CN101879791A - Method for manufacturing paper water pipe - Google Patents
Method for manufacturing paper water pipe Download PDFInfo
- Publication number
- CN101879791A CN101879791A CN2009100983098A CN200910098309A CN101879791A CN 101879791 A CN101879791 A CN 101879791A CN 2009100983098 A CN2009100983098 A CN 2009100983098A CN 200910098309 A CN200910098309 A CN 200910098309A CN 101879791 A CN101879791 A CN 101879791A
- Authority
- CN
- China
- Prior art keywords
- paper
- water pipe
- film
- percent
- wood pulp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for manufacturing a paper water pipe. The paper water pipe comprises the following raw materials in percentage by weight: 85 to 90 percent of wood pulp paper, 8 to 10 percent of paper tube adhesive, 0.08 to 1 percent of film (PE), 1 to 1.2 percent of aluminum plating film (VMPEP) and 0.05 to 0.08 percent of film (OPE). The method comprises the following steps of: 1, slitting paper strips for later use; 2, arranging the paper strips in order; 3, sizing; 4, thermally sealing a device; and 5, rolling paper tubes. The paper water pipe has the advantages of environmental protection, corrosion resistance, rust resistance, cracking resistance in winter, long service life, light weight, convenient construction, thermal seal connection at a joint, low cost and the like.
Description
One, technical field
The present invention relates to a kind of pipeline that is used for industry, domestic water, especially relate to a kind of manufacture method of paper water pipe.
Two, background technology
At present, it is that raw material is made waterpipe that our industry and the pipeline great majority of domestic water are to use metal or plastic pvc, PP, well-known, adopt metal water pipe not only manufacturing process complexity, cost height, and metallic water pipe is perishable gets rusty, influences water quality, construction inconvenience, the price height; Adopt plastic pvc, PP plastics to make water pipe, easily aging, there is problem of ultra-high price equally.
Three, summary of the invention
At the present common metal water pipe of above-mentioned China easily get rusty, the price height, the PVC plastic tube is easily aging, the defective of not environmental protection, the purpose of this invention is to provide that a kind of environmental protection, corrosion-resistant, non-corrosive, winter are not ftractureed, price is low, a kind of paper water pipe and the manufacture method thereof of easy construction.
The technical scheme of the manufacture method of paper water pipe of the present invention: (one) raw material and prescription: its raw material is made up of wood pulp paper, paper tube adhesive, film (PE), aluminizer (VMPEP), film (OPE), and its percent by weight ratio is wood pulp paper 85%-90%; Paper tube adhesive 8%-10%; Film (PE) 0.08%-1%; Aluminizer (VMPEP) 1%-1.2%; Film (OPE) 0.05%-0.08%.(2) processing step: 1, cut paper slip standby → 2, paper slip arranges in order → 3, gluing → 4, hot sealing device → 5, roll out paper tube.1, it is standby the wound packages wood pulp paper to be cut the growth paper slip by the separation machine; 2, with standby long paper slip (wood pulp paper), aluminizer, aluminium platinum paper, paper-plastic composite film is arranged on the paper frame according to a certain order: innermost layer is an aluminum-plastic composite membrane, aluminizer or aluminium platinum paper, the intermediate layer is the multilayer wood pulp paper, how much deciding of its paper according to the big or small thickness of water pipe, outermost layer is a paper-plastic composite film, so-called aluminum-plastic composite membrane is by paper, plastics (PE), aluminizer (VMPEP), film (OPE) is formed, paper-plastic composite film is by wood pulp paper, film (PE), film (OPE) is formed, aluminum-plastic composite membrane is similar to the paper-plastic composite film action principle, can replace mutually; 3, gluing: gluing can be adopted two kinds of single face gluing and two-sided gluings, decides as required, before producing the glue bucket of gluing machine is filled it up with glue, selects glue for use according to the different levels needs that pass through, as glue by wood pulp paper, and adding paper tube special glue in the glue bucket; As by paper-plastic composite film, add the paper special glue in the glue bucket; 4, hot sealing device: on rolling machine, install hot sealing device, and be heated to and the surface melting of composite membrane extremely can be melted state; 5, pipe crimping: with passing through hot sealing device behind the internal layer composite membrane flanging, send into rolling machine plug mould, the multilayer wood pulp paper is sent into rolling machine plug mould with paper-plastic composite film by glue bucket, paper guiding device, rolls out paper tube, is cut into Len req.
In order further to strengthen the intensity of paper water pipe, big or small thickness according to paper water pipe, on original three-ply paper matter water pipe basis, also can thicken to six layers of paper water pipe, in the manufacturing step process, when each level is arranged in order, add one deck paper-plastic composite film again at the inferior internal layer of innermost layer, in outermost skin, add one deck multilayer wood pulp paper again, add one deck aluminum-plastic composite membrane at outermost layer again.In manufacturing process,, roll out paper tube by rolling machine plug mould by above-mentioned process flow steps.
The paper water pipe advantage that the present invention makes: (one) environmental protection, corrosion-resistant, non-corrosive; (2) warmth retention property is good, and can prevent the cracking of enduring cold, long service life winter; (3) easy construction, this paper water pipe is in light weight, and the junction engages with heat-sealing and forms, and is easy and simple to handle, reduce labor intensity greatly; (4) price is low, and the cost of this paper water pipe has only the sixth of metallic water pipe,, 2/3rds of PVC water pipe.
Four, description of drawings
Fig. 1 is the structural representation of paper water pipe of the present invention.
Fig. 2 is a process chart of the present invention.
Five, the specific embodiment
Further illustrate below in conjunction with Fig. 2 process chart specific embodiment:
Embodiment 1:
Composition of raw materials: get 88.54% wood pulp paper, each grade paper tube adhesive 9% is got 1% aluminizer (VMPEP), 0.06% film (OPE), 0.4% film (PE), its manufacturing step is: it is standby 1, to cut paper slip: it is standby that the wound packages wood pulp paper is cut the growth paper slip by the separation machine; 2, paper slip is arranged in order: standby rectangular wood pulp paper, aluminizer, aluminium platinum paper, paper-plastic composite film are arranged on the paper frame according to a certain order: innermost layer is an aluminum-plastic composite membrane, the intermediate layer is the multilayer wood pulp paper, outermost layer is a paper-plastic composite film, and this is the most basic a kind of paper water pipe structure; 3, gluing: gluing can be adopted two kinds of single face gluing and two-sided gluings, selects glue for use according to the different levels needs that pass through, and joins in the gluing machine glue bucket; 4, hot sealing device: on rolling machine, install hot sealing device, and be heated to and the surface melting of composite membrane extremely can be melted state; 5, pipe crimping: behind innermost layer aluminum-plastic composite membrane flanging, send into rolling machine plug mould by hot sealing device, the multilayer wood pulp paper is sent into rolling machine plug mould with paper-plastic composite film by glue bucket, paper guiding device, rolls out paper tube, is cut into Len req.
Embodiment 2:
Composition of raw materials: get 87.83% wood pulp paper, each grade paper tube adhesive 10%, aluminizer (VMPEP) 1.1%, film (OPE) 0.07%, film (PE) 1%.In order to strengthen the intensity of paper water pipe, manufacturing process steps second rapid step by step in: will the arrangement according to a certain order on the paper frame of standby rectangular wood pulp paper, aluminizer, aluminium platinum paper, paper-plastic composite film: innermost layer be an aluminum-plastic composite membrane, the intermediate layer is the multilayer wood pulp paper, when outermost layer is the paper-plastic composite film essential structure, inferior internal layer at innermost layer adds one deck paper-plastic composite film again, in outermost skin, add one deck multilayer wood pulp paper again, add one deck paper-plastic composite film at outermost layer again, have six layers and form paper water pipe.Other processing steps of embodiment 2 are identical with embodiment 1.
Claims (3)
1. the manufacture method of paper water pipe is characterized in that it is wood pulp paper 85%-90% by following raw materials by weight example prescription; Paper tube adhesive 8%-10%; Film (PE) 0.08%-1%; Aluminizer (VMPEP) 1%-1.2%; Film (OPE) 0.05%-0.08%, manufacturing technology steps: 1. cut paper slip standby → 2. paper slip is arranged → hot sealing device of 3. gluing → 4. → 5. roll out paper tube in order.
2. by the manufacture method of the described paper water pipe of claim 1, it is characterized in that described paper slip arranges in order, innermost layer is an aluminum-plastic composite membrane, and the intermediate layer is the multilayer wood pulp paper, and outermost layer is a paper-plastic composite film.
3. by the manufacture method of the described paper water pipe of claim 1, it is characterized in that described hot sealing device, being heated to can be with the extremely molten state of the surface melting of composite membrane.