CN101864229A - Method for preparing hot-melt quick-drying colorful pavement antiskid paint - Google Patents
Method for preparing hot-melt quick-drying colorful pavement antiskid paint Download PDFInfo
- Publication number
- CN101864229A CN101864229A CN 201010199136 CN201010199136A CN101864229A CN 101864229 A CN101864229 A CN 101864229A CN 201010199136 CN201010199136 CN 201010199136 CN 201010199136 A CN201010199136 A CN 201010199136A CN 101864229 A CN101864229 A CN 101864229A
- Authority
- CN
- China
- Prior art keywords
- hot
- melt
- calcium carbonate
- quick
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing a hot-melt quick-drying colorful pavement antiskid paint. The preparation process comprises the following steps of: (1) putting modified thermoplastic acrylic resin together with smashed and sieved aggregate, plasticizer, pigment and stuffing into a hot-melt kettle and uniformly stirring the mixed materials; (2) adding mixed granular calcium carbonate and superfine calcium carbonate powder into the hot-melt kettle; (3) adding an activated water-based paint quick-drying agent into the hot-melt kettle; and (4) fully re-stirring all the materials in the hot-melt kettle, uniformly blending the materials, detecting and packaging the mixture to obtain finished products. In the invention, the modified colorless and transparent thermoplastic acrylic resin is used as the main raw material, dioctyl phthalate serving as the plasticizer is added in the paint, so the prepared product avoids blocking and skinning phenomena, is easy to stir uniformly and short in drying time, is not adhered to tyres and has the characteristics of relative stability of color fastness, high paint bonding strength, high antiskid performance, wear resistance and the like.
Description
Technical field
The present invention relates to a kind of preparation method of hot-melt quick-drying colorful pavement antiskid paint.
Background technology
Present domestic existing antislip colour coating, mainly by developing by material technology and the production technique of introducing and digest and assimilate developed countries in recent years, therefore in the production of antislip colour coating with use and still lack proven technique and construction experience, have that non-skid property instability, execution conditions requirement height, chroma characteristic are poor, defective such as the anti-wear difference of coating and cold cracking, be not suitable for the strict place of road pavement, thereby be badly in need of that a kind of performance is stable more, technology is simple more, the more bright-coloured pavement antiskid paint of color.
Summary of the invention
Technical problem to be solved by this invention just provides a kind of hot-melt quick-drying colorful pavement antiskid paint preparation method, and the hot-melt quick-drying colorful pavement antiskid paint sticking power of preparing is stronger, freedom from cracking better, non-skid property is more stable, construction technology is simpler, the coating color is more bright-coloured.
For solving the problems of the technologies described above, the present invention adopts following technical scheme: a kind of preparation method of hot-melt quick-drying colorful pavement antiskid paint is characterized in that preparation process may further comprise the steps:
(1) selects the water white transparency thermoplastic acrylic resin of handling through modification for use, put into the hot melt still, stir together with the aggregate that crushes and screens, softening agent, pigment and filler;
(2) add granular calcium carbonate and the calcium carbonate superfine micro mist that mixes, strengthen the flowability and the settleability of coating;
(3) add active treated water coating quick dry agent, improve the ridity and the film-forming speed of coating glue-line rapidly, and increase the hardness and the bonding strength on glue-line and road surface;
(4) all raw materials in the hot melt still are fully stirred again, mix, detection, packing get product.
As preferably, its each several part weight percent of the raw material of described hot melt still is: acrylic resin 45%, aggregate 20%, softening agent 10%, pigment 15%, filler 10%.
As preferably, described granular calcium carbonate and calcium carbonate superfine micro mist part by weight are 2: 1, and the add-on of described granular calcium carbonate and calcium carbonate superfine micro mist accounts for 5% of acrylic resin, aggregate, softening agent, pigment and filler gross weight.
As preferably, described water-borne coatings quick dry agent add-on accounts for 2% of acrylic resin, aggregate, softening agent, pigment and filler gross weight.
Main raw material(s) of the present invention adopts the water white transparency thermoplastic acrylic resin of handling through modification, by in coating, adding plasticity dioctyl phthalate (DOP) preferably, the product of preparing does not have caking and skinning, is easy to stir evenly, sticking tire is short time of drying, and have that colour fastness is relatively stable, coating bonding strength height, non-skid property is good and resist characteristics such as wear-resisting.Reduce traffic jam, reduction road accident rate and beautifying the environment etc. played an important role.Be widely used as traffic signs such as motorway, urban road, airport.Feedback is good after the user uses, and has good market popularization value.
Embodiment
A kind of preparation method embodiment of hot-melt quick-drying colorful pavement antiskid paint, preparation process may further comprise the steps:
(1) selects the water white transparency thermoplastic acrylic resin of handling through modification for use, put into the hot melt still, stir 10min together with the aggregate that crushes and screens, softening agent, pigment and filler; Its each several part weight percent of the raw material of described hot melt still is: acrylic resin 45%, aggregate 20%, softening agent 10%, pigment 15%, filler 10%.Wherein, aggregate, pigment and filler are all chosen existing procucts on the market.Aggregate is generally selected wear-resisting colored bauxitic clay granulated aggregate, entire body colored ceramic particle aggregate or lithotome resin dyed particles aggregate of the same colour for use, and softening agent is a dioctyl phthalate (DOP).
(2) add granular calcium carbonate and the calcium carbonate superfine micro mist that mixes by a certain percentage, strengthen the flowability and the settleability of coating; Described granular calcium carbonate and calcium carbonate superfine micro mist part by weight are 2: 1, and the add-on of described granular calcium carbonate and calcium carbonate superfine micro mist accounts for 5% of acrylic resin, aggregate, softening agent, pigment and filler gross weight.
(3) add an amount of active treated water coating quick dry agent, improve the ridity and the film-forming speed of coating glue-line rapidly, and increase the hardness and the bonding strength on glue-line and road surface; Described water-borne coatings quick dry agent add-on accounts for 2% of acrylic resin, aggregate, softening agent, pigment and filler gross weight.The water-borne coatings quick dry agent is selected existing procucts on the market for use.
(4) all raw materials in the hot melt still are fully stirred 20min again, mix, detection, packing get product.
The using method of a kind of hot-melt quick-drying colorful pavement antiskid paint of the present invention is as follows, earlier the hot melt still is heated to 180～200 ℃ during use, is mobile shape, is uniformly applied to the road surface again and forms hard paint film.Surface spreading reflecting microbead during construction, night, reflective function can be better.
Claims (5)
1. the preparation method of a hot-melt quick-drying colorful pavement antiskid paint is characterized in that preparation process may further comprise the steps:
(1) selects the water white transparency thermoplastic acrylic resin of handling through modification for use, put into the hot melt still, stir together with the aggregate that crushes and screens, softening agent, pigment and filler;
(2) add granular calcium carbonate and the calcium carbonate superfine micro mist that mixes, strengthen the flowability and the settleability of coating;
(3) add active treated water coating quick dry agent, improve the ridity and the film-forming speed of coating glue-line rapidly, and increase the hardness and the bonding strength on glue-line and road surface;
(4) all raw materials in the hot melt still are fully stirred again, mix, detection, packing get product.
2. according to the preparation method of the described a kind of hot-melt quick-drying colorful pavement antiskid paint of claim 1, it is characterized in that: its each several part weight percent of the raw material of described hot melt still is: acrylic resin 45%, aggregate 20%, softening agent 10%, pigment 15%, filler 10%.
3. according to the preparation method of the described a kind of hot-melt quick-drying colorful pavement antiskid paint of claim 1, it is characterized in that: described granular calcium carbonate and calcium carbonate superfine micro mist part by weight are 2: 1, and the add-on of described granular calcium carbonate and calcium carbonate superfine micro mist accounts for 5% of acrylic resin, aggregate, softening agent, pigment and filler gross weight.
4. according to the preparation method of the described a kind of hot-melt quick-drying colorful pavement antiskid paint of claim 1, it is characterized in that: described water-borne coatings quick dry agent add-on accounts for 2% of acrylic resin, aggregate, softening agent, pigment and filler gross weight.
5. according to the preparation method of the described a kind of hot-melt quick-drying colorful pavement antiskid paint of claim 1, it is characterized in that: described softening agent is a dioctyl phthalate (DOP).