CN101869793A - 聚四氟乙烯纤维滤料及其制备方法 - Google Patents
聚四氟乙烯纤维滤料及其制备方法 Download PDFInfo
- Publication number
- CN101869793A CN101869793A CN 201010218163 CN201010218163A CN101869793A CN 101869793 A CN101869793 A CN 101869793A CN 201010218163 CN201010218163 CN 201010218163 CN 201010218163 A CN201010218163 A CN 201010218163A CN 101869793 A CN101869793 A CN 101869793A
- Authority
- CN
- China
- Prior art keywords
- fiber filter
- polytetrafluoroethylene
- filter material
- preparation
- ptfe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种聚四氟乙烯纤维滤料及其制备方法，它具有极强的高温化学稳定性、过滤精度高、耐磨损、使用寿命长、应用范围广等优点，尤其适用于工况环境恶劣的过滤需要。本发明的聚四氟乙烯纤维滤料是使用聚四氟乙烯纤维滤布经过浸渍处理，再进行覆膜或涂层处理；所述浸渍处理采用聚四氟乙烯溶液进行浸渍；所述聚四氟乙烯溶液包括：聚四氟乙烯，30wt％～40wt％；聚苯酯，20wt％～30wt％；粘合剂，1wt％～3wt％；水，余量。
Description
技术领域
本发明涉及一种高温过滤材料及其制备方法，尤其是一种聚四氟乙烯纤维滤料及其制备方法。
背景技术
当前，随着城市化进程加快生活垃圾、医疗废物以及其它废旧物品的增多，一些废弃物的焚烧项目也日益增多，虽然其烟尘的排放量相比火电行业、钢铁行业、水泥行业等行业要小很多，但垃圾焚烧炉排放的烟尘含有二噁英，若不严格的控制，产生的危害极大。而且由于我国的垃圾处理不分类，成分复杂，因此垃圾焚烧炉工况恶劣，烟气的腐蚀性强，含有硫化物、氮氧化物、氯化氢、溴化物等，含湿量又很大，对滤袋的性能提出了很高的要求。
目前对于垃圾焚烧烟尘的过滤，主要采用玻璃纤维、聚苯硫醚纤维(PPS)、聚酰亚胺纤维(P84)等纤维制成的过滤材料，不同程度的存在着过滤材料被腐蚀、过滤精度低，使用寿命短等问题，已经不能满足烟尘过滤的要求。
发明内容
本发明提供一种聚四氟乙烯纤维滤料及其制备方法，本发明的聚四氟乙烯纤维滤料具有极强的高温化学稳定性、过滤精度高、耐磨损、使用寿命长、应用范围广等优点，尤其适用于工况环境恶劣的过滤需要。
本发明的聚四氟乙烯纤维滤料的制备方法是对聚四氟乙烯纤维滤布进行浸渍处理，再进行覆膜或涂层处理。
所述浸渍处理采用聚四氟乙烯溶液进行浸渍。
所述聚四氟乙烯溶液包括：聚四氟乙烯，30wt％～40wt％；聚苯酯，20wt％～30wt％；粘合剂，1wt％～3wt％；水，余量。
所述覆膜处理是将浸渍处理后的聚四氟乙烯滤布表面再覆盖聚四氟乙烯薄膜。
所述涂层处理是将浸渍处理后的聚四氟乙烯滤布的表面使用聚四氟乙烯树脂做涂层处理。
所述聚四氟乙烯滤布是将聚四氟乙烯短纤维经过预处理、开松、半精纺梳理、并条、粗纺、细纺成纱、并捻、整经、掏综、织布织成。
所述聚四氟乙烯滤布是将聚四氟乙烯长纤维经过整经、掏综、织布织成。
本发明的聚四氟乙烯纤维滤料是用上述方法制备制得。
具体实施方式
本发明的聚四氟乙烯纤维滤料的实施例如下：
实施例一
使用聚四氟乙烯短纤维，性能指标为：长度51mm；细度3D；卷曲12个/25mm；抗拉强度2.7cn/dtex；热收缩率＜1.5％。将原料松包均匀铺开，喷洒含2％静电剂的水溶液放置24小时后投入生产、开松、半精纺梳理、并条、粗纺、细纺成纱、并捻、整经、掏综、织布、浸渍处理、覆膜处理、检验成包。
并捻工序并成156tex纱，用无梭织布机，采用3/5纬二重的织布工艺织造成650g/m2的聚四氟乙烯纤维过滤布。将该滤布进行浸渍处理，浸渍溶液为聚四氟乙烯溶液，配比为：
| 聚四氟乙烯 | 40％ |
| 聚苯酯 | 20％ |
| 粘合剂 | 1％ |
| 水 | 余量 |
处理好的布表面再覆盖一层聚四氟乙烯薄膜，然后检验成包。
本产品的抗拉强度≥4000N/5cm。
实施例二
使用聚四氟乙烯短纤维，性能指标为：长度51mm；细度3D；卷曲12个/25mm；抗拉强度2.7cn/dtex；热收缩率＜1.5％。将原料松包均匀铺开，喷洒含2.5％静电剂的水溶液放置24小时后投入生产、开松、半精纺梳理、并条、粗纺、细纺成纱、并捻、整经、掏综、织布、浸渍处理、涂层处理、检验成包。
将并捻工序并成的纱线，用剑杆织布机，采用1/3斜纹的织布工艺织造成420g/m2的聚四氟乙烯纤维过滤布。将该滤布进行浸渍处理，浸渍溶液为聚四氟乙烯溶液，配比为：
| 聚四氟乙烯 | 30％ |
| 聚苯酯 | 30％ |
| 粘合剂 | 1.5％ |
| 水 | 余量 |
处理好的布表面再涂覆一层聚四氟乙烯树脂，然后检验成包。
本产品的抗拉强度≥2500N/5cm。
实施例三
使用400D的聚四氟乙烯长丝经过整经、掏综、织布(用喷气织布机)，采用3/5纬二重的织布工艺织造成750g/m2的过滤布(纬纱同样选用400D的聚四氟乙烯长丝)。再将该过滤布进行浸渍处理，浸渍溶液为聚四氟乙烯溶液，其成分如下：
| 聚四氟乙烯 | 35％ |
| 聚苯酯 | 25％ |
| 粘合剂 | 2％ |
| 水 | 余量 |
处理好的布表面再覆盖一层聚四氟乙烯薄膜，然后检验成包。
其抗拉强度≥4500N/5cm。
实施例四
使用450D的聚四氟乙烯长丝经过整经、掏综、用喷气织布机，采用双斜纹工艺织造成720g/m2的过滤布，纬纱同样选用450D的聚四氟乙烯长丝。再将该过滤布浸渍处理，浸渍溶液为聚四氟乙烯溶液，其成分如下：
| 聚四氟乙烯 | 35％ |
| 聚苯酯 | 22％ |
| 粘合剂 | 3％ |
| 水 | 余量 |
处理好的滤布表面做聚四氟乙烯树脂涂层处理，然后检验成包。
本产品的抗拉强度≥4600N/5cm。
本发明的聚四氟乙烯纤维滤料的优点是：
(1)聚四氟乙烯俗称“塑料王”，具有优良的化学稳定性、耐腐蚀性、耐热性、高润滑不粘性、电绝缘性和良好的抗老化耐力。
(2)本发明由于采用聚四氟乙烯纤维织造而成，经过聚四氟乙烯乳液浸渍处理后，再在滤布表面覆有聚四氟乙烯薄膜，或者在滤布表面做聚四氟乙烯树脂涂层处理。上述处理方式由于成分相同，分子结构一致，结合效果好。
(3)本发明的滤布经过覆膜或涂层后结构缜密，牢固耐用，有效地提高了过滤材料的过滤精度。具有耐高温、耐酸碱、易于清灰，使用寿命长的优点，满足了高温烟尘过滤行业的需要。适用于工作环境恶劣的各类工况：如高温、高湿、高粘性粉尘行业、高腐蚀性气体工况的烟尘净化等。适用于垃圾焚烧行业、水泥行业、燃煤锅炉和电厂等。
Claims (8)
1.一种聚四氟乙烯纤维滤料的制备方法，包括：对聚四氟乙烯纤维滤布进行浸渍处理，再进行覆膜或涂层处理。
2.根据权利要求1所述的聚四氟乙烯纤维滤料的制备方法，其特征在于：所述浸渍处理采用的是聚四氟乙烯溶液。
3.根据权利要求1所述的聚四氟乙烯纤维滤料的制备方法，其特征在于：所述聚四氟乙烯溶液包括：聚四氟乙烯，30wt％～40wt％；聚苯酯，20wt％～30wt％；粘合剂，1wt％～3wt％；水，余量。
4.根据权利要求1所述的聚四氟乙烯纤维滤料的制备方法，其特征在于：所述覆膜处理是将所述浸渍处理后的聚四氟乙烯滤布表面再覆盖聚四氟乙烯薄膜。
5.根据权利要求1所述的聚四氟乙烯纤维滤料的制备方法，其特征在于：所述涂层处理是将所述浸渍处理后的聚四氟乙烯滤布的表面使用聚四氟乙烯树脂做涂层处理。
6.根据权利要求1所述的聚四氟乙烯纤维滤料的制备方法，其特征在于：所述聚四氟乙烯滤布的织造工艺是将聚四氟乙烯短纤维经过预处理、开松、半精纺梳理、并条、粗纺、细纺成纱、并捻、整经、掏综、织布织成。
7.根据权利要求1所述的聚四氟乙烯纤维滤料的制备方法，其特征在于：所述聚四氟乙烯滤布是将聚四氟乙烯长纤维经过整经、掏综、织布织成。
8.一种聚四氟乙烯纤维滤料，由权利要求1～7中任意一项所述的制备方法制得。