CN101864202A - Glass paste for reflective panel - Google Patents
Glass paste for reflective panel Download PDFInfo
- Publication number
- CN101864202A CN101864202A CN 201010211480 CN201010211480A CN101864202A CN 101864202 A CN101864202 A CN 101864202A CN 201010211480 CN201010211480 CN 201010211480 CN 201010211480 A CN201010211480 A CN 201010211480A CN 101864202 A CN101864202 A CN 101864202A
- Authority
- CN
- China
- Prior art keywords
- paste
- glass
- reflective panel
- carrier
- sequestrant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a glass paste for a reflective panel. The glass paste is characterized in that: the paste is prepared from the following raw materials in percentage by weight: 44 to 75 percent of glass microballons, 0.2 to 1 percent of carrier, and 24 to 55 percent of chelating agent, and a method for preparing the paste comprises the steps of; weighting the materials in the ratio and mixing, and grinding the mixture by using a three-roller grinding mill or stirring the mixture at a high speed for 30 minutes to ensure that the glass microballons, the carrier and the chelating agent form a uniform system to obtain the required paste. The paste can be directly printed on a surface of clothes and the surface of the reflective panel, and the paste reflects ambient light at night, so the paste can be used for substituting the conventional PVC reflective strips. The glass paste not only provides convenience for production operation, but also reduces the cost of reflective cloths and the reflective panel.
Description
Technical field
The present invention relates to a kind of glass paste that is used for reflective panel, a kind of glass paste that can reflect ambient light.
Background technology
Reflective clothing and reflective panel are a kind of new operation interfaces that collects functional and ornamental electronic system product for one of popular in recent years, collect switch key, panel feature literal, mark, trade mark, transparent window and be shown in one, because reflective clothing and reflective panel have characteristics such as brightness height, reflective strong, good endurance, light weight, cost are low, fields such as the sign of more and more clothes that are applied to the sanitationman, mechanical execution personnel's clothes, the clothes of traffic police, office equipment, electronic toy, household electrical appliance panel.
The reflective clothing and the reflective panel that provide on the present market, what adopt usually is the mode of PVC reflecting strips or other light reflecting materials, has so both increased the difficulty of producing, and has also increased production cost.Therefore, development a kind of can be directly at clothing surperficial and reflective substrate surface printing a kind of can night reflect ambient light reflective slurry become present assistant officer technical problem to be solved.
Summary of the invention
The purpose of this invention is to provide a kind of glass paste that is used for reflective panel, promptly can be directly the clothing surface and the reflective substrate surface printing is a kind of can be at the reflective slurry of reflect ambient light at night, substitute existing P VC reflecting strips with this, promptly make things convenient for the operation when producing, also reduced the cost of reflective clothing and reflective panel.
The objective of the invention is to realize that by following technical proposals a kind of glass paste that is used for reflective panel is characterized in that, this slurry is formulated by following weight percentages:
Glass microballon 44%-75%;
Carrier 0.2%-1%;
Sequestrant 24%-55%.
Described glass microballon is BaO, SiO
2, TiO
2, B
2O
3, ZnO, Na
2O or K
2Among the O one or more are according to arbitrary proportion blended mixture; Mean particle diameter is 40-80 μ m, and its specific refractory power is 1.8-2.5.
Described carrier is 1,4 butyrolactone and vinyl chloride-vinyl acetate resin according to mass ratio is that the ratio thorough mixing dissolving of 9:1 makes.
Described sequestrant is selected the phthalate sequestrant.
Described reflective panel glass paste prepares according to following step:
According to the aforementioned proportion weighing, after the mixing,, make glass microballon, carrier and sequestrant form the uniform system of state carrier, glass microballon and sequestrant, promptly make required slurry through the three-roll grinder grinding or through behind the high-speed stirring 30min.
The present invention is owing to taked the glass paste of reflective panel, can be directly the clothing surface and the reflective substrate surface printing is a kind of can be at the reflective slurry of reflect ambient light at night, substitute existing P VC reflecting strips with this, promptly make things convenient for the operation when producing, also reduced the cost of reflective clothing and reflective panel.
Embodiment
The present invention will be further described below in conjunction with specific embodiment.Need to prove that following embodiment only is used to illustrate the present invention, be not limited to practical range of the present invention.
Embodiment 1
This long-afterglow luminescent panel is prepared as with slurry:
Chosen material: (is the 100g meter according to weight percent)
BaO、SiO
2 50g；
Carrier 0.5g;
Phthalate sequestrant IAM 49.5g.
Described glass microballon is BaO, SiO
2According to arbitrary proportion blended mixture; Mean particle diameter is 40 μ m, and its specific refractory power is 1.8; Its carrier is 1,4 butyrolactone and vinyl chloride-vinyl acetate resin L-871 according to mass ratio is that the ratio thorough mixing dissolving of 9:1 makes.
Described reflective panel glass paste prepares according to following step:
With carrier, glass microballon BaO, SiO
2And phthalate sequestrant IAM is according to the aforementioned proportion weighing, after the mixing, after being ground to median size and being 40 μ m through three-roll grinder, makes glass microballon, carrier and sequestrant form the uniform system of state, promptly makes required slurry.
Embodiment 2
This long-afterglow luminescent panel is prepared as with slurry:
Chosen material: (is the 100g meter according to weight percent)
SiO
2、TiO
2、B
2O
3、ZnO 75g；
Carrier 1g;
Phthalate sequestrant IAM 24g.
Described glass microballon is SiO
2, TiO
2, B
2O
3, ZnO is with arbitrary proportion blended mixture, median size is 60 μ m, specific refractory power is 2.Its carrier is 1,4 butyrolactone and vinyl chloride-vinyl acetate resin L-871 according to mass ratio is that the ratio thorough mixing dissolving of 9:1 makes.
Described reflective panel glass paste prepares according to following step:
With carrier, glass microballon SiO
2, TiO
2, B
2O
3, ZnO and phthalate sequestrant IAM be according to the aforementioned proportion weighing, after the mixing, behind high-speed stirring 30min, makes glass microballon, carrier and sequestrant form the uniform system of state, promptly makes required slurry.
Embodiment 3
This long-afterglow luminescent panel is prepared as with slurry:
Chosen material: (is the 100g meter according to weight percent)
B
2O
3, ZnO, Na
2O and K
2O 65g;
Carrier 0.2g;
Phthalate sequestrant IAM 34.8g.
Described glass microballon is B
2O
3, ZnO, Na
2O and K
2O is with arbitrary proportion blended mixture, and median size is 80 μ m, and specific refractory power is 2.5.Its carrier is 1,4 butyrolactone and vinyl chloride-vinyl acetate resin L-871 according to mass ratio is that the ratio thorough mixing dissolving of 9:1 makes.
Described reflective panel glass paste prepares according to following step:
With carrier, glass microballon B
2O
3, ZnO, Na
2O and K
2O and phthalate sequestrant IAM be according to the aforementioned proportion weighing, after the mixing, after being ground to median size and being 80 μ m through three-roll grinder, makes glass microballon, carrier and sequestrant form the uniform system of state, promptly makes required slurry.
Embodiment 4
This long-afterglow luminescent panel is prepared as with slurry:
Chosen material: (is the 100g meter according to weight percent)
SiO
2 44g；
Carrier 1g;
Phthalate sequestrant IAM 55g.
Described glass microballon is SiO
2, median size is 60 μ m, specific refractory power is 2.5.Its carrier is 1,4 butyrolactone and vinyl chloride-vinyl acetate resin L-871 according to mass ratio is that the ratio thorough mixing dissolving of 9:1 makes.
Described reflective panel glass paste prepares according to following step:
With carrier, glass microballon SiO
2And phthalate sequestrant IAM is according to the aforementioned proportion weighing, after the mixing, behind high-speed stirring 30min, makes glass microballon, carrier and sequestrant form the uniform system of state, promptly makes required slurry.
This slurry is printed in the surface of reflective panel, and perhaps the surface of cloth products promptly can make reflector and reflective clothing.
Claims (5)
1. a glass paste that is used for reflective panel is characterized in that, this slurry is formulated by following weight percentages:
Glass microballon 44%-75%;
Carrier 0.2%-1%;
Sequestrant 24%-55%.
2. a kind of glass paste that is used for reflective panel as claimed in claim 1 is characterized in that described glass microballon is BaO, SiO
2, TiO
2, B
2O
3, ZnO, Na
2O or K
2Among the O one or more are according to arbitrary proportion blended mixture; Mean particle diameter is 40-80 μ m, and its specific refractory power is 1.8-2.5.
3. a kind of glass paste that is used for reflective panel as claimed in claim 2 is characterized in that, described carrier is 1,4 butyrolactone and vinyl chloride-vinyl acetate resin according to mass ratio is that the ratio thorough mixing dissolving of 9:1 makes.
4. a kind of glass paste that is used for reflective panel as claimed in claim 1 is characterized in that, described sequestrant is selected the phthalate sequestrant.
5. a kind of glass paste that is used for reflective panel as claimed in claim 1 is characterized in that, described reflective panel glass paste prepares according to following step:
According to the aforementioned proportion weighing, after the mixing,, make glass microballon, carrier and sequestrant form the uniform system of state carrier, glass microballon and sequestrant, promptly make required slurry through the three-roll grinder grinding or through behind the high-speed stirring 30min.