CN101851731A - 一种高抗应力腐蚀低碳合金化马氏体耐磨衬板 - Google Patents

一种高抗应力腐蚀低碳合金化马氏体耐磨衬板 Download PDF

Info

Publication number
CN101851731A
CN101851731A CN 201010147711 CN201010147711A CN101851731A CN 101851731 A CN101851731 A CN 101851731A CN 201010147711 CN201010147711 CN 201010147711 CN 201010147711 A CN201010147711 A CN 201010147711A CN 101851731 A CN101851731 A CN 101851731A
Authority
CN
China
Prior art keywords
lining plate
liner plate
stress corrosion
hours
heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010147711
Other languages
English (en)
Inventor
黄四亮
谢志东
覃照成
陈益宁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI NINGGUO CHENGXIN WEAR-RESISTANT MATERIAL Co Ltd
Original Assignee
ANHUI NINGGUO CHENGXIN WEAR-RESISTANT MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI NINGGUO CHENGXIN WEAR-RESISTANT MATERIAL Co Ltd filed Critical ANHUI NINGGUO CHENGXIN WEAR-RESISTANT MATERIAL Co Ltd
Priority to CN 201010147711 priority Critical patent/CN101851731A/zh
Publication of CN101851731A publication Critical patent/CN101851731A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高抗应力腐蚀低碳合金化马氏体耐磨衬板，其特征在于：半成品衬板经过打磨，喷丸后采用经过650*2小时1020-1050℃加热保温1.5-4小时保温时间视衬板厚度，装炉量，和升温速度而定，淬入快速淬火油中，在24小时内控制在RJ井式炉内以250℃保温3-6小时回火。本发明的有益效果：最终得到合金含量高，含碳量低的单相板条马氏体(残奥非常少)基体，该材质晶粒度可以达到5-6级，采用该材质可以做湿式矿山球磨机的磨头衬板，头部条形衬板，磨尾衬板，中间磨头衬板。

Description

一种高抗应力腐蚀低碳合金化马氏体耐磨衬板
技术领域：
本发明涉及一种高抗应力腐蚀低碳合金化马氏体耐磨衬板，特别是适用于矿山湿法磨上的马氏体耐磨衬板。
背景技术：
矿山湿法磨，由于矿石粒度大小不均，各地浆料酸碱性差异，球磨机衬板工作条件异常恶劣，各种电化学腐蚀，应力腐蚀，加上各种粒度大小硬度不均的矿石，矿浆不断的对磨机衬板冲刷，腐蚀，一般材质铸件使用寿命大大降低。本发明单相马氏体耐磨衬板，克服了以上诸多缺点，主要表现在以下四个方面：(1)得到的是单相马氏体(残奥非常少)基体，所以不象其他复相组织由于相电极电位差而很容易发生各种电化学腐蚀；(2)由于马氏体含碳量低，经过马氏体相变撞击产生的微裂纹就很小，减少了衬板在使用过程中的应力腐蚀；(3)衬板经过高温奥氏体化热处理，溶入的合金元素多，得到的马氏体碳和合金元素多，增加了衬板的硬度以及耐磨性；(4)衬板的含碳量低，加上其他的微量元素细晶强化，属于本质细晶粒钢，所以热处理后即使炉温有些偏高，也不会产生晶粒粗大的问题，所以该材质冲击韧性指标非常高达到ak≥130(J/C m2)。
发明内容
本适用新型要解决的技术问题是其他材质耐磨铸铁衬板冲击韧性指标低，抗电化学腐蚀，应力腐蚀能力差，矿山球磨机装载使用寿命低的问题。
本发明的主要技术方法在于以下方面：
1.新型马氏体耐磨铸钢衬板的化学成分控制表：
  C Si Mn   S   P   Cr   Ni   V   Ti   Mo   其他
  0.23-0.28   0.2-0.8   0.4-0.8   ≤0.05   ≤0.05   9.0-11.0   1.0-1.5   0.1-0.2   0.04-0.1   0.4-0.8   微量
2.其中钒铁V，钛铁Ti，均经过破碎，粒度为≤1mm，采用冲包加入。
3.由于钛铁Ti的加入，不仅可以细化晶粒，还可以有效的防治衬板的晶间腐蚀。
4.半成品衬板经过打磨，喷丸后采用经过650*2小时1020-1050℃加热保温1.5-4小时保温时间视衬板厚度，装炉量，和升温速度而定，淬入快速淬火油中，在24小时内控制在RJ井式炉内以250℃保温3-6小时回火。
本适用新型的有益效果为：最终得到合金含量高，含碳量低的单相板条马氏体(残奥非常少)基体，该材质晶粒度可以达到5-6级，采用该材质可以做湿式矿山球磨机的磨头衬板，头部条形衬板，磨尾衬板，中间磨头衬板。
具体实施方式
下面在具体实施方式对本发明作进一步详细说明配好化学成分控制表如下：
  C Si Mn   S   P   Cr   Ni   V   Ti   Mo   其他
  0.23-0.28   0.2-0.8   0.4-0.8   ≤0.05   ≤0.05   9.0-11.0   1.0-1.5   0.1-0.2   0.04-0.1   0.4-0.8   微量
其中钒铁V，钛铁Ti，均经过破碎，粒度为≤1mm，采用冲包加入，由于钛铁Ti的加入，不仅可以细化晶粒，还可以有效的防治衬板的晶间腐蚀，半成品衬板经过打磨，喷丸后采用经过650*2小时1020-1050℃加热保温1.5-4小时保温时间视衬板厚度，装炉量，和升温速度而定，淬入快速淬火油中，在24小时内控制在RJ井式炉内以250℃保温3-6小时回火。

Claims (1)

1.一种高抗应力腐蚀低碳合金化马氏体耐磨衬板，其特征在于：
(1)新型马氏体耐磨铸钢衬板的化学成分控制表：
  C Si Mn   S   P   Cr   Ni   V   Ti   Mo   其他   0.23-0.28   0.2-0.8   0.4-0.8   ≤0.05   ≤0.05   9.0-11.0   1.0-1.5   0.1-0.2   0.04-0.1   0.4-0.8   微量
(2)其中钒铁V，钛铁Ti，均经过破碎，粒度为≤1mm，采用冲包加入；
(3)由于钛铁Ti的加入，不仅可以细化晶粒，还可以有效的防治衬板的晶间腐蚀；
(4)半成品衬板经过打磨，喷丸后采用经过650*2小时1020-1050℃加热保温1.5-4小时保温时间视衬板厚度，装炉量，和升温速度而定，淬入快速淬火油中，在24小时内控制在RJ井式炉内以250℃保温3-6小时回火。
CN 201010147711 2010-04-15 2010-04-15 一种高抗应力腐蚀低碳合金化马氏体耐磨衬板 Pending CN101851731A (zh)