CN101812198B - Waterproof product containing chlorinated polyethylene and preparation method thereof - Google Patents
Waterproof product containing chlorinated polyethylene and preparation method thereof Download PDFInfo
- Publication number
- CN101812198B CN101812198B CN2010101676719A CN201010167671A CN101812198B CN 101812198 B CN101812198 B CN 101812198B CN 2010101676719 A CN2010101676719 A CN 2010101676719A CN 201010167671 A CN201010167671 A CN 201010167671A CN 101812198 B CN101812198 B CN 101812198B
- Authority
- CN
- China
- Prior art keywords
- parts
- chlorinatedpolyethylene
- waterproof
- waterproof product
- chlorinated polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a waterproof product containing chlorinated polyethylene, in particular to a waterproof roll sheet containing chlorinated polyethylene and a preparation method, which solve the problem that the waterproof roll sheet in the prior art has low performance index and high formula cost. The waterproof product containing chlorinated polyethylene is prepared by the following steps: mixing and stirring an ethylene-octylene copolymer, the chlorinated polyethylene, linear high-pressure polyethylene, a filler intensifier, a soften plasticizer, phenol antioxidants, a heat stabilizer, a lubricating agent and light stabilizer; pelleting the raw materials with a plastics processing mill, a double-roller mill and a pelleter in sequence; feeding granules into a single screw extruder for extruding and forming by a die; and feeding formed materials into a three-roller cooling coining mill for rolling to form the waterproof roll sheet. The invention not only retains unique softness, extensibility and rebound elasticity of rubber, but also retains high tensile breaking strength of LLDPE (Linear Low Density Polyethylene); the whole sheet has good softness, glancing flatness and planeness; performance indexes exceed the national standard and relative standard of ministry of railways; the ageing resisting performance, physical performance and processing performance are excellent; and the production cost is low.
Description
Technical field
The present invention relates to a kind of waterproof product that contains chlorinatedpolyethylene, be specially a kind of waterproof roll that has chlorinatedpolyethylene and preparation method thereof.
Background technology
At present each manufacturer special-purpose N class (without the composite bed coiled material) of bridge, L class (two-sided compound nonwoven cloth) type waterproof roll of producing adopts high-pressure polyethylene or linear low density polyethylene to come modified chlorinated polyethylene to do the waterproof roll matrix basically.Although the prescription of each manufacturer, technique difference all exist very large defective; (1) if take high-pressure polyethylene or linear low density polyethylene as main body, although every mechanical property can reach the related standards of the Ministry of Railways,, the pliability of product, planeness, rebound resilience do not reach the requirement of construction far away.Because the bridge construction Special waterproof coiled material has certain particular requirement to its pliability, planeness and rebound resilience, otherwise waterproof roll is comprehensive is bonded as one with cement based bridge floor with regard to being difficult to make.A lot of producers are therefore defective and can't normally use and be returned goods; (2) if take chlorinatedpolyethylene (CPE) as main body, the pliability of product, planeness, rebound resilience are all relatively good, but its mechanical performance index then differs greatly, particularly breaking tenacity can only be about 90N/cm/1.5mm (related standards of the Ministry of Railways is 〉=160N/cm/1.5mm-1.8mm); (3) if this bi-material of high-pressure polyethylene and chlorinatedpolyethylene is homogeneous phase, equity, its mechanical property and pliability, planeness, rebound resilience are then all defective.In addition, also have at present part producer to be material of main part with thermoplastic elastomer SBS or thermoplastic elastomer TPE etc., although various performance index can both reach requirement, formulation cost is too high, can not adapt to the running of present market economy.There is not yet up to now ethene-octene copolymer (POE) successful application at the report of bridge construction Special waterproof coiled material.
Summary of the invention
The present invention adopts high-pressure polyethylene to come modified chlorinated polyethylene to do the waterproof roll matrix in order to solve the special-purpose two class waterproof rolls of existing bridge construction basically, can't satisfy the product property indices fully.If adopting thermoplastic elastomer SBS or thermoplastic elastomer TPE is material of main part, cause the too high problem of formulation cost, a kind of modified chlorinated polyethylene waterproof roll and preparation method thereof is provided.
The present invention adopts following technical scheme to realize: a kind of waterproof product that contains chlorinatedpolyethylene, raw material by following parts by weight is made: 110～130 parts of ethene-octene copolymers, 10～30 parts of chlorinatedpolyethylenees, 20～60 parts of linear low density polyethylenes are filled 10～130 parts of tougheners, 5～20 parts in softening softening agent, 0.2～2 part of phenolic antioxidant, 0.2～2 part of thermo-stabilizer, 0.2～2 part of lubricant, 0.5～1.5 part of photostabilizer; Described phenolic antioxidant is that 50% phenols primary antioxidant 1010 and 50% phenols auxiliary antioxidant 168 are made by weight ratio, and described thermo-stabilizer is that 50% dibasic lead phosphite and 50% lead sulfate tribasic are made by weight ratio.
Described filling toughener is activated Calcium carbonate or colloid calcium carbonate; Described softening softening agent is any one in dioctyl phthalate (DOP), clorafin, imitative hydrogen oil or the naphthenic oil; Described lubricant is stearic acid or particle paraffin; Described photostabilizer is UV light absorber UV327 or UV531; Octene content is 30-50wt% in described ethene-octene copolymer, and cl content is 25-45wt% in the chlorinatedpolyethylene.。
In the above-mentioned prescription, ethene-octene copolymer (POE) is the thermoplastic elastomer with narrow molecular weight and uniformly short-chain branch distribution of U.S. DOW chemical company take metallocene as catalyzer, this elastomeric salient features with rubbery is very outstanding, has surpassed common elastomerics in very many-sided performance index.Why POE has excellent performance, can realize that high speed extrusion is relevant with following characteristics: the flexible chain coiled structure of (1) octene and crystalline ethylene chain make it have excellent toughness and have again good processibility as the physical crosslinking point; (2) relative molecular mass narrowly distributing, good with compatible polyolefin, have better flowability; (3) do not have unsaturated double-bond, excellent weather resistance and hard is in other elastomerics; (4) stronger shearing sensibility and melt strength can be realized high speed extrusion, improve output; (5) good flowability can be improved the dispersion effect of stopping composition, also can improve the weld mark strength of goods simultaneously.The singularity of POE molecular structure has been given its excellent mechanical property, rheological property and anti-ultraviolet property.Ethene-octene copolymer (POE) is to combine rubber and a kind of material of plastics advantage, its plastics at high temperature can flow mutually, then play at normal temperatures the effect of physical crosslinking point, this physical crosslinking is that heat is reversible, therefore it both can use the working method moulding of thermoplastics, it has again the elasticity of rubber in wide temperature range, the present invention first with ethene-octene copolymer (POE) successful application on the bridge construction Special waterproof coiled material.
Chlorinatedpolyethylene (CPE) is the chloride polyolefine of being made through chlorination by polyethylene, it is the armorphous chloride saturated elastomerics of a kind of line style, difference according to chlorinity can be divided into soft plastic (chlorinity is less than 25%), elastomerics (chlorinity 25%～45%) and rigid plastics (chlorinity 45%～70%), because the introducing of chlorine atom, so that easily causing the factor of chemical degradation and thermal destruction, primary structure disappears, thereby make it have good weathering resistance, flame resistivity and resistance to low temperature, the present invention quotes chlorinatedpolyethylene in design, except above-mentioned factor, also has the adhesion problem that important factor is exactly N class waterproof roll and cement matrix binding agent, because chlorinatedpolyethylene is a kind of macromolecular material with polarity, superior with the adhesive property of common bond, and POE, the adhesive property of LLDPE and common bond is poor, is difficult to bonding.Prove through test of many times, the present invention preferably is advisable at 35% chlorinatedpolyethylene with chlorinity.
Because above-mentioned two types elastomerics is added certain tenderizer, its tensile strength is had a greatly reduced quality do not reach the design requirements of product far away, even add suitable reinforcing filler, although intensity has some improvement, but with the design requirements of waterproof roll a certain distance is arranged still, and elongation also can descend by straight line, in order both to reach the design requirements of product performance index, consider again the formulation cost of product, the applicant is through test of many times and summary of experience, added linear low density polyethylene (LLDPE) as the plastics phase at prescription, through test in the situation that elongation loss is little, its tensile strength is greatly improved, fracture tensile strength 〉=the 18MPa of N class waterproof roll, tensile yield 〉=900%, fracture tensile strength 〉=the 200N/cm/1.5mm of the two-sided compound nonwoven cloth waterproof coiled material of L class, tensile yield 〉=800%, all other indexs are all above the related standards of national standard and the Ministry of Railways, and the component design cost of product also significantly descends.
For the further prescription of optimizing this product, the index of enhancing product performance, the present invention has also added following raw material, and the effect of filling toughener is the intensity of increase product partly and the formulation cost of reduction product; The Main Function of softening softening agent is the flexibility that increases product; The Main Function of phenolic antioxidant is to improve product heat resistanceheat resistant, ageing resistance in use, prolongs the work-ing life of waterproof roll; The effect of thermo-stabilizer mainly is the thermolysis that prevents or stop chlorinatedpolyethylene to cause owing to high temperature in the course of processing; The Main Function of lubricant is to prevent superpolymer in the process of converted products, and the high temperature that excessively produces owing to friction decomposes superpolymer; The Main Function of photostabilizer is to prevent owing to the width of cloth of light is penetrated the superpolymer decomposition that causes.
A kind of method for preparing the waterproof product that contains chlorinatedpolyethylene may further comprise the steps:
(1) batching: various raw materials are mixed in proportion, stir under the normal temperature; (2) granulation: the compound that stirs is dropped into the closed plastics processing mill, the temperature of closed plastics processing mill is controlled at 150～170 ℃, banburying discharging after 10～15 minutes, directly enter twin-roll machine, the slice when roller temperature of twin-roll machine is controlled at 140～150 ℃, roll spacing and is set to 3.5mm～4mm, and then through the dicing machine pelletizing; (3) pellet that step (2) obtained drops into that single screw extrusion machine is extruded and through mould molding: the machine barrel top temperature of single screw extrusion machine is that to be controlled at 30～40 rev/mins, the core temperature of single screw extrusion machine mould be 10～15 ℃ of the core temperatures that 180～220 ℃, the both sides temperature of mould are higher than mould for 180～200 ℃, screw speed; (4) molding mass that step (3) is obtained drops into the roll-in of three rollers coolings embossing machine and goes out the N class without composite bed waterproof roll or the two-sided compound nonwoven cloth type of L class waterproof roll: it is that 50～70 ℃, lower roller temperature are that 40～60 ℃, upper roller temperature are 60～80 ℃ that the roller temperature of three rollers cooling embossing machine is controlled at middle roller temperature; (5) naturally cooling, cultivation limit.Above-mentioned closed plastics processing mill, twin-roll machine, dicing machine, single screw extrusion machine and three rollers cooling embossing machine are existing known device, and its structure and principle of work are that those of ordinary skill in the art is known.
The present invention adopts thermoplastic elastomer to be mutually ethene-octene copolymer and chlorinatedpolyethylene, plastics are linear low density polyethylene mutually, and suitable in addition an amount of softening agent, fill toughener and various subsidiary material, be the N class of matrix through blending extrusion, the bridge Special waterproof coiled material of L type, produce this rubber plastic blend type waterproof roll and do not need to vulcanize complete processing, can adopt the complete processing of processing ordinary hot thermoplastic plastic, the maximum characteristics of product are both to have kept the distinctive pliability of rubber and higher elongation, rebound resilience, kept again the higher fracture stretching Strong degree of LLDPE, the pliability of integral sheet, planeness, planeness is better, its performance index are considerably beyond the related standards of national standard and the Ministry of Railways, fracture tensile strength＞the 18MPa of the N class waterproof roll of making, tensile yield＞900%, fracture tensile strength＞the 200N/cm/1.5mm of the two-sided compound nonwoven cloth waterproof coiled material of L class, tensile yield＞800%.And the present invention adopts thermoplastic elastomer, the common modification linear low density polyethylene of thermoplastic elastomer, not only property indices is superior, the more important thing is formulation cost of the present invention with other thermoplastic elastomer or rubber phase ratio, at least to hang down about 1/3rd, in a word, adopt waterproof roll ageing-resistant performance, physicals and processing characteristics that prescription of the present invention and method obtain all better and production cost is lower, have good application prospect.
Embodiment
Embodiment 1:
A kind of waterproof product that contains chlorinatedpolyethylene, raw material by following parts by weight is made: octene content is 110 parts of ethene-octene copolymers of 40wt%, cl content is 10 parts of the chlorinatedpolyethylenees of 30wt%, 20 parts of linear low density polyethylenes, 10 parts of activated Calcium carbonates, 5 parts of dioctyl phthalate (DOP)s, 0.2 part of phenolic antioxidant, 0.2 part of thermo-stabilizer, 0.2 part of stearic acid, 0.5 part of UV light absorber (UV327); Phenolic antioxidant is that 50% phenols primary antioxidant 1010 and 50% phenols auxiliary antioxidant 168 are made by weight ratio, and thermo-stabilizer is that 50% dibasic lead phosphite and 50% lead sulfate tribasic are made by weight ratio.
Preparation contains the method for the waterproof product of chlorinatedpolyethylene, may further comprise the steps: (1) batching: various raw materials are mixed in proportion, stir under the normal temperature; (2) granulation: the compound that stirs is dropped into the closed plastics processing mill, the temperature of closed plastics processing mill is controlled at 150 ℃, banburying discharging after 10 minutes, directly enter twin-roll machine, the roller temperature of twin-roll machine is controlled at 140 ℃, slice when roll spacing is set to 3.5mm, and then through the dicing machine pelletizing; (3) pellet that step (2) obtained drops into that single screw extrusion machine is extruded and through mould molding: the machine barrel top temperature of single screw extrusion machine is that to be controlled at 30 rev/mins, the core temperature of single screw extrusion machine mould be 10 ℃ of the core temperatures that 190 ℃, the both sides temperature of mould are higher than mould for 190 ℃, screw speed; (4) molding mass that step (3) is obtained drops into the roll-in of three rollers coolings embossing machine and goes out the N class without composite bed waterproof roll or the two-sided compound nonwoven cloth type of L class waterproof roll: it is that 50 ℃, lower roller temperature are that 40 ℃, upper roller temperature are 60 ℃ that the roller temperature of three rollers cooling embossing machine is controlled at middle roller temperature; (5) naturally cooling, cultivation limit.
Embodiment 2:
A kind of waterproof product that contains chlorinatedpolyethylene, raw material by following parts by weight is made: octene content is 115 parts of ethene-octene copolymers of 35wt%, cl content is 15 parts of the chlorinatedpolyethylenees of 25wt%, 30 parts of linear low density polyethylenes, 40 parts in colloid calcium carbonate, 10 parts of clorafins, 0.5 part of phenolic antioxidant, 0.5 part of thermo-stabilizer, 0.5 part in particle paraffin, 1 part of UV light absorber (UV327); Phenolic antioxidant is that 50% phenols primary antioxidant 1010 and 50% phenols auxiliary antioxidant 168 are made by weight ratio, and thermo-stabilizer is that 50% dibasic lead phosphite and 50% lead sulfate tribasic are made by weight ratio.
Preparation contains the method for the waterproof product of chlorinatedpolyethylene, may further comprise the steps: (1) batching: various raw materials are mixed in proportion, stir under the normal temperature; (2) granulation: the compound that stirs is dropped into the closed plastics processing mill, the temperature of closed plastics processing mill is controlled at 170 ℃, and banburying discharging after 15 minutes directly enters twin-roll machine, the roller temperature of twin-roll machine is controlled at 150 ℃, slice when roll spacing is set to 4mm, and then through the dicing machine pelletizing; (3) pellet that step (2) obtained drops into that single screw extrusion machine is extruded and through mould molding: the machine barrel top temperature of single screw extrusion machine is that to be controlled at 40 rev/mins, the core temperature of single screw extrusion machine mould be 15 ℃ of the core temperatures that 220 ℃, the both sides temperature of mould are higher than mould for 200 ℃, screw speed; (4) molding mass that step (3) is obtained drops into the roll-in of three rollers coolings embossing machine and goes out the N class without composite bed waterproof roll or the two-sided compound nonwoven cloth type of L class waterproof roll: it is that 70 ℃, lower roller temperature are that 60 ℃, upper roller temperature are 80 ℃ that the roller temperature of three rollers cooling embossing machine is controlled at middle roller temperature; (5) naturally cooling, cultivation limit.
Embodiment 3:
A kind of waterproof product that contains chlorinatedpolyethylene, raw material by following parts by weight is made: octene content is 120 parts of ethene-octene copolymers of 45wt%, cl content is 20 parts of the chlorinatedpolyethylenees of 35wt%, 40 parts of linear low density polyethylenes, 70 parts of activated Calcium carbonates, 15 parts of imitative hydrogen oil, 1.5 parts of phenolic antioxidants, 1.5 parts of thermo-stabilizers, 1.5 parts in particle paraffin, 1 part of UV light absorber (UV531); Phenolic antioxidant is that 50% phenols primary antioxidant 1010 and 50% phenols auxiliary antioxidant 168 are made by weight ratio, and thermo-stabilizer is that 50% dibasic lead phosphite and 50% lead sulfate tribasic are made by weight ratio.
Preparation contains the method for the waterproof product of chlorinatedpolyethylene, may further comprise the steps: (1) batching: various raw materials are mixed in proportion, stir under the normal temperature; (2) granulation: the compound that stirs is dropped into the closed plastics processing mill, the temperature of closed plastics processing mill is controlled at 170 ℃, banburying discharging after 10 minutes, directly enter twin-roll machine, the roller temperature of twin-roll machine is controlled at 150 ℃, slice when roll spacing is set to 3.5mm, and then through the dicing machine pelletizing; (3) pellet that step (2) obtained drops into that single screw extrusion machine is extruded and through mould molding: the machine barrel top temperature of single screw extrusion machine is that to be controlled at 35 rev/mins, the core temperature of single screw extrusion machine mould be 10 ℃ of the core temperatures that 200 ℃, the both sides temperature of mould are higher than mould for 185 ℃, screw speed; (4) molding mass that step (3) is obtained drops into the roll-in of three rollers coolings embossing machine and goes out the N class without composite bed waterproof roll or the two-sided compound nonwoven cloth type of L class waterproof roll: it is that 55 ℃, lower roller temperature are that 50 ℃, upper roller temperature are 65 ℃ that the roller temperature of three rollers cooling embossing machine is controlled at middle roller temperature; (5) naturally cooling, cultivation limit.
Embodiment 4:
A kind of waterproof product that contains chlorinatedpolyethylene, raw material by following parts by weight is made: octene content is 125 parts of ethene-octene copolymers of 40wt%, cl content is 25 parts of the chlorinatedpolyethylenees of 40wt%, 50 parts of linear low density polyethylenes, 100 parts of activated Calcium carbonates, 15 parts of naphthenic oils, 1.5 parts of phenolic antioxidants, 1.5 parts of thermo-stabilizers, 1.5 parts of stearic acid, 1.0 parts of UV light absorber (UV531); Phenolic antioxidant is that 50% phenols primary antioxidant 1010 and 50% phenols auxiliary antioxidant 168 are made by weight ratio, and thermo-stabilizer is that 50% dibasic lead phosphite and 50% lead sulfate tribasic are made by weight ratio.
Preparation contains the method for the waterproof product of chlorinatedpolyethylene, may further comprise the steps: (1) batching: various raw materials are mixed in proportion, stir under the normal temperature; (2) granulation: the compound that stirs is dropped into the closed plastics processing mill, the temperature of closed plastics processing mill is controlled at 165 ℃, banburying discharging after 12 minutes, directly enter twin-roll machine, the slice when roller temperature of twin-roll machine is controlled at 145 ℃, roll spacing and is set to 3.5mm～4mm, and then through the dicing machine pelletizing; (3) pellet that step (2) obtained drops into that single screw extrusion machine is extruded and through mould molding: the machine barrel top temperature of single screw extrusion machine is that to be controlled at 38 rev/mins, the core temperature of single screw extrusion machine mould be 14 ℃ of the core temperatures that 210 ℃, the both sides temperature of mould are higher than mould for 195 ℃, screw speed; (4) molding mass that step (3) is obtained drops into the roll-in of three rollers coolings embossing machine and goes out the N class without composite bed waterproof roll or the two-sided compound nonwoven cloth type of L class waterproof roll: it is that 60 ℃, lower roller temperature are that 55 ℃, upper roller temperature are 75 ℃ that the roller temperature of three rollers cooling embossing machine is controlled at middle roller temperature; (5) naturally cooling, cultivation limit.
Embodiment 5:
A kind of waterproof product that contains chlorinatedpolyethylene, raw material by following parts by weight is made: octene content is 130 parts of ethene-octene copolymers of 35wt%, cl content is 30 parts of the chlorinatedpolyethylenees of 25wt%, 60 parts of linear low density polyethylenes, 130 parts in colloid calcium carbonate, 20 parts of clorafins, 2 parts of phenolic antioxidants, 2 parts of thermo-stabilizers, 2 parts of lubricants, 1.5 parts of UV light absorber (UV327); Phenolic antioxidant is that 50% phenols primary antioxidant 1010 and 50% phenols auxiliary antioxidant 168 are made by weight ratio, and thermo-stabilizer is that 50% dibasic lead phosphite and 50% lead sulfate tribasic are made by weight ratio.
Preparation contains the method for the waterproof product of chlorinatedpolyethylene, may further comprise the steps: (1) batching: various raw materials are mixed in proportion, stir under the normal temperature; (2) granulation: the compound that stirs is dropped into the closed plastics processing mill, the temperature of closed plastics processing mill is controlled at 155 ℃, banburying discharging after 14 minutes, directly enter twin-roll machine, the slice when roller temperature of twin-roll machine is controlled at 147 ℃, roll spacing and is set to 3.5mm～4mm, and then through the dicing machine pelletizing; (3) pellet that step (2) obtained drops into that single screw extrusion machine is extruded and through mould molding: the machine barrel top temperature of single screw extrusion machine is that to be controlled at 32 rev/mins, the core temperature of single screw extrusion machine mould be 12 ℃ of the core temperatures that 205 ℃, the both sides temperature of mould are higher than mould for 188 ℃, screw speed; (4) molding mass that step (3) is obtained drops into the roll-in of three rollers coolings embossing machine and goes out the N class without composite bed waterproof roll or the two-sided compound nonwoven cloth type of L class waterproof roll: it is that 68 ℃, lower roller temperature are that 48 ℃, upper roller temperature are 80 ℃ that the roller temperature of three rollers cooling embossing machine is controlled at middle roller temperature; (5) naturally cooling, cultivation limit.
Claims (5)
1. waterproof product that contains chlorinatedpolyethylene, it is characterized in that being made by the raw material of following parts by weight: 125～130 parts of ethylene-octene copolymers, 10～30 parts of chlorinatedpolyethylenees, 20～60 parts of linear low density polyethylenes are filled 10～130 parts of tougheners, 5～20 parts in softening softening agent, 0.2～2 part of phenolic antioxidant, 0.2～2 part of thermo-stabilizer, 0.2～2 part of lubricant, 0.5～1.5 part of photostabilizer; Described phenolic antioxidant is that 50% phenols primary antioxidant 1010 and 50% auxiliary antioxidant 168 are made by weight ratio, described thermo-stabilizer is that 50% dibasic lead phosphite and 50% lead sulfate tribasic are made by weight ratio, octene content is 30-50wt% in the described ethylene-octene copolymer, and cl content is 25-45wt% in the chlorinatedpolyethylene.
According to claim 1 a kind of contain chlorinatedpolyethylene waterproof product, it is characterized in that described filling toughener is activated Calcium carbonate.
3. a kind of waterproof product that contains chlorinatedpolyethylene according to claim 1 and 2 is characterized in that described softening softening agent is any one in dioctyl phthalate (DOP), clorafin or the naphthenic oil.
4. a kind of waterproof product that contains chlorinatedpolyethylene according to claim 1 and 2 is characterized in that described lubricant is stearic acid or particle paraffin.
5. a kind of waterproof product that contains chlorinatedpolyethylene according to claim 1 and 2 is characterized in that described photostabilizer is UV light absorber UV327 or UV531.