A kind of environment-friendly tanning agent for leather, its preparation method and application
Technical field
The present invention relates to make the new technology in fur coat field, concrete, the present invention relates to a kind of fur tanning agent, its preparation method and application, fur tanning agent of the present invention is a kind of high-effect tanning agent of fur cheaply.
Background technology
Along with the adjustment of world's industrial structure and the world's process hides transfer with system fur coat industry center of gravity, leather and fur manufacturing center and trade center of gravity that China has developed into World Focusing (are seen Zhang Zongcai.Pollutant analysis in the process hides discharge " leather science and engineering ", 2002 (15): P44-48).
Chromic tanning is since invention, and in process hides and fur Industrial Application comparatively extensively and occupied dominant position, chromic tanning still has irreplaceable advantage in leather industry up till now.But the raising of Along with people's environmental consciousness; The pollution problem of chromic tanning receives people's attention day by day; Because sexavalent chrome has been proved and has had carinogenicity, one of index that the mass parts number average of sexavalent chrome in waste water classified as strict control by various countries environmental administration (is seen Tang Keyong.The source of pollution of chromium and harm thereof " leather science and engineering ", 1997 (7): P33-48), how to solve the key that the pollution of chromium problem becomes China's process hides system fur coat industrial sustainable development, wherein develop the focus that the chrome-free tanning chemical materials becomes current research.
Chemical name is the compound of four methylol phosphonium salts (tetrakishydroxymethylphosphonium), is called THP salt or THPS usually for short, and its chemical molecular formula is C
4H
12O
4P.THP salt mainly exists with tetrakis hydroxymethyl phosphonium chloride (THPC) and two kinds of forms of tetra methylol sulfuric acid phosphonium (THPS).In the prior art, THP salt is a kind of novel auxiliary chemicals, the fire retardant of making textiles commonly used, and THP salt also is a kind of novel sterilant, is widely used in cooling water treatment system and oil-field water treatment system.
When THP salt is used for tan leather separately, stiff, the consolidation of the dermatotome that obtains; Extensibility is relatively poor in length and breadth in system fur coat process, and the following process of fur coat is caused disadvantageous effect.In early days, U.S. Pat P 3 104 151 once reported the method that THP salt and phenols is combined to be used for leather tanning; November 8 nineteen ninety-five, disclosed EP0681030A2 described THPS, as as the application of casein linking agent in leather finish; The open CN1278304A of the Chinese patent of Britain Rhodia consumption special Co., Ltd (open day on December 27th, 2000) discloses and has proposed to tan or the crosslinking reaction realization leather tanning in retanning stage the master through collagen and three (methylol) phosphonium salt or with the condenses of four (methylol) phosphonium salts and acid amides or amine; Proposition THPS such as A.D.Convigton and aminoresin performed polymer are used, can make Ts reach more than 100 ℃ (see Zhang Tingyou, " tanning chemistry ", 2003, press of Sichuan University, P49-50).But these technology are not all effectively applied in industry.
The inventor uses the peculiar property of various environmental protective type chemical materials on the basis of comprehensive prior art, overcome the various defectives of THPS, makes cheap, high-performance environmentally-friendly type tanning agent.
Summary of the invention
The present invention be directed to the prior art shortcoming and defect, the environment-friendly type tanning agent of a kind of THPS of containing be provided, wherein will with the ingenious collocation of the various chemical materials additives of THPS, be prepared into soft plentiful, tanning agent that color is pure white.This tanning agent product has that perviousness is strong, the tanning agent of stable storing, water white transparency and free from extraneous odour, and shrinkage temperature can reach 83 ℃.
Tanning agent of the present invention is made up of following component:
Tetra methylol sulfuric acid phosphonium salt (THPS): 50-100 part;
Additive: 5-60 part;
Complexing agent: 6-50 part;
Edta salt: 1-10 part; With
Water: 10-100 part;
The proportioning of wherein said component is represented with parts by weight.
Preferably, the composition of each component of tanning agent of the present invention is counted with parts by weight:
Tetra methylol sulfuric acid phosphonium (THPS): 60-90 part;
Additive: 10-50 part;
Complexing agent: 10-30 part;
EDTA:1-5 part; With
Water: 10-60 part.
In above-mentioned tanning agent of the present invention, described additive is selected from N-Methyl pyrrolidone, D-sorbyl alcohol, D-glucose and Hydrocerol A, preferred N-Methyl pyrrolidone or D-sorbyl alcohol.
In the above-mentioned tanning agent of the present invention, wherein said complexing agent is the conventional complexing agent that uses in this area, preferred ethylene diamine tetra methylene phosphonic acid sodium (EDTMPS) or hexanediamine tetramethylene phosphonic acid sylvite (HDTMPA.K
6).
In above-mentioned tanning agent of the present invention, wherein said EDTA is YD 30 and verivate thereof, preferably uses the salt of YD 30, and preferred especially edta salt is EDTA Disodium or tetrasodium ethylenediamine tetraacetate.
Preferably, the additive described in the fur tanning agent according to the invention is N-Methyl pyrrolidone or D-sorbyl alcohol; Described complexing agent is ethylene diamine tetra methylene phosphonic acid sodium or hexanediamine tetramethylene phosphonic acid sylvite; Described EDTA is EDTA Disodium or tetrasodium ethylenediamine tetraacetate.
Employed various auxiliary agents in the tanning agent of the present invention comprise the Chemicals that additive, complexing agent and EDTA etc. all can use on the market to be sold.
Tanning agent of the present invention is a colourless transparent liquid.Tanning agent of the present invention has that perviousness is strong, the advantage of stable storing, water white transparency and free from extraneous odour, and its shrinkage temperature can reach 83 ℃.
Another object of the present invention has provided the preparation method of above-mentioned tanning agent, and this method may further comprise the steps:
(1) with 40-50 ℃ water that EDTA dissolving back is for use;
(2) under agitation; The additive and the complexing agent liquid of required proportioning are slowly added in the tetra methylol sulfuric acid phosphonium, under 25-35 ℃ temperature, stirred 10-30 minute; Then the above-mentioned EDTA aqueous solution is added wherein; Continue to keep temperature-resistant, stirred 40-60 minute, obtain the tanning agent of colourless transparent liquid shape;
Wherein in parts by weight, the composition of said each component is tetra methylol sulfuric acid phosphonium (THPS) 50-100 part, additive 5-60 part, complexing agent 6-50 part, EDTA1-10 part and water 10-100 part; The composition of preferred back tanning agent is tetra methylol sulfuric acid phosphonium (THPS) 60-90 part, additive 10-50 part, complexing agent 10-30 part, EDTA 1-5 part and water 10-60 part.
Employed water can be process water or softening water in the aforesaid method of the present invention, for improving the result of use of tanning agent of the present invention, preferably uses softening water, for example feedwater, zero(ppm) water or deionized water etc.
The operation of above-mentioned steps (2) can be carried out in the corrosion-resistant reaction vessel that chemical field is used always; For example; Described operation can be carried out in the reaction vessel of material manufacturings such as stainless steel, glass reinforced plastic, also can in the reaction vessel that has pottery or enamel lining, carry out; Preferred said operating in the reaction vessel that has pottery or enamel lining carried out; More preferably described reactor drum has temperature demonstration, temperature controlling system and whipping device; For example, described operating in the enamel stirring tank that has whisking appliance, TM and cooling system carried out.
Preferably, the operation of above-mentioned steps (2) is at room temperature carried out, and described room temperature typically refers to the temperature about 25 ℃.
Another object of the present invention has provided the application of tanning agent according to the invention, and this tanning agent can be applicable to the tanning of various furs, is specially adapted to the tanning of woolfell.The fur of using tanning agent tanning of the present invention is soft and full, color is pure white, extension property is good in length and breadth, and shrinkage temperature can reach 83 ℃, and can give certain flame retardant resistance.
Tanning agent of the present invention not only has above-mentioned advantage, and because wherein employed raw material is the industrial chemicals of environment-friendly type, can not pollute environment, and cheap, and the preparation method is simple, on environment protection and production cost, has the tangible market advantage.
Embodiment
Through specific examples the present invention is described in more detail below, the embodiment that provides only is used for example the present invention, but the protection domain that does not limit the present invention in any way.
The preparation of embodiment 1 tanning agent
1, with of the softening water dissolving of 1 part of EDTA Disodium with 25 parts 45 ℃;
2, tetra methylol sulfuric acid phosphonium (THPS) is placed the enamel stirring tank that has TM and cooling system for 60 parts; Open and stir; Slowly 30 parts of ethylene diamine tetra methylene phosphonic acid sodium (EDTMPS) are added reaction kettle, approximately after 10-15 minute 10 parts of N-Methyl pyrrolidone are slowly added reaction kettle, controlled temperature 25-35 ℃; Stirred 60 minutes, and obtained the tanning agent of colourless transparent liquid shape.
The preparation of embodiment 2 tanning agents
1, with of the softening water dissolving of 1 part of tetrasodium ethylenediamine tetraacetate with 40 parts 45 ℃;
2, tetra methylol sulfuric acid phosphonium (THPS) is placed the enamel stirring tank that has TM and cooling system for 75 parts; Open and stir; Slowly 15 parts of hexanediamine tetramethylene phosphonic acid sylvite (HDTMPA.K6) are added reaction kettle, approximately after 10-15 minute 10 parts of D-sorbyl alcohols are slowly added reaction kettle, controlled temperature 25-35 ℃; Stirred 60 minutes, and obtained the tanning agent of colourless transparent liquid shape.
The preparation of embodiment 3 tanning agents
1, with of the softening water dissolving of 5 parts of EDTA Disodiums with 10 parts 45 ℃;
2, tetra methylol sulfuric acid phosphonium (THPS) is placed the enamel stirring tank that has TM and cooling system for 60 parts; Open and stir; Slowly 20 parts of ethylene diamine tetra methylene phosphonic acid sodium (EDTMPS) are added reaction kettle, approximately after 10-15 minute 15 parts of N-Methyl pyrrolidone are slowly added reaction kettle, controlled temperature 25-35 ℃; Stirred 60 minutes, and obtained the tanning agent of colourless transparent liquid shape.
The preparation of embodiment 4 tanning agents
1, with of the softening water dissolving of 1 part of EDTA Disodium with 40 parts 45 ℃;
2, tetra methylol sulfuric acid phosphonium (THPS) is placed the enamel stirring tank that has TM and cooling system for 70 parts; Open and stir; Slowly 10 parts of hexanediamine tetramethylene phosphonic acid sylvite (HDTMPA.K6) are added reaction kettle, approximately after 10-15 minute 20 parts of N-Methyl pyrrolidone are slowly added reaction kettle, controlled temperature 25-35 ℃; Stirred 60 minutes, and obtained the tanning agent of colourless transparent liquid shape.
The preparation of embodiment 5 tanning agents
1, with of the softening water dissolving of 1 part of EDTA Disodium with 40 parts 45 ℃;
2, tetra methylol sulfuric acid phosphonium (THPS) is placed the enamel stirring tank that has TM and cooling system for 80 parts; Open and stir; Slowly 10 parts of hexanediamine tetramethylene phosphonic acid sylvite (HDTMPA.K6) are added reaction kettle, approximately after 10-15 minute 10 parts of N-Methyl pyrrolidone are slowly added reaction kettle, controlled temperature 25-35 ℃; Stirred 60 minutes, and obtained the tanning agent of colourless transparent liquid shape.
The preparation of embodiment 6 tanning agents
1, with of the softening water dissolving of 2 parts of EDTA Disodiums with 50 parts 45 ℃;
2, tetra methylol sulfuric acid phosphonium (THPS) is placed the enamel stirring tank that has TM and cooling system for 50 parts; Open and stir; Slowly 15 parts of ethylene diamine tetra methylene phosphonic acid sodium (EDTMPS) are added reaction kettle, approximately after 10-15 minute 8 parts of N-Methyl pyrrolidone are slowly added reaction kettle, controlled temperature 25-35 ℃; Stirred 60 minutes, and obtained the tanning agent of colourless transparent liquid shape.
The preparation of embodiment 7 tanning agents
1, with of the softening water dissolving of 1 part of tetrasodium ethylenediamine tetraacetate with 10 parts 45 ℃;
2, tetra methylol sulfuric acid phosphonium (THPS) is placed the enamel stirring tank that has TM and cooling system for 70 parts; Open and stir; Slowly 20 parts of ethylene diamine tetra methylene phosphonic acid sodium (EDTMPS) are added reaction kettle, approximately after 10-15 minute 20 parts of D-sorbyl alcohols are slowly added reaction kettle, controlled temperature 25-35 ℃; Stirred 60 minutes, and obtained the tanning agent of colourless transparent liquid shape.
The preparation of embodiment 8 tanning agents
1, with of the softening water dissolving of 1 part of EDTA Disodium with 25 parts 45 ℃;
2, tetra methylol sulfuric acid phosphonium (THPS) is placed the enamel stirring tank that has TM and cooling system for 80 parts; Open and stir; Slowly 10 parts of ethylene diamine tetra methylene phosphonic acid sodium (EDTMPS) are added reaction kettle, approximately after 10-15 minute 20 parts of D-sorbyl alcohols are slowly added reaction kettle, controlled temperature 25-35 ℃; Stirred 60 minutes, and obtained the tanning agent of colourless transparent liquid shape.
The preparation of embodiment 9 tanning agents
1, with of the softening water dissolving of 1 part of EDTA Disodium with 20 parts 45 ℃;
2, tetra methylol sulfuric acid phosphonium (THPS) is placed the enamel stirring tank that has TM and cooling system for 50 parts; Open and stir; Slowly 15 parts of ethylene diamine tetra methylene phosphonic acid sodium (EDTMPS) are added reaction kettle, approximately after 10-15 minute 8 parts of N-Methyl pyrrolidone are slowly added reaction kettle, controlled temperature 25-35 ℃; Stirred 60 minutes, and obtained the tanning agent of colourless transparent liquid shape.
The application example of embodiment 10 tanning agents
A, tanning (is example with wet sour sheepskin)
In rotary drum; Add the water (liquor ratio 1: 10) that is equivalent to 10 times of sour sheepskin (wet pelt) weight, add NaCl 50g/L, controlled temperature 35-38 ℃ with respect to the water yield in the system; Rotate after 5-10 minute, add the environment-friendly type woolfell tanning agent 5-6ml/L (with respect to the water yield in the system) of embodiment 5.Drop in the rotary drum after then sour woolfell being beaten the limit, rotate after 4-6 hour, begin to regulate owse pH value (dividing 0.5 hour at interval four times), after the pH value reaches 6.7, stop drum and spend the night with 5% sodium carbonate solution.After intermittently stirring 20-30 minute next day, surveying the pH value is 6.7, begins skin, takes horse and leaves standstill.
B, oxygen are washed
In rotary drum; The water (liquor ratio is 1: 10) that adds 10 times of the weight of the wet woolfell be equivalent to above-mentioned tanning; About 35 ℃ of controlled temperature; With respect to the water yield in the system, add salt (NaCl) 30g/L, prestige
protects a mao agent M-60 (general rich Company products) 2ml/L and prestige
is floated toner H-21 (general rich Company products) 4g/L, the wet woolfell that adds above-mentioned tanning then carries out oxygen and washes in rotary drum; Rotated about about 15 minutes; Add ydrogen peroxide 50 (30%) 6-8ml/L (with respect to the water yield in the system), intermittently rotated 6-8 hour, control pH value 7.5-8.0; Go out skin; Control water, dries after 20 minutes with Warm Wash naturally.
Can know that through above-mentioned application this tanning agent is easy to use, simple to operate, after the tanning dermatotome soft plentiful, color is pure white.
Below described embodiment of the present invention in detail, can do a lot of improvement and variation obviously for a person skilled in the art and can not deviate from essence spirit of the present invention.All these variations and improvement are all within protection scope of the present invention.