CN101838511B - Heat-resistant clothing hot melt adhesive and preparation method thereof - Google Patents
Heat-resistant clothing hot melt adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN101838511B CN101838511B CN2010101363856A CN201010136385A CN101838511B CN 101838511 B CN101838511 B CN 101838511B CN 2010101363856 A CN2010101363856 A CN 2010101363856A CN 201010136385 A CN201010136385 A CN 201010136385A CN 101838511 B CN101838511 B CN 101838511B
- Authority
- CN
- China
- Prior art keywords
- melt adhesive
- hot melt
- heat
- blend
- blender
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a heat-resistant clothing hot melt adhesive, which is characterized by comprising the following components by mass percent: 29-46.45% of hot melt adhesive, 26.1-45.52% of PE, 0.29-2.32% of bulking agent, 0.29-2.32% of sensitizer or sensitizing agent, 0.95-9.9% of nanoscale montmorillonoid or nanoscale clay, 0.05-0.5% of compatilizer, 5-20% of tackifier, 1-10% of plasticizer and 0.1-2% of antioxygen, wherein the hot melt adhesive is one or more combination of PET, PA, TPU and EVA. The preparation method comprises the following steps: 1) adding the PE, bulking agent, sensitizer or sensitizing agent into a blender and mixing for standby use; 2) adding the compatilizer and nanoscale montmorillonoid or nanoscale clay into the blender, and mixing for standby use; 3) adding the hot melt adhesive into the blender, and mixing with the blending materials obtained in the step 1 and 2; 4) slowly pouring the tackifier, plasticizer and antioxygen and mixing the materials; and 5) pelleting the obtained blending in the step 4, cooling and dicing to obtain the heat-resistant clothing hot melt adhesive. The preparation method of the invention is simple in process, and the obtained hot melt adhesive has good flexibility, adhesiveness and thermal stability.
Description
Technical field
The present invention relates to heat-resistant clothing hot melt adhesive and preparation method thereof, particularly high-grade clothing is with elevated temperature heat melten gel and preparation method.
Background technology
PET, PA, TPU or EVA based melt adhesive have advantages such as bonding strength height and medium-resistance be good; Timber, metal, pottery, fabric, paper and other polyolefine materials are had good adhesiveproperties, yet their thermostability makes its application receive certain restriction.At high temperature, PET, PA, TPU or EVA are the softening easily even fusing of the hot melt adhesive of base material, lose its bonding effect.Therefore, these undressed hot melt adhesives are unfavorable at high temperature using.CN 101070455A discloses a kind of method of coming curing cross-linked EVA through the method for adding the oxidation diisopropylbenzene(DIPB), has improved the temperature classification of EVA; CN 1800287A discloses a kind of modified EVA hot-melt adhesive, adopts the crosslinked EVA of silane coupling agent to improve the thermal stability of EVA hot melt adhesive.For PET, PA, TPU and EVA, though the patent and the report of relevant crosslinking technological are arranged, crosslinking technological is still immature, has hindered its application in the high temperature field.And a large amount of crosslinked its flexibilities of having destroyed, particularly reduced the comfortableness of clothes with hot melt adhesive.
Vilaterm (PE) is a most important derived product in the macromolecular material, accounts for about 70% of world's superpolymer consumption.Chemicalstability, nonpoisonous and tasteless, the low price of anti-organic burn into good mechanical property performance, excellence.Yet, the Vilaterm non-refractory, the maximum operation (service) temperature of new LDPE (film grade) is 60 ℃, the high density polyethylene(HDPE) maximum operation (service) temperature can only reach about 70 ℃.Shortcomings such as CN 200510116675 has introduced the silicone-modified unformed polyolefins hot melt adhesive of a kind of process, still has processing and stores difficulty, and curing speed is slower, and relative initial bonding strength is lower.CN00109087.9 to Vilaterm carry out with radiation after carry out fusion-grafting, grafting gets Vilaterm and adhesivepropertieies such as metal, pottery and glass are good, however the Vilaterm temperature tolerance is still relatively poor, causes its use temperature limited.CN 101570680A has introduced a kind of crosslinkable polyethylene hot-melt adhesive composition; Make crosslinkable Vilaterm pelletizing through adding silane coupling agent, initiator and polar monomer etc.; But this method efficient is low; The Vilaterm pelletizing that makes itself has certain crosslinked, is prone to cause binding property to reduce and has lower molten finger.Vilaterm is carried out crosslinked, not only can improve mechanical property, chemical stability, the anti-organic corrosive nature of PE, and improve thermal stability very significantly, can make PE not have tangible fusing point, thereby widen the use field of PE greatly.But for clothes PE hot melt adhesive, the PE after crosslinked is because the lifting of mechanical moduli, causes the decline with feel that descends of its pliability, causes the comfortableness decline of clothes.
CN 1687280A has introduced a kind of new type hot-melt adhesive and preparation method thereof, and recessed soil is filled among the EVA as additive, can reduce product cost significantly, improves the viscosity and the softening temperature of product.It is less that but its softening temperature improves degree, still hinders the use field of hot melt adhesive.CN 1357589A has introduced a kind of multi-purpose polyamide hot melt adhesive and preparation method thereof, with high-molecular weight branched chain type polymeric amide with in the polymeric amide of molecular weight carry out blend, and fill fillers such as a certain amount of WHITE CARBON BLACK, lime carbonate or Marinco H.CN 1401724A has introduced a kind of High-temp.-resistant hot-melt adhesive; With PA is base material; Add a certain amount of EVA, rosin, glyceride in addition; And fill nano level aluminium sesquioxide, Nano-class zinc oxide and nano level Natural manganese dioxide, the hot melt adhesive that makes can reach 130 ℃～150 ℃, but still can't satisfy the high temperature needs.
Nano imvite and nanoclay are divided into extensively at occurring in nature, and be of a great variety, and reserve is abundant, is a kind of natural resource of preciousness.They have good dispersing property; Can widespread use macromolecular material industry as the additive of nanometer polymer macromolecular material; Improve shock resistance, antifatigue, dimensional stability and gas barrier property etc.; Thereby play the effect that strengthens the comprehensive physicals of polymkeric substance, improve the material processing characteristics simultaneously.Application in polymkeric substance can be added when polymkeric substance, also can when fusion, blend add (adopting the screw rod blend usually).People such as Li Tongnian (nanometer composite polyamide-clay material; The functional polymer journal; The first phase in 2000,112-118) reported the thermal stability of clay and polyamide compoiste material, low clay content (1%～10%) can make the softening point temperature of polymeric amide improve nearly one times.
Summary of the invention
The objective of the invention is to be the relatively poor shortcoming of the temperature tolerance of hot melt adhesive, to have proposed a kind of heat-resistant clothing hot melt adhesive and preparation method thereof in order to solve at present with base materials such as PET, PA, TPU or EVA.Its technical scheme is:
A kind of heat-resistant clothing hot melt adhesive; It is characterized in that forming by mass percentage: hot melt adhesive 29～46.45%, PE 26.1～45.52%, expanding material 0.29～2.32%, sensitizer or sensitizing agent 0.29～2.32%, nano level polynite or nano level clay 0.95～9.9%, compatilizer 0.05～0.5%, tackifier 5～20%, softening agent 1～10%, oxidation inhibitor 0.1～2%, the wherein combination of one or more among hot melt adhesive employing PET, PA, TPU and the EVA by following material.
Described heat-resistant clothing hot melt adhesive, the combination of one or more in PE employing high-pressure polyethylene, high density polyethylene(HDPE) or the linear low density polyethylene, the PE melting index is 0.1～100g/10min.
Described heat-resistant clothing hot melt adhesive, expanding material adopt PE and one or more the combination among the PE behind functionalization and modification of Vestolen PP 7052, the grafted maleic anhydride of grafted maleic anhydride.
Described heat-resistant clothing hot melt adhesive, sensitizer are polyfunctional group, adopt at least a in dimethacrylate Tetraglycol 99 fat and the trimethylammonium vinylformic acid trihydroxy-propyl ester; Sensitizing agent is active small molecules, adopts SiCl
2, CCl
4, at least a in NaF and the carbon black.
Described heat-resistant clothing hot melt adhesive, the particle diameter of nano level polynite and nano level clay is all less than 500nm.
Described heat-resistant clothing hot melt adhesive, compatilizer adopt at least a in silane coupling agent, titanate coupling agent and the Triple Pressed Stearic Acid.
Described heat-resistant clothing hot melt adhesive, tackifier are at least a in rosin, polymerized rosin, 145 resins, 138 resins, terpine resin, petroleum resin and the hydrogenated petroleum resin.
Described heat-resistant clothing hot melt adhesive, softening agent are at least a in PE wax, PP wax, the paraffin low-molecular weight polymer.
Described heat-resistant clothing hot melt adhesive, oxidation inhibitor are at least a in antioxidant 1010 and the oxidation inhibitor 1098.
A kind of preparation method of heat-resistant clothing hot melt adhesive is characterized in that adopting following steps:
1) PE, expanding material, sensitizer and sensitizing agent are put into blender, behind 80 ℃ of following blend 10min, take out subsequent use;
2) blender is put in nano level polynite or nano level clay, and added compatilizer, behind 80 ℃ of following blend 20min, take out subsequent use;
3) PET, PA, TPU or EVA base material are at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) nano level polynite or the nano level clay through the compatilizer modification that obtain put into blender blend 10min, and temperature is 80 ℃;
4) slowly pour tackifier, softening agent, oxidation inhibitor into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
The present invention compared with prior art has the following advantages:
1, be that the clothes of base material use hot melt adhesive to be the basis with PET, PA, TPU and EVA; Through PE and the inorganic nano-particle (nano level polynite or nano level clay) that adds certain content; Make its generation crosslinked under the irradiation through UW, ultraviolet ray, infrared rays or other high-energy radiation sources (high-power electron beam, X ray, neutron and gamma-rays) in the clothing making process; Heat-resistant clothing hot melt adhesive not only can embody mechanical property, adhesion property and other performance characteristics of PET, PA, TPU or EVA (under the high-energy radiation less crosslinking reaction) itself; Can pass through again PE in crosslinkedly reach resistant to elevated temperatures characteristics; And the introducing of inorganic nano-particle (nano level polynite or nano level clay) more can increase substantially the softening point temperature of heat-resistant clothing hot melt adhesive; The present invention has suit property, and the product of processing has the good mechanical performance, good heat resistance, model keeping character is good and characteristics such as anti-organic corrosion.
2, preparation technology is simple, and equipment requirements is low, has efficient, easy and economic characteristics, and raw material is easy to get, and cost is low, and convenient operation and control is easy to realize suitability for industrialized production.
3, the hot melt adhesive that obtains of the present invention can be widely used in fields such as casing, plastics, metal, and heat is not the high-grade clothing field, variforms such as its shape can sheet, film, particle and block.
4, need not specific installation, on conventional melt-processed equipment, can produce heat-resistant clothing hot melt adhesive.
Embodiment
Embodiment 1, and making step is following:
1) Vestolen PP 7052 0.29g and the dimethacrylate Tetraglycol 99 fat 0.29g with PE 28.42g, grafted maleic anhydride puts into blender, behind 80 ℃ of following blend 10min, takes out subsequent use;
2) blender is put in the polynite of 9.90g nano level, and to add quality be the KH-550 silane coupling agent of 0.10g, behind 80 ℃ of following blend 20min, take out subsequent use;
3) 29.00g PET base material is at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) intermingling material that obtains puts into blender and carries out blend 10min, and temperature is 80 ℃;
4) slowly pour 20.00g rosin, 10.00gPE wax and 2.00g antioxidant 1010 again into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
Through test, the heat-resistant clothing hot melt adhesive mass component of acquisition is: the Vestolen PP 7052 0.29g of PET 29.00g, PE 28.42g, grafted maleic anhydride, dimethacrylate Tetraglycol 99 fat 0.29g, nano level polynite 9.90g, KH-550 silane coupling agent 0.10g, rosin 20.00g, PE wax 10.00g, 2.00g antioxidant 1010.
Embodiment 2, and making step is following:
1) Vilaterm 0.68g and the dimethacrylate Tetraglycol 99 fat 1.36g with PE 31.96g, grafted maleic anhydride puts into blender, behind 80 ℃ of following blend 10min, takes out subsequent use;
2) blender is put in the polynite of 8.82g nano level, and to add quality be the Triple Pressed Stearic Acid of 0.18g, behind 80 ℃ of following blend 20min, take out subsequent use;
3) 30.00g PET base material is at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) intermingling material that obtains puts into blender and carries out blend 10min, and temperature is 80 ℃;
4) slowly pour 18.00g rosin, 8.00gPE wax and 1.00g antioxidant 1010 again into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
Through test, the heat-resistant clothing hot melt adhesive mass component of acquisition is: the Vilaterm 0.68g of PET 30.00g, PE 31.96g, grafted maleic anhydride, dimethacrylate Tetraglycol 99 fat 1.36g, nano level polynite 8.82g, Triple Pressed Stearic Acid 0.18g, rosin 18.00g, PE wax 8.00g, 1.00g antioxidant 1010.
Embodiment 3, and making step is following:
1) Vestolen PP 7052 1.14g and the trimethylammonium vinylformic acid trihydroxy-propyl ester 0.76g with PE 36.10g, grafted maleic anhydride puts into blender, behind 80 ℃ of following blend 10min, takes out subsequent use;
2) 7.76g nano level clay is put into blender, and to add quality be the KH-793 silane coupling agent of 0.24g, behind 80 ℃ of following blend 20min, take out subsequent use;
3) 32.00g PET base material is at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) intermingling material that obtains puts into blender and carries out blend 10min, and temperature is 80 ℃;
4) slowly pour 16.00g 145 resins, 5.50g PP wax and 0.50g oxidation inhibitor 1098 again into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
Through test, the heat-resistant clothing hot melt adhesive mass component of acquisition is: the Vestolen PP 7052 1.14g of PET 32.00g, PE 36.10g, grafted maleic anhydride, trimethylammonium vinylformic acid trihydroxy-propyl ester 0.76g, nano level clay 7.76g, KH-793 silane coupling agent 0.24g, 145 resin 16.00g, PP wax 5.50g, 0.50g oxidation inhibitor 1098.
Embodiment 4, and making step is following:
1) Vilaterm 1.60g and the carbon black 1.20g with PE 37.20g, grafted maleic anhydride puts into blender, behind 80 ℃ of following blend 10min, takes out subsequent use;
2) 6.72g nano level clay is put into blender, and to add quality be the KH-793 silane coupling agent of 0.28g, behind 80 ℃ of following blend 20min, take out subsequent use;
3) 34.00g PET base material is at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) intermingling material that obtains puts into blender and carries out blend 10min, and temperature is 80 ℃;
4) slowly pour 145 resin 14.00g, PE wax 3.50g and 1.50g antioxidant 1010 again into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
Through test, the heat-resistant clothing hot melt adhesive mass component of acquisition is: the Vilaterm 1.60g of PET 34.00g, PE 37.20g, grafted maleic anhydride, carbon black 1.20g, nano level clay 6.72g, KH-793 silane coupling agent 0.28g, 145 resin 14.00g, PE wax 3.50g, 1.50g antioxidant 1010.
Embodiment 5, and making step is following:
1) with the Vestolen PP 7052 1.60g and the SiCl of PE 28.80g, grafted maleic anhydride
21.60g put into blender, behind 80 ℃ of following blend 10min, take out subsequent use;
2) blender is put in the polynite of 5.70g nano level, and to add quality be the NDZ-201 titanate coupling agent of 0.30g, behind 80 ℃ of following blend 20min, take out subsequent use;
3) 36.00g PA base material is at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) intermingling material that obtains puts into blender and carries out blend 10min, and temperature is 80 ℃;
4) slowly pour 17.00g terpine resin, 7.20g PE wax and 1.80g oxidation inhibitor 1098 again into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
Through test, the heat-resistant clothing hot melt adhesive mass component of acquisition is: PA 36.00g, PE 28.80g, the Vestolen PP 7052 1.60g of grafted maleic anhydride, SiCl
21.60g, nano level polynite 5.70g, NDZ-201 titanate coupling agent 0.30g, terpine resin 17.00g, PE wax 7.20g, 1.80g oxidation inhibitor 1098.
Embodiment 6, and making step is following:
1) with the Vilaterm 0.42g and the SiCl of PE 41.58g, grafted maleic anhydride
20.42g put into blender, behind 80 ℃ of following blend 10min, take out subsequent use;
2) 4.95g nano level clay is put into blender, and to add quality be the NDZ-201 titanate coupling agent of 0.05g, behind 80 ℃ of following blend 20min, take out subsequent use;
3) 38.00g PA base material is at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) intermingling material that obtains puts into blender and carries out blend 10min, and temperature is 80 ℃;
4) slowly pour 10.00g terpine resin, 4.70g PE wax and 0.30g antioxidant 1010 again into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
Through test, the heat-resistant clothing hot melt adhesive mass component of acquisition is: PA 38.00g, PE 41.58g, the Vilaterm 0.21g of grafted maleic anhydride, SiCl
20.21g, nano level clay 4.95g, NDZ-201 titanate coupling agent 0.05g, terpine resin 10.00g, PE wax 4.70g, 0.30g antioxidant 1010.
Embodiment 7, and making step is following:
1) with the Vestolen PP 7052 0.72g and the CCl of PE 33.84g, grafted maleic anhydride
41.44g put into blender, behind 80 ℃ of following blend 10min, take out subsequent use;
2) blender is put in the polynite of 3.92g nano level, and to add quality be the NDZ-201 titanate coupling agent of 0.08g, behind 80 ℃ of following blend 20min, take out subsequent use;
3) 40.00g TPU base material is at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) intermingling material that obtains puts into blender and carries out blend 10min, and temperature is 80 ℃;
4) slowly pour 9.00g polymerized rosin, 9.70g PP wax and 1.30g oxidation inhibitor 1098 again into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
Through test, the heat-resistant clothing hot melt adhesive mass component of acquisition is: TPU 40.00g, PE 33.84g, the Vestolen PP 7052 0.72g of grafted maleic anhydride, CCl
41.44g, nano level polynite 3.92g, NDZ-201 titanate coupling agent 0.08g, polymerized rosin 9.00g, PP wax 9.70g, 1.30g oxidation inhibitor 1098.
Embodiment 8, and making step is following:
1) the poly quality with PE 41.80g, grafted maleic anhydride is 1.32g and CCl
40.88g put into blender, behind 80 ℃ of following blend 10min, take out subsequent use;
2) 2.91g nano level clay is put into blender, and to add quality be the NDZ-201 titanate coupling agent of 0.09g, behind 80 ℃ of following blend 20min, take out subsequent use;
3) 42.00g TPU base material is at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) intermingling material that obtains puts into blender and carries out blend 10min, and temperature is 80 ℃;
4) slowly pour 5.00g polymerized rosin, 5.90g PE wax and 0.10g antioxidant 1010 again into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
Through test, the heat-resistant clothing hot melt adhesive mass component of acquisition is: the poly quality of TPU 42.00g, PE 41.80g, grafted maleic anhydride is 1.32g, CCl
40.88g, nano level clay 2.91g, NDZ-201 titanate coupling agent 0.09g, polymerized rosin 5.00g, PP wax 5.90g, 0.10g antioxidant 1010.
Embodiment 9, and making step is following:
1) Vestolen PP 7052 1.20g and the NaF 0.90g with PE 27.90g, grafted maleic anhydride puts into blender, behind 80 ℃ of following blend 10min, takes out subsequent use;
2) blender is put in the polynite of 1.92g nano level, and to add quality be the Triple Pressed Stearic Acid of 0.08g, behind 80 ℃ of following blend 20min, take out subsequent use;
3) 44.00g EVA base material is at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) intermingling material that obtains puts into blender and carries out blend 10min, and temperature is 80 ℃;
4) slowly pour 20.00g petroleum resin, 3.20g paraffin and 0.80g oxidation inhibitor 1098 again into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
Through test, the heat-resistant clothing hot melt adhesive mass component of acquisition is: the Vestolen PP 7052 1.20g of EVA 44.00g, PE 27.90g, grafted maleic anhydride, NaF 0.90g, nano level polynite 1.92g, Triple Pressed Stearic Acid 0.08g, petroleum resin 20.00g, paraffin 3.20g, 0.80g oxidation inhibitor 1098.
Embodiment 10, and making step is following:
1) Vilaterm 2.32g and the NaF 2.32g with PE 41.81g, grafted maleic anhydride puts into blender, behind 80 ℃ of following blend 10min, takes out subsequent use;
2) 0.95g nano level clay is put into blender, and to add quality be the Triple Pressed Stearic Acid of 0.05g, behind 80 ℃ of following blend 20min, take out subsequent use;
3) 46.45g EVA base material is at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) intermingling material that obtains puts into blender and carries out blend 10min, and temperature is 80 ℃;
4) slowly pour 5.00g petroleum resin, 1.00g paraffin and 0.10g oxidation inhibitor 1018 again into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.
Through test, the heat-resistant clothing hot melt adhesive mass component of acquisition is: the Vilaterm 2.32g of EVA 46.45g, PE 41.81g, grafted maleic anhydride, NaF 2.32g, nano level clay 0.95g, Triple Pressed Stearic Acid 0.05g, petroleum resin 5.00g, paraffin 1.00g, 0.10g oxidation inhibitor 1018.
After the heat-resistant clothing hot melt adhesive that the foregoing description is obtained was applied to adhesive lining, it is crosslinked that heat-resistant clothing hot melt adhesive is produced, and obtains the temperature tolerance product.
Claims (8)
1. heat-resistant clothing hot melt adhesive; It is characterized in that forming by mass percentage: hot melt adhesive 29～46.45%, PE 26.1～45.52%, expanding material 0.29～2.32%, sensitizer or sensitizing agent 0.29～2.32%, nano level polynite or nano level clay 0.95～9.9%, compatilizer 0.05～0.5%, tackifier 5～20%, softening agent 1～10%, oxidation inhibitor 0.1～2%, the wherein combination of one or more among hot melt adhesive employing PET, PA, TPU and the EVA by following material; Expanding material adopts the Vestolen PP 7052 of grafted maleic anhydride or the PE of grafted maleic anhydride; Sensitizer is a polyfunctional group, adopts at least a in dimethacrylate Tetraglycol 99 ester and the trimethylammonium vinylformic acid trihydroxy-propyl ester; Sensitizing agent is active small molecules, adopts SiCl
2, CCl
4, at least a in NaF and the carbon black.
2. heat-resistant clothing hot melt adhesive according to claim 1 is characterized in that: the combination of one or more in PE employing high-pressure polyethylene, high density polyethylene(HDPE) and the linear low density polyethylene.
3. heat-resistant clothing hot melt adhesive according to claim 1 is characterized in that: the particle diameter of nano level polynite and nano level clay is all less than 500nm.
4. heat-resistant clothing hot melt adhesive according to claim 1 is characterized in that: compatilizer adopts at least a in silane coupling agent, titanate coupling agent and the Triple Pressed Stearic Acid.
5. heat-resistant clothing hot melt adhesive according to claim 1 is characterized in that: tackifier are at least a in rosin, polymerized rosin, 145 resins, 138 resins, terpine resin, petroleum resin and the hydrogenated petroleum resin.
6. heat-resistant clothing hot melt adhesive according to claim 1 is characterized in that: softening agent is at least a in PE wax, PP wax, the paraffin.
7. heat-resistant clothing hot melt adhesive according to claim 1 is characterized in that: oxidation inhibitor is at least a in antioxidant 1010 and the oxidation inhibitor 1098.
8. the preparation method of a heat-resistant clothing hot melt adhesive as claimed in claim 1 is characterized in that adopting following steps:
1) PE, expanding material, sensitizer or sensitizing agent are put into blender, behind 80 ℃ of following blend 10min, take out subsequent use;
2) blender is put in nano level polynite or nano level clay, and added compatilizer, behind 80 ℃ of following blend 20min, take out subsequent use;
3) PET, PA, TPU or EVA base material are at first put into blender, put into the intermingling material mixing 10min of step 1) preparation then, temperature is 80 ℃; Again then with step 2) nano level polynite or the nano level clay through the compatilizer modification that obtain put into blender blend 10min, and temperature is 80 ℃;
4) slowly pour tackifier, softening agent, oxidation inhibitor into, blend 20min in blender, temperature is 80 ℃;
5) raw material that the step 4) blend is good joins and carries out blend on the twin screw extruder and extrude, and then blend composition is carried out granulation, cooling and pelletizing and promptly gets heat-resistant clothing hot melt adhesive.