CN101814551A - Preparation method of back silver paste of solar cell - Google Patents
Preparation method of back silver paste of solar cell Download PDFInfo
- Publication number
- CN101814551A CN101814551A CN201010022844A CN201010022844A CN101814551A CN 101814551 A CN101814551 A CN 101814551A CN 201010022844 A CN201010022844 A CN 201010022844A CN 201010022844 A CN201010022844 A CN 201010022844A CN 101814551 A CN101814551 A CN 101814551A
- Authority
- CN
- China
- Prior art keywords
- preparation
- silver paste
- solar cell
- powder
- diethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a preparation method of a back silver paste of a solar cell. The method comprises the following steps: (1) mixing 200CP ethyl cellulose, 300CP ethyl cellulose and diethylene glycol monobutyl ether to obtain an adhesive; (2) mixing flake silver powder and glass powder to obtain a powder body; (3) mixing diethylene glycol monobutyl ether and terpineol to obtain a diluter; and (4) mixing the adhesive and the powder body, adjusting the fineness by utilizing a three-high mill, and adding the diluter to obtain the silver paste. The invention has the advantage of simple method, and is applicable to industrialized production; and the obtained silver paste has the advantages of good compactness of the silver layer, small contact resistance and high cell conversion rate.
Description
Technical field
The invention belongs to the preparation field of solar cell size, particularly relate to a kind of preparation method of back silver paste of solar cell.
Background technology
Back silver paste of solar cell is one of important raw and processed materials of solar cell as the back silver slurry of solar cell size, influences the key factor of solar cell power conversion.This slurry mainly contains function phase (silver powder), organic carrier (adhesive), glassy phase three most compositions.
Growing along with green energy resource, the photovoltaic industry is advanced by leaps and bounds, and the development of solar cell industry has welcome unprecedented prospect, and the transfer ratio to solar cell requires also more and more higher simultaneously.The exploitation of Ben Yin slurry is researched and developed the development of silver paste of solar cells both at home and abroad in order to satisfy.
Summary of the invention
Technical problem to be solved by this invention provides a kind of preparation method of back silver paste of solar cell, and this method is simple, is suitable for suitability for industrialized production; The silver paste silver layer compactness of gained is good, and contact resistance is little, the cell conversion rate height.
The preparation method of a kind of back silver paste of solar cell of the present invention comprises:
(1) mixes 200CP ethyl cellulose, 300CP ethyl cellulose and diethylene glycol butyl ether, the preparation adhesive;
(2) mix flake silver powder and glass dust, the preparation powder;
(3) mix diethylene glycol butyl ether and terpinol, prepared and diluted agent;
(4) adhesive of mixing 10~20% and 75~85% powder through three-high mill, are adjusted fineness, add 1~5% diluent, promptly obtain silver paste.
The weight ratio of described step (1) 200CP ethyl cellulose, 300CP ethyl cellulose and diethylene glycol butyl ether is 4%~8%: 2%~6%: 70%~90%.
The weight ratio of described step (2) flake silver powder and glass dust is 85%~95%: 5%~15%.
The weight ratio of described step (3) diethylene glycol butyl ether and terpinol is 50%~70%: 30%~50%.
Described step (4) fineness is less than 8 μ m.
Beneficial effect
(1) preparation method of the present invention is simple, is suitable for suitability for industrialized production;
(2) the silver paste silver layer compactness of gained of the present invention is good, and contact resistance is little, the cell conversion rate height.
Embodiment
Below in conjunction with specific embodiment, further set forth the present invention.Should be understood that these embodiment only to be used to the present invention is described and be not used in and limit the scope of the invention.Should be understood that in addition those skilled in the art can make various changes or modifications the present invention after the content of having read the present invention's instruction, these equivalent form of values fall within the application's appended claims institute restricted portion equally.
Embodiment 1
(1) mixes 200CP ethyl cellulose 2~4g, 300CP ethyl cellulose 1~3g, diethylene glycol butyl ether 10~30g, prepare bonding system;
(2) mix flake silver powder 70~75g, glass dust 5~10g, the preparation powder, after stirring evenly, ball milling 3-5 hour;
(3) mix diethylene glycol butyl ether 4~8g, terpinol 2~4g, prepared and diluted agent;
(4) mix above-mentioned adhesive and powder, through three-high mill to fineness less than 8 μ m, add diluent, stirred 1 hour, adjust viscosity with the small diluted amount agent, make silver and starch.
Claims (5)
1. the preparation method of a back silver paste of solar cell comprises:
(1) mixes 200CP ethyl cellulose, 300CP ethyl cellulose and diethylene glycol butyl ether, the preparation adhesive;
(2) mix flake silver powder and glass dust, the preparation powder;
(3) mix diethylene glycol butyl ether and terpinol, prepared and diluted agent;
(4) adhesive of mixing 10~20% and 75~85% powder through three-high mill, are adjusted fineness, add 1~5% diluent, promptly obtain silver paste.
2. the preparation method of a kind of back silver paste of solar cell according to claim 1, it is characterized in that: the weight ratio of described step (1) 200CP ethyl cellulose, 300CP ethyl cellulose and diethylene glycol butyl ether is 4%~8%: 2%~6%: 70%~90%.
3. the preparation method of a kind of back silver paste of solar cell according to claim 1, it is characterized in that: the weight ratio of described step (2) flake silver powder and glass dust is 85%~95%: 5%~15%.
4. the preparation method of a kind of back silver paste of solar cell according to claim 1, it is characterized in that: the weight ratio of described step (3) diethylene glycol butyl ether and terpinol is 50%~70%: 30%~50%.
5. the preparation method of a kind of back silver paste of solar cell according to claim 1, it is characterized in that: described step (4) fineness is less than 8 μ m.