 69.7%
Fumaric acid methyl esters 0.1%
Active carbon 10%
Sodium chloride 1%
Calcium chloride 1%
Calcium oxide 5%
Perlite 3%
Polyacrylic acid glycerol ester 0.2%
Diatomite 5%
Water 5%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 100, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
Calcium chloride, the special-purpose constant humidity agent of tobacco, perlite, calcium oxide are pressed column weight amount ratio and taken by weighing, evenly mix, promptly get and control wet curing agent A type composition.
Calcium chloride 50%
The special-purpose constant humidity agent 15% of tobacco
Perlite 15%
Calcium oxide 20%
In the small package bag (net weight of the Type B controlled atmosphere sealing compound of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with heat sealing machine, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
During use, at first the tobacco leaf with 20000kg seals with composite plastic film, puts into the controlled atmosphere sealing compound 120kg (i.e. 240 pouches) that makes above again, and control wet curing agent 12kg (i.e. 60 pouches) evenly is placed on the two on the cigarette buttress or in the slit between the tobacco bale.Discovery is detected in inner space to composite plastic film, drop to below 2% 30 days oxygen concentrations, humidity was controlled between the 50%-65% in 15 days, there is not microorganism to multiply and plant pest in 2 years, also do not occur mouldyly, rotten, the more satisfactory condition that reaches tobacco storage has improved quality of tobacco.
Embodiment 2:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts the fumaric acid methyl esters, and water absorbing agent adopts calcium sulphate, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Desiccant in the control wet curing agent adopts calcium chloride, and second water-loss reducer adopts the special-purpose constant humidity agent of commercially available tobacco.
Earlier reduced iron powder, fumaric acid methyl esters, active carbon, sodium chloride, calcium sulphate, calcium oxide, perlite, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, after stirring, the water of part by weight stirs then and promptly makes the controlled atmosphere sealing compound below adding again.
100 order reduced iron powders 65.2%
Fumaric acid methyl esters 0.3%
Active carbon 15%
Sodium chloride 2%
Calcium sulphate 1%
Calcium oxide 5%
Perlite 3%
Polyacrylic acid glycerol ester 0.5%
Diatomite 3%
Water 5%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 200, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
Calcium chloride, the special-purpose constant humidity agent of tobacco, perlite, calcium oxide are pressed column weight amount ratio and taken by weighing, evenly mix, promptly get and control wet curing agent A type composition.
Calcium chloride 30%
The special-purpose constant humidity agent 15% of tobacco
Perlite 10%
Calcium oxide 45%
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with heat sealing machine, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
During use, the tobacco leaf of 30000kg is sealed with composite plastic film, put into the controlled atmosphere sealing compound 180kg (i.e. 360 pouches) that makes above again, control wet curing agent 24kg (i.e. 120 pouches) evenly is placed on the two on the cigarette buttress or in the slit between the tobacco bale.Discovery is detected in inner space to composite plastic film, drop to below 2% 25 days oxygen concentrations, humidity was controlled between the 50%-65% in 12 days, do not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Embodiment 3:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts the fumaric acid methyl esters, and water absorbing agent adopts zinc chloride, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Desiccant in the control wet curing agent adopts calcium chloride, and second water-loss reducer adopts the special-purpose constant humidity agent of commercially available tobacco.
Earlier reduced iron powder, fumaric acid methyl esters, active carbon, sodium chloride, calcium chloride, calcium oxide, perlite, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, after stirring, the water of part by weight stirs then and promptly makes the controlled atmosphere sealing compound below adding again.
120 order reduced iron powders 60%
Fumaric acid methyl esters 1%
Active carbon 15%
Sodium chloride 2%
Calcium chloride 3%
Calcium oxide 5%
Perlite 3%
Polyacrylic acid glycerol ester 1%
Diatomite 3%
Water 7%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 300, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
Calcium chloride, the special-purpose constant humidity agent of tobacco, perlite, calcium oxide are pressed column weight amount ratio and taken by weighing, evenly mix, promptly get and control wet curing agent A type composition.
Calcium chloride 60%
The special-purpose constant humidity agent 15% of tobacco
Perlite 10%
Calcium oxide 15%
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with heat sealing machine, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
During use, the tobacco leaf of 10000kg is sealed with composite plastic film, put into the controlled atmosphere sealing compound 60kg (i.e. 120 pouches) that makes above again, control wet curing agent 8kg (i.e. 40 pouches) evenly is placed on the two on the cigarette buttress or in the slit between the tobacco bale.Discovery is detected in inner space to composite plastic film, drop to below 2% 20 days oxygen concentrations, humidity was controlled between the 50%-65% in 7 days, do not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Embodiment 4:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts the fumaric acid methyl esters, and water absorbing agent adopts silica gel, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Desiccant in the control wet curing agent adopts silica, and second water-loss reducer adopts the special-purpose constant humidity agent of commercially available tobacco.
Earlier reduced iron powder, fumaric acid methyl esters, active carbon, sodium chloride, silica gel, calcium oxide, perlite, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, after stirring, the water of part by weight stirs then and promptly makes the controlled atmosphere sealing compound below adding again.
80 order reduced iron powders 55%
Fumaric acid methyl esters 1%
Active carbon 12%
Sodium chloride 1%
Silica gel 1%
Calcium oxide 5%
Perlite 10%
Polyacrylic acid glycerol ester 4%
Diatomite 5%
Water 6%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 400, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
Silica, the special-purpose constant humidity agent of tobacco, perlite, calcium oxide are pressed column weight amount ratio and taken by weighing, evenly mix, promptly get and control wet curing agent A type composition.
Silica 60%
The special-purpose constant humidity agent 15% of tobacco
Perlite 10%
Calcium oxide 15%
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control moisture that the prepares nonwoven that to transfer sealing compound to be contained in a size be 200 * 300mm is made, seal with heat sealing machine, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
During use, the tobacco leaf of 20000kg is sealed with composite plastic film, put into the controlled atmosphere sealing compound 120kg (i.e. 240 pouches) that makes above again, control wet curing agent 16kg (i.e. 80 pouches) evenly is placed on the two on the cigarette buttress or in the slit between the tobacco bale.Discovery is detected in inner space to composite plastic film, drop to below 2% 15 days oxygen concentrations, humidity was controlled between the 50%-65% in 15 days, do not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Embodiment 5:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts the fumaric acid methyl esters, and water absorbing agent adopts zinc chloride, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Desiccant in the control wet curing agent adopts anhydrous sodium sulfate, and second water-loss reducer adopts the special-purpose constant humidity agent of commercially available tobacco.
Earlier reduced iron powder, fumaric acid methyl esters, active carbon, sodium chloride, zinc chloride, calcium oxide, perlite, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, stir and promptly make the controlled atmosphere sealing compound.
80 order reduced iron powders 69.9%
Fumaric acid methyl esters 2%
Active carbon 10%
Zinc chloride 5%
Calcium oxide 5%
Perlite 5%
Polyacrylic acid glycerol ester 0.1%
Diatomite 3%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 500, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
Anhydrous sodium sulfate, the special-purpose constant humidity agent of tobacco, perlite, calcium oxide are pressed column weight amount ratio and taken by weighing, evenly mix, promptly get and control wet curing agent A type composition.
Anhydrous sodium sulfate 40%
The special-purpose constant humidity agent 30% of tobacco
Perlite 10%
Calcium oxide 20%
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with heat sealing machine, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
During use, the tobacco leaf of 24000kg is sealed with composite plastic film, put into the controlled atmosphere sealing compound 144kg (i.e. 288 pouches) that makes above again, control wet curing agent 20kg (i.e. 100 pouches) evenly is placed on the two on the cigarette buttress or in the slit between the tobacco bale.Discovery is detected in inner space to composite plastic film, drop to below 2% 25 days oxygen concentrations, humidity was controlled between the 50%-65% in 10 days, do not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Embodiment 6:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts the fumaric acid methyl esters, and water absorbing agent adopts calcium sulphate, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Desiccant in the control wet curing agent adopts anhydrous cupric sulfate, and second water-loss reducer adopts the special-purpose constant humidity agent of commercially available tobacco.
Earlier reduced iron powder, fumaric acid methyl esters, active carbon, sodium chloride, calcium sulphate, calcium oxide, wood chip, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, after stirring, the water of part by weight stirs then and promptly makes the controlled atmosphere sealing compound below adding again.
100 order reduced iron powders 40%
Fumaric acid methyl esters 0.3%
Active carbon 10%
Sodium chloride 2%
Calcium sulphate 10%
Calcium oxide 8%
Wood chip 14.2%
Polyacrylic acid glycerol ester 0.5%
Diatomite 10%
Water 5%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 800, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
Anhydrous cupric sulfate, the special-purpose constant humidity agent of tobacco, perlite, calcium oxide are pressed column weight amount ratio and taken by weighing, evenly mix, promptly get and control wet curing agent A type composition.
Anhydrous cupric sulfate 60%
The special-purpose constant humidity agent 15% of tobacco
Perlite 10%
Calcium oxide 15%
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with heat sealing machine, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
During use, the tobacco leaf of 8000kg is sealed with composite plastic film, put into the controlled atmosphere sealing compound 80kg (i.e. 160 pouches) that makes above again, control wet curing agent 10kg (i.e. 50 pouches) evenly is placed on the two on the cigarette buttress or in the slit between the tobacco bale.Discovery is detected in inner space to composite plastic film, drop to below 2% 15 days oxygen concentrations, humidity was controlled between the 50%-65% in 12 days, do not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Embodiment 7:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts the fumaric acid methyl esters, and water absorbing agent adopts calcium chloride, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Desiccant in the control wet curing agent adopts calcium chloride, and second water-loss reducer adopts the special-purpose constant humidity agent of commercially available tobacco.
Earlier reduced iron powder, fumaric acid methyl esters, active carbon, sodium chloride, calcium chloride, calcium oxide, perlite, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, stir and promptly make the controlled atmosphere sealing compound.
120 order pyrite dusts 60%
Fumaric acid methyl esters 1%
Active carbon 10%
Sodium chloride 7%
Calcium chloride 10%
Calcium oxide 5%
Perlite 3%
Polyacrylic acid glycerol ester 1%
Diatomite 3%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 300, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
Calcium chloride, the special-purpose constant humidity agent of tobacco, perlite, calcium oxide are pressed column weight amount ratio and taken by weighing, evenly mix, promptly get and control wet curing agent A type composition.
Calcium chloride 60%
The special-purpose constant humidity agent 15% of tobacco
Perlite 10%
Calcium oxide 15%
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with air-heater, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
During use, the tobacco leaf of 20000kg is sealed with composite plastic film, put into the controlled atmosphere sealing compound 120kg (i.e. 240 pouches) that makes above again, control wet curing agent 12kg (i.e. 60 pouches) evenly is placed on the two on the cigarette buttress or in the slit between the tobacco bale.Discovery is detected in inner space to composite plastic film, can drop to below 2% 30 days oxygen concentrations, humidity was controlled between the 50%-65% in 15 days, not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Embodiment 8:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts the fumaric acid methyl esters, and water absorbing agent adopts calcium chloride, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Desiccant in the control wet curing agent adopts calcium chloride, and second water-loss reducer adopts the special-purpose constant humidity agent of commercially available tobacco.
Earlier reduced iron powder, fumaric acid methyl esters, active carbon, sodium chloride, calcium chloride, calcium oxide, perlite, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, after stirring, the water of part by weight stirs and promptly makes the controlled atmosphere sealing compound below adding again.
120 order reduced iron powders 62%
Fumaric acid methyl esters 1%
Active carbon 15%
Calcium chloride 3%
Calcium oxide 5%
Perlite 3%
Polyacrylic acid glycerol ester 1%
Diatomite 3%
Water 7%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 300, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
Calcium chloride, the special-purpose constant humidity agent of tobacco, perlite, calcium oxide are pressed column weight amount ratio and taken by weighing, evenly mix, promptly get and control wet curing agent A type composition.
Calcium chloride 60%
The special-purpose constant humidity agent 15% of tobacco
Perlite 10%
Calcium oxide 15%
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with air-heater, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
After the tobacco leaf of 20000kg sealed with composite plastic film, put into the controlled atmosphere sealing compound 120kg that makes above, i.e. 240 pouches, control wet curing agent 12kg, i.e. 60 pouches, the two is placed on evenly that the cigarette buttress is gone up or tobacco bale between the slit in.Discovery is detected in inner space to composite plastic film, drop to below 2% 25 days oxygen concentrations, humidity was controlled between the 50%-65% in 10 days, do not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Embodiment 9:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts sodium sulphite, and water absorbing agent adopts anhydrous magnesium sulfate, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Desiccant in the control wet curing agent adopts anhydrous magnesium sulfate, and second water-loss reducer adopts the special-purpose constant humidity agent of commercially available tobacco.
Earlier reduced iron powder, sodium sulphite, active carbon, sodium chloride, calcium chloride, calcium oxide, perlite, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, after stirring, the water of part by weight stirs and promptly makes the controlled atmosphere sealing compound below adding again.
100 order reduced iron powders 51.8%
Sodium sulphite 5%
Active carbon 15%
Sodium chloride 4%
Anhydrous magnesium sulfate 2%
Calcium oxide 1%
Perlite 6%
Polyacrylic acid glycerol ester 0.2%
Diatomite 5%
Water 10%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 300, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
Anhydrous magnesium sulfate, the special-purpose constant humidity agent of tobacco, perlite are pressed column weight amount ratio and are taken by weighing, evenly mix, promptly get and control wet curing agent A type composition:
Anhydrous magnesium sulfate 60%
The special-purpose constant humidity agent 10% of tobacco
Perlite 30%
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with air-heater, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
After the tobacco leaf of 36000kg sealed with composite plastic film, put into the controlled atmosphere sealing compound 216kg that makes above, i.e. 432 pouches, control wet curing agent 21.6kg, i.e. 108 pouches, the two is placed on evenly that the cigarette buttress is gone up or tobacco bale between the slit in.Discovery is detected in inner space to composite plastic film, drop to below 2% 25 days oxygen concentrations, humidity was controlled between the 50%-65% in 10 days, do not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Embodiment 10:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts sodium sulphite, and water absorbing agent adopts calcium chloride, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Desiccant in the control wet curing agent adopts calcium chloride, and second water-loss reducer adopts the special-purpose constant humidity agent of commercially available tobacco.
Earlier reduced iron powder, sodium sulphite, active carbon, sodium chloride, calcium chloride, calcium oxide, carbonization rice hulls, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, after stirring, the water of part by weight below adding again, stir again and promptly make the controlled atmosphere sealing compound
100 order reduced iron powders 52.8%
Sodium sulphite 2%
Active carbon 20%
Sodium chloride 2%
Calcium chloride 2%
Calcium oxide 1%
Carbonization rice hulls 5%
Polyacrylic acid glycerol ester 0.2%
Diatomite 5%
Water 10%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 300, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
Calcium chloride, the special-purpose constant humidity agent of tobacco, perlite are pressed column weight amount ratio and are taken by weighing, evenly mix, promptly get and control wet curing agent A type composition:
Calcium chloride 60%
The special-purpose constant humidity agent 10% of tobacco
Perlite 30%
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with air-heater, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
After the tobacco leaf of 20000kg sealed with composite plastic film, put into the controlled atmosphere sealing compound 120kg that makes above, i.e. 240 pouches, control wet curing agent 12kg, i.e. 60 pouches, the two is placed on evenly that the cigarette buttress is gone up or tobacco bale between the slit in.Discovery is detected in inner space to composite plastic film, drop to below 2% 25 days oxygen concentrations, humidity was controlled between the 50%-65% in 10 days, do not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Embodiment 11:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts sodium sulphite, and water absorbing agent adopts anhydrous magnesium sulfate, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Powder in the control wet curing agent adopts polyacrylic acid-marine alga sodium macromolecule resin, and coupling agent adopts starch.
Earlier reduced iron powder, sodium sulphite, active carbon, sodium chloride, calcium chloride, calcium oxide, perlite, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, after stirring, the water of part by weight below adding again, stir again and promptly make the controlled atmosphere sealing compound
100 order reduced iron powders 56.8%
Sodium sulphite 2%
Active carbon 10%
Sodium chloride 2%
Anhydrous magnesium sulfate 2%
Calcium oxide 8%
Perlite 6%
Polyacrylic acid glycerol ester 0.2%
Diatomite 5%
Water 8%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 300, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
With polyacrylic acid-marine alga sodium macromolecule resin (powder), the solid moisture absorbent of starch (coupling agent), low density polyethylene (LDPE), microporosity silica gel is pressed column weight amount ratio and is taken by weighing, and evenly mixes, and promptly gets and controls wet curing agent Type B composition:
Polyacrylic acid-marine alga sodium macromolecule resin 67%
Starch 3%
Low density polyethylene (LDPE) 20%
The solid moisture absorbent 10% of microporosity silica gel
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with air-heater, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
After the tobacco leaf of 20000kg sealed with composite plastic film, put into the controlled atmosphere sealing compound 120kg that makes above, i.e. 240 pouches, control wet curing agent 12kg, i.e. 60 pouches, the two is placed on evenly that the cigarette buttress is gone up or tobacco bale between the slit in.Discovery is detected in inner space to composite plastic film, drop to below 2% 25 days oxygen concentrations, humidity was controlled between the 50%-65% in 10 days, do not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Embodiment 12:
In the present embodiment, the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts sodium sulphite, and water absorbing agent adopts anhydrous magnesium sulfate, and first water-loss reducer adopts the polyacrylic acid glycerol ester; Powder in the control wet curing agent adopts polyacrylic acid-marine alga sodium macromolecule resin, and coupling agent is a starch.
Earlier reduced iron powder, sodium sulphite, active carbon, sodium chloride, calcium chloride, calcium oxide, perlite, polyacrylate glyceride, diatomite are taken by weighing by following part by weight, pour agitator respectively into, stir and promptly make the controlled atmosphere sealing compound,
80 order reduced iron powders 70%
Sodium sulphite 3%
Active carbon 12%
Sodium chloride 4%
Anhydrous magnesium sulfate 1%
Calcium oxide 1.5%
Perlite 3%
Polyacrylic acid glycerol ester 0.5%
Diatomite 5%
In the controlled atmosphere sealing compound for preparing the above inner wrapping PE plastic film bag (net weight of the controlled atmosphere sealing compound of being adorned in every bag is 500g) that to be loaded on a size be 150 * 210mm, punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, the punching number is 300, adopt heat sealing machine that its opening is sealed up again, then, 10 inner wrapping PE plastic film bags are loaded in the big packing PE plastic film bag that is of a size of 400 * 500mm, sealing is preserved.
The solid moisture absorbent of polyacrylic acid-marine alga sodium macromolecule resin (powder), starch (coupling agent), low density polyethylene (LDPE), microporosity silica gel is pressed column weight amount ratio takes by weighing, evenly mix, promptly get and control wet curing agent Type B composition:
Polyacrylic acid-marine alga sodium macromolecule resin 60%
Starch 5%
Low density polyethylene (LDPE) 20%
The solid moisture absorbent 15% of microporosity silica gel
In the small package bag (net weight of the control wet curing agent of being adorned in every bag is 200g) that the control wet curing agent that the prepares nonwoven that to be contained in a size be 200 * 300mm is made, seal with air-heater, then 10 small package bags are loaded in the big packing PE plastic film bag that is of a size of 450 * 550mm, sealing is preserved.
After the tobacco leaf of 10000kg sealed with composite plastic film, put into the controlled atmosphere sealing compound 60kg that makes above, i.e. 120 pouches, control wet curing agent 6kg, i.e. 30 pouches, the two is placed on evenly that the cigarette buttress is gone up or tobacco bale between the slit in.Discovery is detected in inner space to composite plastic film, drop to below 2% 25 days oxygen concentrations, humidity was controlled between the 50%-65% in 10 days, do not have microorganism to multiply and plant pest in 2 years, do not occur mouldyly, rotten yet, reach the more satisfactory condition of tobacco storage.
Claims (13)
1. oxygen, control wet curing agent fall in a tobacco leaf storage, it is characterized in that comprising the controlled atmosphere sealing compound and the control wet curing agent that cooperatively interact and use, and both operating weight proportions are (2-10): 1,
The component of controlled atmosphere sealing compound comprises:
Reduced iron powder or pyrite dust 40-80%
Mildew-resistant auxiliary agent 0.1-5%
Active carbon 10-21%
Sodium chloride 0-12%
Water absorbing agent 1-15%
Calcium oxide 1-8%
Perlite or wood chip or carbonization rice hulls 3-15%
The first water-loss reducer 0.1-5%
Diatomite 2-10%
Water 0-10%
More than each components contents be weight percent content;
The component of control wet curing agent is an A type composition, comprising:
Desiccant 30-60%
The second water-loss reducer 2-40%
Perlite 5-40%
The component of perhaps controlling the wet curing agent is the Type B composition, comprising:
Powder 60-70%
Coupling agent 3-5%
Low density polyethylene (LDPE) 15-20%
The solid moisture absorbent 10-15% of microporosity silica gel
Described powder is: polyacrylic acid-marine alga sodium macromolecule resin
Described coupling agent is: starch
More than each components contents be weight percent content.
2. oxygen, control wet curing agent fall in tobacco leaf storage according to claim 1, it is characterized in that the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts the fumaric acid methyl esters.
3. oxygen, control wet curing agent fall in tobacco leaf storage according to claim 1, it is characterized in that the mildew-resistant auxiliary agent in the controlled atmosphere sealing compound adopts sodium sulphite.
4. oxygen, control wet curing agent fall in tobacco leaf storage according to claim 1, it is characterized in that the water absorbing agent in the controlled atmosphere sealing compound adopts calcium chloride, calcium sulphate, anhydrous sodium sulfate, silica gel or zinc chloride.
5. oxygen, control wet curing agent fall in tobacco leaf storage according to claim 1, it is characterized in that first water-loss reducer in the controlled atmosphere sealing compound adopts polyacrylacid ester compounds.
6. oxygen, control wet curing agent fall in tobacco leaf storage according to claim 1, it is characterized in that controlling the calcium oxide that also comprises 10-50% in the wet curing agent A type composition.
7. oxygen, control wet curing agent fall in tobacco leaf storage according to claim 1, the desiccant that it is characterized in that controlling in the wet curing agent is alkaline earth metal salt desiccant or silica, anhydrous cupric sulfate, anhydrous zinc sulfate or anhydrous sodium sulfate, and alkaline earth metal salt desiccant is calcium chloride, calcium sulphate or anhydrous magnesium sulfate.
8. oxygen, control wet curing agent fall in tobacco leaf storage according to claim 1, second water-loss reducer that it is characterized in that controlling in the wet curing agent A type composition adopts the special-purpose constant humidity agent of commercially available tobacco, mediate the product that makes in the polyacrylamide for the magnesium sulfate that will have equilibrium humidity, have the effect of regulating relative moisture.
9. the preparation method of the controlled atmosphere sealing compound described in claim 1, it comprises the following steps:
(1) raw material is pressed column weight amount ratio and is taken by weighing after, mix:
Reduced iron powder or pyrite dust 40-80%
Calcium oxide 1-8%
Mildew-resistant auxiliary agent 0.1-5%
Active carbon 10-21%
Water absorbing agent 1-15%
Perlite or wood chip or carbonization rice hulls 3-15%
The first water-loss reducer 0.1-5%
Diatomite 2-10%
Sodium chloride 0-12%
Described mildew-resistant auxiliary agent adopts the fumaric acid methyl esters, and water absorbing agent adopts calcium chloride, calcium sulphate, anhydrous sodium sulfate, silica gel or zinc chloride, and first water-loss reducer adopts polyacrylacid ester compounds;
(2) above-mentioned each mixture is stirred.
10. the preparation method of controlled atmosphere sealing compound according to claim 9 is characterized in that after each mixture is stirred, adding the water of 0-10% again, and then stirring in step (2).
11., it is characterized in that also including step (3), that is: according to the preparation method of claim 9 or 10 described controlled atmosphere sealing compounds
(3) the controlled atmosphere sealing compound for preparing is loaded in the inner wrapping PE plastic film bag of a size for the mm of (100-180) mm * (150-250), punching on described inner wrapping PE plastic film bag two-sided, the pore size scope is 0.1-1.5mm, and the punching number is 100-1500, seals again; Then, 6-15 inner wrapping PE plastic film bag is loaded in the big packing PE plastic film bag, sealing is preserved.
12. the preparation method of the control wet curing agent described in claim 1, it comprises the following steps:
(1) A type composition material being pressed column weight amount ratio takes by weighing:
Desiccant 30-60%
The second water-loss reducer 2-40%
Perlite 5-40%
Calcium oxide 10-50%
Described second water-loss reducer is the agent of solid constant humidity, adopts the special-purpose constant humidity agent of commercially available tobacco, for the magnesium sulfate that will have equilibrium humidity is mediated the product that makes in the polyacrylamide, can buy on the market, has the effect of regulating relative moisture.
Or the Type B composition material pressed column weight amount ratio take by weighing:
Powder 60-70%
Coupling agent 3-5%
Low density polyethylene (LDPE) 15-20%
The solid moisture absorbent 10-15% of microporosity silica gel
Described powder is: polyacrylic acid-marine alga sodium macromolecule resin
Described coupling agent is: starch
(2) said mixture is mixed.
13. the preparation method of control wet curing agent according to claim 12 is characterized in that also including step (3), that is:
The control wet curing agent that (3) will prepare is contained in a size in the small package bag that (150-250) mm * (250-350) nonwoven of mm is made, again small package bag is sealed, then 7-15 small package bag is loaded in the big packing PE plastic film bag, sealing is preserved.