CN101831097A - 一种生物降解地膜 - Google Patents

一种生物降解地膜 Download PDF

Info

Publication number
CN101831097A
CN101831097A CN201010149437A CN201010149437A CN101831097A CN 101831097 A CN101831097 A CN 101831097A CN 201010149437 A CN201010149437 A CN 201010149437A CN 201010149437 A CN201010149437 A CN 201010149437A CN 101831097 A CN101831097 A CN 101831097A
Authority
CN
China
Prior art keywords
percent
mulching film
biodegradable
film
biodegradable mulching
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201010149437A
Other languages
English (en)
Other versions
CN101831097B (zh
Inventor
王惠民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGZHOU BIOLEGEEN ECOTECH MATERIAL Co Ltd
Original Assignee
CHANGZHOU BIOLEGEEN ECOTECH MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGZHOU BIOLEGEEN ECOTECH MATERIAL Co Ltd filed Critical CHANGZHOU BIOLEGEEN ECOTECH MATERIAL Co Ltd
Priority to CN2010101494373A priority Critical patent/CN101831097B/zh
Publication of CN101831097A publication Critical patent/CN101831097A/zh
Application granted granted Critical
Publication of CN101831097B publication Critical patent/CN101831097B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明一种生物降解地膜，其组份的重量百分比为：合金母粒33～68％；7042(LDPE)30～65％；1F7B 5～7％。所述合金母粒组份的重量百分比为：叔丁过氧异丙基苯0.01～0.03％；富马酸1.50～2.25％；微晶蜡4.50～5.60％；聚乙烯蜡3.60～5.40％；MG70 3.00～4.20％；N210 9.00～13.0％；玉米淀粉68～80％。本发明的积极效果是：能适应各地气候、土壤环境及不同农作物的要求，在设计寿命内开始降解，不影响下季农作物种植，地膜降解均匀、彻底；解决了耐水性和亲水性的平衡问题，地膜贴地性更好；比重小，地膜厚度仅为0.005mm，耗料少，使用成本低，可大面积推广应用。

Description

一种生物降解地膜
【技术领域】
本发明涉及生物材料技术领域，涉及生物降解薄膜的制备，具体地说，是一种生物降解地膜。
【背景技术】
农用地膜是继种子、化肥、农药之后的农业重要生产资料。地膜具有良好的增温保墒效果，能大幅提高农作物的产量。但是，随着大规模使用普通的塑料地膜，造成地膜碎片大量残留在土壤里。随着地膜碎片的积累，大量的残留地膜破坏了土壤结构，造成土壤板结、通透性变差、地力下降，严重影响农作物的生长发育和产量，使农作物减产。若每亩地残留的地膜超过22kg，农作物将减产25％；若每亩地残留的地膜超过50kg，土地将无法耕种，将导致荒漠化，它们对农业的可持续发展构成严重的威胁。
为解决农作物的正常耕作与保护环境及耕地之间的矛盾，市场迫切需要可降解的农用地膜，尤其是每亩耕地塑料地膜残留超过35kg的新疆垦区及我国的西北地区。在环保要求极其严格的日本、欧洲、北美等地区，对可调控的降解地膜都有着迫切的需求。
目前有光降解、氧化降解、生物降解几种降解地膜的制造技术。但是，由于地膜需要在各地迥异的气候、土壤环境中满足不同农作物不同的保温、保墒期的要求，要能按时降解，既不能提前，也不能推迟。所以降解地膜必须根据各地气候、土壤环境和不同农作物保温保墒期的要求设计降解寿命，这对地膜制造商有着极高的精确调控降解周期的技术要求。由于技术难度大、生产成本较高，至今市场上鲜有成功的降解地膜产品。
现有的生物降解地膜由于技术问题还存在一些不足，例如：①降解寿命不可调控，导致生物地膜提前或推后降解，失去了地膜对农作物保温保墒的作用；②制造地膜的母粒不能与聚乙烯(PE)结构重组，是一种包裹的形式，不能形成网络架桥的结构，造成可降解地膜的降解不均匀，降解不彻底，残留颗粒或碎片，造成二次污染；③不能解决耐水性和亲水性的平衡问题，其表现为，制成的地膜不能紧贴地表，容易被风吹走，作为地膜的功能性相对较差；④对原材料粒径有极高的要求，吹出的膜较厚，耗料多，成本较高。
【发明内容】
本发明的目的在于提供一种能适应各地迥异的气候和土壤环境，能满足不同农作物保温保墒期的要求，膜体更薄、贴地性更好、而且能完全降解、无污染、无残留、无需回收的生物降解地膜。
为实现以上目的，本发明采取的技术方案是：
一种生物降解地膜，其组份的重量百分比为：
合金母粒：33～68％；
7042(LDPE)：30～65％；
1F7B(LDPE)：5～7％；
所述合金母粒的组份的重量百分比为：
叔丁过氧异丙基苯(BIPB)：0.01～0.03％；
富马酸(反丁烯二酸)：1.50～2.25％；
微晶蜡：4.50～5.60％；
聚乙烯蜡：3.60～5.40％；
MG70(LDPE)：3.00～4.20％；
N210：9.00～13.0％；
玉米淀粉：68～80％。
所述的玉米淀粉为98目的工业淀粉。
本发明一种生物降解地膜的积极效果是：
(1)能适应各地迥异的气候和土壤环境，满足不同农作物保温保墒期的要求，在设计寿命内开始降解，既不提前，也不推后，不影响下一季农作物的种植；
(2)地膜降解的均匀而彻底，无残留、无污染、无需回收，综合使用成本低；
(3)解决了耐水性和亲水性平衡的问题，使地膜能贴在地表，不易被风吹走，作为地膜的功能性较好；
(4)比重小，地膜的厚度可以达到0.005mm，耗料少，使用成本相应较低。
【附图说明】
附图为本发明一种生物降解地膜的降解效果检测曲线图。
【具体实施方式】
在本发明一种生物降解地膜的具体实施中，可采取上述组分进行地膜的生产，其原料的来源可以是：
合金母粒采用常州百利基生物材料科技有限公司生产的产品；
7042(LDPE)采用广东茂名石化公司生产的产品；
1F7B(LDPE)采用北京燕山石化公司生产的产品。
国家合成树脂和塑料质量监督检验中心对本发明一种生物降解地膜的送检样品在紫外辐照温度为63℃，强度为1000uW/C m2的条件下进行了降解效果的检测。检测的结果见下表，按其制作的曲线图见附图：
序号 检验项目 单位   技术要求   实测值   单项判定
  1   粘均分子量   /   /   3.95×104   /
  2   红外   /   /   聚乙烯   /
  3   粘均分子量(紫外光照5天)   /   /   1.36×104   /
  4   粘均分子量(紫外光照10天)   /   /   1.07×104   /
序号 检验项目 单位   技术要求   实测值   单项判定
  5   粘均分子量(紫外光照15天)   /   /   0.60×104   /
  6   粘均分子量(紫外光照20天)   /   /   0.24×104   /
  7   粘均分子量(紫外光照25天)   /   /   0.015×104   /

Claims (3)

1.一种生物降解地膜，其特征在于，其组份的重量百分比为：
合金母粒：33～68％；
7042：30～65％；
1F7B：5～7％。
2.根据权利要求1所述的一种生物降解地膜，其特征在于，所述合金母粒的组份的重量百分比为：
叔丁过氧异丙基苯：0.01～0.03％；
富马酸：1.50～2.25％；
微晶蜡：4.50～5.60％；
聚乙烯蜡：3.60～5.40％；
MG70：3.00～4.20％；
N210：9.00～13.0％；
玉米淀粉：68～80％。
3.根据权利要求2所述的一种生物降解地膜，其特征在于，所述的玉米淀粉为98目的工业淀粉。
CN2010101494373A 2010-04-09 2010-04-09 一种生物降解地膜 Active CN101831097B (zh)