CN101818029B - Mixed polishing solution - Google Patents
Mixed polishing solution Download PDFInfo
- Publication number
- CN101818029B CN101818029B CN2010101623618A CN201010162361A CN101818029B CN 101818029 B CN101818029 B CN 101818029B CN 2010101623618 A CN2010101623618 A CN 2010101623618A CN 201010162361 A CN201010162361 A CN 201010162361A CN 101818029 B CN101818029 B CN 101818029B
- Authority
- CN
- China
- Prior art keywords
- sodium
- mixed
- polishing
- polishing solution
- emulsifying agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a mixed polishing solution which is prepared by mixing and stirring the following components: 10-30g/L of sodium tetraborate, 8-20g/L of sodium citrate, 1-3g/L of sodium silicate, 8-12g/L of sodium benzoate, 1-5ml/L of OP-10 emulsifying agent and the balance of water, wherein the sodium tetraborate and the sodium citrate are main polishing agents; the sodium silicate and the sodium benzoate are antirusting agents; and the OP-10 emulsifying agent is a degreasing agent. Compared with the prior art, the invention has the advantages that the mixed polishing solution is safe and non-toxic and has no offensive odour; favorable polishing performance is achieved due to taking the sodium tetraborate and the sodium citrate as the main polishing agents, and the surface of a polished valve is silver-white and bright; interprocess rust protection is not needed to be carried out on the polished valve due to taking the sodium silicate and the sodium benzoate as the antirusting agents; and the surface of the polished valve does absorb dust due to taking the OP-10 emulsifying agent as the degreasing agent.
Description
Technical field
The present invention relates to a kind of polishing fluid, belong to the chemical industry solutions product technical field, refer in particular to a kind of mixed polishing solution that is applicable to valve.
Background technology
Valve is a key part of mover, and its manufacturing processed will be passed through heat treatment step, and the valve surface after the thermal treatment can produce thermal oxide layer, and on the other hand, mechanical workout will be no longer carried out on some surface of the valve after the thermal treatment.So, need to adopt other method to remove thermal oxide layer, traditional method is to adopt shot peening, and its shortcoming is that dust pollution is big, and the valve surface is easy to generate tiny crack, and brightless; And use chemical etching method, valve surface can not produce tiny crack, but the valve surface is brightless, and the spot that stays after thermal oxide layer is sloughed can not be eliminated, and has so both influenced outward appearance, also gives the antirust difficulty that causes of valve.And be to solve the problem that chemical etching produces; Generally the valve after the chemical etching is packed into and have in the swivel arrangement of polishing sand and mixed polishing solution; Through turning effort the valve surface is constantly slided with polishing sand and mixed polishing solution and wiped, realize polishing the valve surface, yet; A little less than existing mixed polishing solution exists polishing performance; Get rusty easily after being easy to generate smell, surface of polished dust, polishing, need do problems such as rust prevention during manufacture processing, the present invention is promptly to the technological improvement of this mixed polishing solution.
Summary of the invention
The objective of the invention is to overcome shortcoming of the prior art with not enough, provide that a kind of polishing performance is good, safety non-toxic, easy to manufacture, the mixed polishing solution that has polishing and antirust function concurrently.
To achieve these goals, the present invention realizes by following technical scheme:
A kind of mixed polishing solution, every liter is mixed together by following component: sodium tetraborate 10-30g/L, Trisodium Citrate 8-20g/L, water glass 1-3g/L, Sodium Benzoate 8-12g/L, OP-10 emulsifying agent 1-5ml/L, surplus is a water; Wherein, sodium tetraborate and Trisodium Citrate are main rumbling compound, and water glass and Sodium Benzoate are rust-preventive agent, and the OP-10 emulsifying agent is a degreaser.
Further, described every liter of mixed polishing solution is mixed together by following component: sodium tetraborate 10-20g/L, and Trisodium Citrate 8-14g/L, water glass 1-3g/L, Sodium Benzoate 8-12g/L, OP-10 emulsifying agent 1-3ml/L, surplus is a water.
Further, described every liter of mixed polishing solution is mixed together by following component: sodium tetraborate 15g/L, and Trisodium Citrate 11g/L, water glass 2g/L, Sodium Benzoate 10g/L, OP-10 emulsifying agent 2ml/L, surplus is a water.
Further, described every liter of mixed polishing solution is mixed together by following component: sodium tetraborate 20-30g/L, and Trisodium Citrate 14-20g/L, water glass 1-3g/L, Sodium Benzoate 8-12g/L, OP-10 emulsifying agent 3-5ml/L, surplus is a water.
Further, described every liter of mixed polishing solution is mixed together by following component: sodium tetraborate 25g/L, and Trisodium Citrate 17g/L, water glass 2g/L, Sodium Benzoate 10g/L, OP-10 emulsifying agent 4ml/L, surplus is a water.
The present invention compared with prior art, its beneficial effect is: safety non-toxic, no bad smell; With sodium tetraborate and Trisodium Citrate is main rumbling compound, and polishing performance is good, the valve surface silvery white after the polishing, bright; With water glass and Sodium Benzoate is rust-preventive agent; Valve after the polishing need not carry out rust prevention during manufacture, and is degreaser with the OP-10 emulsifying agent, and the valve surface after the polishing is dust not.
In order to understand the present invention more clearly, below will set forth embodiment of the present invention.
Embodiment
Embodiment 1
The technical scheme of present embodiment: a kind of mixed polishing solution, its every liter solution is mixed together by following component: sodium tetraborate 10-30g/L, Trisodium Citrate 8-20g/L; Water glass 1-3g/L; Sodium Benzoate 8-12g/L, OP-10 emulsifying agent 1-5ml/L, surplus is a water; Wherein, sodium tetraborate and Trisodium Citrate are main rumbling compound, and water glass and Sodium Benzoate are rust-preventive agent, and the OP-10 emulsifying agent is a degreaser.
The mixed polishing solution that adopts the said technical scheme of present embodiment to produce, safety non-toxic, no bad smell; With sodium tetraborate and Trisodium Citrate is main rumbling compound, and polishing performance is good, the valve surface silvery white after the polishing, bright; With water glass and Sodium Benzoate is rust-preventive agent; Valve after the polishing need not carry out rust prevention during manufacture, and is degreaser with the OP-10 emulsifying agent, and the valve surface after the polishing is dust not.
Embodiment 2
Present embodiment is applied to structure iron; For making effect better, adopt following technical scheme: described every liter of mixed polishing solution is mixed together by following component: sodium tetraborate 10-20g/L, Trisodium Citrate 8-14g/L; Water glass 1-3g/L; Sodium Benzoate 8-12g/L, OP-10 emulsifying agent 1-3ml/L, surplus is a water.
The mixed polishing solution that adopts the said technical scheme of present embodiment to produce, safety non-toxic, no bad smell; With sodium tetraborate and Trisodium Citrate is main rumbling compound, and polishing performance is good, the valve surface silvery white after the polishing, bright; With water glass and Sodium Benzoate is rust-preventive agent; Valve after the polishing need not carry out rust prevention during manufacture, and is degreaser with the OP-10 emulsifying agent, and the valve surface after the polishing is dust not.
Embodiment 3
Present embodiment is applied to structure iron, and is based on embodiment 2, better for making effect; Adopt following technical scheme: described every liter of mixed polishing solution is mixed together by following component: sodium tetraborate 15g/L; Trisodium Citrate 11g/L, water glass 2g/L, Sodium Benzoate 10g/L; OP-10 emulsifying agent 2ml/L, surplus is a water.
The mixed polishing solution that adopts the said technical scheme of present embodiment to produce, safety non-toxic, no bad smell; With sodium tetraborate and Trisodium Citrate is main rumbling compound, and polishing performance is good, the valve surface silvery white after the polishing, bright; With water glass and Sodium Benzoate is rust-preventive agent; Valve after the polishing need not carry out rust prevention during manufacture, and is degreaser with the OP-10 emulsifying agent, and the valve surface after the polishing is dust not.
Embodiment 4
Present embodiment is applied to martensitic steel and austenitic steel; For making effect better, adopt following technical scheme: described every liter of mixed polishing solution is mixed together by following component: sodium tetraborate 20-30g/L, Trisodium Citrate 14-20g/L; Water glass 1-3g/L; Sodium Benzoate 8-12g/L, OP-10 emulsifying agent 3-5ml/L, surplus is a water.
The mixed polishing solution that adopts the said technical scheme of present embodiment to produce, safety non-toxic, no bad smell; With sodium tetraborate and Trisodium Citrate is main rumbling compound, and polishing performance is good, the valve surface silvery white after the polishing, bright; With water glass and Sodium Benzoate is rust-preventive agent; Valve after the polishing need not carry out rust prevention during manufacture, and is degreaser with the OP-10 emulsifying agent, and the valve surface after the polishing is dust not.
Embodiment 5
Present embodiment is applied to martensitic steel and austenitic steel, and is based on embodiment 4, better for making effect; Adopt following technical scheme: described every liter of mixed polishing solution is mixed together by following component: sodium tetraborate 25g/L; Trisodium Citrate 17g/L, water glass 2g/L, Sodium Benzoate 10g/L; OP-10 emulsifying agent 4ml/L, surplus is a water.
The mixed polishing solution that adopts the said technical scheme of present embodiment to produce, safety non-toxic, no bad smell; With sodium tetraborate and Trisodium Citrate is main rumbling compound, and polishing performance is good, the valve surface silvery white after the polishing, bright; With water glass and Sodium Benzoate is rust-preventive agent; Valve after the polishing need not carry out rust prevention during manufacture, and is degreaser with the OP-10 emulsifying agent, and the valve surface after the polishing is dust not.
The present invention is not limited to above-mentioned embodiment; If various changes of the present invention or modification are not broken away from the spirit and scope of the present invention; If these are changed and modification belongs within claim of the present invention and the equivalent technologies scope, then the present invention also is intended to comprise these changes and modification.
Claims (5)
1. mixed polishing solution, it is characterized in that: said every liter of mixed polishing solution is mixed together by following component:
Sodium tetraborate 10-30g/L, Trisodium Citrate 8-20g/L, water glass 1-3g/L, Sodium Benzoate 8-12g/L, OP-10 emulsifying agent 1-5ml/L, surplus is a water;
Wherein, sodium tetraborate and Trisodium Citrate are main rumbling compound, and water glass and Sodium Benzoate are rust-preventive agent, and the OP-10 emulsifying agent is a degreaser.
2. mixed polishing solution according to claim 1 is characterized in that: said every liter of mixed polishing solution is mixed together by following component:
Sodium tetraborate 10-20g/L, Trisodium Citrate 8-14g/L, water glass 1-3g/L, Sodium Benzoate 8-12g/L, OP-10 emulsifying agent 1-3ml/L, surplus is a water.
3. mixed polishing solution according to claim 2 is characterized in that: said every liter of mixed polishing solution is mixed together by following component:
Sodium tetraborate 15g/L, Trisodium Citrate 11g/L, water glass 2g/L, Sodium Benzoate 10g/L, OP-10 emulsifying agent 2ml/L, surplus is a water.
4. mixed polishing solution according to claim 1 is characterized in that: said every liter of mixed polishing solution is mixed together by following component:
Sodium tetraborate 20-30g/L, Trisodium Citrate 14-20g/L, water glass 1-3g/L, Sodium Benzoate 8-12g/L, OP-10 emulsifying agent 3-5ml/L, surplus is a water.
5. mixed polishing solution according to claim 4 is characterized in that: said every liter of mixed polishing solution is mixed together by following component:
Sodium tetraborate 25g/L, Trisodium Citrate 17g/L, water glass 2g/L, Sodium Benzoate 10g/L, OP-10 emulsifying agent 4ml/L, surplus is a water.