CN102705591B - Heat-resistant and pressure-resistant polyethylene composite pipe - Google Patents
Heat-resistant and pressure-resistant polyethylene composite pipe Download PDFInfo
- Publication number
- CN102705591B CN102705591B CN201210220586.3A CN201210220586A CN102705591B CN 102705591 B CN102705591 B CN 102705591B CN 201210220586 A CN201210220586 A CN 201210220586A CN 102705591 B CN102705591 B CN 102705591B
- Authority
- CN
- China
- Prior art keywords
- resistant
- heat
- polyethylene resin
- composite pipe
- resin material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a heat-resistant and pressure-resistant polyethylene composite pipe consisting of three layers, wherein the inner layer is made from a heat-resistant PERTII polyethylene resin material, the outer layer is made from a high density polyethylene resin material, and the two layers are closely combined through an adhesive resin containing a polyolefin main chain and a polar branch chain. The heat-resistant and pressure-resistant polyethylene composite pipe provided by the invention fully utilizes the following properties of the heat-resistant PERTII polyethylene resin and has the advantages of average utilization temperature being 60 DEG C, mature production extrusion technique and high stress cracking resistance.
Description
The present invention relates to the production technology of polyvinyl piping materials, concrete upper saying is a kind of preparation method of heat-resistant pressure-resistant polyethylene composite pipe.
Background technique
At present; due to the excellent cracking resistance of hdpe pipe, low temperature resistant, health is nontoxic, resistant to chemical media corrosion and easy for installation and can adopt the advantage such as trenchless technology, long service life, is commonly used to building water supply, draining, building and heating, cities and towns plumbing, gas, underground coal mine conveying, electric power, telecommunication protect and the field such as industrial, agriculture.But because itself material does not possess heat resistance, when conveying more than 45 DEG C media, the reduction of meeting build-up of pressure, bearing capacity significantly reduces, and causes its tubing to be restricted in medium transport field application such as middle high temperature.
At present, just partly its resistance to heat problem is solved in known patented technology and practical technique, all well do not solve its can heat-resisting again can be withstand voltage problem, traditional solution is only solve the problems such as its bearing capacity is low by increasing tube wall thickness, but tubing cost is very high, serious waste of resources, uses dissemination little.
Summary of the invention
The object of the invention is to overcome prior art defect, a kind of preparation method of heat-resistant pressure-resistant polyethylene composite pipe is provided.
Technological scheme of the present invention is:
A kind of heat-resistant pressure-resistant polyethylene composite pipe, be made up of two-layer, described composite pipe internal layer is heat-resisting PERT II type polyethylene resin material, and skin is high-density polyethylene resin material, between two-layer by take polyolefin as main chain, the resin of binding property of band polarity side chain combines closely and forms;
Described high-density polyethylene resin material is PE100 level or PE80 polyethylene grades resin;
Described adhering resin is a kind of resin of binding property developed based on EVA;
Above-mentioned heat-resisting PERT II type polyethylene resin material used is a kind of based on hervene copolymer high-performance mixed ingredients.
The present invention take full advantage of heat-resisting PERT II type polyethylene resin have average serviceability temperature up to 60 DEG C, produce and extrude work technical maturity, have the feature of high stress crack resistance performance, by pipeline prepared by the present invention, its use is safer, owing to having higher minimum desired strength (MRS,) make it have thinner wall thickness, cost reduces significantly.It is high that the present invention takes full advantage of hdpe pipe voltage endurance capability, the features such as cost of production is low, heat resistance after compound is withstand voltage polyethylene composite pipe is under same size pressure, 20% ~ 30% tubing cost can be saved compared with traditional PERT tubing, 30% ~ 40% cost can be saved compared with PP-R pipeline, and bearing capacity is higher, can substitute steel pipe completely in heavy caliber heating or the overheated media application of conveying with pressure, tubing has more economic advantages.
embodiment:
Heat resistance PERT II type polyethylene resin is extruded sizing by extruder and does Inner tubing layers, internal layer evenly applies one deck EVA type binding resin by glue-line extruder after extruding traction cooling on PERT II type polyvinyl plastic core pipe, then by another extruder PE100 rank high-density polyethylene resin and additive extruding and moulding evenly wrapped and do skin outside glue-line (EVA), by adhering resin by internal layer and skin is permanent bonds together, three layers of composite pipe altogether after agent make tubing through sizing, cooling twice.
The specific embodiment of the present invention is not limited to the mode that above-described embodiment provides.
Claims (1)
1. a heat-resistant pressure-resistant polyethylene composite pipe, form by three layers, internal layer is heat-resisting PERT II type polyethylene resin material, and skin is high-density polyethylene resin material, between two-layer by take polyolefin as main chain, the resin of binding property of band polarity side chain combines closely and forms;
Described high-density polyethylene resin material is PE100 level polyethylene resin;
Described take polyolefin as main chain, the resin of binding property of band polarity side chain is a kind of resin of binding property developed based on EVA;
Heat-resisting PERT II type polyethylene resin material used is a kind of based on hervene copolymer high-performance mixed ingredients;
The preparation method of described heat-resistant pressure-resistant polyethylene composite pipe is: heat-resisting PERT II type polyethylene resin is extruded sizing by extruder and does Inner tubing layers, internal layer evenly applies one deck EVA type binding resin via glue-line extruder, then by another extruder by the extruding and moulding of PE100 rank high-density polyethylene resin, make it evenly wrap and do skin outside glue-line, the composite pipe after three-layer co-extruded is finished product through sizing, cooling twice.