CN101880455A - Plastic suitable for parts of fishing winder and preparation method and application thereof - Google Patents
Plastic suitable for parts of fishing winder and preparation method and application thereof Download PDFInfo
- Publication number
- CN101880455A CN101880455A CN 201010210803 CN201010210803A CN101880455A CN 101880455 A CN101880455 A CN 101880455A CN 201010210803 CN201010210803 CN 201010210803 CN 201010210803 A CN201010210803 A CN 201010210803A CN 101880455 A CN101880455 A CN 101880455A
- Authority
- CN
- China
- Prior art keywords
- nylon
- fishing
- parts
- special plastic
- winder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to plastic special for parts of a fishing winder (also named a fishing reel or a reel) and a preparation method and application thereof. The plastic special for the parts on the fishing winder is prepared from glass fiber serving as a main material and nylon fiber serving as an auxiliary material and comprises the following main components in percentage by mass: 34 to 38 percent of nylon PA6, PA66 or the mixture of nylon PA6 and PA66, 61 to 65 percent of glass fiber and a small quantity of other aids. The preparation method comprises the following steps of: (1) metering the needed components, namely, nylon PA, a small quantity of aids and glass fiber according to the mass percentage for later use; (2) melting the nylon PA on a screw extruder heated by a high temperature, adding the glass fiber into the molten nylon PA, melting and mixing the glass fiber and the molten nylon PA and extruding the mixture into strips; and (3) cooling the striped extruded by using the screw extruder with water for shaping so as to obtain granular special plastic. The method has the advantages of simple and rapid whole preparation process, extremely high efficiency and capability of meeting the requirement of mass production. Experimental tests and practical use prove that the special plastic has the characteristics of high rigidity, high strength, little deformation and the like.
Description
Technical field
The present invention relates to a kind of special plastic that is applicable to the component on the fishing reel (also claiming fishing line reel, fish strand) and its production and use.
Background technology
Component on traditional fishing reel (also claiming fishing line reel, fish strand) are produced required plastics, its component generally comprises nylon PA and glass fibre, their mass percent is: nylon PA is more than 50%, glass fibre is then less than 50%, that is: based on nylon PA, glass fibre is the mode of assisting, and produces a kind of plastics that are used for the component on the fishing reel (also claiming fishing line reel, fish strand); But the plastics according to said components and mass percent are made have the following disadvantages: (1) this method is made next plastics, its poor rigidity, weak strength, easy compressive deformation.
Summary of the invention
In order to overcome above-mentioned existing in prior technology deficiency, the object of the present invention is to provide a kind ofly based on glass fibre, nylon PA is the special plastic that the mode of assisting is made the parts of fishing winder of high rigidity, high strength, low deformation characteristic.
Another object of the present invention also is to provide a kind of preparation method who is applicable to the special plastic of parts of fishing winder; This preparation method has the advantage that technology is simple and easy, efficient is high, can be fit to requirements of mass production.
Still a further object of the present invention provides the purposes of above-mentioned special plastic, is used for making the purposes of the parts of fishing winder of high rigidity, high strength, low modification.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of special plastic that is applicable to parts of fishing winder, it is characterized in that based on glass fibre, nylon PA is that the mode of assisting is made the component special plastic on the fishing reel of high rigidity, high strength, low modification characteristic,, it comprises following component and mass percentage content is:
Nylon PA 34～38%;
Glass fibre 61～65%;
As scheme more specifically, make in the component of above-mentioned plastics, nylon PA is PA6PA66 or their mixture, also comprises a spot of other auxiliary agents.
The technical scheme that another object of the present invention adopted is as follows:
A kind of described method that is applicable to the special plastic of parts of fishing winder of claim 1 for preparing is characterized in that it comprises the steps:
Step 1 according to mass percent, measures required component nylon PA, a little auxiliary and glass fibre, and is standby;
Step 2 on the forcing machine of a heat, is earlier melted nylon PA and a little auxiliary, adds glass fibre again, through melting mix, mixing after, extrude lines by forcing machine again;
Step 3, the lines by above-mentioned forcing machine is extruded by cooling shaping, cut into particulate state earlier again, and packing gets final product at last.
As scheme more specifically, the lines that described forcing machine is extruded can pass through the tank cooling shaping.
Described lines can become particulate state by the cutting machine fly-cutting after cooling.
The technical scheme that still a further object of the present invention adopted is:
With above-mentioned special plastic is earlier after drying, is injection molded into component on the fishing reel by injection moulding machine again.
Beneficial effect of the present invention is as follows:
(1) the present invention is applicable to the special plastic of parts of fishing winder, based on glass fibre, nylon PA is that the mode of assisting is made required special plastic, test and actual use are as can be known by experiment, this special plastic has characteristics such as high rigidity, high strength and low distortion, the nylon component that overcome on traditional fishing reel (also claiming fishing line reel, fish strand) are produced required plastics, based on nylon PA, glass fibre is the plastics that the mode of production of assisting is made, and has poor rigidity, weak strength and deficiency such as compressive deformation easily.
(2) preparation method of the plastics of parts of fishing winder of the present invention, by screw extrusion press with the quick melting of nylon PA and glass fibre mix, mixing after, can extrude many lines, after water cooling, by cutting machine fly-cutting granulating, packing gets final product, and whole process of preparation is simple and easy, quick, efficient is high, can satisfy requirements of mass production.
Description of drawings
Fig. 1 is preparation method's schema of the plastics of fishing reel of the present invention (also claiming fishing line reel, fish strand) component.
Embodiment
A kind of plastics that are applicable to parts of fishing winder, it comprises following component and mass percentage content is: nylon PA 34～38%; Glass fibre 61～65%; And other auxiliary agent on a small quantity; Said components is based on glass fibre, and nylon PA is the special plastic that the mode of assisting is made parts of fishing winder, and this special plastic is tested and actual the use as can be known by experiment, has characteristics such as good high rigidity, high strength and low distortion.
As shown in Figure 1, for a kind of preparation is applicable to the method for the plastics of parts of fishing winder, it comprises the steps:
Step 1 according to mass percent, is produced out required component nylon PA, a little auxiliary and glass fibre, and is standby;
Step 2 on the screw extrusion press of a heat, is earlier melted nylon PA and a little auxiliary, adds glass fibre again, through melting mix, mixing after, extrude lines by forcing machine again;
Step 3, the lines by above-mentioned forcing machine is extruded by the tank cooling shaping, become particulate state by the dicing machine fly-cutting earlier again, and packing gets final product at last.
Above-mentioned said, forcing machine can be extruded many lines as required, produces needs in batches to satisfy.
The plastics preparation method of the component on this fishing reel (also claiming fishing line reel, fish strand), by forcing machine with the quick melting of two components mix, mixing after, can extrude many lines, after cooling, by cutting machine fly-cutting granulating, packing gets final product, and whole process of preparation is simple and easy, quick, efficient is high, can satisfy requirements of mass production.
Above-mentioned special plastic system of making is injection molded into component on the fishing reel by injection moulding machine earlier after drying again.
Claims (6)
1. special plastic that is applicable to parts of fishing winder, it is characterized in that, based on glass fibre, nylon PA is the special plastic that the mode of assisting is made the component on the fishing reel of high rigidity, high strength, low modification characteristic, and it comprises following component and mass percentage content thereof:
Nylon PA 34～38%;
Glass fibre 61～65%;
2. according to the described special plastic that is applicable to parts of fishing winder of claim 1, it is characterized in that, also comprise a spot of other auxiliary agents, as carbon black etc.
3. according to the described special plastic that is applicable to parts of fishing winder of claim 1, it is characterized in that described nylon PA is PA6, PA66 or both mixtures.
4. one kind prepares the described preparation method who is applicable to the special plastic of parts of fishing winder of claim 1, it is characterized in that it comprises the steps:
Step 1 according to mass percent, measures the thawing of required component nylon PA and a little auxiliary, glass fibre;
Step 2 on the forcing machine of a heat, is earlier melted nylon PA and a little auxiliary, adds glass fibre again, through melting mix, mixing after, extrude lines by forcing machine again;
Step 3, the lines by above-mentioned forcing machine is extruded by cooling shaping, cut into particulate state earlier again, and packing gets final product at last.
5. according to the described preparation method who is applicable to the special plastic of parts of fishing winder of claim 1, it is characterized in that described special plastic can be the particle of black or other colors.
6. a purposes that is applicable to the special plastic of parts of fishing winder according to claim 1 is characterized in that, described special plastic is earlier after drying, is injection molded into component on the fishing reel by injection moulding machine again.