CN1018633B - 一种耐(抗)碱玻璃纤维的制备方法 - Google Patents

一种耐(抗)碱玻璃纤维的制备方法

Info

Publication number
CN1018633B
CN1018633B CN 87108257 CN87108257A CN1018633B CN 1018633 B CN1018633 B CN 1018633B CN 87108257 CN87108257 CN 87108257 CN 87108257 A CN87108257 A CN 87108257A CN 1018633 B CN1018633 B CN 1018633B
Authority
CN
China
Prior art keywords
alkali
glass
glass fiber
wollastonite
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
CN 87108257
Other languages
English (en)
Other versions
CN87108257A (zh
Inventor
林云飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan Polytechnic University
Original Assignee
Wuhan Polytechnic University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan Polytechnic University filed Critical Wuhan Polytechnic University
Priority to CN 87108257 priority Critical patent/CN1018633B/zh
Publication of CN87108257A publication Critical patent/CN87108257A/zh
Publication of CN1018633B publication Critical patent/CN1018633B/zh
Expired legal-status Critical Current

Abstract

一种新型的中碱及无碱玻璃纤维材料，他主要是以硅灰石作为主要原料，然后按一定的比例加入二氧化硅、氧化铝、氧化镁以及硼酸等经过一定的温度下熔制成玻璃，然后再拉制成玻璃纤维。这种材料制成的玻璃纤维，其特点是：强度高，电绝缘性能好，化学稳定性高，不燃烧等优点；同时利用硅灰石作主要原料还可以充分利用现有的丰富资源，降低成本。

Description

本发明属于新型玻璃纤维类材料。
在现有的熔制玻璃纤维材料中是以硅砂、白云石、长石、芒硝、纯碱、硝酸钠、硼砂等为主要原料，而且玻璃熔制温度一般控制在1500-1600℃。由于上述所用的玻璃纤维材料的价格，比较昂贵，耐碱性较低，同时，由于熔制及拉丝温度高，给制造玻璃纤维带来困难。为了克服上述缺点《抗碱玻璃纤维》第二集中摘译日本专利昭50-26563号中提出在玻璃组份中添加氧化锆、氧化铝以及氧化钙，使玻璃具有耐碱性。
50-26563号专利的各种成份范围：
成份    重量范围
SiO254-58
Na2O 14-18
Al2O30-4
MgO    0-3
CaO    5-9
BaO    1-5
ZrO24-8
MnO    5-8
Fl2O30-5
Cr2O30-1.5
虽然这种玻璃纤维具有良好的抗碱性，但是，由于这种纤维含有一定成份的氧化锆和氧化铬，使生产出来的纤维不仅成本高，而且给制造也带来了一些困难等缺点。
本发明对已有的纤维材料中存在的问题和缺点，研究出一种新型中碱及无碱玻璃纤维，这种中碱及无碱玻璃纤维与现有玻璃纤维相比较，具有耐碱性好，特别是玻璃的熔制，温度低;本发明更重要的目的是可以充分利用现有的丰富资源，节约能耗，降低成本的新型中碱及无碱玻璃纤维。
本发明的玻璃纤维成份是由硅灰石、氧化硅、氧化铝、氧化镁、硼酸等组成，首先将磨细的原料混匀，放入坩锅内在1350-1400℃温度下熔制成玻璃，再经1200-1300℃拉制成玻璃纤维。具体成份如：
成份    重量范围（%）
硅灰石    55-75
氧化硅    0-18
氧化铝    5-15
氧化镁    5-10
硼酸    0-10
以上各组份总和为100%。
下面举出本发明的实施例。
将硅灰石、氧化硅、氧化铝、氧化镁、硼酸等配制的配合料，在制备过程中，先将原料装在坩锅内，在1350-1400℃的温度下熔制1小时，再将制成的玻璃在拉丝炉中经1200-1300℃的温度下，拉制成玻璃纤维;这种抗碱纤维的抗碱性能良好，比普通的E玻璃纤维抗碱性降低了1/3到2/3。
以硅灰石为主要原料制得新型玻璃纤维（称SA4＃）与普通的E玻璃纤维的抗碱性对比。
玻璃的成份和特性对比 SA45＃
成份    %
硅灰石    61.32
氧化硅    14.15
氧化镁    13.21
氧化铝    5.66
硼酸    5.66
拉丝温度    1200℃
上述成份配比的玻璃纤维经测试抗碱性8.35%
成份    %
氧化钙    17
氧化硅    54
氧化铝    14
氧化镁    5
B2O310
拉丝温度    1220℃
按此配比所得的玻璃纤维经测试抗碱性24%。
玻璃的成份和特性对比 SA45＃
成份    硅灰石    氧化硅    氧化镁    氧化铝    硼酸    拉丝温度
%    61.32    14.15    13.21    5.66    5.66    1200℃
上述成份配比的玻璃纤维经测试抗碱性8.35%
成份 氧化钙 氧化硅 氧化铝 氧化镁 B2O3拉丝温度
%    17    54    14    5    10    1220℃
按此配比所得的玻璃纤维经测试抗碱性24%

Claims (2)

1、一种新型耐(抗)碱玻璃纤维的制备方法，是将原料混匀熔制成玻璃，然后拉成玻璃纤维，其特征在于以硅灰石为主要原料加入适量的氧化铝、二氧化硅、氧化镁、硼酸，其玻璃原料配合比为(以重%计)：
成分      重量范围(%)
硅灰石    55-70
二氧化硅  0-18
氧化铝    5-15
氧化镁    5-10
硼酸      0-10
2、根据权利要求1所述的制备方法，其特征在于玻璃熔制温度应控制在1350-1400℃，纤维拉制温度控制在1200-1300℃。
CN 87108257 1987-12-29 1987-12-29 一种耐(抗)碱玻璃纤维的制备方法 Expired CN1018633B (zh)